The automotive industry has focused on the development of metallic materials with high specific strength, which can meet both fuel economy and safety goals. Here, a new class of ultrafine-grained high-Mn steels containing nano-scale oxides is developed using powder metallurgy. First, high-energy mechanical milling is performed to dissolve alloying elements in Fe and reduce the grain size to the nanometer regime. Second, the ball-milled powder is consolidated using spark plasma sintering. During spark plasma sintering, nanoscale manganese oxides are generated in Fe-15Mn steels, while other nanoscale oxides (e.g., aluminum, silicon, titanium) are produced in Fe-15Mn-3Al-3Si and Fe-15Mn-3Ti steels. Finally, the phases and resulting hardness of a variety of high-Mn steels are compared. As a result, the sintered pallets exhibit superior hardness when elements with higher oxygen affinity are added; these elements attract oxygen from Mn and form nanoscale oxides that can greatly improve the strength of high-Mn steels.

The composition of martensite transformation in NiAl alloy is determined using pure nickel and aluminum powder by vacuum hot press powder metallurgy, which is a composition of martensitic transformation, and the characteristics of martensitic transformation and microstructure of sintered NiAl alloys are investigated. The produced sintered alloys are presintered and hot pressed in vacuum; after homogenizing heat treatment at 1,273 K for 86.4 ks, they are water-cooled to produce NiAl sintered alloys having relative density of 99 % or more. As a result of observations of the microstructure of the sintered NiAl alloy specimens quenched in ice water after homogenization treatment at 1,273 K, it is found that specimens of all compositions consisted of two phases and voids. In addition, it is found that martensite transformation did not occur because surface fluctuation shapes did not appear inside the crystal grains with quenching at 1,273 K. As a result of examining the relationship between the density and composition after martensitic transformation of the sintered alloys, the density after transformation is found to have increased by about 1 % compared to before the transformation. As a result of examining the relationship between the hardness (Hv) at room temperature and the composition of the matrix phase and the martensite phase, the hardness of the martensite phase is found to be smaller than that of the matrix phase. As a result of examining the relationship between the temperature at which the shape recovery is completed by heating and the composition, the shape recovery temperature is found to decrease almost linearly as the Al concentration increases, and the gradient is about -160 K/ at% Al. After quenching the sintered NiAl alloys of the 37 at%Al into martensite, specimens fractured by three-point bending at room temperature are observed by SEM and, as a result, some grain boundary fractures are observed on the fracture surface, and mainly intergranular cleavage fractures.

In this paper, a new Co10Fe10Mn35Ni35Zn10 high entropy alloy (HEA) is identified as a strong candidate for the single face-centered cubic (FCC) structure screened using the upgraded TCFE2000 thermodynamic CALPHAD database. The Co10Fe10Mn35Ni35Zn10 HEA is fabricated using the mechanical (MA) procedure and pressure-less sintering method. The Co10Fe10Mn35Ni35Zn10 HEA, which consists of elements with a large difference in melting point and atomic size, is successfully fabricated using powder metallurgy techniques. The MA behavior, microstructure, and mechanical properties of the Co10Fe10Mn35Ni35Zn10 HEA are systematically studied to understand the MA behavior and develop advanced techniques for fabricating HEA products. After MA, a single FCC phase is found. After sintering at 900℃, the microstructure has an FCC single phase with an average grain size of 18 μm. Finally, the Co10Fe10Mn35Ni35Zn10 HEA has a compressive yield strength of 302 MPa.

Harmonic structure materials are materials with a core–shell structure having a shell with a small grain size and a core with a relatively large grain size. They are in the spotlight because their mechanical properties reportedly feature strength similar to that of a sintered powder with a fine grain size and elongation similar to that of a sintered powder with a coarse grain size at the same time. In this study, the tensile properties, microstructure, and stretchflangeability of harmonic structure SUS304L made using powder metallurgy are investigated to check its suitability for automotive applications. The harmonic powders are made by mechanical milling and sintered using a spark plasma sintering method at 1173 K and a pressure of 50 MPa in a cylindrical die. The sintered powders of SUS304L having harmonic structure (harmonic SUS304L) exhibit excellent tensile properties compared with sintered powders of SUS304L having homogeneous microstructure. In addition, the harmonic SUS304L has excellent stretch-flangeability compared with commercial advanced high-strength steels (AHSSs) at a similar strength grade. Thus, the harmonic SUS304L is more suitable for automotive applications than conventional AHSSs because it exhibits both excellent tensile properties and stretch-flangeability.

