This short review focuses on fouling by proteins and macromolecules in microfiltration/ultrafiltration. First, an experimental system that enables investigation of how the extent of the adsorption of proteins and macromolecules on membrane surfaces contributes to a decrease in filtrate flux in microfiltration/ultrafiltration is described. Using this system, a causal relationship - not a correlation - indicating that adsorption results in a decrease in filtrate flux could be clearly demonstrated in some cases. Second, a hydration structure at the membrane surface that can suppress adsorption is discussed, inspired by biomaterial research. In their hydrated states, polymers with low-fouling properties have water molecules with a particular structure. Finally, some successful examples of the development of low-fouling membranes via surface modification using low-fouling polymers are discussed.

Existing reinforced concrete frame buildings designed for only gravity loads have been seismically vulnerable due to their inadequate column detailing. The seismic vulnerabilities can be mitigated by the application of a column retrofit technique, which combines high-strength near surface mounted bars with a fiber reinforced polymer wrapping system. This study presents the full-scale shaker testing of a non-ductile frame structure retrofitted using the combined retrofit system. The full-scale dynamic testing was performed to measure realistic dynamic responses and to investigate the effectiveness of the retrofit system through the comparison of the measured responses between as-built and retrofitted test frames. Experimental results demonstrated that the retrofit system reduced the dynamic responses without any significant damage on the columns because it improved flexural, shear and lap-splice resisting capacities. In addition, the retrofit system contributed to changing a damage mechanism from a soft-story mechanism (column-sidesway mechanism) to a mixed-damage mechanism, which was commonly found in reinforced concrete buildings with strong-column weak-beam system.

We fabricated a Li-S battery with post-treated carbon nanotube (CNT) films which offered better support for sulfur, and investigated the effect of the surface properties and pore structure of the post-treated CNT films on Li-S battery performance. Post-treatments, i.e., acid treatment, unzip process and cetyltrimethylammonium bromide (CTAB) treatment, effectively modified the surface properties and pore structure of the CNT film. The modified pore structure impacted the ability of the CNT films to accommodate the catholyte, resulting in an increase in initial discharge capacity.

Sb-doped SnO2 (ATO) transparent conducting films are fabricated using horizontal ultrasonic spray pyrolysis deposition (HUSPD) to form uniform and compact film structures with homogeneously supplied precursor solution. To optimize the molar concentration and transparent conducting performance of the ATO films using HUSPD, we use precursor solutions of 0.15, 0.20, 0.25, and 0.30 M. As the molar concentration increases, the resultant ATO films exhibit more compact surface structures because of the larger crystallite sizes and higher ATO crystallinity because of the greater thickness from the accelerated growth of ATO. Thus, the ATO films prepared at 0.25 M have the best transparent conducting performance (12.60±0.21 Ω/□ sheet resistance and 80.83% optical transmittance) and the highest figure-of-merit value (9.44±0.17 × 10-3 Ω-1). The improvement in transparent conducting performance is attributed to the enhanced carrier concentration by the improved ATO crystallinity and Hall mobility with the compact surface structure and preferred (211) orientation, ascribed to the accelerated growth of ATO at the optimized molar concentration. Therefore, ATO films fabricated using HUSPD are transparent conducting film candidates for optoelectronic devices.

Carbon nanofiber (CNF) is used as an electrode material for electrical double layer capacitors (EDLCs), and is being consistently researched to improve its electrochemical performance. However, CNF still faces important challenges due to the low mesopore volume, leading to a poor high-rate performance. In the present study, we prepared the unique architecture of the activated mesoporous CNF with a high specific surface area and high mesopore volume, which were successfully synthesized using PMMA as a pore-forming agent and the KOH activation. The activated mesoporous CNF was found to exhibit the high specific surface area of 703 m2 g−1, total pore volume of 0.51 cm3 g−1, average pore diameter of 2.9 nm, and high mesopore volume of 35.2 %. The activated mesoporous CNF also indicated the high specific capacitance of 143 F g−1, high-rate performance, high energy density of 17.9-13.0Wh kg−1, and excellent cycling stability. Therefore, this unique architecture with a high specific surface area and high mesopore volume provides profitable synergistic effects in terms of the increased electrical double-layer area and favorable ion diffusion at a high current density. Consequently, the activated mesoporous CNF is a promising candidate as an electrode material for high-performance EDLCs.

