The Ti-Ni alloy nanopowders were synthesized by a levitational gas condensation (LGC) by using a micron powder feeding system and their particulate properties were investigated by x-ray diffraction (XRD), transmission electron microscopy (TEM) and Brunauer-Emmett-Teller (BET) method. The starting Ti and Ni micron powders were incorporated into the micron powder feeding system. An ingot type of the Ti-Ni ahoy was used as a seed material for the levitation and evaporation reactions. The collected powders were finally passivated by oxidation. The x-ray diffraction experiments have shown that the synthesized powders were completely alloyed with Ti and Ni and comprised of two different cubic and monoclinic crystalline phases. The TEM results showed that the produced powders were very fine and uniform with a spherical particle size of 18 to 32nm. The typical thickness of a passivated oxide layer on the particle surface was about 2 to 3 nm. The specific surface area of the Ti-Ni alloy nanopowders was based on BET method.

Tin oxide nanoparticles (n-SnO and ) were synthesized by the inert gas condensation (IGC) method under dynamic gas flow of oxygen and argon at various conditions. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) method were used to analysis the size, shape and crystal structure of the produced powders. The synthesized particles were mostly amorphous and their size increased with increasing the partial pressure of oxygen in the processing chamber. The particles also became broader in size when higher oxygen pressures were applied. Low temperature annealing at in air resulted to crystallization of the amorphous n-SnO particles to .

The copper oxide nano powders were synthesized by levitational gas condensation(LGC) method, and their high heterogeneous catalytic effects of oxidation of 2,3,5-trimethyl-1,4- hydroquinone (TMHQ) and catalase activity were studied. The observation of transmission electron microscopy (TEM) shows that most of these nano powders are uniform in size, with the average particle size of 35 nm. The nano powder consists of mainly , but it is aged to CuO phase. The catalytic effect which was clarified by oxidation of TMHQ and catalase depends on the amount of cuprite phase and the particle size.

Nanoparticles of iron oxides have been prepared by the levitational gas condensation (LGC) method, and their structural and magnetic properties were studied by XRD, TEM and Mossbauer spectroscopy. Fe clusters were evaporated from a surface of the levitated liquid Fe droplet and then condensed into nanoparticles of iron oxide with particle size of 14 to 30 nm in a chamber filled with mixtures of Ar and gases. It was found that the phase transition from both - and -Fe to , which was evaluated from the results of Mossbauer spectra, strongly depended on the flow rate. As a result, - was synthesized under the flow rate of 0.1(Vmin)0.15, whereas was synthesized under the , flow rate of 0.15(Vmin)0.2.