세리아 입자의 합성을 위하여 분무열분해 시 유기 첨가제인 EG(ethylene glycol)과 CA(citric acid)를 첨가하여 중공성 및 다공성을 갖는 CeO2 마이크로 크기의 입자를 제조하였으며 첨가량에 따른 특성을 비교하였다. 분무열분해과정, 후소성 및 볼밀링 과정을 적절히 조합하여 만든 6가지 경로에 의해 나노 크기의 세리아 입자를 합성하였다. 6가지 경로 중 EG 및 CA가 0.05M 첨가된 Ce(III)가 전구체 수용액을 이용하여 분무열분해→후소성→볼밀링→후소성의 경로에 의해 얻어진 CeO2 입자에 대해 TEM 분석으로 측정한 입자의 평균 크기 24 nm(편차=3.8 nm)는 Debye-Scherrer식에 의해 계산된 1차 입자의 크기(20 nm)와 가장 유사한 크기를 나타내었다. 제조된 나노입자분말의 형태적 및 구조적 특성을 알아보기 위하여 SEM(Scanning Electron Microscopy), XRD(X-Ray Diffractometer) 및 TEM(Transmission Electron Microscopy)을 통하여 특성을 분석하였다.

We investigated the effect of ZnO buffer layer on the formation of ZnO thin film by ultrasonic assisted spray pyrolysis deposition. ZnO buffer layer was formed by wet solution method, which was repeated several times. Structural and optical properties of the ZnO thin films deposited on the ZnO buffer layers with various cycles and at various temperatures were investigated by field-emission scanning electron microscopy, X-ray diffraction, and photoluminescence spectrum analysis. The structural investigations showed that three-dimensional island shaped ZnO was formed on the bare Si substrate without buffer layers, while two-dimensional ZnO thin film was deposited on the ZnO buffer layers. In addition, structural and optical investigations showed that the crystalline quality of ZnO thin film was improved by introducing the buffer layers. This improvement was attributed to the modulation of the surface energy of the Si surface by the ZnO buffer layer, which finally resulted in a modification of the growth mode from three to two-dimensional.

In this study, nano-sized tin oxide powder with an average particle size of below 50 nm is prepared by the spray pyrolysis process. The influence of air pressure on the properties of the generated powder is examined. Along with the rise of air pressure from 0.1kg/cm2 to 3kg/cm2, the average size of the droplet-shaped particles decreases, while the particle size distribution becomes more regular. When the air pressure increases from 0.1kg/cm2 to 1kg/cm2, the average size of the dropletshaped particles, which is around 30-50 nm, shows hardly any change. When the air pressure increases up to 3kg/cm2, the average size of the droplet-shaped particles decreases to 30 nm. For the independent generated particles, when the air pressure is at 0.1kg/cm2, the average particle size is approximately 100 nm; when the air pressure increases up to 0.5kg/m2, the average particle size becomes more than 100 nm, and the surface structure becomes more compact; when the air pressure increases up to 1kg/cm2, the surface structure is almost the same as in the case of 0.5kg/cm2, and the average particle size is around 80- 100 nm; when the air pressure increases up to 3kg/cm2, the surface structure becomes incompact compared to the cases of other air pressures, and the average particle size is around 80-100 nm. Along with the rise of air pressure from 0.1kg/cm2 to 0.5kg/cm2, the XRD peak intensity slightly decreases, and the specific surface area increases. When the air pressure increases up to 1kg/cm2 and 3kg/cm2, the XRD peak intensity increases, while the specific surface area also increases.

Mesoporous alumina particles were prepared by spray pyrolysis using cetyltrimethyl-ammonium bromide (CTAB) as a structure directing agent and the effect of Al precursor types on the texture properties was studied using N2 adsorption isotherms, small-angle X-ray scattering (SAXS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The surface area and the microstructure of alumina particles were significantly influenced by the Al precursor type. The largest BET surface area was obtained when Al chloride was used, whereas alumina particles prepared from Al acetate had the largest pore volume. According to small-angle X-ray scattering (SAXS) analysis, the alumina powders prepared using nitrate and acetate precursors had a clear single SAXS peak around 2θ = 1.0~1.5°, indicating that regular mesopores with sponge-like structure were produced. On the basis of TEM, SAXS, and N2 isotherm results, the chloride precursor was most profitable to obtain the largest surface area (265 m2/g), whereas, the nitrate precursor is useful for the preparation of non-hollow mesoporous alumina with regular pore size, maintaining high surface area (~233 m2/g).

Nano-sized BaNd2Ti5O14 powders were prepared by the spray pyrolysis process. Sucrose used as the organic additive enabled the formation of nano-sized BaNd2Ti5O14 powders. The powders prepared from the spray solution without sucrose had a spherical shape, dense structure and micron size before and after calcination. However, the precursor powders prepared from the spray solution with sucrose had a large size, and hollow and porous morphology. The precursor powders had an amorphous crystal structure because of the short residence time of the powders inside the hot wall reactor. The complete decomposition of sucrose did not occur inside the hot wall reactor. Therefore, the precursor powders obtained from the spray solution with sucrose of 0.5M had a carbon content of 39.2wt.%. The powders obtained from the spray solution with sucrose of 0.5M had a slightly aggregated structure of nano-sized primary powders of BaNd2Ti5O14 crystalline phase after calcination at 1000˚C. The calcined powders turned into nano-sized BaNd2Ti5O14 powders after milling. The mean size of the BaNd2Ti5O14 powders was 125 nm.