In this study, as high temperature performance capable thermoelectric materials was manufactured by powder metallurgy.The as-casted Fe-Si alloy was annealed for homogenization below for 3 h. Due to its high brittleness, the cast alloy transformed to fine powders by ball-milling, followed by subsequent compaction (hydraulic pressure; 2 GPa) and sintering (, 12 h). In order to precipitate , heat treatment was performed at with varying dwell time (7, 15 and 55 h). As a result of this experiment thermoelectric phase was quickly transformed by powder metallurgical process. There was not much change in powder factor between 7h and 55h specimens.

The bi-materials composed of and its composite reinforced with SiC particles were prepared by ball-milling and subsequent sintering process. The size of powder in Al-Mg/SiCp mixture decreased with increasing ball-milling time, it was saturated above 30 h when the ball and powder was in the ratio of 30 to 1. Both powders mixture and mixture were compacted under a pressure of 350MPa and were bonded by sintering at temperatures ranging from 873K to 1173K for 1-5h. At 873k, the sound bi-mate-rials could not be obtained. In contrast, the bi-materials with the macroscopically well-bonded interface were obtained at higher temperatures than 873K. The length of well-bonded interface became longer with increasing temperature and time, indicating the improved contact in the interface between unreinforced Al-Mg part and Al-Mg/SiCp composite part. The relative density in the bi-materials increased as the sintering temperature and time increased, and the bi-materials sintered at 1173K for 5h showed the highest density.

ABS sensor ring has been manufactured by powder metallurgy (P/M) method using 400 series ferrite stainless steel. The results are following. It is supposedly sufficient to use for control computer due to good experimental results of magnetic characteristics. Compared with sensor ring made by iron, 400 series ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. Thus the decreasing production process has been obtained. As a result mechanical characteristics of hardness and tensile test, 400 series ferrite stainless steel shown a good endurance when it is combined to constant velocity joint(C/V), and has a good hardness properties endurable to sand and pebble impact. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition.

분말야금법으로 제조된 Cu-7.5Ni-5Sn 합금의 용체화 및 시효 열처리 조건에 따른 기계적 특성의 변화를 관찰하였다. As-received 상태의 Cu-7.5Ni-5Sn 합금을 시효한 경우에는 시효 20분 후에 γ' 상의 석출에 의한 강도 증가를 나타내는데 반해, 재용체화 처리된 시편에서는 시효 수십초부터 스피노달 분해에 의한 급격한 강도의 증가를 나타내고 있다. 그러나 전체적인 인장강도는 재용체화 처리를 행한 경우에 비해 as-received 상태에서 등온 시효한 경우가 더욱 우수한 것으로 나타났다. 이러한 현상은 재용체화 처리에 의한 결정립 성장에 기인한 것으로 사료된다. As-received 상태의 Cu-7.5Ni-5Sn 합금을 장시간 시효하게 되면 결정립계에 불연속 석출물이 생성되었으며, 이러한 불연속 석출물의 생성과 성장은 열처리 조건에 영향을 받는 것으로 관찰되었으며, 합금의 최종 기계적 성질에 크게 영향을 미치는 것으로 판단된다.

원소 분말을 합성하여 Ti5SI3 화합물을 합성하는 방법을 연구하였다. 합성법으로서는 기본적으로 반응소결법을 사용하였으며, 치밀화를 위하여는 유사-열간 정수압 성형법(PHIP, pseude-hot isostatic pressing)을 사용하였다. 반응소결법에서는 분말의 입도, 반응온도 및 유지시간이 소결밀도에 영향을 주었으며, PHIP법에 의한 치밀화에서는 압력 및 유지 간이 주요 변수로 사용되었다. 이들 변수중 미세한 입도와 유지시간이 기공을 감소시켰다. 또한 Cu의 첨가 영향을 연구하였는데, 약 6wt%이내의 Cu 첨가는 밀도 향상에 좋은 영향을 미쳤다. 반응소결 및 PHIP를 통해 Ti5SI3 -Cu의 상대밀도를 약 99%까지 높일 수 있었으며, 이때 Cu의 효과는 감도지수 부합됨을 확인하였다.