Energy and environmental are always two major challenges for the sustainable development of the modern human being. For avoiding the serious environmental pollution caused in the fabrication process of porous carbon, a popular energy storage material, we reported a facile, green and activating agent free route hereby directly carbonizing a special biomass, Glebionis coronaria. A nitrogen doped hierarchical porous carbon with a specific surface area of up to 1007 m2 g−1 and a N doping content of up to 2.65 at.% was facilely fabricated by employing the above route. Benefiting from the peculiarly hierarchical porous morphology, enhanced wettability and improved conductivity, the obtained material exhibits superior capacitance performance, which capacitance reaches up to 205 F g−1 under two-electrode configuration, and no capacitance loss is observed after 5000 cycles. Meanwhile, the capacitance retention of the obtained material arrives up to 95.0% even under a high current density of 20 A g−1, illuminating its excellent rate capability. The fabricated nitrogen-doped hierarchical porous carbon with larger capacitance than commercial activated carbon, excellent rate capability and cycle stability is an ideal cost-efficient substitution of commercial activated carbon for supercapacitor application.

Microtextural and surface chemical heterogeneities of activated carbons (AC) have been studied to see their distinctive role for the adsorption of CO2, CO and N2 at 25 °C and up to 850 Torr. Not only the microtextural properties influence the adsorption of the gases, particularly CO2, but the chemical surface heterogeneity also plays a significant role for CO2 adsorption. The volume of ultramicropores < 7 Å is of predominantly importance in high CO2 adsorption at pressures above 30 Torr. However, the average size of micropores and their size distribution, and the chemical surface heterogeneity are much more critical at the Henry’s law region (< 30 Torr). The latter could be well characterized by the amount and Henry constant of CO2 adsorption at the low pressures, the Toth model parameters, the change in CO2/ CO and CO2/ N2 selectivities with respect to pressure, the amount of CO from the thermal decomposition, and the direct probing of very strong basicity sites using a technique that is the temperature-programmed desorption of CO2 adsorbed. All of them are consistent with the difference in the energetic nonuniformity between ACs studied, except for the last measure whose results could be reasonably explained when combining with the microtextural heterogeneity.

Macro-porous carbon foams are fabricated using cured spherical phenolic resin particles as a matrix and furfuryl alcohol as a binder through a simple casting molding. Different sizes of the phenolic resin particles from 100– 450 μm are used to control the pore size and structure. Ethylene glycol is additionally added as a pore-forming agent and oxalic acid is used as an initiator for polymerization of furfuryl alcohol. The polymerization is performed in two steps; at 80oC and 200oC in an ambient atmosphere. The carbonization of the cured body is performed under Nitrogen gas flow (0.8 L/min) at 800oC for 1 h. Shrinkage rate and residual carbon content are measured by size and weight change after carbonization. The pore structures are observed by both electron and optical microscope and compared with the porosity results achieved by the Archimedes method. The porosity is similar regardless of the size of the phenolic resin particles. On the other hand, the pore size increases in proportion to the phenol resin size, which indicates that the pore structure can be controlled by changing the raw material particle size.

본 연구에서는 구리 이온(Cu2+ ion) 제거를 위한 산화철(Fe3O4)/다공성 탄소 복합체를 합성하였으며, 이를 바탕으로 구리 이온 제거에 대한 특성 평가를 실시하였다. SEM, XRD 분석을 진행하여 수열합성(hydrothermal) 반응을 이용한 산화철/다공성 탄소 복합체의 형태와 구조를 확인하였다. BET 분석을 통해 비표면적과 기공 크기를 확인하였으며, UV-vis 장비를 통해 성능 평가를 실시하여 자성이 있는 Fe3O4와 다공성 탄소와의 시너지효과를 통해 액체 상태에서 존재하는 구리 이온을 제거할 수 있는 가능성을 제시하였다.

The present work introduces a new method for the recycling of waste flocculation sludge to prepare electrode materials for supercapacitor. Hazardous azo dye was removal from textile dying wastewater by a new chitosan-based flocculant, and the generated dye sludge flocs was used as a nitrogen-containing precursor for the fabrication of N-doped carbon materials. The influence of azo dye on specific surface areas, nitrogen content, pore evolution of the resulting products and their electrochemical performance were investigated in detail. The results demonstrated a dual role of azo dye worked as both a nitrogen resource and pore-forming agent. The resulting N-doped carbon nanosheets derived from azo dye flocs demonstrated high electrochemical capacitance and good stability for supercapacitor electrode, which is attributed to the unique nitrogen doping, higher specific surface area and efficient charge transfer ability.

Because of their excellent stability and highly specific surface area, carbon based materials have received attention as electrode materials of electrical double-layer capacitors(EDLCs). Biomass based carbon materials have been studied for electrode materials of EDLCs; these materials have low capacitance and high-rate performance. We fabricated tofu based porous activated carbon by polymer dissolution reaction and KOH activation. The activated porous carbon(APC-15), which has an optimum condition of 15 wt%, has a high specific surface area(1,296.1 m2 g−1), an increased average pore diameter(2.3194 nm), and a high mesopore distribution(32.4 %), as well as increased surface functional groups. In addition, APC has a high specific capacitance(195 F g−1) at low current density of 0.1 A g−1 and excellent specific capacitance(164 F g−1) at high current density of 2.0 A g−1. Due to the increased specific surface area, volume ratio of mesopores, and surface functional groups, the specific capacitance and high-rate performance increased. Consequently, the tofu based activated porous carbon can be proposed as an electrode material for high-performance EDLCs.

