The collapse of reinforced concrete (RC) frame buildings is mainly caused by the failure of columns. To prevent brittle failure of RC column, numerous studies have been conducted on the seismic performance of strengthened RC columns. Concrete jacketing method, which is one of the retrofitting method of RC members, can enhance strength and stiffness of original RC column with enlarged section and provide uniformly distributed lateral load capacity throughout the structure. The experimental studies have been conducted by many researchers to analyze seismic performance of seismic strengthened RC column. However, structures which have plan and vertical irregularities shows torsional behavior, and therefore it causes large deformation on RC column when subjected to seismic load. Thus, test results from concentric cyclic loading can be overestimated comparing to eccentric cyclic test results, In this paper, two kinds of eccentric loading pattern was suggested to analyze structural performance of RC columns, which are strengthened by concrete jacketing method with new details in jacketed section. Based on the results, it is concluded that specimens strengthened with new concrete jacketing method increased 830% of maximum load, 150% of maximum displacement and changed the failure modes of non-strengthened RC columns.

In the case of columns in buildings with soft story, the concentration of stress due to the difference in stiffness can damage the columns. The irregularity of buildings including soft story requires retrofit because combined load of compression, bending, shear, and torsion acts on the structure. Concrete jacketing is advantageous in securing the strength and stiffness of existing members. However, the brittleness of concrete make it difficult to secure ductility to resist the large deformation, and the complicated construction process for integrity between the existing member and extended section reduces the constructability. In this study, two types of Steel Grid Reinforcement (SGR), which are Steel Wire Mesh (SWM) for integrity and Steel Fiber Non-Shrinkage Mortar (SFNM) for crack resistance are proposed. One reinforced concrete (RC) column with non-seismic details and two columns retrofitted with each different types of proposed method were manufactured. Seismic performance was analyzed for cyclic loading test in which a combined load of compression, bending, shear, and torsion was applied. As a result of the experiment, specimens retrofitted with proposed concrete jacketing method showed 862% of maximum load, 188% of maximum displacement and 1,324% of stiffness compared to non-retrofitted specimen.

이 연구는 탄소섬유시트의 보강겹수에 따른 I형 PFRP 휨부재의 휨보강 효과를 조사하기 위해 길이 600mm의 PFRP 휨부재와 상하부 플랜지에 1mm 두께의 탄소섬유시트로 보강하여 휨실험을 수행하였다. 또한, 탄소섬유시트의 보강겹수와 보강 위치에 따른 I형 PFRP 휨부재의 휨보강 효과와 단면 감소량에 대해 조사하였다. 그 결과 2겹으로 보강하였을 때 휨강도와 휨강성이 증가함을 확인하였다.

This study is an experimental study to evaluate the vehicle-protection performance of the reinforced F section of a concrete median barrier. To reinforce the strength performance and durability of the F section, the design strength of concrete was increased and a wire mesh was added. The reinforced F section was tested in an actual collision to verify the protection performance of the SB4 class(Impact Severity: 160kJ) concrete barrier. In the truck-crash test for strengthperformance evaluation, no damage or no sufficient scattering occurred to cause damage to a third party. In addition, the truck smoothly moved through an escape box after the collision. THIV and PHD, which are criteria for evaluating the occupant-protection performance, were measured at 75% and 64% of the limit, respectively, and were confirmed to provide good occupant-protection performance. The vehicle rotations after the collision were 12%–19% of the allowed limits.

현무암 섬유를 함유한 BFRP 시트와 복합섬유 패널로 보강한 정사각형 단면 철근콘크리트 기둥에 대한 반복하중 실험을 수행하여 지진 거동을 검토하였다. 30%가량의 상당한 수준의 축하중비 조건 하에서 전단 손상이 발생하였음에도 불구하고, 보강 실험체에서 변위연성도 및 에너지 소산능력의 증가를 확인하였다. 실험체의 파괴 모드는 휨-전단 고연성 파괴로 분류 되며, 철근콘크리트 구조물에서 자주 관찰되는 파괴 모드이다. 하지만 이러한 파괴에 이르는 정사각형 단면 철근콘크리트 기둥에 BFRP을 포함한 복합재료 보강이 미치는 영향에 대한 연구가 현재까지 광범위하게 이루어지지는 않았다. 복합재료로 보강한 철근콘크리트 기둥의 휨-전단 거동을 보다 깊이 이해하는데 본 연구의 결과가 기여할 것으로 기대한다.

