Porous carbon nanofiber (CNF) electrodes for supercapacitors were prepared by using polyacrylonitrile (PAN) and cucurbituril (CB), which is a macrocyclic compound comprising glycoluril units containing hollow cores. Mixture of PAN and CB in dimethyl sulfoxide was electrospun, and thermally treated to produce CNF electrodes. Their thermal stability, surface morphology, carbon microstructures, and surface porosity were investigated. Electrochemical properties were measured using three-electrode with synthesized CNFs without further treatment as a working electrode and 1 M Na2SO4 as an electrolyte. CNFs derived from PAN and CB exhibited a high specific capacitance of 183.5 F g− 1 and an energy density of 25.4 Wh kg− 1 at 0.5 A g− 1 with stable cyclic stability during 1000 cycles, which is significantly higher than those for CNFs derived from PAN only. This demonstrated that the introduction of CB successfully improved the energy storage performance of CNF electrodes.

The discharge of industrial oily wastewater and oil spill accidents has resulted in significant environmental pollution, creating an urgent need for the treatment of oily wastewater. Nanofiber membranes, known for their high stability, flux, and efficiency, are widely employed in oil–water separation. This study systematically compared the performance of polyacrylonitrile/ graphene oxide (PAN/GO) composite nanofiber membranes prepared through immersion and electrospinning methods for oily wastewater treatment. Experimental findings demonstrated that immersion-prepared membranes achieved high flux (772.9 ± 2.9 L·m−2·h−1, n-hexane/water mixture) and efficiency (98.8%) at a GO concentration of 1.0 g/mL. On the other hand, electrospinning-prepared membranes exhibited superior flux (1500.3 ± 4.4 L·m−2·h−1, n-hexane/water mixture) and efficiency (99.6%) at a higher GO concentration (1.5 g/mL). This membrane displayed excellent stability, maintaining their exceptional performance even after ten cycles of separation. This study compared the advantages and disadvantages of the two methods for preparation of PAN/GO composite nanofiber membrane, offering valuable guidance for practical applications.

In this study, a milled carbon nanofiber-reinforced composite paint was prepared to enhance the anti-corrosive properties of concrete structures. Shorter-length (40 μm) milled carbon fibers (MCFs) showed an increased viscosity relative to longer MCFs (120 μm) owing to their 2 weeks (the decrease was especially strong in the acid solution). A carbon nanotube (CNT)- reinforced composite paint showed similar results in uniform distribution in the epoxy resin. The latter showed a decrease in viscosity owing to agglomerative movement in the epoxy resin. The surface hardness and tensile strength of the composite paint linearly increased as the carbon nanofiber loading was increased by up to 7.2 wt% in the epoxy resin, and slowly decreased after soaking in a sulfuric acid or sodium hydroxide solution for to those of the MCFs, whereas CNTs dispersed in isopropyl alcohol (IPA) in advance and mixed with resin showed lower hardness values than those without dispersion in IPA at the same loading. The mechanical properties such as the Shore D hardness and tensile strength of the MCF-reinforced composite paint increased significantly, resulting in a slower surface degradation of the composite paint concrete in a sulfuric acid and sodium hydroxide solution.

Energy storage systems should address issues such as power fluctuations and rapid charge-discharge; to meet this requirement, CoFe2O4 (CFO) spinel nanoparticles with a suitable electrical conductivity and various redox states are synthesized and used as electrode materials for supercapacitors. In particular, CFO electrodes combined with carbon nanofibers (CNFs) can provide long-term cycling stability by fabricating binder-free three-dimensional electrodes. In this study, CFO-decorated CNFs are prepared by electrospinning and a low-cost hydrothermal method. The effects of heat treatment, such as the activation of CNFs (ACNFs) and calcination of CFO-decorated CNFs (C-CFO/ACNFs), are investigated. The C-CFO/ACNF electrode exhibits a high specific capacitance of 142.9 F/g at a scan rate of 5 mV/s and superior rate capability of 77.6% capacitance retention at a high scan rate of 500 mV/s. This electrode also achieves the lowest charge transfer resistance of 0.0063 Ω and excellent cycling stability (93.5% retention after 5,000 cycles) because of the improved ion conductivity by pathway formation and structural stability. The results of our work are expected to open a new route for manufacturing hybrid capacitor electrodes containing the C-CFO/ACNF electrode that can be easily prepared with a low-cost and simple process with enhanced electrochemical performance.

