The leisure life pattern of people is changing to a familial and enthusiastic way that eventually develops the camping culture. Thus, the number of campers and the size of camping market have been dramatically increased due to significant expansion of camping people. However, many camp grounds and facilities are operating without a proper registration by government rules and regulations. In addition, many of electronic and gas equipment and tools are not used in a safe way and in a safety regulatory boundary. Therefore, campers at the camping ground is situated in a fire and safety hazard. In addition, there is limitation in rules and regulations associated with camping ground safety and fire. This study analyzed the fire and hazard guidelines and rules regulations of developed countries of campground and compared them to the current situation in South Korea. Therefore, this study is to develop a safety and fire hazard guidelines and rules and regulations related to camp ground operation, gas and electronic equipment operation and management. The study will eventually reduce the future fire and safety incidents in a campground in South Korea.

A fire sprinkler system is very important to extinguish fire in the building. The sprinkler system initiates sprinkler discharge if the detection system identifies a developing fire and opens the pre-action valve. However, pre-action fire sprinkler systems mainly installed in the underground parking lot at the apartment complex do not properly operate at fire if the connection type of fire sprinkler systems does not properly installed and operated. This study identified the relationship between fire dispersion & damage and the connection type of water supply in the sprinkler system from many fire cases at the apartment complex in South Korea. In addition, this study also identified the water supply differences and characteristics between South Korea and foreign countries. The main purpose of this study is also to improve the water connection types in the sprinkler system that can reduce the potential failures of pre-action valve operation through electrical signal system. The study also suggests the improvement plan for water connection types in pre-action fire sprinkler system that can minimize potential failure of pre-action fire sprinkler system. The suggestions for revising the fire safe standard in South Korea includes letting the water supply pipe of sprinkler system water inlet connect to the second side of pre-action valve and the water flow device that can minimize potential failure of sprinkler system.

Crimes with explosives is one of the mass-destructive crimes that involves the most victims. It is heavily punished under the Korean laws. Mid-eastern area is one of the leading places that are home to improvised explosive device attacks, in the form of religious or political terrorism because of its convenience of use, production and disguise. Improvised bombs are permeating into domestic crimes in Korea as their tools. Use of explosive substances are strictly restricted in this country, but it is not impossible to find its information online and to create private explosives with a bit of interest. And they are being traded in the grey market. For this reason, this thesis offers the method of an efficient safety control of explosive substances, which can be used as raw materials for improvised explosive devices, in order to protect citizens’lives and properties and to promote national security down the road.

This study is about determination of fire origin by using analysis of shadow that was recorded CCTV data at the fire scene. This analysis is based on straight and radiate nature of light. At fire experiment with about 1m flame, we conformed that 2-dimensional extension line is focused at the bottom of the fire. If the fire is burning at the same level with shadow, it indicate the point of origin exactly. In 3-dimensional analysis that connect extensional line between distinctive points the shadow and the objet, the line focused in the Ø 50cm-circle. We estimate the reason of that is because of the character of combustion of gases. The line indicate not the point of origin but the flame that is over the point of origin. thus, you have to consider the line indicate the flame when you do 3-dimensional analysis.

It is not an exaggeration to say that modern chemicals take a leading place in our life, and people live with the chemicals, having a huge impact on their daily life. The chemical industry in South Korea, ranked seventh in the world, is one of the key industries that are forming greater part of Korean economy. The actual state of the chemical industries, however, is that over 14 tons of hazardous chemicals are being discharged annually and threaten people's lives with a lack of knowledge of its potential danger. In this way, not only beneficial to us, some of these substances, All chemicals, but also present a threat fundamentally our living environment to hazards to human health and the environment, accidents such chemicals, unlike accidents general understanding the scale of damage and propagation velocity has a complex very difficult risk profile, that can occur during deployment of an accident type is also very diverse. Is the actual situation of public concern against harmful chemicals management's is amplified by the chemical accident in the wake such accidents, government and corporate and reactive system and management system prior to the chemical accident the need for communication to exchange ideas with each other between residents, providing information is important. Therefore, the government departments and corporations, which manage variety of chemicals, ought to contribute toward a development of national security by rigid control over the Hazardous chemicals.