FRP 보강이 RC 기둥의 내진성능에 미치는 효과를 평가하고자 다양한 실험 연구가 수행되어 왔다. 그 중 많은 연구가 휨지배를 받는 원형 단면 RC 기둥의 거동에 초점을 맞추었다. 단면 형태가 FRP 보강에 의한 구속효과에 영향을 주기 때문에, 단면 형태에 따라 보강효과 및 최종손상 양상이 다를 수 있다. 또한, 기존 RC 기둥 중 일부는 현재의 구조기준을 만족하지 못하는 설계로 인하여 취성적인 파괴 모드인 전단 파괴가 발생할 것으로 여겨진다. 이 두 가지 조건을 고려하여, 현무암 섬유를 함유한 FRP 시트와 복합섬유 패널로 보강한 정사각형 단면을 가진 짧은 RC 기둥의 전단 거동을 살펴보기 위하여 반복하중 실험을 수행하였다. 실험 결과에서 전체적인 전단 거동의 개선을 확인하였으며, 이러한 경향은 모서리 부분에서 심각한 손상이 발생할 때까지 유효하였다.

In this paper, four point bending tests were carried out to analyse flexural strengthening effect by CFRP (Carbon Fiber Reinforced Polymer) layers for I shape PFRP (Pultruded Fiber Reinforced polymer) flexural member retrofitted with CFRP sheet. Comparing load-displacement relation and sectional stress distribution, the flexural strengthening effect by the number of CFRP layers was founded.

Recent studies have revealed that plates stiffened by closed-section ribs can be designed to have greater strength. Thus, this study is about the increasing effect on local plate buckling strength of isotropic plates when longitudinally stiffened with closed-section ribs, which is mainly due to the rotational restraint of the closed-section ribs. The effects on buckling strengths of the stiffened plates are examined by numerical analyses. Three-dimensional finite element models were obtained using a general structural analysis program ABAQUS and a series of eigenvalue analyses were conducted. Through this study, the increasing effect on the local buckling strength due to the rotational stiffness is numerically verified. From the parametric studies, there is an obvious tendency that the local buckling strength of the stiffened plate would converge to the buckling strength of plate with fixed boundary condition. The findings of this study would contribute in improving the optimum design of longitudinally stiffened isotropic plates.

본 연구에서는 섬유 그리드 보강재로 인한 아스팔트 포장의 단면 감소 효과를 정량적으로 분석하기 위 해, 포장 두께를 축소하지 않은 일반 아스팔트 포장 구간(그림 1 왼쪽)과 기층 두께를 5cm 축소하고 섬유 그리드를 시공하지 않은 구간(그림 1 가운데) 및 기층 두께를 5cm 축소하고 표층 하부에 섬유 그리드를 보강하여 시공한 구간(그림 1, 오른쪽)의 거동을 FWD를 이용하여 비교･분석하였다. FWD(Falling Weight Deflectometer) 하중은 4.1톤 2회, 8.0톤 2회 및 10.0톤 2회를 재하하였다. 일 반 아스팔트 포장구간과, 기층 두께를 5cm 축소한 구간, 기층 두께를 5cm 축소하고 섬유 그리드를 보강 한 구간의 처침량 데이터를 수집하였고, 동시에 시험구간 포장체 내부에 설치되어있는 계측기를 이용하여 변형률을 수집하였다. FWD 실험 결과, 기층두께 5cm 축소 + 섬유 그리드 보강 구간이 기층두께 5cm 축소 구간에 비해 처짐량 이 약 14% 작게 나타나 섬유 그리드의 구조적 보강 효과를 확인할 수 있었다. 또한 섬유 그리드 보강구간이 일반 아스팔트 포장구간에 비해서 처짐값은 37% 크지만 표층 하단부에서의 변형률은 유사하게 나타났으며 이를 이용한 구조해석 결과, 약 3cm의 섬유 그리드로 인한 포장 층의 두께 감소 효과를 확인할 수 있었다.