본 연구에서는 고분자인 polyacrylonitrile (PAN) 고분자에 산화 그래핀(Graphene Oxide, GO)을 첨가하여 전기방사법을 통해 나노섬유 복합막(GO-PAN)을 제조하였으며, 과량의 GO를 첨가하기 위해 표면개질 전략을 사용하였다. 계면활성제를 사용하여 GO의 표면을 간단히 변형하면 GO의 안정성 및 분산도 증가로 인해 최종적으로 분리막에 필러의 함량을 3wt%까지 증가시켰다. 이렇게 변형된 GO(mGO)의 PAN 나노섬유막으로의 도입은 원래의 PAN 나노섬유막과 GO-PAN 막에 비해 향상된 친수성과 기계적 강도를 가진다. 따라서 나노필러의 표면 개질은 최종 복합막의 성능에 영향을 미치며 이는 GO의 분산도와 상관관계가 있는 것으로 보인다.

본 연구에서는 전기방사법을 이용해 다양한 고분자에 nanofiller인 clay를 복합시켜 나노섬유 복합막을 제조하였다. 나노섬유에 clay를 첨가함으로써 일반적인 나노섬유가 가지는 취약한 물리적 특성을 증가시키고 수처리 막으로의 활용 가능성을 확인하였다. 또한 고분자의 친⋅소수성에 따라 발생하는 고분자와 clay간의 interaction을 고찰해보았다. 따라서 본 연구에서 나타난 결과를 통해 clay를 활용한 나노섬유 복합막의 제조 및 나노섬유의 특성 보완 연구의 기초자료로 활용할 수 있을 것으로 판단된다.

Volatile organic compounds (VOCs) are a source of air pollution and are harmful to both human health and the environment. In this study, we fabricated polyurethane/rare earth (PU/RE) composite nanofibrous membranes via electrospinning with the aim of removing VOCs from air. The morphological structure of PU/RE nanofibrous mats were investigated using FE-SEM, EDX, and XRD experimental analyses. A certain amount of RE (up to 50 wt% compared to PU pellets) particles could be loaded on/into PU fibers. The PU nanofiber containing 50 wt% RE powder had the smallest fiber diameter of 356 nm; it also showed the highest VOCs absorption capacity compared with other composite membranes, having an absorption capacity about 3 times greater than pure PU nanofibers. In addition, all of the PU/RE nanofibrous membranes readily absorbed styrene the most, followed by xylene, toluene, benzene and chloroform. Therefore, the PU/RE nanofibrous membrane can play an important role in removing VOCs from the air, and its development prospects are impressive because they are emerging materials.

본 연구에서는 복합막의 물성향상을 위해 clay를 도입한 polysulfone 나노섬유 복합막을 제조하였다. Polysulfone/clay 복합막은 clay가 들어간 N,N-dimethyl acetamide와 acetone 혼합용매에 polysulfone을 첨가한 후 전기방사법 을 이용하여 제조하였으며, 제조된 나노섬유 복합막은 적층수를 변화해 기공크기를 조절한 후 사용하였다. 전반적인 분리막 의 특성은 SEM, contact angle, 기공특성, tensile strength, water flux 분석을 사용하여 고찰하였다. 특히 SEM image로 clay의 도입을 확인하였으며 contact angle 측정을 통해 표면이 개질된 결과를 확인할 수 있었다. 그리고 clay의 도입량에 따른 복합 막의 기계적 물성을 확인하였다. 따라서 본 연구에서 제조된 분리막은 수처리용 분리막으로 충분히 활용 가능할 것으로 판단 된다.

본 연구에서는 clay를 고분자와 복합하여 전기방사법을 이용해 나노섬유 복합막을 제조하였다. 다양한 친·소수성 고분자에 균일하게 clay를 nanofiller로 첨가함으로서 일반적으로 나노섬유 자체가 보여주는 취약한 물리적 기계적 특성을 증가시켜 수처리 막으로의 활용 가능성을 확인하였다. 그리고 고분자와 clay간의 interaction이 제조된 복합막들의 특성에 어떤 영향을 나타내는지 고찰해보았다. 이러한 결과를 바탕으로 nanofiller를 활용한 다양한 나노섬유 복합막의 제조 및 나노섬유의 물리적 특성을 보완 하는 연구의 기초자료로 활용할 수 있을 것이라 생각된다.

