Commercial carbon fiber is sized with Bisphenol A type epoxy, a thermosetting resin, to prevent fiber damage due to friction during weaving and manufacturing processes. When the thermoplastic resin is used as the base material, the interface between the carbon fiber and the thermoplastic resin is very weak because the bonding force with the thermosetting resin is not good, which greatly affects the mechanical properties of the composite material. Therefore, in order to improve the mechanical properties of the thermoplastic composite material, a process of removing the epoxy sizing layer on the surface of the carbon fiber in a furnace is required. In this process, the physical properties of the carbon fiber are changed according to the change of carbon fiber heat treatment conditions. In this paper, the study was carried out to evaluate the tensile strength required for automobile parts by extrusion and injection of thermoplastic resin based carbon fiber composites. Depending on the heat treatment temperature and time of the carbon fiber was a slightly tensile strength of the carbon composite material occurs, the tensile strength of the carbon composite material with a 6 hour heat-treated carbon fiber was measured at 550 ℃ the highest to 93 MPa. When the heat treatment holding time is more than 6 hours or the heat treatment temperature is more than 600 ℃, it may be the damage to the carbon fiber, which can cause a decrease in the tensile strength of the carbon fiber composite material.

탄소섬유 한외여과막 및 광촉매 혼성 수처리를 위해 관형 여과막 외부와 원통형 막 모듈 내부 사이 공간에 광촉매를 충전하였다. 광촉매는 PP (polypropylene) 구에 이산화티타늄 분말을 플라즈마 화학증착 공정으로 코팅한 것이다. 휴믹산과 카올린 모사용액을 대상으로 막오염을 최소화하기 위해 10분 주기로 10초 동안 물 역세척을 시행하였다. 기존 결과와 동일하게 휴믹산을 10 mg/L부터 2 mg/L로 변화시킴에 따라, 막오염에 의한 저항 (Rf)이 감소하여 2 mg/L에서 최대 총여과부피 (VT)를 얻었다. 탁도와 휴믹산의 처리효율은 각각 97.1%와 74.2% 이상으로 휴믹산 농도의 영향을 받지 않았다. 그러나 기존 결과에서는 휴믹산의 농도가 증가할수록 휴믹산의 처리효율이 다소 증가하는 경향을 나타냈다.

In this paper, internal thermal stresses of the cementitious matrix were evaluated by incorporating polypropylene fibers. By using the temperature heating method specified in KS F 2257-1, the temperatures by a depth were measured. Thermal stress was calculated based on Kodur's thermal stress formula. Different thermal stress behaviors were observed depending on amount of PP fiber. Thas, it will become fundamental data to analyze the thermal stresses behavior of structure members subjected to higher temperature.

The mechanical properties of high temperature mortar reinforced by polypropylene fibers were investigated in this paper. Ordinary portland cement was used as basic binder and the effect of the replacement of fly ash, slag, silica fume and graphite for Ordinary portland cement was investigated.

This research investigated the pullout behavior of high strength polypropylene fibers. Test results showed that the frictional bond between polypropylene fiber and cement matrix of water to binder ratio 0.23 is 0.2 MPa

폴리비닐알코올 섬유와 폴리에틸렌 섬유 등의 합성 섬유는 고연성 섬유보강 시멘트 복합재료를 제조하는데 성공적으로 사용되고 있다. 폴리프로필렌 섬유 역시 복합재료를 제조하는데 사용되고 있지만, 고연성을 구현하는 목적보다는 고온에 노출된 콘크리트의 내화 성능 향상 목적으로 사용되고 있다. 이 연구에서는 폴리프로필렌 섬유로 보강된 시멘트 복합재료의 성능을 향상시키는 방법에 대하여 논하고자 한다. 폴리프로필렌 섬유보강 시멘트 복합재료의 성능을 평가하기 위하여 5가지 배합을 결정하였다. 1종 보통포틀랜드시멘트 (OPC)와 OPC를 다량 치환한 플라이애시를 결합재로 사용하였고 물-결합재 비는 0.23~0.25이다. 또한 부피비로 2%의 폴리프로필렌 섬유가 사용되었으며, 연성을 향상시킬 목적으로 폴리스틸렌 비드가 사용되었다. 슬럼프, 밀도, 압축강도, 1축 인장 실험을 포함한 일련의 실험을 수행하였으며, 실험결과, 파괴역학, 마이크로역학, 통계이론을 이용하여 폴리프로필렌 섬유보강 시멘트 복합재료의 성능을 향상할 수 있는 것으로 나타났다.

Spite of the several advantages of durability and economic characteristics, such as civil engineering and construction materials, which is widely used as a mortar and concrete, and the tensile strength of fragility and brittleness due to local damage caused. This mechanical shortcoming ensure ductility and brittle complement the various fibers used in concrete and mortar has been developed in order to improve the energy absorption capacity, and increase the use of multiple structures in the form of.Now widely used in the polypropylene fiber polypropylene and affordable, excellent chemical stability and durability, but mainly use the nature of water and mix well so the fluorinated surface hydrophilic polypropylene fibers that can be granted through the processing unit,to overcome this.

폴리프로필렌섬유보강 시멘트 복합재료와 구조용 합성섬유의 부착특성을 평가하였다. 폴리프로필렌섬유는 0.10%, 0.15% 및 0.20%의 체적비로 적용하여 dog-bone 시험을 실시하였다. 구조용 합성섬유와 폴리프로필렌섬유보강 시멘트 복합재료 사이의 부착강도는 폴리프로필렌섬유의 혼입률이 증가할수록 증가하였으나 0.20% 이상이 되면 감소하였다. 또한 폴리프로필렌섬유의 첨가는 계면인성과 마찰저항을 증가시킨다. 인발시험 후 구조용 합성섬유 표면의 미소구조 분석은 폴리프로필렌섬유의 혼입률이 증가할수록 긁힘 현상이 증가하였다.