In this study, we investigate the relationship between the peeling behavior of the backsheet of a photovoltaic(PV) module and its surface temperature in order facilitate removal of the backsheet from the PV module. At low temperatures, the backsheet does not peel off whereas, at high temperatures, part of the backsheet remains on the surface of the PV module after the peeling process. The backsheet material remaining on the surface of the PV module is confirmed by X-ray diffraction(XRD) analysis to be poly-ethylene(PE). Differential scanning calorimetry(DSC) is also performed to investigate the interfacial characteristics of the layers of the PV module. In particular, DSC provides the melting temperature(Tm) of laminated ethylene vinyl acetate(EVA) and of the backsheet on the PV module. It is found that the backsheet does not peel off below the Tm of ethylene of EVA, while the PE layer of the backsheet remains on the surface of the PV module above the Tm of the PE. Thus, the backsheet is best removed at a temperature between the Tm of ethylene and that of PE layer.

Single crystals, which have complexed composition, are fabricated by solid state grain growth. However, it is hard to achieve stable properties in a single crystal due to trapped pores. Aerosol deposition (AD) is suitable for fabrication of single crystals with stable properties because this process can make a high density coating layer. Because of their unique features (nano sized grains, stress inner site), it is hard to fabricate single crystals, and so studies of grain growth behavior of AD film are essential. In this study, a BaTiO3 coating layer with ~ 9 μm thickness is fabricated using an aerosol deposition method on (100) and (110) cut SrTiO3 single crystal substrates, which are adopted as seeds for grain growth. Each specimen is heat-treated at various conditions (900, 1,100, and 1,300℃ for 5 h). BaTiO3 layer shows different growth behavior and X-ray diffraction depending on cutting direction of SrTiO3 seed. Rectangular pillars at SrTiO3 (100) and laminating thin plates at SrTiO3 (110), respectively, are observed.

지금까지 진성 리더십 연구들은 한정된 맥락 속(예: 영리 조직)에서만 진행되었으며, 진성 리더십의 개 발 가능성과 선행요인을 확인한 연구는 미흡한 편이다. 따라서 본 연구는 군 조직에서 리더의 자아존중감, 자아 성찰(빈도, 초점, 시간), 인생의미(존재, 탐색)가 리더 자신의 진성 리더십에 미치는 영향과 리더의 진성 리더십이 부하들의 리더에 대한 신뢰, 리더 지향 조직시민행동에 미치는 영향을 실증하는데 목적을 두고 있다. 이를 검증하기 위해 리더 양성 프로그램으로 수양록(일기)을 작성하고 있는 사관학교에서 사관생도 719명(소대장 생도 32명, 분대장 생도 93명, 분대원 생도 594명)을 대상으로 설문조사를 실시하여 실증 분석하였다. 분석결과 자아존중감이 높은 리더, 자아에 대한 반복적인 성찰(수양록 작성의 빈도)을 하는 리더, 현재 자신의 모습을 원인 중심으로 성찰(수양록 작성의 초점)하는 리더가 진성 리더십이 높게 나타났으며, 인생의 의미를 발견한(인생의미 존재) 리더 역시 진성 리더로써 개발될 가능성이 컸다. 또한, 진성 리더십은 분대 수준에서 리더에 대한 신뢰, 리더 지향 조직시민행동과 긍정적인 관계를 갖는 것으로 나타났다. 이러한 분석결과를 통해 본 연구는 기존 진성 리더십 연구들에서 밝혀지지 않은 진성 리더십의 선행요인을 확인하였으며, 군 조직에서 진성 리더십이 부하들의 리더에 대한 신뢰, 조직시민행동에 중요한 역할을 한다는 것을 밝혔다.

