Copolymers (HSA-98-20, HSA-98-0, HSA-98+20) which are acrylic resin containing 80% solid content were synthesized by the reaction of monomers, including methyl methacrylate, n-butyl acrylate, and 2-hydroxyethyl acrylate with a functional monomer, such as acetoacetoxyethyl methacrylate (AAEM), which may improve in cross-linking density and physical properties of films. The physical properties of prepared acrylic resins, containing AAEM, are as follows : viscosity, 1420~5760cps ; number average molecular weight, 2080~2300 ; polydispersity index, 2.07~2.19 ; conversions, 88~93%, respectively. To prepare acryl resins, four kinds of initiators including α,α'-azobisisobutyronitirile (AIBN), di-tert-butyl peroxide (DTBP), t-amylperoxy-2-ethyl hexanoate (APEH), benzoyl peroxide (BPO) were used. The viscosity of the acrylic resins prepared with these initiators was increased in the order of DTBP〉APEH〉AIBN〉BPO. APEH was proved as a suitable initiator in this study. Shear rates of acrylic resins were constant in respect to viscosity. From these results, it would appear that the resins have Newtonian flow characteristics and good workability.

The physical characteristics of polyurethane were examined by SEM, FT-IR tensile strength and mole % [NCO/OH]. Growing concerns in the environment-friendly architecture and public works have led to the development of solvent-free formulations that can be cured and foamed in air. Compared with general packing materials, this resin is much stronger in intensity and much longer in durability. Polyurethane foam resins were mainly composed of polyol, MDI, silicone surfactant, fillers, catalyst and blowing agent. The rigid foam of polyurethane in mechanical characteristics were due to chain extender and the increase of mole % [NCO/OH]. The change in the microstructure of polyurethane should be taken into account when considering the process of construction and durability through the polyurethane polymer resin in lots of industries.

본 연구는 상토의 보수성 증가를 위하여 혼합되는 acrylamide 계통 고흡수성 수지인 Stocksorb C(STSB)의 수분 흡수 특성, 수분 흡수에 영향을 미치는 각종 무기염의 종류 및 농도, STSB가 침지된 외부용액속의 무기염 농도 변화를 구명하고자 수행하였다. STSB의 수분 흡수량은 증류수에 침지한 경우 약 180 mL·g-1였다. 1가의 양이온을 포함한 염인 KH2PO4, KNO3 또는 (NH4)2SO4를 용해시킨 용액의 농도가 높아질수록 흡수량이 저하되었으나 세 종류 양이온의 종류에 따른 차이는 크지 않았다. Ca(NO3)2·4H2O 다양한 농도로 용해시킨 용액 속에 STSB를 침지시킨 경우 수분흡수능 저하가 심하여 20 meq·L-1Ca(NO3)2·4H2O 용액에서 약 25 mL·g-1 수분을 흡수하였다. Mg(NO3)2·6H2O나 MgSO4·7H2O를 용해시킨 용액의 농도가 높아질수록 수분 흡수량이 심하게 저하하였고, 1가의 양이온이 포함된 염을 용해시킨 용액에서보다 그 정도가 심하였다. 그러나 요소의 농도를 증가시킨 용액에서의 수분 흡수량은 저하되지 않았다. 침지전 Hoagland용액의 농도가 높거나, 침지시간이 길어질수록 STSB를 침지시킨 용액에서의 K+및 NH4+-N의 농도가 점차 높아졌다. Hoagland 용액의 희석배수와 무관하게 침지시간이 길어질수록 외부용액의 NO3--N, H2PO4- 및 SO4-2 농도가 약간 상승하였고, 24시간 경과 후 각각 5,300, 250 및 1,500 mg·L-1 농도로 분석되었다.

