Ni(Fe)Al powders containing a homogeneous distribution of the in-situ formed AIN and dispersoids have been produced by mechanical alloying process in a controlled atmosphere using high energy attrition mill. The powders have been successfully consolidated by hot extrusion process. The phase information investigated by TEM and XRD analysis reveals that Fe can be soluble up to 20% to the NiAl phase () at room temperature after MA process. Subsequent thermomechanical treatment under specific condition has been tried to induce secondary recrystallization (SRx) to improve high temperature properties, however, the clear evidence of SRx was not obtained in this material. Mechanical properties in term of strength at room temperature as well as at high temperatures have been improved by the addition pf AIN, and the room temperature ductility has been shown to be improved after heat treatment, presumably due to the precipitation of second phase of in this material.

Ni 및 AI단원소 분말을 혼합하여 attrition mill을 사용하여 분위기 속에서 기계적 합금화 NiAI 기 산화물 분산강화 금속간화합물을 제조하였다. 제조된 분말은 여러 가지 다른 미세조직을 얻기 위하여 각기 다른 공정으로 열간성형을 하였으며, 연이어 이차 재결정 조직을 얻기 위한 가공열처리(thermomechanical treatment)를 실시하였다. 이차 재결정이 일어날 수 있는 선수조건으로서의초기 미세조직과 가공열처리와의 상관관계를 조사하였다. 정상 결정립 성장의억제와 접합조직의 존재가 이차 재결정을 일으키기 위한 필요조건으로 판명되었다. 이 재료에 있어서, 잔류 변형에너지를 공급할 수 있고 결정립을 미세화 할 수 있는 특정 공정하에서 항온 열처리 후 이차 재결정이 생성됨을 알 수 있었다.