The purpose of this study is to analyse the hydration reaction of paste according to fineness of non-cement binder, as a basic for the development of non-cement concrete block. As the fineness of binder increased, compressive strength of paste increased, and C-S-H gel was produced actively.

The objective of this study is to investigated the compressive characteristics properties used cement paste containing Silica Fume Binder with elapsed curing time.

The objective of this study is to investigated the compressive characteristics properties used cement paste containing 30% blast furnace slag with curing days.

The objective of this study is to investigated the compressive characteristics properties used cement paste containing 20% fly ash with curing days.

This study investigates the fundamental properties of the water-binder (W/B) ratio and fine aggregate-binder (F/B) ratio in the alkali-activated slag cement (AASC) mortar. The W/B ratios are 0.35, 0.40, 0.45, and 0.50, respectively. And then the F/B ratios varied between 1.00 and 3.00 at a constant increment of 0.25. The alkali activator was an 2M and 4M NaOH. The measured mechanical properties were compared, flow, compressive strength, absorption, ultra sonic velocity, and dry shrinkage. The flow, compressive strength, absorption, ultra sonic velocity and dry shrinkage decreased with increases W/B ratio. The compressive strength decreases with increase F/B ratio at same W/B ratio. Also, at certain value of F/B ratio significant increase in strength is observed. And S2 (river sand 2) had lower physical properties than S1 (river sand 1) due to the fineness modulus. The results of experiments indicated that the mechanical properties of AASC depended on the W/B ratio and F/B ratio. The optimum range for W/B ratios and F/B ratios of AASC is suggested that the F/B ratios by 1.75~2.50 at each W/B ratios. Moreover, the W/(B+F) ratios between 0.13 and 0.14 had a beneficial effect on the design of AASC mortar.

There are great and comprehensive efforts to reduce green house gases, especially carbon dioxide, in a global community of nations. Carbon dioxide emissions of South Korea placed ninth in the world in 2007, 13 percent of that is a field of construction materials. Domestic portland cement(OPC) is made up of clinker, gypsum and 5% of admixtures. If 5% of Admixture contents of portland cement add to 10%, CO2 reduction effect can be expected. In this study, the strength properties of mortar using two types of cement were evaluated.

This study examines the strength development of non cement binder using blast furnace slag, which is generated as a by-product in the manufacturing the irons. In the experiment, we used KOH, Ca(OH)2 as the blast furnace slag stimulus. As the results of this experiments, it was shown that the compressive strength increased when mixing ratio of KOH and Ca(OH)2 was increased.

본 연구에서는 황토에 시멘트나 유기계 접착제를 첨가하지 않은 천연재료 황토결합재를 사용하여 황토경화체를 제작하고, 배합조건에 따른 강도성상을 평가하였다. 황토와 석회의 결합재에 천연재료를 첨가할 경우 사용한 천연재료는 모두 물리적 성능을 개선하는 효과가 있었다. 천연재료 중에서 석회는 황토경화체의 물성을 증가시키는데 가장 큰 영향을 미치고 있다. 황토경화체의 물리적 특성은 적용한 배합비 중에서 W/B 45%, 단위수량 285kg/m3, 석회첨가율 60%일 때 가장 우수하게 나타나고 있다.

본 연구에서는 고비용의 실리카흄의 대체재로서 인산부산석고와 카올린을 활용한 시멘트매트릭스의 화학적, 기계적 성질에 대하여 분석하였다. 실험을 위하여 인산부산석고는 이수석고 형태인 건조석고, 반수석고, Ⅲ형 무수석고, Ⅱ형 무수석고로 실험용시료를 제조하였으며, 900℃에서 소성된 카올린은 서냉과 급냉의 형태로 제조된 메타카올린의 형태로 제조하였다. 또한 이재료를 활용하여 혼합시멘트를 제조하였으며, 제조된 시멘트를 사용하여 실리카 흄을 혼입한 시멘트 매트릭스와 재료적 성능을 비교 평가하였다. 실험결과 급냉제조된 메타카올린이 다른 재료에 비하여 성능이 우수한 것으로 분석되었다.

본 연구는 대형․대단면 지하공간에 적용하기 위한 고강도 콘크리트의 개발 및 적용을 위한 연구의 일환으로 50MPa급의 고강도 콘크리트의 제조를 위해 플라이애쉬와 고로슬래그미분말의 치환에 따른 최적 배합을 선정하고, 비구속 수축 실험과 수축균열 실험을 통해 정량적으로 평가하였다. 콘크리트의 압축강도는 전 배합이 7일 재령에서 30MPa을 넘었고, 28일 재령에서는 설계강도를 모두 안정적으로 획득하였다. 고강도 콘크리트에 고로슬래그를 사용할 경우 자기수축량이 커지고, 다량 치환할 경우 수축변형이 증가하고 강도발현이 지연되어 수축에 의한 균열 발생의 우려가 있다. 혼화재를 다량 치환한 고강도 콘크리트 배합은 수화반응과 건조 효과에 영향을 주는 초기 재령의 양생 조건에 대한 검토가 필요하다.