In this study, we investigate the relationship between the peeling behavior of the backsheet of a photovoltaic(PV) module and its surface temperature in order facilitate removal of the backsheet from the PV module. At low temperatures, the backsheet does not peel off whereas, at high temperatures, part of the backsheet remains on the surface of the PV module after the peeling process. The backsheet material remaining on the surface of the PV module is confirmed by X-ray diffraction(XRD) analysis to be poly-ethylene(PE). Differential scanning calorimetry(DSC) is also performed to investigate the interfacial characteristics of the layers of the PV module. In particular, DSC provides the melting temperature(Tm) of laminated ethylene vinyl acetate(EVA) and of the backsheet on the PV module. It is found that the backsheet does not peel off below the Tm of ethylene of EVA, while the PE layer of the backsheet remains on the surface of the PV module above the Tm of the PE. Thus, the backsheet is best removed at a temperature between the Tm of ethylene and that of PE layer.

난류경계층이 유지되기 위한 에너지 공급은 경계층 내 구조물인 와류들의 상호작용으로 끊임없이 이루어진다. 이러한 난류 유동은 수송분야의 마찰저항 및 해양구조물의 침식 및 진동을 유발하기 때문에 유동 제어를 위한 연구가 활발히 진행되고 있다. 이러한 제어의 극대화를 위해서는 난류 에너지 전달이 어떻게 이루어지는지에 대한 메카니즘 규명이 필수적이고, 이를 위해서는 층류경계층 내 유동현상으로 파악하는 것이 명확하고 용이하다는 장점이 있다. 따라서, 본 연구에서는 층류경계층 내 평판에 반구를 설치하여 역압력구배을 발생시킴으로써 교란된 유동현상의 상호작용을 분석하였다. 즉, 반구를 둘러싼 목걸이 와류와 반구 표면의 유동 박리에 의한 후류영역에서 머리핀 와류가 생성되어 상호 유기적으로 영향을 주고받는다. 이 과정에서 목걸이 와류는 후류영역으로 높은 운동량의 유체를 유입시켜 머리핀 와류의 발생 주파수를 증가시킨다. 반구 전방에 구멍을 뚫어 국부적인 흡입제어로 목걸이 와류의 와도를 감소시킴으로써 그 영향이 완화되는 과정을 유동 가시화 및 열선유속계로 측정하여 정성 및 정량적으로 분석하였다.

현재 국내 콘크리트 포장은 고속도로에서 약 40%, 일반 도로에서는 2% 정도를 차지하고 있다. 콘크리트 포장은 중차량에 대한 뛰어난 적용성과 20년 이상의 장기 공용연수를 가진다는 장점을 가지고 있다. 최근 국내 고속도로의 콘크리트는 장기간 사용으로 인해 노후화 되어있으며, 개통한지 오래되지 않은 콘크리트포장에서도 줄눈부 파손 및 표면박리, 표면마모 등으로 인한 보수비가 증가하고 있는 추세이다. 특히 강원 및 전북지역은 매년 겨울 많은 눈으로 인해 많은 양의 제설제를 사용하고 있어 표면박리상태가 심각 상태이다. 따라서 본 논문에서는 실리카퓸과 폴리머분말을 사용한 포장용 콘크리트의 표면박리저항성을 평가하고자 한다. 기배합된 콘크리트에 실리카퓸과 폴리머 분말을 후 첨가하였으며, 혼화재료의 혼입으로 부족한 단위수량은 혼화재료 혼입 시 추가하여 W/C를 42%로 보정해주었다. 표 1은 실험에 사용한 배합표이다. 압축강도 시험결과 재령 28일에 모든 변수에서 30 MPa 이상을 발도를 발현하였고, 실리카퓸 사용량이 증가할수록 강도가 증진되었지만 폴리머에 따른 영향은 거의 없는 것으로 나타났다. 휨강도 시험결과 실리카퓸과 폴리머 분말을 사용한 배합의 휨강도가 OPC 배합에 비해 큰 폭으로 증가하였으며, 폴리머 분말의 혼입량이 증가할수록 그러한 경향이 더 뚜렷하게 나타났다. 실리카퓸도 휨강도가 증가하는 경향을 보였지만 그 영향은 크지 않았다. 표면박리저항성 시험결과 실리카퓸이 혼입된 변수에서 실리카퓸에 의한 수밀성 증가로 인해 저항성이 상당히 증가하는 경향을 보였으며, 혼입률의 증가에 따라 그러한 경향은 더 뚜렷하게 나타났다. 하지만 폴리머 분말의 혼입량이 증가할수록 박리량이 증가하여 폴리머 분말이 표면박리 저항성에 악영향을 미치는 것으로 판단된다.

PURPOSES: The purpose of this study is to verify the causes of surface scaling at L-shoulder concrete structure. METHODS : From the literature reviews, mechanisms of frost damage were studied and material properties including strength, air void, spacing factor and scaling resistance of L-shoulder concrete structure were analyzed using core specimens taken by real fields. RESULTS : The spacing factor of air void has relatively high correlation of surface conditions : lower spacing factor at good surfacing condition and vice versa. If the compressive strength is high, even thought spacing factor does not reach the threshold value of reasonable durability, the surface scaling resistance shows higher value. Based on these test results, the compressive strength also provide positive effect on the surface scaling resistance. CONCLUSIONS: The main causes of surface scaling of L-shoulder could be summarized as unsuitable aid void amount and poor quality of air void structure. Secondly, although the compressive strength is not the governing factor of durability, but it shows the positive effect on the surface scaling resistance.

Recently, scaling of pavement concrete is becoming problem by excessive use of deicer. The current study measured durability of concrete not considering multi-deterioration using design and construction mixing used general concrete pavement.

The bond performance of Latex modified concrete(LMC) is excellent when compared with conventional pavement concrete. But LMC have a several problems. In order to improve the problem of LMC, Remicon latex modified concrete(Remicon LMC) was developed. In this study, the surface scaling resistance and bond properties of Remcion LMC containing extra admixture was compared with latex ratio. From the results, when latex and admixture were mixed in concrete, bond strength was improved. And, the surface scaling resistance of Remicon LMC was quite good comparing to LMC. The surface scaling resistance of Remicon LMC mixed latex ratio 8% more showed the equivalent capacity of LMC.

This study evluated the Freeze-thaw and scaling resistance characteristic of high early-strength low heat cement concrete. The result Freeze-thaw and scaling resistance appeared to be excellent, and using high early-strength low heat cement can be applied to concrete structures of road facilities.

Domestic expressway are exposed to damage of combined deterioration by excessive use of deicer and a lot of cost is required for maintaining damage structures. Therefore, now is the time that durability of subsidiary concrete structures is required to enhanced in order to reduce maintenance cost of structures and to promote road safety. Thus, in this study measured compression strength and scaling resistance of concrete using the waste glass sludge