적외선을 이용한 무기체계의 발달로 인해 항공기의 생존은 큰 위협에 직면해 있다. 따라서 항공기의 생존성 향상을 위해 서 적외선 스텔스 기술이 매우 중요하다. 본 논문에서는 수치해석을 통해 실제 비행환경에서의 항공기 표면온도 및 주위 배 경에 따른 적외선 신호를 분석하고 이를 바탕으로 적외선 스텔스를 위한 항공기 표면 구조체 방사율의 가이드라인을 제시하 고 그 성능을 검증하고자 한다. 수치해석 결과, 주위 배경에 따라서 항공기 표면 방사율을 최적화한다면 항공기와 배경간의 복사대비강도를 감소시킬 수 있음을 확인하였다.

본 연구에서는 막구조 건축물의 유지관리를 위한 막재의 표면 및 코팅층의 열화진단을 수행하였다. 막재는 내화학성능 및 내부식 성능을 포함하는 내구성능이 가장 중요시 되는 재료이다. 일반적으로 대공간 건축물의 지붕재료로 사용되는 막재의 유지관리 진단항목은 막재의 표면 열화진단, 막재의 코팅층 열화진단, 막재의 코팅층 및 섬유포 사이의 열화진단, 막재 전면에 걸친 열화진단, 로프의 열화진단, 보강벨트의 열화진단, 커버고무 등의 열화진단 등으로 대별된다. 본 연구는 대공간 건축물의 지붕재료로 많이 사용되는 PVDF계 막재를 대상으로 표면 및 코팅층의 열화도 진단 결과를 보고한다.

Mold infestation problems in building are a complex phenomenon due to various causes such as environmental conditions including temperature and relative humidity, substrates (building materials), exposure time, and so on. Earlier studies showed the interrelationship among humidity, temperature conditions and mold growth. However, surface structure also can be a key factor to mold germination. This study conducted experiments on the mold germination and growth on wallpapers with different surface structures. Four wallpapers and two fungal species (Aspergillus versicolor, Penicillium chrysogenum) were selected for experiment and observed fungal germination and growth on the different surface structures of wallpapers using scanning electron microscope. The resulfts showed that the shape of the micro structure of wallpaper surface affected to the growth of fungi.

To improve the filtration efficiency of porous materials used in filters, an extensive specific surface area is required to serve as a site for adsorption of impurities. In this paper, a method for creating a hybridized porous alloy using a powder metallurgical technique to build macropores in an Al-4 wt.% Cu alloy and subsequent surface modification for a microporous surface with a considerably increased specific surface area is suggested. The macropore structure was controlled by granulation, compacting pressure, and sintering; the micropore structure was obtained by a surface modification using a dilute NaOH solution. The specific surface area of surface-modified specimen increased about 10 times compare to as-sintered specimen that comprised of the macropore structure. Also, the surface-modified specimens showed a remarkable increase in micropores larger than 10 nm. Such a hybridized porous structure has potential for application in water and air purification filters, as well as membrane pre-treatment and catalysis.

The influence of carbon surface area, carbon-oxygen groups associated with the carbon surface and the solution pH on the adsorption of Pb(II) ions from aqueous solutions has been studied using three activated carbons. The adsorption isotherms are Type I of BET classification and the data obeys Langmuir adsorption equation. The BET surface area has little effect on the adsorption while it is strongly influenced by the presence of acidic carbon oxygen surface groups. The amount of these surface groups was enhanced by oxidation of the carbons with different oxidizing agents and reduced by eliminating these groups on degassing at different temperatures. The adsorption of Pb(II) ions increases on each oxidation and decreases on degassing the oxidized carbons. The increase in adsorption on oxidation has been attributed to the formation of acidic carbon-oxygen surface groups and the decrease to the elimination of these acidic surface groups on degassing. The adsorption is also influenced by the pH of the aqueous solution. The adsorption is only small at pH values lower than 3 but is considerably larger at higher pH values. Suitable mechanisms consistent with the adsorption data have been suggested.

대기-해양의 상호작용과 제주도 후면에서 발생하는 카르만소용돌이행렬의 상관관계를 수치실험을 통하여 분석하였다. 카르만 소용돌이는 한라산의 제한된 높이에서 형성되는 경향을 가지고 있다. 그리고 본 연구에서는 900 hPa고도에서 카르만 소용돌이가 뚜렷이 생성되었다. 카르만소용돌이행렬의 발생초기에는 하나의 소용돌이세포가 나타나고 시간이 경과함에 따라 소용돌이는 이류를 한다. 이때 작은 소용돌이로 분리되는 경향이 있다. 분리된 소용돌이의 강도와 지속시간은 해수면 온도 분포와 밀접한 관계를 가진다. 즉 약한 해수면의 온도경도는 카르만 소용돌이의 지속 시간을 길게 하며, 산 후면의 소용돌이도를 감소시킨다. 강한 해수면 온도경도는 혼합층과 대기하층 수증기량을 증가시키고, 강화된 하층대기 혼합은 산악에 의하여 형성되는 기계적 응력을 감소시키는 경향이 있다.

