The 2-packaged polyurethane coatings were synthesized, blending pheylmodified polyesters(of which synthetic methods were reported in the previous paper), Desmodur L-75(polyisocyanate wide1y used for coatings), wetting-dispersing agent, white pigment. etc. A variety of coating properties were tested for the coating treatment polyurethane coationgs. Compared with conventional 2-packaged polyure-thane coating, abrasion resistance and lightness index difference of the ones synthesized in the present work were somewhat decreased, but the coating properties such as hardness, gloss specular, cross hatch adhesion. etc. were improved. Especially, resistance against chemical reagents and salt were strikingly improved. In addition. the coationgs had short drying time and long pot-life. This shows that the coationgs are appropriate for rapid drying coatings.

Oil and fats has been using as the important raw materials in the coating industry from ancient time to date. This article was prepared with the aim of helping to the forward development trend for coating uses of oil and fats, as understand together the history using oil and fats for coatings, composition and classification coatings, types and composition of oil and fats using for coatings nowaday, how to use oil and fats for coating, film for coatings, film forming mechanism.

솔-제법에 의한 고분자솔 제조를 위하여 금속 알콕사이드에 β-diketonate(DKT)기의 유기 리간드를 치환시켜 만든 전구체를 합성한 결과, 가수분해와 축합 반응의 속도 조절이 가능하였고, 이를 이용하여 코팅에 적합한 nm단위의 입자 크기를 갖는 알루미나, 티타니아 솔을 제조하고 그 물성을 파악하였다. 코팅에 적합한 알루미나 솔의 최적조건은 알콕사이드 1몰당 물 1몰, 산 0.3-0.4몰이었다. 티타니아 솔의 제조시는 물/알콕사이드의 몰비가 1이고, 산의 양은 치환수에 따라 달라 1개와 2개 치환된 전구체의 경우 1목의 알콕사이드당 각각 0.25, 0.20몰 이하였다. Dynamic light scattering 장치를 이용하여 제조한 솔의 평균 입자 크기를 측정한 결과 수 nm단위의 미세한 입자를 갖고 있었다. 슬라이드 글라스 위에 코팅하여 450˚C에서 소결한 막을 SEM으로 관찰한 결과 알루미나와 타타니아의 경우 각각 4-4.5μ m, 2-2.5μ m두께의 매끄럽고 균열이 없는 막이 형성되었음을 알 수 있었다. 이때의 입자 크기는 TEM사진을 통하여 알 수 있었으며 티타니아의 경우 수 nm에서 최대 30nm, 알루미나는 1-2nm이하 심지어 수 Å정도의 입자들로 이루어졌음을 관찰하였다. 또한 회절무늬 분석 결과 알루미나는 γ구조, 티타니아는 anastase결정임을 알 수 있었다.

베아링강(AISI S2100) 위에 TiCi4, N2,H2,그리고 Ar의 기체혼합계를 이용하여 플라즈마화학증착법으로 내마모 TiN증착층을 얻었다. 증착된 TiN층 내의 잔류 CI에 의한 결정성, 미소경도, 접착력, 그리고 마모특성에 대해 연구하였다. TiN 중착층은 좋은 내마모성을 가지고 있었으며, TiN의 기계적 특성은 잔류CI함량이 증가할때 나빠졌다. 마모측정결과 마모면의 trailing edge에 인장응력이 걸려 많은 crack이 관찰되엇다.

Plasma 용사된 단열피복에 내재하는 기공의 크기, 형상 및 분포는 피복층 자체의 물성에 지대한 영향을 미치므로 이를 용사변수에 따라 조사하였다. MgO 안정화 지르코니아 피복시 도입되는 기공은 미세기공 외에 각각 생성기구가 다른 조대한 기공 즉 구형과 불규칙한 기공, 그리고 crack으로 구성되었다. 용사거리에 따라 기공의 생성과정과 특성이 변하였으며 Plasma 전류 및 가스 유량의 증가에 의해서 기공도는 감소하는 경향을 보였다. Plasma 가스가 N2인 경우가 Ar보다 더 높은기공도를 보였고 전체적으로 단열피복의 기공도는 10~18%였다. Scratch test로 측정된 단열피복층의 상대적인 경도는 기공도와 높은 상관관계를 보였다.

Investigated were relationships between deteriorated coating surface conditions of laboratory test panels determined by image processing software and coating impedance data collected with Electrochemical Impedance Spectroscopy (EIS). This study demonstrates that estimation of log(Rpo)at a certain deterioration stage is feasible via field image processing alone without running in-situ EIS measurements and going through time consuming EIS fitting analysis.

To promote applicability of steel bridge coating diagnosing system developed and used by Korea Expressway Corporation, problems found in deterioration degree evaluation standard for steel bridge coatings were revised in this study. Suitability of revised evaluation standard was confirmed by field survey.

Manufactures of automotive repair finishes are tending to reduce more and more the level of volatile organic compounds (VOCs) in their paint processes in order to comply with increasingly strict environmental legislation. The production of high solids paints is a way to solve this problem. However, the application of high-solids paints is limited primarily by the viscosity of resin which is strongly related to painting ability: the higher solid content, the lower desired property. In this study, alkyl copolymer with low viscosity was synthesized by the introduction of the monomers with long-side chains and functional groups which improve flexibility and cross-linking density, respectively. The solid content of the paint prepared with the synthesized resin was 80 wt% and its VOCs was reduced by 20%, compared to the commercialized paint. Also, the physical and mechanical properties of coatings on steel sheets were similar to commercialized one.

가식성 코팅 처리가 신선절단 배의 품질특성에 미치는 영향을 조사하기 위하여 단백질 소재인 albumin, 탄수화물 소재인 dextrin, 지질 소재인 SPE(Sucrose polyester) 그리고 WSF(Whole soy flour)를 코팅재료로 선택하여 일정 농도로 조제한 코팅용액을 배를 dipping하여 코팅처리 한 후 에서 10일간 저장하면서 품질변화를 측정하였다. 중량감소율은 모든 코팅 처리구에서 대조구에 비해 억제되었다. 배의 경우는