The purpose of this study is to characterize various electrolytes on electrochemical mechanical planarization (ECMP). The ECMP system was modified from conventional CMP system to measure the potentiodynamic curve and removal rate of Cu. The potentiodynamic curves were measured in static and dynamic states in investigated electrolytes using a potentiostat for the evaluation of the polishing behavior on ECMP. KOH (alkaline) and NaNO3 (salt) were selected as electrolytes which have high conductivity. In static and dynamic states, the corrosion potential decreased and the corrosion current increased as a function of the electrolyte concentration. But, the electrochemical reaction was prevented by mechanical polishing effect in the dynamic state. The static etch and removal rate were measured as functions of concentration and applied voltage. When NaNO3 was used, the dissolution was much faster than that of KOH. It was concluded that the removal rate was strongly depended on electrochemical dissolution. The removal rate increased up to 350 nm/min in NaNO3 based electrolyte.

본 연구에서는 SEBS와 여러 가지의 유기화물로 처리된 MMT type의 clay를 이용하여 SSEBS-clay 하이브리드 막을 용액법으로 제조하였다. clay의 함량은 5 phr로 고정하였다. 용액법을 사용하여 clay를 SEBS에 분산시켰으며, 제조된 SSEBS-clay 하이브리드에서 clay의 특성피크가 완전히 박리되거나 이동하는 XRD 결과로부터 고분자의 clay 층간삽입을 확인하였다. Clay의 종류에 따라서 제조된 SSEBS-clay 하이브리드 막의 가스투과도, 기계적 물성 및 열적 성질을 측정하였다. SSEBS-clay 하이브리드 막은 clay 자체의 도입과 층간거리의 확대로 기체분자의 tortuosity를 증가시켜서 가스투과도를 저하시키는 것을 확인하였다.

The optimum polymer gel electrolyte composition ratio was 23 : 66 : 11 wt% of P(VdF-co-HFP) : PVP =20 : 3), (PC: EC =44 : 22) and TEABF4. And the optimal thickness of polymer gel electrolyte was 50um . The electrochemical characteristics result of unit cell were 31.41 Fig of specific capacitance, and 3.21x10-3 S/cm of ion conductivity. Ion conductivity of polymer gel electrolytes decreased according to added PVP through impedance analysis, and it was higher in 7 wt%, but electrochemical characteristics of unit cell were better in 3 wt% PVP. And for excellent ion conductivity of polymer gel electrolytes, the use of a thin layer electrolyte(20um) was an effective method, but with unit cell application, the best thickness was 50um . Unit cell showed higher capacitance and more stable electrochemical performance when hot pressed between polymer gel electrolyte and electrode. This results from enhancement of the physical contact between the electrode and the polymer gel electrolyte and good accessibility of the liquid electrolyte to the electrode surface.

A characterization of the permeation and separation using single salt solution was carried out with charged composite membranes. Various charged composite membranes were fabricated by blending an ionic polymer with a nonionic polymer in different ratios. In this study, sodium alginate, chitosan and poly(vinyl alcohol) were employed as anionic, cationic and nonionic polymers, respectively. The permeation and separation behaviors of the aqueous salt solutions have been investigated through the charged composite membranes with various charge densities. As the content of the ionic polymer increased in the membrane, the hydrophilicity of the membrane increased, and pure water flux and the solution flux increased correspondingly, indicating that the permeation performance through the membrane is determined mainly by its hydrophilicity. Electrostatic interaction between the charged membrane and ionic solute molecules, that is, Donnan exclusion, was observed to be attributed to salt rejection to a greater extent, and molecular sieve mechanism was effective for the separation of salts under a similar electrostatic circumstance of solutes.