다중채널 탄성파 자료를 이용하여 낙동강 하구 삼각주 지역 연약지반의 지반 특성을 구하기 위하여 S파 속도와 Qs-1 구조를 구하고 이를 시추조사 결과와 비교하였다. 다중채널 신호의 분산곡선을 역산하여 S파 속도구조를 구하고 감쇠지수(attenuation coefficient)를 구하였다. 다중채널 신호 중 음원에서 가장 가까운 신호를 기준 신호로 정하고 10 Hz에서 45 Hz 사이의 주파수에 대하여 거리에 따라 기준 신호에 대한 진폭의 비가 감소하는 정도를 나타내는 기울기를 구하여 감쇠지수를 결정하였다. 이 감쇠지수를 역산하여 지반 최상부 8 m 층의 S파 속도와 함께 Qs-1를 구하였다. 이 지역의 시추조사에 의하면 이 지역의 지층은 크게 상부 4 m 실트질 모래층과 하부 4 m 실트질 점토층으로 나누어진다. 표면파 역산에 의해 구해진 S파 속도와Qs-1를 시추조사 결과와 비교해보면, 상부 실트질 모래층에서 S파 속도의 공간적 해상도는 약 80m/sec로 하부 실트질 점토층의 속도 40m/sec보다 상대적으로 높은 값을 보인다. 각 층에서 S파 속도의 공간적 해상도는 뚜렷하다. Qs-1의 공간구조는 상부 실트질 모래층에서 약 0.02를 보이고 하부 실트질 점토층에서 0.03으로 증가하는 양상을 보인다. Qs-1의 공간적 해상도는 상부 약 5 m 구간에서는 양호하나 그 보다 깊은 곳에서는 공간적 해상도가 아주 낮아지는 것을 볼 수 있다. 이 조사지역에서는 실트질 모래층에서 실트질 점토층보다 높은 S파 속도가 나타나고 낮은 Qs-1 값을 보인다. 그러나, 지반의 S파 속도와 Qs-1를 결정하는 다른 많은 요인들이 있으므로 이를 일반화하기 위해서는 연약지반의 S파 속도와Qs-1에 관한 자료와 연구가 집적되어야 할 것이다.

Oligomer type anionic surfactants(RmM-Na or RmD-Na were synthesized from C8~C16 long chain alkylvinylether and maleic anhydride (or maleic diethylether). And also their fluorescent anionic surfactants (RmF- Na) were obtained from alkali neutralization which opens the lactone ring of the condensing materials produced by maleic anhydride alkylvinylether copolymer and 3-aminophenol. The measurement results for the surface active properties of water soluble oligomer type anionic surfactants with fluorescent structure (RmF-Na) exhibited a remarkable surface tension lowing property, foam breaking property, and a ernulsing power.

TiC(001) 면위에 Mg 금속을 단원자층으로 증착시킨 후 산화 및 열처리 과정을 거쳐서 MgO 초박막을 성장시키고, 성장된 MgO 막의 전자상태 및 표면포논을 UPS, XPS 및 HREELS를 사용하여 측정하였다. 전도성 기판위에 epitaxial 산화물막을 성장시킨 후 성장된 막의 전자구조 및 표면포논을 측정함으로써 벌크에서 분리된 2차원적 특성을 갖는 '표면 모델'의 물성을 연구하고자 하였는데, 이러한 '표면모델'은 잘 배열된 원자구조를 얻을 수 있고 두께가 충분히 얇아서 전하축적을 피할 수 있기 때문이다. 기판으로는 MgO와 같은 암염형 결정구조를 갖고 있고, 격자상수 차이가 2.6% 로서 매우 작으며, 비저항이 매우 낮은 전이 금속 탄화물 중의 하나인 TiC(001) 면을 사용하였다. TiC(001)면에 증착된 MgO층의 UPS He-l 스펙트럼을 측정한 결과 O2p및 XPS스펙트럼은 열처리를 전후로 하여 변하지 않았으며, 이로부터 상온에서 산소의 확산만으로 MgO 상이 형성됨을 알 수 있었다. MgO초박막의 표면 포논을 HREELS를 사용하여 검출하였다. 거시적 포논중에서 F-K 파 및 Rayleigh 모드가 관찰되었는데, F-k파는 MgO막의 2차원성으로 인하여 벌크의 경우보다 높은 진동 에너지를 갖고 있었고 Rayleigh모드는 벌크 MgO와 유사한 분산관계를 보였다. 미시적 포논중에서 Wallis(S2)모드가 측정되었는데, 그 진동에너지는 벌크에서와 같고 off-specular방향에서도 소멸되지 않았다.