The PU flame-retardant coatings (TTBAH, ATBAH-10C, -20C, and -30C) were prepared using the synthesized ATBAs and HDI-trimer as curing agent at room temperature. The physical properties of PU flame-retardant coatings with chlorine and phosphorus were inferior to those with phosphorus only and the properties were getting worse with increasing chlorine content. Flame retardancy was tested with three methods. With the vertical method, complete combustion time of ATBAHs were 259~347 seconds, which means that the prepared coatings are good flame-retardant. With the 45˚ Meckel burner method, char lengths of the three prepared coatings were less than 2.9 cm, which indicates that the prepared coatings are first grade. With the limiting oxygen index (LOI) method, the LOI values of the three prepared coatings were in the range of 30~35%, which proves good flame retardancy of the prepared coatings. from the result of flame retardancy tests of the specimens that contain the same amounts of flame retarding compounds. it was found that the coatings containing both phosphorus and chlorine show higher flame retardancy than the coatings containing only phosphorus. This indicates that there exists, some synergy effect between coexisting phosphorus and chlorine.

High-solid coatings were prepared by blending of previosly synthesized acrylic resins and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, cross-hatch adhesion, 60˚specular gloss, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. As a result of Rigid-body pendulum visco-elasticity measurement, dynamic Tg values of cured films increased with dynamic Tg values.

PU flame-retardant coatings (APHD) containing phosphorous were prepared by blending of hexamethylene diisocyanate-trimer, white pigment, dispersing agent, flowing agent, and previously prepared benzoic acid modified polyester (APTB) that contains phosphorous. Physical properties of the prepared APHD were examined. With the introduction of BZA (contained in APTB), the film viscosity and film hardness of APHD decreased. With the introduction of caprolactone group, the flexibility, impact resistance, accelerated weathering resistance of APTBs increased. Flame retardancy of the coatings was tested. In a vertical burning method, APHD shows 210~313 seconds, and in a 45˚ Meckel burner method, shows 1.3~4.0cm2 of char length, which indicates that the coatings are good flame-retardant coatings. Moreover, the amount of afterglow and flame retardancy of the coatings are decreased with increasing BZA content.

The high-solid coatings were prepared by blending the synthesized acrylic resin in the previous paper and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, 60℃ specular gloss, cross-hatch adhension, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. From a viscoelastic measurement using a rigid-body pendulum, curing was accelerated with the Tg value. With the increase in Tg, log damp value was lowered and dynamic viscoelasic Tg of a cured film was increased.