To prepare an environmental friendly high-solid coatings an acrylic resin containing 80% of solid content was synthesized by addition polymerization of caprolactone acrylate, n-butyl acrylate, ethyl methacrylate, and 2-hydroxyethyl methacrylate. The conversion was 78~93% and the prepared resin's physical properties are as follows: viscosity, 212~3424cps: Mn 1740~2400. There was a trend that viscosity and molecular weight of the resin increased with Tg, but no direct proportionality was observed.

The objectives of this study is to investigate the optimum reaction conditions and to identify the product formula in the synthesis of a silicone/acrylic resin that curing in moisture at room temperature. By the addition polymerization of monomers, n-butyl acrylate, methyl methacrylate, n-butyl methacrylate, and 3-methacryloxypropyltrimethoxysilane. a quarter polymer was obtained. Among various initiators investigated in this study, 2.2'-azobisisobutyronitrille was found to be the most suitable initiator. The optimum reaction conditions found in this study are 70 wt% of initial solvent amount, 120 minutes of dropping time, 3 times of initiator addition, 82~105℃ of reaction temperature, and 8 hrs of reaction time. Also, number average molecular weight of 11700~33100 and molecular weight distribution of 1.81~3.44 were obtained.

지질과학 분야에서 암석의 생성 시기, 지각과 맨틀 진화연구의 기초자료로 활용되는 Sr 동위원소비는 열이온화 질량분석기(thermal ionization mass spectrometry, TIMS) 혹은 다검출기 유도결합 플라즈마 질량분 석기(multi-collector plasma ionization mass spectrometry, MC-ICP-MS)와 같은 질량분석기를 이용하여 측정할 수 있다. 이 기술보고에서는, Sr 동위원소비 측정시, 원소의 불완전한 화학적 분리가 Sr 동위원소비의 참값 (true value)에 어떤 영향을 미치는지를 비교하였다. 실험에는 상업용 레진, NBS987(NIST SRM987) Sr 동위 원소 표준물질 그리고 일본지질조사소의 암석표준시료 JG1a, JB3, JA1를 이용하였다. 비교실험 결과, NBS987 Sr 동위원소 표준시료, 일본지질조사소의 암석표준시료 JG1a, JB3, JA1 모두 불완전한 분리에 의해 Rb이 남 아있는 경우 87Sr/86Sr의 측정값이 변하는 것이 명확하게 관찰된다. 이는 질량분석기 특히 MC-ICP-MS로 동위 원소비를 측정하고자 하는 경우, 동종동위원소의 간섭에 대한 보정에도 불구하고 측정값은 참값에서 벗어나 므로 완전한 분리가 중요한 인자임을 지시해준다. 그러므로 MC-ICP-MS를 이용한 Sr 동위원소비 측정결과를 보고할 때는, 동종동위원소에 의한 영향을 판단할 수 있도록 Sr의 동위원소 전체의 측정강도와 더불어 85Rb의 측정강도도 함께 보고돼야 할 것이다.

금속을 함유하고 있는 산업폐자원과 관련한 재활용 기술을 개발하기 위해 다양한 접근이 시도되고 있으며, 그 중에서 유리는 미생물로 분해되지 않기 때문에 매립은 적합하지 않아 폐유리의 재활용에 대한 관심은 증대되고 있다. 따라서 본 논문에서는 폐유리를 잔골재로 사용하고 폐유리의 중금속 용출을 억제하기 위한 킬레이트 수지를 혼입함으로써, 차폐 채움재의 강도, 건조수축, 알칼리-실리카반응, 중금속 용출 등을 평가하여 폐유리를 경제적이며 환경 친화적인 차폐 채움재로서 활용하기 위한 기초자료를 제시하고자 한다. 시험결과, 폐유리를 잔골재로 사용하였을 경우 강도 발현에 효과적이었으며, 킬레이트 수지를 혼입하였을 경우 강도 발현에 영향이 있는 것으로 나타났다. 또한 킬레이트 수지를 혼입하였을 경우 건조수축의 개선에는 효과적이었으나 알칼리-실리카반응에 영향을 미치는 것으로 나타났다. 중금속 용출 시험결과, 한국 KSLP 시험법에서는 중금속 용출 허용 기준치를 모두 만족하였으나, 납의 경우 미국 ANSI 67-2007a의 허용 기준치를 초과하여 이에 대한 추가적인 연구가 진행되어야 할 것으로 판단되었다.

This study investigated the applicability of synthetic resins as neutron shielding aggregates in cementitious materials with SEM analysis. Synthetic resins contain lots of hydrogen atoms, which is effective in neutron shielding by an elastic scattering because its mass is almost the same as that of the neutron. The SEM results showed that the binding force between HDPE/PP particles and cement matrix is very week compared to that of UPE particles so that additional treatment such as surface reforming should be needed.

This study was performed to investigate the feasibility of ion-exchange resins as soil amendment. To select resins, weinvestigate four kinds of ion exchange resins, which ions have the most adsorption efficiency of ions (N+, PO4−, K+). Inthe Cation (H+) vs Anion (OH−)=1:2 (w:w), it showed that the highest N, P, K adsorption efficiency was about 80%and reached pH 6~7 & EC 1~2dS/m after 20min. The ability to maintain ion adsorption, it was investigated that thegentle curve of the residual ion ratio of nitrate nitrogen, available phosphorus, exchangeable potassium was maintained.On the other hand, the control (Slow release fertilizer) was significantly reduced under artificial rainfall conditions. Inaddition, the results of three consecutive crop test were showed that the growth of crops decreased 41.8% than the earlygrowth in the control group, whereas decreased 8.3% in the treatment group (ion exchange resins). According to the resultsof soil analysis, it was reduced that the fertilizer ingredients (N 94%, P 74.5%, K 98.6%) in the control and reducedfertilizer ingredients (N 64%, P 60.3%, K 58.4%) in the treatment. Overall, it was estimated that the Ion-exchange resinscould be used as a soil amendment.

건조물문화재의 부식 및 노후화에 대한 보존수리는 원형유지를 기본원칙으로 하며, 수리로 인해 인위적인 훼손을 가하는 과오를 범해서도 안 된다. 따라서 합성수지를 이용한 보존처리방법이 부각되어지고 있다. 본 연구의 목적은 합성수지로 보강한 사각단면 목재의 휨 성능에 관한 연구로서 합성수지의 보강길이, 보강면적비율, 합성수지 재료강도, 보강위치를 변수로 하여 총 11개의 시험체를 제작하여 실험하였다. 이 연구의 결과는 목재의 휨 보강재로 합성수지의 보강효과가 있는 것으로 나타났으며, 사용 가능성을 확인할 수 있었다.

The adsorption of the anionic surfactants, sodium lauryl sulfate (SLS) and sodium dodecylbenzene sulfonate (SDBS) anion surfactants from aqueous solutions with nonionic resins, Amberlite XAD-2, XAD-4 and XAD-7 at temperatures in 15∼45℃ range was studied. Several adsorption isotherm models were used to fit the experimental data. The best results were obtained with the Redlich-Peterson equation and the Freundlich model provided remarkably good fits. For a particular resin at a particular temperature, SDBS was more extensively adsorbed than SLS. The highest adsorption were obtained with XAD-4 resin and the specific surface area of the resins plays a major role in adsorption of the surfactants. Estimations of the isosteric heat of adsorption were indicative of an exothermic process, and their magnitudes manifested a physisorption process.