This study reports an environment-friendly synthetic strategy to process nickel oxide nanocrystals. A mesoporous nickel oxide nanostructure was synthesized using an environmentally benign biomimetic method. We used a natural rambutan peel waste resource as a raw material to ligate nickel ions to form nickel-ellagate complexes. The direct decomposition of the obtained complexes at 700 oC, 900 oC and 1100 oC in a static air atmosphere resulted in mesoporous nickel oxide nanostructures. The formation of columnar mesoporous NiO with a concentric stacked doughnuts architecture was purely dependent on the suitable direct decomposition temperature at 1100 oC when the synthesis was carried out. The prepared NiO nanocrystals were coated on cotton fabric and their antibacterial activity was also analyzed. The NiO nanoparticle-treated cotton fabric exhibited good antibacterial and wash durability performance.
The silver nanoparticles (AgNPs) incorporated reverse osmosis (RO) membranes with an excellent antibacterial property has been reported. However, the incorporated AgNPs could increase the hydraulic resistance of membrane, indicating the decline of water flux. Here, hybrid silver nanoparticles (Ag@SiO2, 400 nm) were strongly immobilized using Ag-S chemical bonding on the polyamide surface of RO membrane for both protecting the decline membrane performance and having a strong antimicrobial property. The membrane performance was unchanged after the immobilization of silver nanoparticles, when compared to that of unmodified membrane. In addition, the silver-polyamide composite membrane significant reduced the number of live bacteria attached on the membrane surface by 92.7 ± 1.8, 99.5 ± 0.3, and 73.3 ± 5.5% for E. coli, P. aeruginosa, and S. aureus, respectively. The strong antimicrobial property is ascribed to the combination effect by the directly attachment to bacteria surface and the penetration of released silver ions inside the cell membrane of bacteria.
곤충에 진균병을 유발하여 사멸케 이르게 하는 곤충병원성 곰팡이는 다양한 해 충의 밀도를 자연적으로 억제하며, 최근에는 친환경적인 방제 수단으로 계발되어 여러 해충방제에 이용되고 있다. 이러한 곤충병원성 곰팡이는 생장하면서 약학적 치료제로 이용될 수 있는 다양한 이차대사산물을 분비 하는데 이 이차대사산물은 목적 생체를 촉진, 저해시키는 물질들이 포함되어 항생물질, 세포독성물질, 살충성 물질로서 쓰이고 있다. 그리하여 본 연구에서는 우리나라 토양에서 분리된 많은 수 의 다양한 347개 곤충병원성 곰팡이 균주의 배양액 중에서 식물병원성 세균 Ralstonia solanacearum, 병원성 세균 Escherichia coli에 항균효과를 가지는 곤충 병원성 곰팡이 배양액과 항산화효과를 가지는 곤충병원성 곰팡이 배양액을 빠르 고 쉽게 선발하였다. 그 결과, 전체 347개 균주의 배양액 산물에서 약 7%에 해당하 는 25개의 배양액이 항산화활성효과를 보였고, 약 20%(347균주 중 72 균주) 그리 고 6%(347균주 중 22 균주)에 해당하는 균주의 배양액이 R. solanacearum, E. coli 에 대한 항균활성을 가지는 것으로 확인되었다. 선발된 곰팡이 균주들의 배양액 산 물들은 각각의 세균방제 및 약학적 재료로써 이용될 수 있을 것으로 생각 된다.