This study was to investigate the firing method of limestone in Joseon Dynasty, and analyze the physical·chemical properties of lime mortars in Joseon Dynasty. This study was to manufacture and evaluate the firing experiment and mortar of Limestone by each sort in order to reproduce the traditional lime mortars in Joseon Dynasty, and investigate the behavior to improve physical properties according to the firing method of Limestone. This study has found out that there were screening criteria and standard of appropriate firing temperature about the Limestone in Joseon Dynasty. Accordingly, this study was to improve its strength through various additives and mixture. In particular, in case of Limestone, the black and blue Limestone were preferred, and most of domestic Limestones were low grade Limestone including the clay and took ivory white or blue with low whiteness. This study has shown that the low grade Limestone was mined by the surface mining compared with the high grade Limestone as underground mining method, and could be used because it was easy to mine relatively and there was possibility that Natural Hydraulic Lime(NHL) was used with the traditional lime mortars in Joseon Dynasty.

This study was conducted to improve the economy, quality, and load of Soil paving concrete by using waste materials such as Oystery and Dolomitic to solve strength reduction and durability reduction caused by hardening agents in Korea. According to the results of the study, for the curing expenses, the Fine part agreement (FC) and the Furnace slag power lower (BS) are 5:5, It was possible to verify that the best results were obtained in terms of the quality of cement mortar when the natural organic lime and dolomitic lime were mixed at a ratio of 5:5.

본 연구는 남한산성 한봉성 여장에 사춤으로 사용된 석회 모르타르를 분석하여 조선시대에 사 용된 석회의 광물학적 특성을 파악하고자 하였다. 편광현미경 관찰 결과 여장의 모르타르는 기질에 석영, 장석, 운모, 휘석과 불투명 광물을 함유하고 있으며 XRD 분석을 통해 점토 광물인 녹니석, 카올 린을 추가로 확인하였다. 입도 분석 결과 시료의 입도 분포가 넓고 크기가 균일하지 않으며 입도의 60%가 모래영역에 해당되었다. XRF 분석 결과 석회의 주성분인 Ca은 8.71-11.18%로 나타났으며 토 양에서 확인되는 SiO2, Al2O3, Fe2O3가 주요 성분으로 확인되었다. TG-DTA 분석 결과 약 750℃ 부근에 서 탄산칼슘의 탈탄산반응으로 인한 흡열피크와 약 10%의 중량감소율을 확인하였으며, SEM을 통한 미세조직 관찰 결과 조밀하게 응집된 비정질, 능면상의 방해석 결정이 관찰되었다. 이를 바탕으로 여장의 사춤재는 석회와 토양이 혼합된 모르타르이며 여장의 위치나 사용부위에 따른 광물 조성 차이는 보 이지 않으므로 당시 한봉성 여장은 동일한 재료와 기법을 사용하여 개축된 것으로 판단된다.

Limestone powder can be used for concrete as a partial replacement of Portland cement so that concrete becomes more environment-friendly construction material. One of the great applications of limestone powder added cement concrete might be a cement concrete pavement since the concrete pavement consumes massive quantity of Portland cement. However, it has been reported recently that Alkali-Silica Reaction (ASR) occurs on the cement concrete pavement causing a serious damage. This study investigates the resistance of limestone powder added cement mortar to ASR. The mortar used very high reactive silicious aggregate for accelerated ASR. Experimental procedures followed ASTM C 1260 and variables included different replacement levels of limestone powder in the mortar mix.

최근 생태․친환경 건축이 화두로 등장하면서 친환경 건축재료인 점토벽돌과 공기의 흐름과 수분의 이동이 가능한 석회모르타르의 사용이 증가하고 있다. 하지만 국내 연구는 콘크리트벽돌과 시멘트모르타르에 집중되고 있어 점토벽돌 및 석회모르타르에 대한 연구가 거의 없는 실정이며, 조적조의 국내 기준 또한 국내에서 사용되는 재료와 다른 물리적 값을 사용하고 있는 국외기준을 바탕으로 제정되어 국내 실정을 적절히 반영하지 못하고 있다. 따라서 본 연구는 프리즘압축강도, 부착강도, 전단 및 사인장강도 실험을 통해 점토벽돌과 석회모르타르를 사용한 조적구조의 물리적 특성을 파악하고자 한다. 또한, 콘크리트벽돌과 시멘트모르타르를 사용한 조적구조와의 물리적 특성을 비교분석하여 국내 조적기준을 개정하기 위한 근거를 제시하고자 한다. 점토벽돌과 석회모르타르를 적용한 조적구조는 콘크리트벽돌과 시멘트모르타르를 사용한 조적구조와는 다른 양상을 보이므로 점토벽돌과 석회모르타르를 적용한 조적구조의 프리즘압축강도와 탄성계수에 대한 추정식을 제안한다.

본 연구는 석회석미분말을 4단계(0, 10, 20 및 30%)로 대체한 모르타르 및 콘크리트의 내해수성을 평가하기 위하여 수행되었다. 내해수성 평가를 위하여 모르타르의 해수침식 저항성 및 콘크리트의 염소이온 침투저항성 실험을 각각 실시하였다. 실험결과에 의하면, 시멘트 경화체의 내해수성은 석회석미분말의 대체율에 의존적으로 나타났다. 다시 말해서, 석회석미분말을10% 대체한 모르타르 및 콘크리트는 대체적으로 OPC와 유사한 내해수성을 나타낸 반면, 석회석미분말의 대체율이 큰 모르타르 및 콘크리트의 내해수성은 OPC와 비교하여 현저하게 떨어지는 것으로 조사되었다.

50년 이상 경과된 조적조 건축물은 석회모르타르로 시공되었으나 보수공사 시 시멘트모르타르를 사용하여 기존 재료와의 상이함으로 인한 문제가 다수 발생하였다. 또한, 조적조 건축물의 보수공사 시 참고할 수 있는 석회모르타르에 대한 객관화된 자료의 부족과 상세기준이 없으며, 미숙련 조적공의 시공으로 인하여 건축물의 객관적인 구조성능을 평가하기가 어렵다. 조적조 건축물의 원형을 보존하기 위해서는 해당 건물의 재료와 기법에 대한 기술사적 연구가 중요하다. 그러므로 본 연구는 석회모르타르의 배합비, 배합재료, 양생기간 및 조건 등에 따른 압축강도 실험을 행하고, 이를 토대로 시멘트모르타르와 석회모르타르를 비교분석하여 석회모르타르의 구조적 특성을 정리한다.