본 연구는 혼합상토에 polyacrylamide 고흡수성 수지 Stocksorb C를 혼합할 경우 혼합상토 종류별 화학성에 미치는 영향을 밝히기 위하여 수행하였다. 네종류 혼합상토, 피트모쓰+버미클라이트(PV, 1:1; v/v), 피트모쓰+부숙왕겨(PR, 1:1: v/v), 피트모쓰+부숙톱밥(PS, 1:1; v/v), 그리고 피트모쓰+부숙수피(PB, 1:1; v/v)를 조제하는 과정에서 STSB를 혼합하고 5주 후에 측정한 상토의 pH는 모두 7.04~7.30 범위에 포함되어 너무 높았다. STBS의 혼합량이 많아질수록 전기전도도도 상승하였고, 네 종류 상토에서 처리 간 통계적인 차이와 함께 직선 및 2차곡선회귀가 성립하여 경향을 찾을 수 있었다. STBS의 혼합량이 많아질수록 상토의 NH4+-N, NO3--N, PO4-P3-, K+, Ca2+ 및 Mg2+ 농도가 높아졌다. 그러나 PS 상토에서는 다른 세 종류 상토에서 보다 상대적인 NO3--N의 농도가 낮았다. STSB의 혼합비율이 증가함에 따라 PV, PR 및 PS 상토에서의 Fe2+ 농도가 높아졌으나, PB 상토에서는 경향을 찾을 수 없었다. 또한 PS 상토에서의 Fe2+, Mn2+, Cu2+ 및 Zn2+ 농도가 다른 세 종류 상토에서 보다 높았다.

본 연구는 혼합상토의 보수성 증가를 위하여 polyacrylamide 고흡수성 수지 Stocksorb C를 혼합할 경우 상토의 물리성에 미치는 영향을 밝히기 위하여 수행하였다. 네종류 혼합상토, 피트모쓰 + 버미큘라이트(1:1 , v/v; PV), 피트모쓰+부숙왕겨(1:1, v/v; PR), 피트모쓰+부숙톱밥(1:1, v/v; PS), 그리고 피트모쓰+부숙수피(1:1, v/v; PB)를 조제하는 과정에서 STSB를 혼합하고, 플라스틱 포트에 충전하였으며, 5주 후에 상토의 물리적 특성을 측정하였다. STSB의 혼합비율이 증가할수록 PV, PS 및 PB 상토의 공극률이 증가하여 5% 수준의 통계적인 차이가 인정되었고, 직선 또는 2차곡선회귀가 성립하여 경향을 찾을 수 있었다. STSB의 혼합비율 증가로 PS와 PB상토의 용기용수량이 뚜렷하게 증가하였으나 PV 및 PR상토에서는 STSB의 혼합비율에 따른 처리간 차이가 인정되지 않았다. 특히 STSB의 혼합은 PV PS및 PB 상토의 기상률을 뚜렷하게 증가시켜 처리간 통계적인 차이와 함께 직선 및 2차곡선회귀가 성립하여 경향이 뚜렷하였다. 고흡수성 수지의 혼합비율이 높아질수록 4.90 kPa, 9.81 kPa, 29.4 kPa및 1.5 MPa 토양 수분장력 하에서 존재하는 수분량이 많았다. 각 상토별로 29.4 kPa이나 1.5 MPa에서 존재하는 수분은 PV 혼합상토에서 적었고, PB와 PR 혼합상토에서 유사한 수준이었으며, PS 혼합상토에서 가장 많았다. 이는 고흡수성 수지의 혼합비율이 높아짐에 따라 상토가 보유하는 수분량이 증가하지만 식물이 쉽게 흡수할 수 있는 수분량이 증가하지 않음을 의미한다.

Cs 이온에 대해 선택성을 갖는 ferrocyanide-음이온 교환수지를 제조하여 모의 제 염폐액 내에 존재하는 Cs 이온에 대한 흡착실험을 수행하였다. 제조된 이온교환 수지가 citric acid를 주제염제로 하는 제염폐액 내에 존재하는 Cs+ 이온에 대한 흡착능력은 상용 양이온교환수지에 비해 4배 이상 효과적인 것으로 나타났다. 모의 제염폐액과 선택성 이온교환수지를 접촉시킨 후 360분이 경과하면 금속이온에 대한 흡착반웅이 평형에 도달하였다. 본 연구범위에서 Co 이온농도가 필요이상 증가하게 되면 Cs 이온의 흡착율은 감소하였다. 과산화수소와 히드라진을 사용한 선택성 폐 이온교환수지의 재생실험 결과 전기중성화조건을 만족시키기 위해 Cs 이온이 수지로부터 용출됨을 확인하였고 열화없이 재 사용가능성을 확인하였다.

High-solid coatings were prepared by blending of previosly synthesized acrylic resins and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, cross-hatch adhesion, 60˚specular gloss, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. As a result of Rigid-body pendulum visco-elasticity measurement, dynamic Tg values of cured films increased with dynamic Tg values.

