In this study, corrosion fatigue crack propagation was investigated in pH buffer environment using the giga strength steel and its heat-affected zone, and the results were compared with theoretical model prediction. Also, the pure corrosion effect on fatigue crack propagation in a corrosive environment was compared with the modified Forman equation. As results, the average value of corrosion rate obtained as the ratio of the net corrosion-induced crack length to the total crack length under cyclic loading in the base metal and heat-affected zone under experimental loading conditions. These results exhibit a new theoretical method for corrosion fatigue crack propagation that predicts a purely corrosion effect on the behavior to be determined.
We have carried out measurements of 1.2-1.6GHz radio interferences around Seoul Radio Astronomy Observatory located in the campus of Seoul National University. We received interference signals using a pyramidal horn antenna and measured its power using a spectrum analyzer with 1MHz resolution after ~60dB amplification. In order to check the spatial characteristics, we made observations at every 30∘ 30∘ in azimuth at elevation of 30∘and60∘ 30∘and60∘ . Also, in order to check the temporal characteristics, we repeated the all-sky observations five times at every six hours. The results may be summarized as follows: (1) There are strong (≥−20dBm) (≥−20dBm) interferences between 1.2 and 1.4GHz. Particularly strong interferences are observed at 1.271 and 1.281GHz, which have maximum powers of -0.34dBm and -0.56dBm, respectively. (2) The characteristics of the interferences do not depend strongly on directions, although the interferences are in general weak at high elevation and in east-west direction. (3) The interferences appear for a very short (≤0.01s) (≤0.01s) period of time, so that the average power is much smaller than the maximum power. Strong interferences with large (≤−49.0dBm) (≤−49.0dBm) average power have been observed at 1.271, 1.281, 1.339, and 1.576GHz. At these frequencies, the interferences appear repeatedly with a period of ≤0.1s ≤0.1s By analyzing the observed power, we find that, for the strongest 1.271GHz interference, the average intensity is −171dBW/m2/Hz −171dBW/m2/Hz and that the maximum intensity is −122dBW/m2/Hz −122dBW/m2/Hz . If this interference is delivered to the detector without any shielding, then its power would be much greater than the rms noise of a typical line spectrum. Therefore, it is important to shield all the parts of receiver carefully from radio interferences. Also, without appropriate shielding, the sensitivity of a receiver could be limited by the interference.
최근 빠르고 편리하게 데이터 송수신이 가능한 무선LAN은 가정, 사무실 등 다양한 장소에서 사용이 증가하고 있다. 그러나 실내에서 무선LAN을 사용할 경우 천장, 벽, 바닥, 책상 등에서의 반사파에 의한 다중반사가 발생하여 데이터 전송의 오류 및 성능 저하의 주된 원인이 된다. 이를 해결하기 위해 본 논문에서는 Graphite의 특성을 분석하고 최적의 조성비를 찾아내서 무선LAN 환경에 적합한 전파흡수체를 연구하였다. 먼저 Graphite와 지지재인 CPE(Chlorinated Polyethylene)를 이용하여 조성비별 전파흡수체 샘플을 제작하고, 각 샘플의 반사계수를 측정하였다. 측정된 데이터로부터 재료정수를 계산하고, 전파흡수체를 설계 및 제작하여 전파흡수능을 비교, 분석 하였다. 그 결과 조성비가 Graphite : CPE=50:50 wt%이고, 두께 1.7 mm 인 전파흡수체가 5.2 GHz에서 27 dB 이상의 전파흡수능을 가지는 우수한 전파흡수체를 개발하였다.
본 논문에서는 실내 무선LAN 환경에서 발생하는 다중반사에 의한 통신속도 저하 및 데이터 손실과 같은 문제점을 해결하기 위한 전파흡수체를 설계하였다. 먼저 자성손실 재료인 Sendust와 지지재인 CPE(Chlorinated Polyethylene)조성비별 전파흡수체 샘플을 제작하였고, 각 샘플의 재료정수를 이용하여 시뮬레이션 한 결과, 최적의 조성비가 Sendust : CPE = 80 : 20 wt.% 임을 확인하였다. 그리고 시뮬레이션 결과를 토대로 전파흡수체를 실제작하였다. 제작된 전파흡수체의 측정 결과 시뮬레이션 결과와 잘 일치하였으며, 제작된 전파흡수체는 두께 3.2 5mm 조성비 Sendust : CPE = 80 20 wt.%이며, 중심주파수 2.4 GHz에서 19 dB의 전파흡수 특성을 보였다.
디지털 TV 방송은 기존 아날로그 방송에 비해 해상도나 음질 등이 매우 뛰어나고 홈쇼핑, 홈뱅킹, 인터넷 검색, 재택근무 및 VOD(video on demand) 등의 멀티미디어 기능을 제공할 수 있는 등 많은 장전을 가지고 있다. 따라서 본 논문에서는 디지털 TV 서비스 전에 본질적인 지역적 전파환경의 분석이 필요하며, ETRI 모델을 적용하여 부산지역에 대한 전파모델을 적용하여 그 제한성을 분석하고자 한다. 따라서 본 논문에서는 디지털 TV 신호가 고품질을 유지할 수 있도록 하기 위하여 산악지역과 고층빌딩이 많은 부산지역의 전계강도를 측정하였다. 본 논문에서는 TV 전파모델을 기준으로 전반적으로 기준모델에 대한 시뮬레이션 결과보다. 낮은 결과를 갖지만 분포 패턴은 비슷하게 나타남을 알 수 있었다. 이론치와 실측치를 비교한 결과 평탄한 지형에 대해서는 비슷한 결과를 가지지만 도심 밀집지역 및 산악 지형에 대해서는 상당한 차이를 가지는 것으로 나타났다. 따라서 ETRI 전파모델 및 자유공간에 대한 전파전파의 이론적 모델링이 부산 지역에 대해서는 적합하지 않는 것으로 판단되었다.