PURPOSES: This study is to investigate the mechanical performance of the fiber reinforced lean concrete with respect to different types of fibers. METHODS: Increased vehicle weight and other causes from the exposed conditions have accelerated the deteriorations of road pavement. A new multi-functional composite pavement system is being developed recently in order to extend service life and upgrade the pavement. A variety of tests were conducted before and after hardening of the concrete. RESULTS: From the test results, it was found that the use of different types of fibers did not affect the compressive strength development. This might be due to the inherent property of the lean concrete. When steel fibers were used relatively greater flexural strength and flexural fracture toughness were developed. Also addition of fly ash by replacing a part of Portland cement the fracture toughness was slightly increased. CONCLUSIONS: It has been known that the addition of fibers and use of mineral admixture can be positively considered in the development of multi-functional composite pavement system as its required mechanical performance is obtained.

PURPOSES : This study is to investigate the fundamental properties of limestone added cement concrete for application of pavement. METHODS : As the production of Portland cement causes environmental problems, engineers have sought more environment-friendly concrete construction materials. Limestone powder can be used for concrete as a partial replacement of Portland cement. One of the great applications of limestone powder added cement concrete might be a cement concrete pavement since the concrete pavement consumes massive quantity of Portland cement. Experimental variables were different replacement level of limestone powder by 0% to 25% with 5% increment. Before hardening of fresh concrete, setting time and plastic shrinkage characteristics were investigated in addition to other basic properties. Properties of hardened concrete included compressive, tensile and flexural strength as well as drying shrinkage. RESULTS : The addition of limestone powder did not significantly affect the properties of fresh concrete. Strength deceased as the replacement ratio increased and when the replacement ratio was greater than 10% decrease rate increased. CONCLUSIONS : It was found that the partial replacement of the limestone powder to cement in pavement materials can be positively considered as its mechanical properties show comparable performance to those normal concrete.

배수성 포장에 있어 기능적 평가인 투수성 실험과 더불어 소음저감 측정을 서울시에서 시공한 구간에서 실시하였다. 소음측정은 두 가지 방법을 이용하였는데 그 방법은 Pass-by 방법과 NCPX(Novel Close Proximity) 방법을 이용하였다. Passby 방법은 교통량에 따른 소음원이 전달되는 것을 측정하는 방법이고, NCPX는 타어어와 포장 표면간의 마찰음을 측정하는 방법이다. 현장투수시험을 위해서는 총 5개의 구간에서 실시하였으며 각 구간마다 주행부와 비주행부로 나뉘어 측정하였다. 3개 구간의 Pass-by 측정을 위해서는 교통소음원 발생점으로부터 인접한 곳에서 측정을 실시하였고 또한 공원내부 혹은 단지 내부에서도 소음을 측정하였다. 마지막으로 NCPX 측정은 4군데서 실시하였다. 결과적으로 배수성 포장의 기능인 투수성과 소음저감이 2, 3년 사이에서는 그 기능을 잘 유지함을 알 수 있었다.

역학적-경험적 포장설계 프로그램 중에서, 미국 AASHTO 설계법을 기초로 개발된 MEPDG는 교통량, 기상, 재료물성, 포장구조 등을 입력변수로 하여 기술자가 최적의 대안을 찾도록 한다. 하지만 MEPDG에서 기술적 문제가 발견되고 있기 때문에 이를 해결하여 프로그램을 개선하기 위한 노력이 계속되고 있다. 한편, 국내에서도 KPRP 연구과제에서 역학적-경험적 포장설계 프로그램이 개발되어 왔다. 이 한국형 포장설계 프로그램을 더욱 합리적으로 개발하고 개선하기 위해서는 이미 사용되고 있는 MEPDG를 분석하여 서로 비교할 필요가 있다. 콘크리트 포장설계의 경우, 피로균열은 다른 공용성 인자와는 달리 매우 복잡한 로직을 통해 예측된다. 따라서 본 논문에서는 MEPDG 버전 0.5, 버전 1.0, 그리고 버전 1.1의 피로균열 전이함수를 분석하였다. 그리고 버전별 MEPDG와 KPRP 입력변수들의 누적피로손상에 대한 민감도를 서로 비교하였다.

지중구조물 주위는 다짐이 잘 되지 않아 지반이 장기 침하하므로 콘크리트 포장 하부에 공동이 발생하기 쉬우며, 이로 인해 지지력이 저하되기 쉽다. 여기에 하중이 가해지면 설계 시 기대한 것보다 큰 응력이 도입되어 포장에 파손이 발생하고 수명이 감소하게 된다. 본 논문에서는 한국도로공사 시험도로의 박스형 암거 상부 콘크리트 포장 슬래브의 파손을 조사하였다. 토피고가 다른 상행선과 하행선의 암거 위치에 발생한 슬래브의 횡방향 균열을 비교하였다. 시험도로의 횡방향 균열을 검증하기 위해 토피고가 없는 박스형 암거와 콘크리트 포장을 유한요소 방법으로 모형화하고 해석하였다. 포장의 자중을 고려하고 시험도로가 위치한 경기도 여주 지역 콘크리트 슬래브의 온도구배를 적용한 후 윤하중을 재하하였다. 각 하중조합에 대해 최대인장 응력이 발생하는 위치와 이때의 윤하중 위치를 찾아냈다. 이를 통해 최대인장응력을 감소시킬 수 있는 줄눈 위치를 찾아내고 암거 크기 별로 상부에 위치하는 슬래브의 적정 길이를 제안하였다.