PURPOSES : In this study, the initial behaviors of shoulder concrete slabs and tiebars at the longitudinal construction joints between the shoulder JCP and mainline CRCP are investigated. METHODS : The strains of concrete and tiebars were measured at the longitudinal construction joint between the CRCP and JCP. Measurements were performed using data accumulated over a month after concrete placement. The contact conditions were investigated by comparing the strains at each location. RESULTS : The longitudinal construction joints between the shoulder JCP and mainline CRCP exhibited the composite behavior of bonding and friction, and a virtual neutral axis was formed inside the JCP. At the connection of the shoulder concrete, the strain and temperature of the concrete were inversely proportional. The tiebars connecting the CRCP and JCP exhibited different behaviors depending on the bonding conditions around the tiebars of the construction joints. In the presumed state in which the bonding condition was maintained, the concrete temperature and tiebar strain were directly proportional; however, the presumed state of the separation condition exhibited an inversely proportional relationship. In the 24-h behaviors of the tiebars, the effects of the horizontal and curling movements overlapped, and the strains of the measured tiebars increased at the minimum and maximum temperatures of the shoulder JCP. CONCLUSIONS : The strains in the tiebars and concrete slabs primarily depended on the boundary conditions (bonding and friction) of the longitudinal construction joint between the shoulder JCP and mainline CRCP.

PURPOSES : The purpose of this study is to verify the effectiveness of the developed ultra-thin-continuously reinforced concrete partition (UT-CRCP) overlay method through a comparative analysis of the early-behavior of the UT-CRCP with a 100 mm cutting overlay of the existing JPCP. METHODS : This study aims to minimize the vulnerability of the existing JPCP (joint section behavior) by overlaying the continuous reinforcement form to constrain joint behavior. For this purpose, the early-behavior of the JPCP section was measured and the early-behavior of the UT-CRCP section was compared with that of the cutting overlay of the same section. The testbed was constructed for comparative analysis of the two types of pavements and the early behavior was measured using the pure environmental loads, i.e., situations where there was no traffic load. For the UT-CRCP, which is a comparative test group, UT-CRCP was constructed approximately one year after the JPCP was constructed by milling the top of the existing JPCP by 100 mm. RESULTS : 1) UT-CRCP was shown to effectively reduce the amount of crack width change on the surface by 17 %, compared to JPCP, by placing reinforcement inside the pavement. 2) The restricting effect of the UT-CRCP was analyzed by comparing the strain generated by the cross-section depth for the two pavement types. As a result, the restricting rate by depth (20, 80, 120, and 280 mm) was 68.4 %, 80.2 %, 89.2 %, and 26.7 %, respectively. 3) We reviewed the comprehensive gauge restricting rate at depths of 80 mm and 120 mm (80.2 % and 89.2 %, respectively) and the absolute value of behavior that is located at the ±20 mm of the interface of JPCP and UT-CRCP. Thus, it was possible to estimate that both layers of pavements exhibit the same behavior (tied) at the interface between the two pavement layers. CONCLUSIONS : In this study, the early behavior of the BCO concept UT-CRCP overlay technique was analyzed and quantitatively presented to overcome the limitations of JPCP with relatively weak point behavior and to increase the commonality of aged concrete pavement to the performance of the new pavement.

신개념 철근콘크리트 포장(ARCP: Advanced Reinforced Concrete Pavement)은 균열유도장치를 이용하여 원하는 위치에 균열을 유도하고 연속철근 콘크리트 포장(CRCP)의 거동에 영향을 미치지 않는 균열 사이의 종방향 철근을 다수 제거하여 철근 사용량을 대폭 감소시키는 포장 공법이다. ARCP 공법의 주요 요소 기술의 하나인 균열유도는 균열유도장치의 형상, 설치깊이, 콘크리트와의 부착유무에 따라 균열의 진전 및 거동에 차이가 발생할 수 있다. 따라서 본 연구에서는 최적의 균열 유도를 위한 방안을 마련하고자 균열유도장치의 형상, 설치깊이, 콘크리트와의 부착 유무에 따른 유도균열을 형성하여 각각의 거동을 계측 및 분석하였다. 그림 1과 같은 야드 실험체에 7종류의 서로 다른 균열유도장치를 설치하였으며 유도균열의 거동 측정을 위한 균열게이지를 설치하였다. 거동 계측은 균열발생 초기부터 균열폭 및 슬래브 온도를 측정하였으며, 계측 10일차부터 20일까지의 데이터를 분석하였다. 균열폭 거동을 그림 2에 나타내었다. 균열폭 거동이 크게 발생하는 균열유도장치는 균열유도장치와 콘크리트가 부착되지 않은 경우(C4)와 콘크리트 다짐을 위하여 균열유도장치의 면적이 작은 경우(C5)인 것으로 나타났으며, 가장 작은 균열폭 거동이 나타나는 것은 비닐을 삽입하였던 경우(C6)인 것으로 나타났다. 균열유도장치의 형상 및 설치깊이, 콘크리트와의 부착 유무에 따라 균열폭 거동에 다소 차이는 발생하지만 모든 경우에서 균열폭이 0.1mm 이하의 작은 거동이 발생하는 것으로 보아 계획한 균열유도장치는 모두 사용이 가능한 것으로 분석되었다.