점차 심화하고 있는 산업 간 경쟁과 4차 산업혁명 시대의 도래에 따라 기업은 존속을 위한 다양한 노력 이 필요한 실정이다. 그동안 많은 선행연구에서 기업 효과성 제고를 위한 연구들이 수행되었지만, 구성원 개인 차원의 혁신행동, 몰입, 지식공유의 규명은 미흡한 상황이다. 따라서 본 연구에서는 조직구성원의 자발적인 참여와 혁신, 기업 내 지식공유에 대한 중요성과 효과성, 구성원에 대한 조직지원의 필요성을 중심으로 조직경쟁력의 향상방안을 탐색하는데 그 목적을 두고 있다. 이에, 본 연구는 지식공유, 일몰입 및 혁신행동 간의 관계, 지식공유와 혁신행동 사이에서 일몰입의 매개효과, 그리고 지식공유와 혁신행동 사이에서 조직지원인식의 조절효과를 검증하고자 하였다. 이를 위해 서비스업 및 공공조직의 종사자들을 대상으로 설문지법을 통한 자기 보고방식으로 538부의 설문을 수집하였으며, 구조방정식을 사용하여 분석하였다. 실증분석결과 첫째, 지식공유는 일몰입 및 혁신행동에 정(+)의 영향을 미쳤으나, 지식공유의 하위요인인 형식적 지식공유는 일몰입 간의 관계에서 표준화 계수 값이 유의하지 않게 나타나 지지 되지 않았다. 둘째, 지식공유와 혁신행동 간의 관계에서 일몰입의 매개효과를 검증한 결과, 암묵적 지식공유와 혁신행동 간의 관계에서 일몰입은 매개역활을 하였으나, 형식적 지식공유와 혁신행동 간의 관계에서 일몰입은 매개효과가 없는 것으로 나타났다. 끝으로, 지식공유와 혁신행동 간의 관계에서 조직지원인식의 조절효과를 검증한 결과, 높은 조직지원인식은 혁신행동에 정(+)의 영향을 미치는 것으로 밝혀졌다. 이는 조직의 지속적인 성장과 번영을 위해 조직구성원들 간의 지식공유가 필요하며, 구성원의 혁신행 동에 지식공유가 중요한 선행요인임을 확인시켜주었다. 끝으로 지식공유 및 혁신행동 강화를 위해서는 조직의 구성원에 대한 인정과 배려가 중요한 요인으로 작용하므로, 조직운영의 효과성 제고나 경쟁력 향상을 위해서 경영자는 조직지원을 강화하여야 함을 주지시켜주고 있다.

급변하는 조직환경 속에서 조직의 효과성을 극대화하는데 기여할 수 있는 리더의 특성과 행동은 조직 연구에서 오랜 관심사였다. 오늘날 조직연구에서 리더십에 대한 논의는 다양한 양상으로 나타나고 있는데, 특히, 21세기 들어서면서 조직의 규모나 성격을 막론하고 리더의 윤리성에 대한 관심이 점차 확산되고 있다. 이는 리더의 윤리성이 조직의 성패에 지대한 영향을 미친다는 공감대가 확산되어 가기 때문인 것으로 보인다. 본 연구는 상사의 윤리적 리더십이 구성원의 조직시민행동에 미치는 영향을 사회학습이론을 기반으로 살펴보고자 하였다. 또한 윤리적 리더십이 구성원의 조직시민행동에 미치는 영향력 과정에서 마음챙김의 매개효과를 검증하고자 하였으며, 나아가 윤리적 리더십이 마음챙김을 매개로 조직시민행동에 미치는 영향력 과정에서 구성원의 도덕적 강도의 조절효과를 검증하였다. 공군 장병을 대상으로 자료를 수집하여 연구가설을 분석한 결과 상사의 윤리적 리더십은 조직구성원의 조직시민행동에 정(+)적인 영향을 미치며 이러한 영향력 관계를 마음챙김이 매개함이 확인되었다. 이는 리더가 윤리적 리더십을 발휘하면 조직구성원들은 조직시민행동을 할 가능성이 높아짐을 의미한다. 또한, 윤리적 리더십을 발휘하는 리더는 조직구성원들로 하여금 항상 주의를 기울이고 직무환경에 대해서 깨어있음을 느끼게 하고, 조직구성원들의 마음챙김이 높아지면 조직을 위한 자발적 행동인 조직시민 행동을 더 많이 하게 됨을 의미한다. 한편 윤리적 리더십이 마음챙김에 미치는 영향에서 도덕적 강도의 조절효과를 확인하였는데, 윤리적 리더십이 마음챙김에 미치는 영향은 도덕적 강도가 높을 때 더 강하게 나타났다. 또한, 윤리적 리더십이 마음챙김을 매개로 조직시민행동에 미치는 간접효과도 도덕적 강도에 의해서 정(+)적으로 조절됨이 확인되었다. 즉, 윤리적 리더십이 조직시민행동에 미치는 간접효과는 도덕적 강도가 높을 때 더 강하게 나타났다. 본 연구의 결과는 상사의 윤리적 리더십이 구성원의 조직시민행동에 미치는 영향을 사회학습이론 관점에서 논의하고 이를 실증적으로 규명하였다는 점에서 이론적 시사점을 가진다. 보다 중요하게도 그러한 영향력이 어떠한 과정으로 이루어졌는지를 마음챙김과 도덕적 강도를 활용하여 검증하였다는 점에서 이론적 시사점을 가진다. 또한, 조직의 관점에서 구성원의 조직시민행동을 촉진하기 위해서는 관리자로 하여 금 윤리적 리더십을 발휘하게 하는 방안을 마련할 필요성을 제기하였다는 점에서 실무적 시사점을 가진다.

