이 연구에서는 친환경 선박용 재료로 각광받는 탄소나노물질에 대하여 실험적 연구를 수행하였다. 탄소나노물질의 합성을 위한 열원으로서는 대향류 메탄 화염을 이용하였다. 탄소나노물질 합성을 위한 촉매로서는 페로센을 사용하였다. 합성 특성을 파악하기 위한 주요 파라메타로는 대향류 메탄 화염에 수소의 혼합 비율과 샘플링 위치를 변화시켰다. 탄소나노물질의 성향은 SEM과 TEM 이미지를 이용하여 결정되었다. 실험 결과로서는 수소의 혼합 비율이 증가할수록 탄소나노물질의 생성이 잘 이루어졌다. 또한 대향류 메탄 확산화염 내 탄소나노튜브의 생성을 위한 적정 온도로는 1500 K 정도가 적당하다는 것을 알 수 있었다.

The goal of this investigation was to produce a zirconia-family black ceramics that has enhanced functionality andreliability. Color zirconia ceramics have been produced by adding pigments. Pigments cause structural defects within zirconiaand result in a drop in physical properties. Using environmentally friendly rice husk, we produced a black zirconia that is freeof structural defects. In optimal firing conditions for black zirconia the calcining temperatures of the molding product arechanged from 400oC to 1200oC, and the firing temperatures are changed from 1400oC to 1600oC. Color of testing the specimenswas analyzed using Ultraviolet (UV) spectroscopy. Scanning Electron Microscope (SEM), EDAX (EDX), and Fourier transforminfrared spectroscopy (FT-IR) analyses were carried out in order to examine impregnation properties and crystal phases.Universial Test Machine (UTM) was used to measure the flexual strength as well as the compressive strength. Fromexperimental results, it was found that in optimal firing conditions the sample was calcined from 1000oC to 1500oC. Commissioninternationalde I’Edairage (CIE) values of manufactured black zirconia color were L*=29.73, a*=0.23, b*=−2.68. Thebending strength was 918 MPa and the compressive strength was 2676 MPa. These strength values are similar to typicalstrength values of zirconia, which confirms that carbon impregnation did not influence physical properties.

In a view point of environment, the advanced electric contact material without environmental load element such as cadmium has to be developed. Extensive studies have been carried out on electric contact material as a substitute of Ag-CdO contact materials. In the present study, powder metallurgy including compaction and sintering is introduced to solve the incomplete oxidation problems in manufacturing process of electrical contact material. The contact material, fabricated in this study, was actually set in an electric switchgear of which working voltage is 462V and current is between 25 and 40A, for the purpose of testing its performance. As a result, it exceeded the existing Ag-CdO contact materials in terminal-temperature ascent and main contact resistance

본 연구에서는 원적외선의 방출을 증진시켜 쾌적한 실내 환경을 조성시키며 아울러 비중이 높은 재료를 사용하여 층간소음을 저감시키기 위한 방안으로서 건축용 친환경 바닥 마감재에 자철석 잔골재를 사용하는 모르터의 기초물성 연구를 수행하였다. 실험에 사용된 모르터의 배합은 자철석 잔골재를 자연사로 0, 20, 40, 60, 100% 치환하였다. 먼저 원적외선 방출성능으로서 방사율과 방사에너지를 측정하여 KICM의 기준을 훨씬 상회하는 결과를 얻었다. 단위용적질량 압축강도 실험결과 치환율이 증가함에 따라 선형적으로 증가하는 결과를 얻었다. 그러나 건조수축 시험결과 자철석 잔골재의 치환율이 증가함에 따라 건조수축 변화율이 기준 시험체 대비 급격하게 증가하는 것으로 나타나 향후 이를 해결하기 위한 방안이 강구되어야 함을 알 수 있었다.