본 논문에서는 탄소성 영역 내 패치 로딩 크기에 따른 알루미늄 합금 사각형 판의 초기 처짐 영향을 수치해석방법으로 이용한 탄성 및 탄소성 대변형 시리즈 해석을 수행하였다. 주변 지지조건은 단순지지로 가정하고 초기 처짐 크기(w/t), 종횡비(a/b), 세장비(b/t)를 고려하여 알루미늄 합금 A6082-T6 사각형 판의 임계 탄성 좌굴하중과 좌굴 후 거동을 검토하였다. 탄성 및 탄소성 대변형 시리즈 해석은 상용프로그램을 사용하였다. 초기 처짐 크기가 작을 경우 하중증가와 함께 면내 강성이 처음부터 감소하며 크기가 커질수록 훨씬 두드러지게 발생한다. 종횡비가 커질수록 초기항복강도는 점차 감소하며 판 두께가 두꺼울수록 패치 로딩 크기(l/b) 0.5 이후 초기 항복강도 감소비율은 얇은 두께보다 더 크게 발생한다.

PURPOSES : The purpose of this study is to analyse the longitudinal steel strain and stress of continuously reinforced concrete pavement(CRCP) with longitudinal and transverse direction at early age using stress dependent strain analysis method. METHODS : To measure the longitudinal steel strain, 9-electrical resistance and self-temperature compensation gauges were installed to CRCP test section (thickness = 250mm, steel ratio = 0.7%) and continuously measured 10min. intervals during 30days. In order to properly analyze the steel stress first, temperature compensation process has been conducted. Secondly, measured steel strains were divided into stress dependent strain (elastic strain) and stress independent strain (thermal strain) and then stress dependent strain was applied to stress calculation of longitudinal steels. RESULTS: Steel strains were successfully measured during 30days. To verify the accuracy of temperature compensation process, measured coefficient of thermal expansion(COTE,11.46×10-6m/m/℃) of longitudinal steel before paving was compared with that of unrestrained steel. Max. steel stress in the transverse direction shows about 266MPa at 23days after placement. CONCLUSIONS: Steel stresses in the longitudinal and transverse direction have been evaluated. In longitudinal direction, steel stress from the crack was rapidly reduced from 183MPa at crack to 18MPa from 600mm apart the crack. From this observation, stress effective length can be identified as within 600mm apart from the crack. In transverse direction, max. stress point was located near the center of pavement width and stress level(266MPa) is about 66% of yield stress of steel

복합적층판은 다른 금속재료에 비해 높은 비강도, 비강성 등의 우수한 역학적 특성을 지니므로 최근 다양한 분야에서 사용하고 있다. 그러나 이러한 복합적층판은 일반 금속재료에 비해 충격에 약하다는 단점이 있다. 이 점을 해결하기 위한 연구는 많은 연구자들에 의해 다양하게 시도되고 있다. 본 연구는 복합적층판에 초기응력을 도입하여 충격거동 특성을 파악한다. 고전적인 이론식인 Hertz의 접촉법칙과 실험식인 Sun과 Tan의 압입법칙을 포함한 유한요소프로그램을 이용하여 복합적층판의 초기응력에 의한 충격거동 특성을 조사한다.

본 연구는 조립식 콘크리트 포장 공법을 이용하여 도심지 버스전용차로의 정거장 구간 아스팔트 포장을 강성 포장으로 교체하는 시공을 수행한 후 이러한 포장의 초기 공용성을 분석하기 위해 수행되었다. 추적조사 항목으로는 조립식포장의 진출입 구간에서 아스팔트 포장과 조립식포장과의 단차, 프리캐스트 슬래브간의 줄눈 간격 및 단차, 슬래브의 침하, 슬래브의 미끄럼저항 성능 등을 선정하였으며, 다이아몬드 그라인딩 공법의 적용성도 분석하였다. 추적조사 결과 조립식포장의 단차, 줄눈 간격, 미끄럼저항, 침하 등은 시간에 따라 변화가 거의 없었으며, 이를 통해 프리캐스트 슬래브가 차량하중을 안정되게 지지한다는 것을 알 수 있었다. 또한 다이아몬드 그라인딩 공법을 적용하면 슬래브의 단차 및 미끄럼저항 성능을 크게 개선할 수 있는 것도 확인할 수 있었다.

횡하중을 받는 RC 기둥의 전단강도는 기둥의 변위연성도가 증가함에 따라 감소하는 것으로 알려져 있다. 연성도의 증가에 따른 전단강도의 감소율은 초기전단강도에 따라 크게 좌우되므로 이를 합리적으로 예측하기 위해서는 초기전단강도의 평가가 매우 중요하다. 기둥의 전단거동은 단면모양, 형상비, 축력, 축방향철근비, 연성도 등 다양한 요인에 의하여 영향을 받아 복잡하다. 본 연구에서는 형상비, 단면의 중공비, 축방향철근비, 중공 및 중실단면을 변수로 하는 시험체를 제작하여 실험적 연구를 수행하여 전단거동특성을 살펴보았다. 또한, 축방향철근이 전단강도에 미치는 영향을 분석하여 형상비와 축력을 고려한 기존의 초기전단평가식을 보완하였으며, 그 타당성을 검증하였다.