구름이 유입하는 경우 해양대기경계층의 발달을 분석하기 위하여, 울릉도에서 관측한 레윈존데 자료와 AWS 자료, 위성사진, 동해에 설치된 부이 자료를 이용하였다. 이 자료를 이용하여 열의 이류와 표층 열속, 구름 유입에 따른 복사에너지를 추정하였다. 혼합층 내의 열 변화 및 혼합층의 발달을 표층 열속과 구름에 의한 장파복사속으로 설명하였다. 열속의 변화를 알아보기 위해 벌크법을 이용하였다. 울릉도, 동해상의 부이, 포항에서 관측한 자료를 이용한 열수지 방정식으로 대기경계층의 열보존 관계를 분석하였다. 구름의 유입으로 인해 일몰 후 지면의 복사냉각이 방해되고, 구름에서 장파복사가 방출된다. 그로 인해 야간에 오히려 기온이 증가하였다. 또 남서쪽으로부터 따뜻한 공기가 이류되어, 하층 대기의 온도를 증가시켰다. 이러한 이유로 혼합층이 파괴되지 않고, 잔류층을 형성하며 남아있었다.

Acrylic resins (HSCs : EA/EMA/2-HEMA/CLA) which contain 70% solid content were synthesized by the copolymerization of monomers (2-hydroxyethyl methacrylate, ethyl acrylate, and ethyl methacrylate) and functional monomer (caprolactone acrylate : CLA) which improves the crosslinking density and physical properties of films. The physical properties of the prepared acrylic resins (HSCs) containing CLA, are as follows : viscosity 245~515 cps ; Mn 2670~2840 ; and conversions, 83~91%, respectively. From the correlation of Tg values, viscosities, and Mn of the HSCs, it was found that viscosity and Mn increased with Tg value.

반응성 페놀수지 폐액을 처리하기 위해 중공사막 모듈을 이용한 투과증발 막 탈수공정을 연구하였다. 이 공정의 거동을 예측하기 위한 모사모델을 확립하였고 여기에 사용되는 중요 기본 파라메타들을 평판형 막을 사용하여 직접 구하여 사용함으로써 공정모사의 정확성을 얻을 수가 있었다. 이들을 모사치와 중공사 투과증발 막으로 부터 직접 측정한 각 투과특성들을 비교한 결과 서로 잘 일치함을 보여 본 모사모델의 타당성을 입증하였다. 사용된 중공사막은 중공사 안쪽에 활성층이 도포되어 있으며 공급액은 중공사 내부로 공급하였다. 공급액의 막내에서의 흐름속도에 따라 온도분포가 결정되며 이에 따라 막 투과특성이 달라짐을 모사결과로부터 얻을 수가 있었다. 공급액 온도증가는 막을 통한 탈수 투과 속도를 증가시킬 뿐 아니라 반응속도 증가로 인하여 물 생성속도도 증가시킴으로써 공급액 저장조 내의 수분 함량은 이들 상반된 공정들에 의해 결정이 됨을 보였다. 투과압력이 공급액 증기압보다 훨씬 작은 범위에서 증가할 경우 투과추진력인 공급액과 투과부의 투과물 활성도비 감소가 크지 않아 투과특성을 약간 저하시킨다. 그러나 투과압력이 공급액의 증기압에 접근할 경우 활성도비 감소가 현저하게 일어나 투과특성저하가 급격히 일어난다.

The high-solid coatings were prepared by blending the synthesized acrylic resin in the previous paper and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, 60℃ specular gloss, cross-hatch adhension, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. From a viscoelastic measurement using a rigid-body pendulum, curing was accelerated with the Tg value. With the increase in Tg, log damp value was lowered and dynamic viscoelasic Tg of a cured film was increased.

A copolymer 〈HSAs : EA/EMA/2-HEMA/AAEM) which is an acrylic resin containing 70% solid content was synthesized by the reaction of monomers, including ethyl acrylate, ethyl methacrylate, and 2-hydroxyethyl methacrylate with a functional monomer, such as acetoacetoxyethyl methacrylate, which may give improvements in cross-linking density and physical properties of films. The physical properties of prepared acrylic resins, HSA containing AAEM, are as follows : viscosity, 203~550cps ; Mn, 2590~2850 ; and conversion, 82~89%, respectively. It was found from the plotting of Tg versus viscosity and Tg versus molecular weight that viscosity increased with Tg while number averaged molecular weight decreased with increasing Tg.