Tungsten carbide is widely used in carbide tools. However, its production process generates a significant number of end-of-life products and by-products. Therefore, it is necessary to develop efficient recycling methods and investigate the remanufacturing of tungsten carbide using recycled materials. Herein, we have recovered 99.9% of the tungsten in cemented carbide hard scrap as tungsten oxide via an alkali leaching process. Subsequently, using the recovered tungsten oxide as a starting material, tungsten carbide has been produced by employing a self-propagating high-temperature synthesis (SHS) method. SHS is advantageous as it reduces the reaction time and is energy-efficient. Tungsten carbide with a carbon content of 6.18 wt % and a particle size of 116 nm has been successfully synthesized by optimizing the SHS process parameters, pulverization, and mixing. In this study, a series of processes for the highefficiency recycling and quality improvement of tungsten-based materials have been developed.

Cobalt (Co) is mainly used to prepare cathode materials for lithium-ion batteries (LIBs) and binder metals for WC-Co hard metals. Developing an effective method for recovering Co from WC-Co waste sludge is of immense significance. In this study, Co is extracted from waste cemented carbide soft scrap via mechanochemical milling. The leaching ratio of Co reaches approximately 93%, and the leached solution, from which impurities except nickel are removed by pH titration, exhibits a purity of approximately 97%. The titrated aqueous Co salts are precipitated using oxalic acid and hydroxide precipitation, and the effects of the precipitating agent (oxalic acid and hydroxide) on the cobalt microstructure are investigated. It is confirmed that the type of Co compound and the crystal growth direction change according to the precipitation method, both of which affect the microstructure of the cobalt powders. This novel mechanochemical process is of significant importance for the recovery of Co from waste WC-Co hard metal. The recycled Co can be applied as a cemented carbide binder or a cathode material for lithium secondary batteries.

General end-mill is considered and chosen by kinds and properties of material before machining, but in case of orthopedic surgery, cutting performance of orthopedic end-mill must be always best because bone condition is checked after operative preparation including skin incision. Generally hard metal end-mill is used for high cutting performance in industrial fields. To apply hard metal end-mill to robotic orthopedic surgery, prototypes with STS are manufactured and tested for determining proper number of flutes and helix angle, additionally proper overhang length of end-mill from sleeve end was determined by checking deflection under cutting load and critical speed using FEM program. As a result helix angle, blade number and overhang length are determined as 45∘, 3, 7cm respectively.

항공기 산업이 발전함에 따라 그 부품의 수는 더욱 다양해지며 복잡해지고 있다. Boeing B777, B747 엔진 부품인 블레이드의 경우 볼트 조립을 위한 드릴 가공 및 보링 가공이 필요하다. 블레이드의 형상의 영향으로 보링 공정이 들어가게 된다. 블레이드 형상의 일반 Machining Center에서의 보링공정은 공구수명을 불분명 한 상태에서 절삭속도 및 이송속도를 매우 낮추어 가공하여 가공시간이 늘어남으로서 생산성의 저하를 가져왔다. 절삭시간의 감소를 위해 최적가공조건 중 중요한 요소 중의 하나인 Tool Life는 필수적이다. 본 논문에서는 Aluminum을 Carbide Tool로 가공할 때 사이의 Tool Life를 연구한다.

In this paper, experimental studies of the regrinding of tungsten carbide (WC-Co) tools for high-speed machining were conducted. Regrinding and a subsequent evaluation test were carried out for a flat endmill tool with diameters of 10 mm and 3 mm using a CNC five-axis tool grinder and a CNC three-axis machining center. Tool wear on the two types of endmill tools increased as the cutting length increased, and the tool wear was not influenced by the regrinding state. In case of the micro endmill with a tool diameter of 3 mm, the effective regrinding time was determined for a flank wear threshold of 0.3 mm considering the tool life according to cutting length. The tool lives of the 10 mm and 3 mm endmill tools were increased by 80% and 72%, respectively. This conclusion proves the Feasibility of the recycling of tungsten carbide materials in the high-speed machining of high-hardened materials for industrial applications.