The purpose of this study was to develope the environmentally favorable method of roller compacted soil concrete pavement using industrial waste red mud. Red mud was the major solid waste produced in the process of alumina extraction from bauxite(Bayer process). For recycling purpose, red mud was treated and applied to use as concrete admixtures. To this end, laboratory test such as compressive strength of soil concrete, and field test such as construction characteristics of soil concrete pavement, had been conducted. From the study results, the compressive strength of soil concrete was strongly related to its matrix proportion and compaction energy. The optimum mix proportion was comprised of cement 300 kg/m3, water 110 kg/m3, fine aggregate 600 kg/m3, course aggregate 1400 kg/m3, red mud admixture 50 kg/m3 and compaction energy above 2.86 cm-kgf/cm3. The 7th-day and 28th-day mean compressive strength of soil concrete were 43.8 MPa and 53.3 MPa each under the optimum condition. Pavement application of soil concrete using red mud admixture indicated that the proposed method was simple in case of construction and showed a good surface texture.

본 연구의 목적은 저열 시멘트를 활용한 콘크리트와 고밀도 폴리에틸렌을 활용한 친환경 저수조를 평가하는 것이다. 친환경 저수조의 강도와 파괴모드를 평가하기 위하여 콘크리트와 고밀도 폴리에틸렌 복합체의 인장강도 시험, 다양한 종류의 콘크리트 수화열 실험, 다양한 혼화재를 활용한 수화열 실험 등을 수행하였다. 수행결과 전단키가 콘크리트와 고밀도 폴리에틸렌의 복합체로 거동할 수 있는 중요한 역할을 한다는 것을 규명하였고, ㄱ 타입의 전단키가 V 타입보다 40% 이상 인장강도를 증진시킨다는 것을 보여주었다. 연구결과 새로운 친환경 저수조는 기존의 콘크리트 저수조보다 안전성을 개선시키며, 보다 적용성과 활용성이 많은 것으로 기대된다.

본 연구는 꽃장식에 있어서 침봉이나 플로랄 폼만큼 고정능력이 뛰어남과 동시에 환경에 무해하면서 미적 가치가 뛰어난 꽃 고정재료를 제시함으로써 친환경적인 꽃꽂이 방법을 제시하고자 하였다. 연구방법은 2008년 8월 독일 GBF(Grunbergr Bildungszentrum Floristik)의 플로리스트 연수과정에서 제시된 작품을 분석하였다. 고정재료는 자연에서 얻을 수 있는 재료와 재활용으로 사용되어진 재료로 나누어 분석하였다. 식물의 기관, 즉 잎, 줄기, 뿌리, 열매를 꽃 고정재료로 이용하여 장식해 본 결과 플로랄 폼 이상으로 고정 능력이 뛰어났으며 세우는 기능까지도 탁월하다는 것을 알 수 있었다. 그리고 재활용으로사용되어지는 재료들도 자연물만큼 고정능력이 뛰어나지는 않지만 꽃 고정재료가 가지고 있는 빈공간과 지탱 할 수 있는 힘을 잘 파악한 뒤에 적합한 꽃을 선택한다면 고정기능과 세우는 기능이 가능한 것을 볼 수 있었다. 이와 같이 친환경적 꽃 고정재료로써 사용되어진 식물을 포함한 자연물과 생활 속 재활용품은 침봉이나 플로랄 폼과 비슷한 고정능력과 세우는 능력을 가지고 있었다. 따라서 가급적 플로랄 폼의 사용을 자제하고 환경에 피해를 주지 않는 친환경적 꽃장식을 하는 것이 바람직할 것이다.

This research is intended to extrapolate the environmental problem caused by the flower fixation design materials and to find a solution by enabling ecological flower designing through discovering environment friendly materials that fix the flowers and analyzing their utilizations. Such use of pro-environmental materials shall lead changes in awareness among the professional florists as well as the consumers. The result of analyzing 67 flower works produced by the environment friendly flower fixation materials is as follows: 1) The design makes the most use of natural characteristics of the original plants used. 2) The pro-environmental materials were minimized to it functional usage, yet visual beautification was emphasized to make the design harmonized. 3) The design showed excellent coordination with vases. The vase was selected to match the color and shape of the flowers contained in it. This allows the vase to be included as part of the overall design of the work. The 67 flower design works reviewed in this research reveal a common design tendency: the environment friendly fixation materials not only were functionally solid, environmentally safe and recyclable but also played outstanding role as visually beautiful design element. This indeed is a revolutionary finding that could impact on the future of the flower design as a whole.