Feasibility is investigated for reduction of chromium ore by Si sludge with mixed silicothermic and carbothermic reaction. The reduction behavior of chromium ore using Si sludge is investigated precisely to determine the effects of carbon addition, reaction time, and reaction temperature. The pellets are dropped into the furnace after temperature stabilized. As the amount of C addition increases, the amounts of CO and CO2 gas generation increase. After the dropping of the pellets, the pellets are heated and the reaction starts at about 1,573 K or higher. The pellets maintain their shape until 10 min after the drop, and then melted. As the holding time increased, the size of the reduced metal particles increased. The chromium ore is rapidly reduced by the Si sludge, and the slag penetrated into the chromium ore and reduction progressed inside. As the reduction temperature increased, the reaction initiation time is shortened and the reaction fraction of the reduction reaction increased. As the reaction temperature increased, agglomeration of reduced ferrochrome metal is promoted.

As the concept of “marriage age” gradually disappears, the consumption class of the wedding market includes not only X and Y generations but also Z generations, and each generation has its own characteristics as it is already known, and there are differences in the consumption. So this research analyzed age-related behavior differences in both awareness of and preparation for marriage. Three hundred sixteen unmarried Korean males and females comprised the study population and data was collected from March 5, 2019, to April 3, 2019. The SPSS Statistics 23.0 Package was used for analysis, specifically the functions of frequency, cross tabulation, factor analysis, chi-squared test, Cronbach’s alpha, Duncans’s new multiple range test (MRT), and analysis of variance (ANOVA). Marriage motivation was analyzed by three factors, and there were significant differences in two types. Marital involvement was analyzed by two factors, and both factors showed significant age-related differences. Concerns relating to marriage preparation were analyzed by four factors, and two varied according to respondent age. Regarding marriage preparation behaviors, the analysis revealed that the marriage preparation method appreciably differed between age groups. Our analysis also found significant age-related differences in “the main media usually used to acquire information” and “the paths preferred for acquiring information in preparing for marriage”. We expect that study results will be useful for identifying new research directions, understanding the dimensions of the wedding industry, and developing related marketing strategies.

In this study, the thermal behavior characteristics of flange case interior were analyzed by the numerical method. The boundary conditions at the inlet port of flange case were the heat flux and heat flux time. As the heat flux time at inlet of case increased, the temperature values gradually increased, and the degree of increase was very small. If the heat flux of the melted iron increases to 2,000,000 W/m2, the temperature change at the case interior will occur largely, causing heat deformation. As a result, in order to reduce thermal defects at the case interior, the heat flux and heat flux time of the melted iron should be set within 500,000 W/m2 and 5 seconds, respectively.

The hydrogen reduction behavior of the CuO-Co3O4 powder mixture for the synthesis of the homogeneous Cu-15at%Co composite powder has been investigated. The composite powder is prepared by ball milling the oxide powders, followed by a hydrogen reduction process. The reduction behavior of the ball-milled powder mixture is analyzed by X-ray diffraction (XRD) and temperature-programmed reduction at different heating rates in an Ar-10%H2 atmosphere. The scanning electron microscopy and XRD results reveal that the hydrogen-reduced powder mixture is composed of fine agglomerates of nanosized Cu and Co particles. The hydrogen reduction kinetics is studied by determining the degree of peak shift as a function of the heating rate. The activation energies for the reduction of the oxide powders estimated from the slopes of the Kissinger plots are 58.1 kJ/mol and 65.8 kJ/mol, depending on the reduction reaction: CuO to Cu and Co3O4 to Co, respectively. The measured temperature and activation energy for the reduction of Co3O4 are explained on the basis of the effect of pre-reduced Cu particles.

본 연구는 대학생의 계획된 우연 기술이 진로적응성과 진로준비행동에 미치는 영향을 확인 하고 계획된 우연 기술의 향상을 위한 진로코칭 교육의 필요성에 대해 논의하는 것을 목적으로 진행하였다. 이를 위하여 본 연구는 서울 소재 4년제 대학교에 재학 중인 3, 4학년 학생 256명의 설문조사 결과를 분석하였다. 본 연구의 결과는 다음과 같다. 첫째, 대학생의 계획된 우연 기술은 진로적응성에 정적인 영향을 미치는 것으로 나타났다. 계획된 우연 기술의 호기심, 인내심과 낙관성 요인은 진로적 응성에 정적인 영향을 미치는 것으로 확인되었으며 낙관성 요인은 진로적응성의 모든 하위요인들에 정적인 영향이 있음을 확인하였다. 둘째, 대학생의 계획된 우연 기술은 진로준비행동에 정적인 영향을 미치는 것으로 확인되었다. 계획된 우연 기술의 호기심, 낙관성과 위험감수 요인은 진로준비행동에 정적인 영향을 미치는 것으로 나타났으며 호기심, 인내심, 낙관성과 위험 감수 요인은 진로준비행동의 하위요인들에 부분적으로 영향을 미치는 것으로 확인되었다. 대학생의 계획된 우연 기술을 향상하기 위하여 기존의 진로코칭 프로그램과 더불어 진로코칭 교육의 확대 실시가 필요하다고 사료된다. 아울러 이에 대한 대학 당국과 교수자들의 이해와 실천에 대해 제언하고자 한다.