This study describes the effects of polyurethane/loess powder (PU/LP) nanofiber thin films composite produced from electrospun for absorption volatile organic compounds (VOCs) from air. Environmental issue has become a focus with improving people's living quality. The VOCs are one of the factors that affect the environmental safety. So, in order to improve the environment and safety for people, many air cleaning techniques have been investigated. One of the methods is nanofiber filtration technology. In this study, the PU nanofiber thin film has been studied that it has the adsorption of VOCs capacity, and LP nanoparticles (NPs) can be used as an additive to load into PU nanofiber thin film by electrospinning. For studying PU/LP nanofiber thin films's absorption of VOCs capacity, 4 samples (0, 10, 30, and 50 wt% LP with respect to PU) were manufactured, respectively. The results show that PU composite mats containing 30 wt% LP NPs has the highest VOCs absorption capacity, and the adsorption capacity for toluene was the highest compared to benzene and chloroform.

본 연구는 Hummer`s method를 이용하여 GO를 합성 후, 필터링을 통해 GO 막을 만들어. PVdF를 이용하여 나노섬유 막을 제조하였다. PVdF의 경우 접촉각 측정의 분석을 통해 친수성의 특징이 나타남을 알 수 있었으며, SEM, FT-IR, 라 만 분석 및 인장시험기, flux 실험을 실시하여, 카드뮴 이온 및 납 이온이 제거되는 것을 확인할 수 있었다. PVdF/GO 나노섬유 막의 경우 수처리에 활용 시, 중금속이온의 함량이 감소할 것이라 예상된다.

본 연구는 수중 비소제거를 위해 망간-철 산화물을 합성하고, PVdF와 복합화하여 전기방사법으로 제조하였다. TEM에서 산화물은 철이 망간을 감싼 형태이다. 인장강도는 PMF10이 PVdF보 다 2배 증가하였고 기공크기는 PVdF보다 작아지는 것이 확인되었다. 비소제거 실험에서 산화물은 As(Ⅲ)제거율이 80%이상 나왔고, As(V)도 제거되 었다. As(Ⅲ) 제거율은 PMF01이 30%로 상대적으로 우수한 결과를 보였다. 따라 서 이산화물은 나노섬유와 복합화를 통해 수처리 필터소재에 대한 기초연구에 활용될 것으로 기대된다.

본 연구는 Hummer’s method를 이용하여 Graphene oxide (GO)를 합성하였으며, poly acrylonitrile (PAN)과 복합화하여 나노섬유 막을 제조하였다. 접촉각 측정, SEM, FT-IR, 인장강도, DI water를 이용한 flux 실험 및 BSA rejection 실험을 실시하여 막의 특성 분석을 진행하였다. PAN/GO 0.3 나노섬유의 경우, rejection 값이 59%로 PAN/GO 복합 나노섬유 막들 중 상대적으로 우수하였다. PAN/GO 복합 나노섬유 막을 수 처리 분야에 이용하여 얻은 자료는, 폐수 속의 유기물질 함량 감소 연구에 대한 기초자료로 활용될 수 있을 것으로 기대된다.

본 연구에서는 비소(arsenic, As) 제거 특성을 가진 망간-철 산화물(manganese-iron oxide, MF)을 제조하고, 이를 poly vinylidene fluoride (PVdF)와 복합화를 진행하여 As(III)와 As(V)를 동시에 제거가 가능한 수처리용 나노섬유복합막 (polymer nanofiber membrane with Mn-Fe, PMF) 제조에 관한 기초 연구를 진행하였다. Transmission electron microscope (TEM) 분석을 통해 MF 소재의 형상 및 구조를 확인하였으며, PMF 복합막의 수처리용 분리막으로의 활용가능성을 조사하 기 위하여 기계적 강도, 기공크기, 접촉각 및 수투과도 분석을 진행하였다. 측정결과로부터 망간과 철 비율이 같은 PMF11 복 합막의 기계적 강도가 가장 높은 결과값(232.7 kgf/cm2)을 나타낸 것을 확인할 수 있었다. 또한, MF 소재의 도입에 따라 기공 크기가 점차 줄어드는 경향성을 확인할 수 있었으며, 특히, 철 산화물의 조성비가 증가할수록 기공크기가 감소하는 경향성을 보여주었다. 수투과도 측정결과 MF 소재의 도입에 따라 PVdF 나노섬유막에 비해 약 10~60% 이상 향상되는 결과를 나타내 었다. 제조된 MF 소재 및 PMF 복합막의 비소 제거 특성평가를 통해 As(III)와 (V)의 동시 제거 가능하며, 특히, MF01 샘플 의 경우 As(III)와 (V)에 각각 93, 68%의 가장 높은 흡착제거율을 나타내었다. 따라서 본 연구에서는 제조된 MF소재 및 PMF 복합막을 통해 수처리용 분리막의 기능성 향상을 위한 기초연구 자료로 활용할 수 있을 것으로 기대된다.