본 연구에서는 노후 콘크리트 포장의 효율적 유지보수를 위하여 국내 최초 적용된 Thin Bonded Continuously Reinforced Concrete Overlay (CRCO) 공법의 초기 공용성이 평가되었다. 서해안 고속도로의 표층 파손 구간에 Jointed Plain Concrete Pavement (JPCP) 덧씌우기와 CR8O 공법을 이용한 보수가 진행되었다. JPCP 덧씌우기 공법이 적용된 구간에서는 인접 슬래브가 완전히 분리되도록 덧씌워진 층의 줄눈을 완전히 커팅하였으며, CRCO 공법이 적용된 구간에서는 0.5% 종방향 철근과 위치 고정용 횡방향 철근을 설치한 후 그 위에 덧씌우기를 수행하였다. 두 구간 모두에서 3종시멘트가 이용되었다. 현장 강도 시험 결과, 1~3일 내에 교통개방이 가능한강도가 발현된 것이 확인되었으며, vibrating wire gauge (VWG) 데이터 분석 결과 CRCO 공법이 기존 포장의 줄눈 거동을 억제하는 것으로 나타났다. 부착강도 시험결과, 재령에 상관없이 높은 부착강도가 확인되었다. 한편 JPCP 덧씌우기 공법이 적용된 구간에서는 중앙부에서, CRCO 공법이 적용된 구간에서는 CRCO 포장과 같은 무작위 횡방향 균열이 관찰되었으며, CRCO 공법의 균열폭 거동이 JCP 보다 50% 정도 낮은 것으로 나타났다.

국내 줄눈콘크리트 포장의 줄눈간격은 6m로 획일적으로 설계 건설되어 왔으며 이에 대한 과학적 근거는 제시된 바 없었다. 현재 진행중인 한국형 포장설계법 개발에서는 국내 지역별 기후조건 등을 고려하여 줄눈간격 변화에 따른 줄눈콘크리트 포장의 장 단기 파손을 역학적-경험적 방법을 토대로 분석하여 줄눈간격을 지역별로 6~8m로 설계할 것을 제시한 바 있다. 본 연구는 한국형 포장설계법에서 제시한 줄눈간격 잠정안에 대한 타당성을 검증하기 위한 연구의 일환이다. 줄눈간격이 증가할 경우 시공초기에 하중전달률의 변화, 무작위균열 등의 발생가능성에 문제점이 없는지를 검증하기 위해서 한국형 포장설계법의 줄눈간격 잠정안에서 줄눈간격이 7m로 제시된 지역에 대해서 7m 줄눈간격으로 시험시공하고 초기거동을 모니터링 하였다. 하중전달률, 무작위균열, 줄눈폭변화 등 모니터 링 결과를 시공조건이 동일한 인접 6m 줄눈간격 비교구간의 초기거동과 비교분석하였다.

연속철근콘크리트포장에서 횡방향 균열은 초기의 온도와 습도변화로 인해 발생하며 횡 방향 균열의 폭과 간격은 하중전달효율 및 펀치아웃과 같은 포장공용성에 직접 관련된다. 또한, 연속철근콘크리트포장에서 균열폭은 콘크리트의 건조수축 뿐만아니라 소위 특성 온도변화 시점으로 정의되는 "제로-스트레스 온도"에 의존한다. 연속철근콘크리트포장의 양호한 장기공용성을 위해서 횡방향 균열은 매우 작은 폭으로 유지될 필요가 있으며 초기재령 에서 온도제어는 이를 위한 필수요소라 할 수 있다. 따라서, 본 연구에서는 페이브프로를 사용하여 콘크리트 온도를 예측하였으며 현장실험을 통한 실측온도와 비교하고 균열조사를 수행하였다. 본 연구로부터 도출된 결과는 첫째, 실측온도는 0.2~4.5℃의 범위에서 예측온도보다 큰 것으로 나타났으며 정확한 콘크리트 온도예측을 위해서는 수화특성치로 고려되는 활성화 에너지와 단열온도상수가 입력변수에서 정확히 고려되어야 할 것으로 판단되었다. 둘째. 콘크리트 타설 후 24시간 이내의 온도는 오후에 비하여 오전에 타설된 콘크리트에서 더 크게 나타났으며 최대온도는 정오에 타설된 온도에서 발생되었다. 마지막으로 재령 12일에 조사된 균열발생률은 오전에 타설된 구간에서 25% 증가되고 그 만큼 균열간격은 감소하는 것으로 나타났다. 이 결과로부터 최대 콘크리트 온도는 균열발생에 크게 영향을 미치며 콘크리트 온도제어는 연속철근콘크리트포장의 양호한 공용성을 위해 필요할 것으로 판단되었다.