To satisfy the demand of higher cutting performance, mechanical properties with tungsten carbide (WC-Co) tool materials were investigated. Hardness and transverse rupture strength with WC grain size, Co content and density were measured. Compared to H, K, and S manufacture maker as tungsten carbide (WC-Co) tool materials were used for high-speed machining of end-milling operation. The three tungsten carbide (WC-Co) tool materials were evaluated by cutting of STD 11 cold-worked die steel (HRC25) under high-speed cutting condition. Also, tool life was obtained from measuring flank wear by CCD wear measuring system. Tool dynamometer was used to measure cutting force. The cutting force and tool wear are discussed along with tool material characteristics. Consequently, the end-mill of K, H manufacture maker showed higher wear-resistance due to its higher hardness, while the S maker endmill tool showed better performance for high metal removal.

새로운 급속소결방법인 고주파유도가열 소결법과 펄스전류활성 소결법을 이용하여 습식 볼밀링으로 혼합한 WC-8wt.%Co분말에 60MPa의 압력과 90%의 고주파출력 또는 2800A의 필스전류를 가하여 상대밀도가 98.6% 이상인 초경재료를 2분이내의 짧은 시간에 제조하였다. 초기의 WC분말의 입도가 미세해짐에 따라 고주파유도가열 소결법과 펄스전류활성 소결법 모두 소결시간이 단축되는 경향을 보였으며 그 소결체의 결정립 크기도 감소하였다. 고주파유도가열 소결

급속소결방법인 고주파유도가열 소결법과 펄스전류활성 소결법을 이용하여 습식 볼밀링으로 혼합한 WC-8wt.%Ni분말에 60MPa의 압력과 고주파유도가열장치의 경우 전체 용량 (15kw)의 90%에 해당하는 고주파출력을, 펄스전류활성 소결장치의 경우 2800A의 펄스전류를 가하여 치밀한 소결체를 2분이내의 짧은 시간에 제조하였다. WC 초기입자크기가 증가함에 따라 제조된 소결체의 입자크기와 평균자유행로는 증가하였다. 또한 WC 결정립 크기가 증가함에 따라

In the present study, the focus is on the analysis of carbothermal reduction of oxide powder prepared from waste WC/Co hardmetal by solid carbon under a stream of argon for the recycling of the WC/Co hard-metal. The oxide powder was prepared by the combination of the oxidation and crushing processes using the waste hardmetal as the raw material. This oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under a flowing argon atmosphere. The changes in the phase structure and gases discharge of the mixture during carbothermal reduction was analysed using XRD and gas analyzer. The oxide powder prepared from waste hardmetal has a mixture of . This oxide powder reduced at about , formed tungsten carbides at about , and then fully transformed to a mixed state of tungsten carbide (WC) and cobalt at about by solid carbon under a stream of argon. The WC/Co composite powder synthesized at for 6 hours from oxide powder of waste hardmetal has an average particle size of .

WC and dense WC-10 vol%Co materials with grain size of~1 were synthesized by high-frequency induction heated combustion synthesis (HFIHCS) method in one step from elemental powders of W, C and Co within several minutes. Simultaneous combustion synthesis and densification were accomplished under the combined effects of an induced current and mechanical pressure. In the absence of cobalt additive, WC can be formed, but its relative density was low (about 73%) under simultaneous application of a 60 MPa pressure and the induced current. However, in the presence of 10 vol.%Co, the relative density increased to 99% under the same experimental condition. The percentages of the total shrinkage occurring before and during the synthesis reaction of WC-10 vol.%Co were 5% and 51%, respectively. The fracture toughness and hardness values of WC-10 vol.%Co were 10 MPa . m and 1840 kg/, respectively.

In this study, the WC-10 wt.%Co nanopowders doped by grain growth inhibiter were produced by three different methods based on the spray conversion process. Agglomerated powders with homeogenous distribution of alloying elements and with internal particles of about 100-200 nm in diameter were synthesized. The microstructural changes and sintering behavior of hardmetal compacts were compared with doping method and sintering conditions. The microstructure of hardmetals was very sensitive to doping methods of inhibitor. Nanostructured WC-Co hardmetal powder compacts containing TaC/VC doped by chemical method instead of ball-milling shown superior sintering densification, and the microstructure maintained ultrafine scale with rounded WC particles.