The purpose of this study was to assess power loss in the computer and office automation equipment and identified a way to save power consumptions through field measurement. In this study, the meaning of standby power was to consume power while waiting for the use of any electronic equipment. This standby consumption was about 11% of total power consumption even though we did not seriously realize it. Therefore, it was very important to measure accurate power consumption at the standby status of electronic equipment. In addition, it also helped to reduce potential risks of electricity associated disasters. This study proposed the way to reduce power losses through automatic turn off switches for power outlets and switches. Finally, this study can evaluate power consumption patterns that can reduce power consumptions and potential risks of power related disasters. This also can achieve the goals of sustainability that can reduce environmental impacts by lowering energy consumptions and greenhouse gas emissions.

When a fire breaks out, it is difficult to find out the causes of the fire, because combustible things around fire scene are usually burnt away. Among many causes of fires are electronic wires, this thesis deal with the destroyed sheath of electronic wires caused by fire. It was studied with the use of measurement devices focusing on the distinctions of wires and conductors. This study especially emphasized the process of deterioration, burning pattern, and composition of electronic wire conductor. It also has a phenomenological approach to the distinctive cause of fire by some partial force. The fire prevention methods have been suggested through the analysing results of fire patterns. This study is expected to be a useful material for analyzing various electrical fires.

The victims of fire are increasing steadily. Fires have been occurred by arson, spontaneous combustion and various causes. As a result of that, the damages of fire got out of hand. Especially, the fires of flammable liquids are can be spreaded easily because of high calorific value and fire loads. These rapid fire spread cause the huge losses of both life and property and the malfunction of extinguishing systems. In these studies, we examined the spread pattern of surface fire on the water surface by the reappearance experiment.

As a results of comparing with fire occurrences and gross national income(GNI), annual fire increasing rate has been 5.6%, and that of GNI has been 11% for the past 55 years. As GNI shows 5.4% higher than fire occurrences, economy growing rate is faster than that of fires. In addition, study has been done every 10 years from 1950's to 2000's. Fire occurrences increase twice as much annually and GNI increases above 3.3 times as much.

국보 1호인 숭례문 화재는 화재조사자뿐만 아니라 국민들에게 크나큰 아픔을 안겨 주었다. 이 연구의 목적은 현장조사를 통하여 목조 문화재 화재 시 생성되는 연소패턴과 목재 마루바닥에 인화성물질을 살포 후 착화하였을 때 나타나는 촉진제에 의한 연소 흔적 등을 확인하는데 있다. 또한 이 연구결과는 유사한 화재 발생 시 화재조사요원에게 정확한 화재 원인을 감식할 수 있는 자료가 될 것이다.

The aim of these studies is to confirm the red and blue painting damages during the fire suppression of wooden cultural assets by using the loaded stream charge extinguishant. As a results of these experiments, the ingredients of extinguishant existing on the surface of wooden cultural assets were perfectly eliminated by the water washing only. Any changes on the surface of wooden cultural assets couldn't be detected. Moreover, any color changes of the red and blue painting didn't occur.

