        검색결과 4

        1.
        2023.05 구독 인증기관·개인회원 무료
        Corrosion-related challenges remain a significant research topic in developing next-generation Molten Salt Reactors (MSRs). To gain a deeper understanding of preventing corrosion in MSRs, previous studies have attempted to improve the corrosion resistance of structural alloys by coating surfaces such as alumina coating. To conduct a corrosion test of coating alloys fully immersed in molten salt, it’s important to ensure that the coating application process is carefully carried out. Ideally, coating all sides of the alloy is necessary to avoid gaps like corners of the alloy, while only applying a one-sided coating alloy can lead to galvanic corrosion with the base metals. Using the droplet shape of eutectic salt applied to only one side of the coating alloy would avoid these problems in conventional corrosion immersion tests, as corrosion would occur solely on the coating surface. Although the droplet method for corrosion tests cannot fully replicate corrosion in the MSRs environment, it offers a valuable tool for comparing and evaluating the corrosion resistance of different coating surfaces of alloys. However, the surface area is important due to the effect of diffusion in the corrosion of alloy in molten salt environments, but it is difficult to unify in the case of droplet tests. Therefore, understanding the droplet-alloy properties and corrosion mechanism is needed to accurately predict and analyze these test systems’ behavior highlighting unity for corrosion tests of different coating surfaces of alloys. To analyze the molten salt droplet behavior on various samples, pelletized eutectic NaCl-MgCl2 was prepared as salt and W-, Mo-coating, and base SS316 as samples. At room temperature, the same mass of pelletized eutectic NaCl-MgCl2 was placed on different samples under an argon atmosphere and heated to a eutectic point of 500°C in a furnace. After every hour, the molten droplets were hardened by rapid cooling at room temperature outside the furnace. The mass loss of salts and the contact area of the samples were measured by mass balance and SEM. The shape, surface area to volume ratio, and evaporation of the droplets of NaCl-MgCl2 per each coating sample and hour were analyzed to identify the optimal mass to equalize the contact coating surface of alloys with salts. Furthermore, We also analyzed whether their results reached saturation of corrosion products through ICP-MS. This will be significant research for the uniformity of the liquid-drop shape corrosion test of the coating sample in molten eutectic salts.
        2.
        2022.06 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Novel Ni- and Fe-based alloys are developed to impart improved mechanical properties and corrosion resistance. The designed alloys are manufactured as a powder and deposited on a steel substrate using a high-velocity oxygen-fuel process. The coating layer demonstrates good corrosion resistance, and the thus-formed passive film is beneficial because of the Cr contained in the alloy system. Furthermore, during low-temperature heat treatment, factors that deteriorate the properties and which may arise during high-temperature heat treatment, are avoided. For the heattreated coating layers, the hardness increases by up to 32% and the corrosion resistance improves. The influence of the heat treatment is investigated through various methods and is considered to enhance the mechanical properties and corrosion resistance of the coating layer.
        4,000원
        3.
        2014.06 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Using alkali treatment solution, neutrality treatment solution and acid treatment solution, the surface corrosion layer of copper plates and bronze plates that have been artificially corroded using HCl, H2SO4 and HNO3 solutions were removed. In the case of alkali treatment solution, only air oxidation in the form of black tenorite and white cuproous chloride remained without being removed. In the case of using a neutrality treatment solution, a anhydrous type layer of reddish brown cupric chloride remained without being removed, together with this black and white corrosion substance. In the case of using an acid treatment solution, this red corrosion substance also remained, but all of the oxide was removed on the surface of the specimen that was treated by alternatively using alkali treatment solution and acid treatment solution. In the case of this treatment solution with the order of alkali-acid, oxidation no longer proceeded only through the distilled water cleaning process after treatment, thereby showing that oxidation from the cleaning solution no longer proceeded.
        4,000원
        4.
        2010.04 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        Chromium nitride (CrN) samples with two different layer structures (multilayer and single layer) were coated on bipolar plates of polymer electrolyte membrane fuel cells (PEMFC) using the reactive sputtering method. The effects with respect to layer structure on corrosion resistance and overall cell performance were investigated. A continuous and thin chromium nitride layer (Cr0.48 N0.52) was formed on the surface of the SUS 316L when the nitrogen flow rate was 10 sccm. The electrochemical stability of the coated layers was examined using the potentiodynamic and potentiostatic methods in the simulated corrosive circumstances of the PEMFC under 80˚C. Interfacial contact resistance (ICR) between the CrN coated sample and the gas diffusion layer was measured by using Wang's method. A single cell performance test was also conducted. The test results showed that CrN coated SUS316L with multilayer structure had excellent corrosion resistance compared to single layer structures and single cell performance results with 25 cm2 in effective area also showed the same tendency. The difference of the electrochemical properties between the single and multilayer samples was attributed to the Cr interlayer layer, which improved the corrosion resistance. Because the coating layer was damaged by pinholes, the Cr layer prevented the penetration of corrosive media into the substrate. Therefore, the CrN with a multilayer structure is an effective coating method to increase the corrosion resistance and to decrease the ICR for metallic bipolar plates in PEMFC.
        4,000원