Electrochemical charateristics of activated carbon fiber cloth(ACFC) electrode were studied with propylene carbonate(PC), γ-butyrolactone(GBL) and N,N-dimethyl-formamide(DMF) as a solvent and tetraethylammoniumtetrafluoroborate(TEABF4), tetraethylammoniumhexafluorophosphate(TEABF6), tetrabutylammoniumtetrafluoroborate(TBABF4) and tetrabutylammonium hexafluorophosphate(TBAPF6) as an electrolytes(active material). The concentrations of electrolytes were in the range of 0.2~1.2 N, the volume ratios of PC and DMF as a mixed solvent system, were 90：10, 80：20, 70：30, 60：40, 50：50, and 40：60 vol%. Electrochemical characteristics such as electric conductivity, internal resistance, and electric capacitance of fabricated unit cells were measured after the moisture of activated material was removed with molecular sieve. Electrochemical characteristics were better in mixed solvents system than in mono solvent system. The mono solvent system of 1.0 N electrolyte of GBL/TEABF4 with activated carbon cloth electrodes showed better result but the mixed solvent system with PC and DMF/TEABF4(50：50 vol%) and the concentration of 1.0 N electrolyte showed the best characteristics. Internal resistance was 3.47 Ω and specific capacitance was 19.1 F/g respectively.y.

고분자 전해질의 화학구조가 감습특성에 미치는 효과를 조사하기 위하여 C1~ C12의 알킬,benzy1, 2,2-diethoxy dthy1기가 치환된 메타크릴계 4차 암모늄 단량체들을 합성하였다. 이들의 감습용액을 0.15mm간격의 빗살 모양의 금전극이 인쇄된 알루미나 기판에 마이크로 주사기로 도포하여 광중합 후 상대습도에 따른 임피던스 변화를 측정하였다. 도포된 막의 두께가 증가하면 임피던스는 감소하고, 치환기의 탄소 길이가 증가할수록 임피던스는 증가하였다. C6~ C8의 알킬기를 가지는 고분자 전해질의 감습특성은 30-90% RH 범위에서 18MΩ-5KΩ의 직선적인 임피던스 변화를 보였다. 또한 임피던스는 온도 의존성을 보여주며 온도가 증가하면 임피던스가 감소하며 온도 의존성 계수는 -0,45% RH/˚C이다. 히스테리시스는 ±2%RH이내이며, 33%-85% RH 사이에서의 응답 속도는 약 35sec이었다.

폴리에틸렌 옥사이드(PEO)/리튬 삼불화메탄 술포네이트(LiCF3SO3)착제에 평균 직경 1μm인 미세 세라믹 분말 (γ -LiALO2)을 혼합하여 얻은 복합체 고분자 전해질의 특성을 형태학 및 기계적 성질의 관점에서 고찰하였다. 균일하게 분산된 세라믹 분말을 상온에서 고체 고분자 전해질의 전기적, 기계적 성질을 크게 향상시키는 것으로 관찰되었으며, 그 조성에 따라 그 특성이 변하였다. 본 연구에서 조사된 복합체 고분자 전해질의 경우, 상온에서 최대 이온 전도도를 나타내는 LiAlO2의 최적 함량은 약 20%인 것으로 나타났다.

단옥수수와 초당옥수수 종자의 활력을 높일 수 있는 탈곡방법을 알기 위하여 단옥수수(EarlySunglow×GCB70 )와 초당옥수수(Xtrasweet82×Fortune ) 종자의 수분함량을 12, 15, 18, 21%로 건조한 후 손과 전기 탈곡기로 탈곡하여 25℃ 발아율, cold test에서 출아율, 당 및 전해질 누출, α-amylase 활성 등 종자특성을 조사한 결과를 요약하면 다음과 같다. 1. 손 탈곡은 종자수분 함량에 관계없이 기계적 상처가 없었으나 기계 탈곡할 때 종자의 상처를 줄일 수 있는 수분함량은 단옥수수는 15~21% , 초당옥수수는 12~21% 이었다. 2. Cold test에서 출아율은 종자수분 함량에 관계없이 손 탈곡한 종자가 기계 탈곡한 종자보다 단옥수수는 6~14% , 초당옥수수는 9~18% 높았다. 3. 단옥수수는 25℃ 발아율과 cold test 출아율과 정의 상관이 있었으나 초당옥수수는 관계가 없었다. 단옥수수와 초당옥수수의 cold test에서 출아율은 침종 시 당 누출과는 부의 상관, α-amylase 활성과는 정의 상관이 있었다. 4. 기계 탈곡 시 25℃ 에서 상처립 비율, 발아율, cold test에서 출아율, 당과 전해질 누출량, α-amylase 활성을 고려한 적정 종자수분 함량은 단옥수수는 15%, 초당옥수수는 12%이었다.