본 연구에서는 주위에서 취할 수 있는 식물을 이용하여 엽록체를 추출하고, PP부직포 위에 도포하여 복합막을 제작하였으며, 산소 발생에 대한 연구를 진행하였다. 엽록체의 도입 방법에 따른 실험에서 딥 코팅법과 스프레이 코팅법을 이용하였으며, 밀폐된 용기와 진공오븐내 초를 이용한 연소시험에서 스프레이 코팅이 우수한 결과를 나타내었다. 엽록체 활성증가를 위해 nylon6/6 나노섬유를 부직포 위에 전기방사하여 지지체를 제조 후, 엽록체를 도입하였다. 따라서 본 연구는 산소발생용 분리막 및 공기청정기용 필터소재로의 응용에 대한 기초연구 자료로 활용할 수 있을 것으로 기대된다.

본 연구에서는 우리 주위에서 흔히 채취할 수 있는 식물을 이용하여 엽록체를 추출하고, 이를 다양한 방법으로 PP부직포 위에 도포하여 복합막을 제작하였으며, 산소 발생여부에 대한 연구를 진행하였다. 제조된 엽록체의 도입 방법에 따 른 실험에서, 딥(dipping) 코팅법과 스프레이(spraying) 코팅법을 이용하였으며, 밀폐된 용기와 진공오븐 내 초를 이용한 연소 시험 모두에서 스프레이 코팅이 비교적 우수한 결과를 나타내었다. 또한, 엽록체의 활성을 증가시키기 위해 nylon6/6 나노섬 유를 PP부직포 위에 전기방사하여 복합지지체를 제조한 후, 엽록체를 도입하여 제조한 샘플의 경우, 나노섬유가 도입되지 않 은 샘플에 비해 낮은 활성을 가진다는 것을 확인하였다. TiO2가 포함된 샘플들의 경우, 포함되지 않은 샘플들에 비해 엽록체 함량이 50%가 도입되었지만, 16%에서 21%까지 도달되는 시간과 초를 이용한 연소실험에서 각각 유사한 결과값을 나타내었 다. 따라서 본 연구에서 도입된 스프레이 코팅법과 TiO2 접목은 산소발생용 분리막 및 공기청정기용 필터소재로의 응용에 대 한 기초연구 자료로 활용할 수 있을 것으로 기대된다.

본 연구에서는, 산화그래핀(GO) 및 산화철이 기능화된 산화그래핀(M-GO)을 용매인 dimethylformamide (DMF)에초음파분쇄법을 이용하여 완전히 분산시킨 후, 기질고분자인 polyacrylonitrile (PAN)에 첨가하여 전기방사함으로써, 나노섬유 형태의 복합분리막을 제조하였다. 제조된 나노섬유 분리막은 적층수를 변화시켜 기공크기를 조절하였다. Scanning Electron Microscope (SEM) 분석 결과로부터 약 500 nm 크기의 고른 직경분포를 가진 나노섬유 복합분리막이 제조되었음을 확인하였다. 또한, Raman spectroscopy 분석과 Energy Dispersive x-ray Spectroscopy (EDS) 분석 결과로부터 GO 및 M-GO가 분리막 내에 분산되어 있음을 확인하였다. 최종 나노섬유 복합분리막은 상용막(0.27 µm, 55%)과 유사한 기공특성(0.21~0.24 µm,40%)을 보여주었으며, 수투과도 측정결과 PAN 막에 비해 약 200% 향상된 성능을 보여주었다. 이러한 결과로부터, 전기방사법으로 제조된 나노섬유 복합분리막은 수처리용 분리막으로서 충분한 활용가능성이 있다고 판단된다.