Fe powders with elongated and aggregated structure as heat pellet material for thermal battery applications were prepared by spray pyrolysis under various preparation conditions. The precursor powders with spherical shapes and hollow morphologies turned into Fe powders after reduction at a temperature of 615˚C under 20% H2/Ar gas. The powders had pure Fe crystal structures irrespective of the preparation conditions of the precursor powders in the spray pyrolysis. The morphologies and mean sizes of the Fe powders are affected by the preparation conditions of the precursor powders in the spray pyrolysis. Therefore, the ignition sensitivities and the burn rates of the heat pellets formed from the Fe powders prepared by spray pyrolysis are affected by the preparations of the precursor powders. The Fe powders prepared under the optimum preparation conditions have a BET surface area of 2.9 m2g1. The heat pellets prepared from the Fe powders with elongated and aggregated structure have a good ignition sensitivity of 1.1W and a high burn rate of 18 cms1.

In spray pyrolysis, the effects of the preparation temperature, flow rate of the carrier gas and concentration of the spray solution on characteristics such as the morphology, size, and emission intensity of Ca8Mg(SiO4)4Cl2:Eu2+ phosphor powders under long-wavelength ultraviolet light were investigated. The phosphor powders obtained post-treatment had a range of micron sizes with regular morphologies. However, the composition, crystal structure and photoluminescence intensity of the phosphor powders were affected by the preparation conditions of the precursor powders. The Ca8Mg(SiO4)4Cl2:Eu2+ phosphor powders prepared at temperatures that were lower and higher than 700˚C had low photoluminescence intensities due to deficiencies related to the of Cl component. The phosphor powders with the deficient Cl component had impurity peaks of Ca2SiO4. The optimum flow rates of the carrier gas in the preparation of the Ca8Mg(SiO4)4Cl2:Eu2+ phosphor powders with high photoluminescence intensities and regular morphologies were between 40 and 60 l/minute. Phosphor powders prepared from a spray solution above 0.5 M had regular morphologies and high photoluminescence intensities.

In this study, nano-sized indium oxide powder with the average particle size below 100 nm is fab-ricated from the indium chloride solution by the spray pyrolysis process. The effects of the reaction temperature, the concentration of raw material solution and the inlet speed of solution on the properties of powder were studied. As the reaction temperature increased from 850 to , the average particle size of produced powder increased from 30 to 100 nm, and microstructure became more solid, the particle size distribution was more irregular, the intensity of a XRD peak increased and specific surface area decreased. As the indium concentration of the raw material solution increased from 40 to 350 g/l, the average particle size of the powder gradually increased from 20 to 60 nm, yet the particle size distribution appeared more irregular, the intensity of a XRD peak increased and spe-cific surface area decreased. As the inlet speed of solution increased from 2 to 5 cc/min., the average particle size of the powder decreased and the particle size distribution became more homogeneous. In case of the inlet speed of 10 cc/min, the average particle size was larger and the particle size distribution was much irregular compared with the inlet speed of 5 cc/min. As the inlet speed of solution was 50 cc/min, the average particle size was smaller and microstructure of the powder was less solid compared with the inlet speed of 10 cc/min. The intensity of a XRD peak and the variation of specific area of the powder had the same tendency with the variation of the average par-ticle size.

In this study, nano-sized powder of Ni-ferrite was fabricated by spray pyrolysis process using the Fe-Ni complex waste acid solution generated during the shadow mask processing. The average particle size of the produced powder was below 100 nm. The effects of the reaction temperature, the inlet speed of solution and the air pressure on the properties of powder were studied. As the reaction temperature increased from 80 to 110, the average particle size of the powder increased from 40 nm to 100 nm, the fraction of the Ni-ferrite phase was also on the rise, and the surface area of the powder was greatly reduced. As the inlet speed of solution increased from 2 cc/min. to 10 cc/min., the average particle size of the powder greatly increased, and the fraction of the Ni-ferrite phase was on the rise. As the inlet speed of solution increased to 100 cc/min., the average particle size of the powder decreased slightly and the distribution of the particle size appeared more irregular. Along with the increase of the inlet speed of solution more than 10 cc/min., the fraction of the Ni-ferrite phase was decreased. As the air pressure increased up to 1 , the average particle size of the powder and the fraction of the Ni-ferrite phase was almost constant. In case of 3 air pressure, the average particle size of the powder and the fraction of the Ni-ferrite phase remarkably decreased.

In the present study, the focus is on the synthesis of titanium carbide/cobalt composite powder by the spray thermal conversion process using metallic salt solution as the raw materials. Two types of oxide powders of Ti-Co-O system were prepared by the spray drying of two types of metallic salt solutions : titanium chloride-cobalt nitrate and powder-cobalt nitrate solutions. These oxide powders were mixed with carbon black, and then these mixtures were carbothermal reduced under a flowing argon atmosphere. The changes in the phase structure and thermal gravity of the mixtures during carbothermal reduction were analysed using XRD and TG-DTA. In the case of using the titanium chloride-cobalt nitrate solution, it could not be obtained TiC/Co composite powder due to contamination of the impurities during the spray drying of the solution. However, in tile case of using the powder-cobalt nitrate scullion, TiC-15 wt. %Co composite powder could be synthesized by the spray thermal conversion process. The synthesized TiC-15 wt. %Co composite powder at 120 for 2 hours has average particle size of 150 nm.