Nano Fe-6.5wt%Si powders have been synthesized by mechano-chemical process (MCP) for an application of soft magnetic core. Owing to hard and brittle characteristics of Fe-6.5Si nano powders having large surface area, it is very difficult to reach high density more than 70% of theoretical density (~7.4 g/) by cold compaction. To overcome such problem a magnetic pulsed compaction (MPC), which is one of dynamic compaction techniques, was applied. The green density was achieved about 78% (~5.8 g/) by MPC at room temperature.

1. The oxidation resistance of containing Ni-base alloy is superior to that of the alloy without . 2. The appearance of oxides of Ni-20Cr-20Fe-5Nb- alloy is similar to that of oxides in commercial PM1000 and MA754 alloy. 3. The oxides in ODS alloy are grown mainly at particle boundaries.

Mechanically-alloyed NiAl powder was sintered by Spark-Plasma Sintering (SPS) process. Densification and behavior mechanical property were determined from the experimental results and analysis ,such as changes in linear shrinkage, shrinkage rate, microstructure, and phase during sintering process, Victors hardness, and transver.ie-rupture-strength (TRS). Above 97% relative density was obtained after sintering at 115 for 5 min. Crystallite size determined by the Scherrer method was approximately 50 nm. From the X-ray diffraction analysis it was confirmed that the sintered bodies were composed mainly of NiAl phase together with NiAl phase. Measured Vickers hardness and TRS value were 55510 and 139375 MPa , respectively.

σ-VFe 금속간화합물에 대한 기계적 합금화(MA) 효과를 중성자 및 X선 회절법으로 조사하였다. MA 분말의 구조분석은 X선 회절(Cu-Kα) 린 중성자회절(HRPD, λ=1.835Å)을 이용하여 행하였다. σ-VFe화합물의 MA시 큰 구조변화가 관찰되었으며, MA 60시간의 경우 Fe-Fe 훤자분포는 unit cell에 30개의 원자를 포함하고 있는 σ상의 tetragonal구조에서 120˚C이상에서 안정하게 존재하는 α-(V,Fe) 고용체의 bcc 구조로 상변화함을 알 수 있었다. 또한 α-VFe 화합물에 대한 중성자 및 X선 회절패턴의 비교분석을 행하였으며 그 결과 σ상이 가지는 화학적 규칙성에 기인하는 (101)과 (111) 회절 피크가 중성자 회절에서 뚜렷하게 관찰됨을 알 수 있었다.

기계적 합금화 공정을 이용하여 열전재료FeSi2분말을 제조하여 열간압축법을 사용하여 성형하였다. 열간압축 성형된 FeSi2는 열전특성을 나타내는 β-FeSi2 상 및 상변태가 완료되지 않은 α-Fe2Si5와 ε-FeSi의 혼합상으로 이루어져 있음이 확인되었다. 열전재료로의 β-FeSi2 상변태 유도를 위해 항온열처리를 행하여 상변태 조건을 조사하였다. SEM, TEM, XRD, DTA 등을 이용하여 상변태 거동을 분석한 결과, 830˚C에서 24시간 진공 항온열처리 후 단상의 β-FeSi2 상을 얻을 수 있었다. 항온열처리 전의 열간압축 성형체와 상변태가 완료된 β-FeSi2의 기계적 성질과 열전 특성을 측정하여 비교 분석하였다.

Ni-36at.%Al을 함유하는 나도 결정립의 NiAl 합금이 기계적 합금화법에 의해 제조되었다. 제조된 분말은 방전 플라즈마 소결법에 의해 만들어졌다. 상변테에 영향을 주는 인자는 냉각속도와 열처리 시간의 조건으로 논의되었다. 소결체의 상변태 거동은 시차 열분석(DSC)과 X-선 회절(XRD) 분석법에 의해 조사되었다. 미세구조는 주사전자현미경(SEM)으로 관찰되었다. 마르텐사이트 격사상수와 체적 분율은 X-선 회절분석법 중 직접비교법에 의해 계산되었다.

Mechanically-alloyed NiAl powder and ball-milled (Ni+Al) powder mixture were sintered by spark-plasma sintering(SPS) process. Mechanical alloying was performed in a horizontal attritor for 20 h with rotation speed of 600 rpm. (Ni+Al) powder mixtures were prepared by ball milling for 1 and 10 h with 120 rpm. Both powders were sintered at for 5 min under torr vacuum with 50 MPa die pressure in a SPS facility. Sintered densities of 97% and 99% were obtained from mechanically-alloyed NiAl powder and (Ni+Al) powder mixture, respectively. The sintered compact of (Ni+Al) powder mixture showed large grain size by a very rapid grain growth, while the grain size of mechanically-alloyed NiAl powder compact after sintering was extremely fine(80 nm). The difference in densification behavior of both powders were discussed.

In order to enhance sinterability of W-Cu composites used for heat sink materials, mechanical alloying process where both homogeneous mixing of component powders and fine dispersion of minor phase can be easily attained was employed. Nanostructured W-Cu powders prepared by mechanical alloying showed W grain size ranged of 20-50 nm and were able to be efficiently sintered owing to the fine particle size as well as uniform distribution of Cu phase. The thermal properties such as electrical resistivity, coefficient of thermal expansion and thermal conductivity were evaluated as functions of temperature and Cu content. It was found that the coefficient of thermal expansion could be controlled by changing Cu content. The measured electrical resistivities and thermal diffusivities were also varied with Cu content. The thermal conductivities calculated from the values of resistivities and diffusivities showed similar tendency as a function of temperatures. However, this is in contradiction with thermal conductivities of pure W and Cu which decrease with increasing temperature.

3%C-10%Cr-5%Mo-5%W, 3%C-10%V-5%Mo-5%W 및 3%C-17%Cr-3%V의 3종류 고합금백주철에 있어서 열처리후의 기지조직의 변태거동을 연구하였다. 15kg 용량의 고주파 유도용해로에 선철, 고철, Fe-Cr, Fe-V, Fe-Mo 및 Fe-W 등을 장입시켜 용해시킨 후 슬래그를 제거시키고 1550˚C에서 Y-block의 펩 주형에 주입시켰다. 적당한 크기로 절단한 시편을 진공분위기하에950˚C에서 5시간동안 우선 균질화처리를 실시하였다. 그 후 다시 이 시편을 1050˚C에서 2시간동안 오스테나이징시킨 후 강제공냉을 행하였다. 강제공냉된 시편을 300˚C에서 3시간 유지시킨 후 템퍼링을 실시하였다. 주방상태에서의 기지조직은 3합금 공히 퍼얼라이트이었으며 강제공냉후에는 마르텐사이트 및 오스테나이트로 변태하였다. 또한 기지조직내에 무수히 많은 이차탄화물 입자들의 석출되었다. 템프링 후 일부 오스테나이트 및 마르텐사이트는 템퍼드마르텐사이트로 변태하였다. 변태하였다.