Zn-ion supercapacitors (ZICs) show high energy densities with long cycling life for use in electronic devices. Porous Zn electrodes as anodes for ZICs are fabricated by chemical etching process using optimized conditions. The structures, morphologies, chemical bonding states, porous structure, and electrochemical behavior are examined. The optimized porous Zn electrode shows a root mean square of roughness of 173 nm and high surface area of 153 μm2. As a result, ZIC using the optimized porous Zn electrode presents excellent electrochemical performance with high specific capacitance of 399 F g−1 at current density of 0.5 A g−1, high-rate performance (79 F g−1 at a current density of 10.0 A g−1), and outstanding cycling stability (99 % after 1,500 cycles). The development of energy storage performance using synergistic effects of high roughness and high surface area is due to increased electroactive sites by surface functionalization of Zn electrode. Thus, our strategy will lead to a rational design and contribute to next-generation supercapacitors in the near future.

다공성 분리막은 입자성 물질을 제거하는데 산업적으로 다양하게 응용되고 있다. 기존 다공성 분리막 제작 방법 과 다르게, 용액퍼짐 상분리법은 매우 간단하게 기공을 형성할 수 있다. 먼저 지지층으로 메쉬 위에 물을 적신 후, 물과 혼합 되지 않은 용매에 폴리설폰 용액을 흘려준다. 이때 물과 혼합되지 않은 용매는 쉽게 기화되어 폴리설폰은 얇은 막으로 만들어지게 된다. 기공을 형성하기 위해 폴리설폰 용액에 물과 혼합할 수 있는 물질을 넣게 되면, 넣어주는 농도 비율에 따라 기공크기를 조절할 수 있게 된다. 막의 두께는 쉽게 용액의 농도로 조절이 된다. 다공성 분리막은 메쉬의 형성을 그대로 유지하고 있어 3차원 구조체를 형성하는데 매우 유용하다. 본 연구에서 제시된 용액 퍼짐 상분리법은 매우 낮은 생산단가와 쉬운 공정조절에 의해 기존 분리막에 비해 높은 가격경쟁력을 가질 수 있는 특징을 보이고 있다.

To improve the performance of carbon nanofibers as electrode material in electrical double-layer capacitors (EDLCs), we prepare three types of samples with different pore control by electrospinning. The speciments display different surface structures, melting behavior, and electrochemical performance according to the process. Carbon nanofibers with two complex treatment processes show improved performance over the other samples. The mesoporous carbon nanofibers (sample C), which have the optimal conditions, have a high sepecific surface area of 696 m2 g−1, a high average pore diameter of 6.28 nm, and a high mesopore volume ratio of 87.1%. In addition, the electrochemical properties have a high specific capacitance of 110.1 F g−1 at a current density of 0.1 A g−1 and an excellent cycling stability of 84.8% after 3,000 cycles at a current density of 0.1 A g−1. Thus, we explain the improved electrochemical performance by the higher reaction area due to an increased surface area and a faster diffusion path due to the increased volume fraction of the mesopores. Consequently, the mesoporous carbon nanofibers are demonstrated to be a very promising material for use as electrode materials of high-performance EDLCs.

Dual porous structures are observed for the first time on a metallic Cu surface underneath anodic Cu oxide by the application of an anodizing voltage to Cu in oxalic acid. The as-prepared porous Cu surface contains macropores of less than 1 μm diameter and mesopores of about tens of nanometers diameter with circular shapes. The size and density (number of pores/area) of the macropores are dependent on the applied voltage. It is likely that the localized dissolution (corrosion) of Cu in oxalic acid under the anodizing voltages is responsible for the formation of the mesopores, and the combination of a number of the mesopores might create the macropores, especially under a relatively high anodizing voltages or a prolonged anodizing time. The variations of pore structure (especailly macropores) with applied voltage and time are reasonably explained on the basis of the proposed mechanism of pore formation.

In this study, freeze drying of a porous Ni with unidirectionally aligned pore channels is accomplished by using a NiO powder and camphene. Camphene slurries with NiO content of 5 and 10 vol% are prepared by mixing them with a small amount of dispersant at 50℃. Freezing of a slurry is performed at -25℃ while the growth direction of the camphene is unidirectionally controlled. Pores are generated subsequently by sublimation of the camphene during drying in air for 48 h. The green bodies are hydrogen-reduced at 400℃ and then sintered at 800℃ and 900℃ for 1 h. X-ray diffraction analysis reveals that the NiO powder is completely converted to the Ni phase without any reaction phases. The sintered samples show large pores that align parallel pores in the camphene growth direction as well as small pores in the internal walls of large pores. The size of large and small pores decreases with increasing powder content from 5 to 10 vol%. The influence of powder content on the pore structure is explained by the degree of powder rearrangement in slurry and the accumulation behavior of powders in the interdendritic spaces of solidified camphene.