SMC(Sheet molding compound)욕조 생산시 발생하는 폐 FRP를 보강재로서 재활용하기 위하여 불포화 폴리에스테르 매트릭스 수지에 보강하고 보강재와 매트릭스 수지의 계면 결합력을 증진시키기 위하여 보강재를 실란계 커플링제[3-methylacryloxyviny1 silane (MAOS)]로 전 처리하여 복합재를 제조하고 기계적 물성 및 계면현사에 대하여 관찰하였다. 보강률이 20wt%인 복합재의 굴곡강도 및 굴곡탄성률이 각 각 110MPa, 8.0GPa로 가장 우수하였으며 커플링제(MAOS)의 노동가 0.50wt%인 복합재의 굴곡강도 및 굴곡탄성률은 약 10%정도 향상되어 각 각 120MPa, 9.2GPa을 나타내었다. 또한 주사전자현미경 관찰 결과 보강재를 커플링제(MAOS)로 처리한 복합재의 보강재와 매트릭스 수지는 물리, 화학적을 잘 결합하여 보강재와 매트릭스 수지의 계면에서 pull out현상이 확인되지 않았으며 크랙도 발생하지 않았다.

PAN계 탄소섬유와 페놀수지를 이용하여 rod를 인발성형 한 후, 다른 섬유분율을 갖는 두종류의 hexagonal type 4D 프리폼을 제작하였다. 석탄계 핏치를 가압함침 탄화공정을 통하여 함침한 후 탄화와 고온열처리를 하였다. 이와 같은 공정을 반복하여 고밀도화된 4D CRFC를 제조하였다. 열충결 시험 후 새로운 크랙이 생성되었을 뿐만 아니라 기존의 크랙이 확장되었으며 이와 같은 크랙들은 공기와의 접촉면을 제공하여 중량감소를 보였다. 공기 산화 저항성을 고온열처리 공정을 거친 것이 약 20% 우수하게 나타났다. 4D CFRC의 밀도와 섬유의 분율이 높을 수록 삭마 저항성이 커지고, 삭마량은 시간에 따라 선형적으로 증가하였으며 type II가 type I보다 삭마저항성이 우수하였다. 삭마 메카니즘을 관찰한 결과 1차적으 기질의탈리가 먼저 일어난 다음 섬유가 삭마되었다.

페놀수지 결합재에 PAN섬유(PF), PAN계 탄소섬유(CF) 그리고 아라미드 섬유(AF)를 보강재로 사용하여 단일섬유 보강복합재를 제조하였으며 이들 섬유를 각각 두 종류씩 혼성하여 혼성섬유 보강복합재를 제조하였다. 각 보강복합재를 섬유의 보강분율에 따른 마찰 및 마모특성을 시험하였다. CF 보강복합재(CFRP)가 마찰계수와 마모량이 가장 낮게 나타났으며, PF 보강복합재(PFRP)는 가장 높은 마찰계수와 마모량을 나타내었다. PF에 CF나 AF를 보강한 혼성복합재의 경우 마찰계수가 0.311~0.328로 혼성비에 따라서는 큰 차이를 보이지 않은 반면, PF의 보강분율이 증가할수록 마모량은 증가하였다. CF와 AF를 보강한 혼성복합재의 마찰계수는 0.264~0.309로 가장 낮게 나타났고, AF의 보강분율이 증가함에 따라 마찰계수는 증가하는 양상을 나타내었으며, 가장 적은 마모량과 함께 안정된 마모형태를 보였다.

페놀수지 결합재에 보강섬유의 종류에 따라서 내염섬유 보강 복합재(OFRP), 탄소섬유 보강 복합재(CFRP), 유리섬유 보강 복합재(GFRP), 아라미드 섬유 보강 복합재(AFRP)를 제조하였다. 각 보강섬유의 분율을 달리함에 따라 마찰계수 및 마모율을 측정하여 각 보강섬유의 특성이 미치는 영향을 관찰하였다. 아라미드의 섬유량이 45tw%일 때 평균 마찰계수가 0.353-0.383으로 가장 높게 나타난 반면에 핏치계 탄소섬유를 45wt% 보강한 경우 0.164-0.190으로 가장 낮게 나타났다. AFRP와 CFRP의 마모율은 낮게 나타내었으며, GFRP와 OFRP는 섬유분율이 증가함에 따라 급격히 증가하는 양상을 보였다. OFRP는 마모 diagram이 불안정하였으며 CFRP와 AFRP는 대체적으로 안정한 형태를 나타내었다. GFRp는 상당히 불안정한 마모diagram을 나타낸 것으로 보아 마찰 안정성이 가장 떨어짐을 알 수 있었다.