최근 문화유산에 대한 관심이 고조 되면서 노후화된 건조물문화재의 보존에 대한 중요성이 대두되고 있다. 건조물문화재의 대부분이 목재를 주재료로 사용하였으며, 이들 건조물문화재의 노후화에 따른 부식 및 손상에 대한 보존수리는 부재자체의 문화재적 가치를 고려하여 원형유지를 기본원칙으로 한다. 이에 따라, 합성수지를 이용한 보존처리방법이 부각되고 있다. 이에 본 논문은 합성수지로 보강한 원형단면 목재의 압축보강 성능에 관한 실험적 연구로서 합성수지의 보강단면적비율, 단면의 보강방향, 보강길이, 합성수지강도를 변수로 하여 총 14개의 시험체를 제작하여 실험하였다. 실험결과 합성수지를 이용하여 적절하게 보강할 경우 신재이상의 보강효과가 있는 것으로 나타났으며 문화재의 보수 및 보강에서 가장 중요한 오센티시티(authenticity)를 확보할 수 있을 것이다.

This paper examined the flexural behavior of section enlargement strengthening columns with prefabricated reinforcement units in the jacket section. The developed strengthening column was particularly effective in enhancing the ductility of the columns.

이 연구에서는 실제 단면크기를 갖는 철근 콘크리트 기둥의 내진보강을 위한 단면확대 공법에서 효율적인 띠철근 배근 방법을 평가하였다. 비내진 상세를 갖는 기존 기둥의 단면크기는 450 × 450 mm이며, 단면확대 보강기둥의 단면크기는 750 × 750 mm이다. 확대 단면에서의 폐쇄형 외부 띠철근 배근을 위해 ㄷ-형 띠철근의 겹칩이음 및 철근 선조립 공법을 제시하였으며, 보조 띠철근으로서 크로스타이 앵커링 시공 및 V-타이를 고려하였다. 실험 결과, 무보강 기둥 및 ㄷ-형 외부 띠철근을 적용한 보강기둥의 압축내력은 ACI 318-14의 공칭내력과 비슷한 수준인 반면 철근 선조립 공법을 적용한 기둥의 압축내력은 ACI 318-14의 공칭내력 대비 1.25배 높았다. 특히 철근 선조립 공법을 적용한 보강 기둥의 압축 연성비는 크기효과에 의한 연성비 저하 가능성에도 불구하고 기존 기둥에 비해 139% 증가하였다. 즉, 제시된 철근 선조립 공법은 단면확대 보강기둥에서 주철근 조기 좌굴방지 및 콘크리트 구속에 효율적인 띠철근 상세로 평가될 수 있었다.

This paper examined the axial behavior of full-scale section enlargement strengthening columns with different supplementary ties in the jacket section. The supplementary V-ties were effective in enhancing the confinement of core concrete and preventing the premature buckling of longitudinal reinforcement.

This study evaluated the P-M interaction behavior of RC columns strengthened with section enlargement method with the supplementary V-ties. The estimated P-M interaction is well corresponded with test results.

To examine the practical potentials of V-ties to provide a confinement to a strengthening jacket section of existing reinforced concrete members, direct bond tests were conducted under a parameter of the V-tie details. Test results showed that V-ties with headed-end had a higher bond strength than those with the other details.

The thin cylindrical shell structure under compression should be checked with buckling stability. In DNV, there is a spacing criteria of stiffener which based on linear theory without initial imperfection. In this study, structural analysis, using geometry nonlinear analysis, of stiffened cylindrical buckling strength with various initial imperfection were performed and compared with DNV and FEM results.

In this paper, punching shear test of flat plate reinforced by plates with openings has performed. And compared critical section of ACI 318, BS 8110, and Eurocode 2. Non-reinforced specimens and specimens that reinforced by GFRP plates with openings are manufactured. Shear reinforcement spacing was used as parameter for specimens reinforced by GFRP plates. Crack pattern showed that critical section increased as shear reinforcement spacing increased compared to critical section of ACI 318, BS 8110, and Eurocode 2. Critical section calculated by ACI 318 was the smallest predicted section, and sections calculated by BS 8110 and Eurocode 2 are larger predicted section.

Complete closed-type carbon fiber reinforced polymer stirrups with a rectangular section (CFRPRS) were developed and tested in this research. The CFRPRS was intended to relieve stress concentration and to reduce the number of kinked fibers at the bent portion. A total of 16 B.5 specimens were tested regarding the bend strength of the CFRPRS and CFRP stirrups with circular section. Test results showed that CFRPRS improved the bend strength compared to its counterpart of conventional CFRP stirrups having a circular section, with the larger ratio of width to thickness being more effective for the same sectional area. The best correlation between the test results and predictions on CFRPRS bend strength was observed when the section of CFRPRS was modeled as a collection of transformed individual circular sections.