본 연구에서는 원료 석탄 핏치와 흑연화성이 우수한 THF 가용성분만을 추출한 핏치 결합재에 8H/Satin woven fabric 프리프레그 및 고탄성 및 고강도계 연속 탄소섬유 등을 보강하여 가압열성형법으로 green body 를 제조한 다음 탄화, 함침, 재탄화 및 흑연화 공정을 거쳐 열적 미 기계적물성이 우수한 CFRC를 제조하였으며, 주사전자현미경, 편광현미경, X선회절분석,열중량분석, 굴곡강도, 굴곡탄성률, 충간전단강도 등을 시험하였다. THFSP결합재를 2300˚C까지 열처리 한 다음 X선회절분석을 한 결과, 결정성이 가장 우수하여 (002) 면에서 C0/2인 값이 3.380Å였으며, 2θ값도 26.276˚로 천연흑연의 Bragg angle에 거의 접근하였으며 공기산화 반응특성을 시험하기 위하여 등온 열중량분석을 한 결과 2300˚C까지 흑연화 한 THFSP결합재가 산화에 대하여 가장 우수한 저항성을 나타내었다. 섬유용적률이 증가됨에 따라 65~70%까지는 기계적 물성이 중가하는 경향을 보였지만 그이상 섬유가 보강된 CFRC는 결합재의 부족으로 인하여 오히려 기계적 물성이 감소하였다. 또한 굴곡강도 시험후 주사전자현미경으로 파괴 단면을 관찰한 결과 THFSP결합재가 흑연화성이 우수하여 파괴시 결합재가 외력에 대한 흡수가 양호하여 보강재의 파괴를 억제했기 때문에 기계적 물성도 우수하게 나타났다.

탄소/탄소 복합재의 산화 저항성을 개선시키기 위하여 aluminum iso propoxide및 aluminum tri sec butoxide졸을 2D-탄소/탄소 복합재에 도포하여 산호 억제층으로서의 효과를 관찰하였다. 촉매/알콕사이드의 몰비가 0.07, 물/알콕사이드의 몰비가 100일때의 산화 억제효과가 양호했으며, 승온속도를 20˚C/min로 하여 승온분석시험한 결과는 도포시편이 80˚C 정도의 산화 개시온도가 20%감소되는 시간을 측정한 TGA분석에서는 도포시편이 20% 정도의 산화 저항성 개선효과를 나타냈다. 도포막의 두께는 1회 도포막이 3μm, 2회 및 3회 도포막이 4-5μm 정도였고, 열충격 시험은 횟수에 따라 산화량이 증자하였다. 5% 전환률에서의 도포하지 않은 시편의 활성화 에너지는 33.2Kcal/mole이었으며 도포시편의 활성화 에너지는 37.1Kcal/mole이었다.

본 연구에서는 2D-woven fabric에 결합재로 페놀수지를 사용하여 성형한 CFRP의 탄화거동을 관찰하였다. TMA분석 결과 적층 두께방향에서는 365-370˚C 법선방향에서는 118-128˚C 에서 치수변화가 일어났다. 각 온도 구간별로 광학현미경으로 관찰한 결과 CFRP제조시 형성된 크랙이나 기공은 열처리온도에 따라 성장하였으며, 400-500˚C 부근에서 새로운 많은 크랙이 형성되었다. 기공률과 밀도가 400-500˚C 에서 급격히 변화한 것을 볼 때 이 구간에서 복합재 내부에서 크랙이 형성 및 성장하는 것을 알 수 있었다. 따라서 CFRP를 탄화할 때 승온속도를 구간별로 조절할 필요성이 있는 것으로 판단되었다.