Embedding of active devices in a printed circuit board has increasingly been adopted as a future electronic technology due to its promotion of high density, high speed and high performance. One responsible technology is to embedded active device into a dielectric substrate with a build-up process, for example a chipin-substrate (CiS) structure. In this study, desmear treatment was performed before Cu metallization on an FR-4 surface in order to improve interfacial adhesion between electroless-plated Cu and FR-4 substrate in Cu via structures in CiS systems. Surface analyses using atomic force microscopy and x-ray photoemission spectroscopy were systematically performed to understand the fundamental adhesion mechanism; results were correlated with peel strength measured by a 90o peel test. Interfacial bonding mechanism between electrolessplated Cu and FR-4 substrate seems to be dominated by a chemical bonding effect resulting from the selective activation of chemical bonding between carbon and oxygen through a rearrangement of C-C bonding rather than from a mechanical interlocking effect. In fact, desmear wet treatment could result in extensive degradation of FR-4 cohesive strength when compared to dry surface-treated Cu/FR-4 structures.

In high-efficiency Cu(In,Ga)Se2 solar cells, Na is doped into a Cu(In,Ga)Se2 light-absorbing layer from sodalime-glass substrate through Mo back-contact layer, resulting in an increase of device performance. However, this supply of sodium is limited when the process temperature is too low or when a substrate does not supply Na. This limitation can be overcome by supplying Na through external doping. For Na doping, an NaF interlayer was deposited on Mo/glass substrate. A Cu(In,Ga)Se2 absorber layer was deposited on the NaF interlayer by a three-stage co-evaporation process As the thickness of NaF interlayer increased, smaller grain sizes were obtained. The resistivity of the NaF-doped CIGS film was of the order of 103Ω·cm indicating that doping was not very effective. However, highest conversion efficiency of 14.2% was obtained when the NaF thickness was 25 nm, suggesting that Na doping using an NaF interlayer is one of the possible methods for external doping.

The brazing adhesion properties of Ag coated W-Ag electric contact on the Cu substrate have been investigated in therms of microstructure, phase equilibrium and adhesion strength. Precoating of Ag layer ( in thickness) on the contact material was done by electro-plating method. Subsequently the brazing treatment was conducted by inserting BCuP-5 filler metal (Ag-Cu-P alloy) layer between Ag coated W-Ag and Cu substrate and annealing at in atmosphere. The optimum brazing temperature of was semi-empirically calculated on the basis of the Cu atomic diffusion profile in Ag layer of commercial electric contact produced by the same brazing process. As a mechanical test of the electric contact after brazing treatment the adhesion strength between the electric contact and Cu substrate was measured using Instron. The microstructure and phase equilibrium study revealed that the sound interlayer structure was formed by relatively low brazing treatment at . Thin Ag electro-plated layer precoated on the electric contact ( in thickness) is thought to be enough for high adhesion strength arid sound microstructure in interface layer.

Sn-Bi-X(X:2Cu, 2Sb, 5In) 계 땜납과 Cu 기판과의 계면반응 및 기계적성질에 대하여 고찰하였다. Cu판과 땜납의 접합부는 100˚C에서 60일까지 열처리하여 광학현미경, SEM, EDS,분석을 통하여 시효처리에 따른 미세조직과 계면반응을 분석하였으며, 인장강도 및 연신율은 제조된 시편을 30일까지 열처리 한 후 0.3mm min-1로 인장하여 시험하였다. 미세조직 분석결과 Cu의 첨가로 미세조직이 미세화 됨을 알 수 있으며, 계면에 형성된 화합물은 첨가원소에 따라 다르게 나타났다. 인장시험 결과 열처리 초기에는 땜납쪽에서의 파괴가 발생하였으나 열처리 시간이 증가하면서 계면반응층고 땜납의 계면에서 파괴가 발생하였다. 열처리에 따른 인장강도는 Cu를 첨가한 경우에 가장 높은 값을 나타냈다.

리모트 수소 플라즈마를 이용하여 Si 기판 위의 구리 오염의 제거 효과에 관하여 조사하였다. 최적의 공정 조건을 찾기 위하여 Si 기판을 1ppm CuCI2 표준 화학 용액으로 인위적으로 오염시킨 후 rf power와 세정시간, 거리 (수소플라즈마 중심에서 Si 기판표면까지의 거리)등의 공정 변수를 변화시키며 리모트 수소 플라즈마 세정을 실시하였다. 리모트 수소 플라즈마 세정 후 Si 표면의 분석을 위하여 TXRF(total x-ray reflection fluorescence)와 AFM(atomic force microscope)측정을 실시하였다. 리모트 수소 플라즈마 세정이 Cu의 제거에 효과적이며 Si 표면의 거칠기에 나쁜 영향을 주지 않음을 TXRF와 AFM 분석결과로부터 알 수 있었다. Cu 불순물의 흡착 메커니즘은 산화 환원 전위 이론으로 설명될 수 있으며, Cu 불순물의 제거 메커니즘은 XPS(x-ray photoelectron spectroscopy)분석결과를 근거로 하여 다음과 같이 설명할 수 있다. :먼저 Cu 이온이 Si 표면에 흡착되어 화학적 산화막을 생성한다. 그 다음, 수소 플라즈마 중의 반응성이 강한 수소이온이 이 산화막을 분해시켜 제거하며 Cu 불순물은 산화막이 제거될 때 함께 제거된다.

TiN 기판상에 CVD와 무전해 도금을 이용하여 구리막을 성장시킬 때 여러 가지 전처리에 따른 증착 양상의 변화에 관하여 조사하였다. Cu(hfac)2를 선재(precursor)로 사용하여 CVD 증착을 실시할 때 각 전처리에 따른 TiN상의 구리막의 덮힘성(coverage)향상은 Pd-HF 활성화 처리>>HF dip> RF remote plasma의 순이었다. 특히 Pd-HF 활성화 처리를 해줄 경우 거의 완전한 연속막을 얻을수 있었으며 scotch tape peel test 결과 매우 양호한 부착특성을 보였으나, 이에 비해 전처리를 해주지 않은 경우에는 오랜 시간이 경과되어도 연속막으로 성장하지 못하고 섬모양의 큰 결정립을 이룰 뿐이었다. 이러한 차이는 Pd-HF 활성화 처리에 의해 표면에 미세하게 형성된 Pd층이 구리의 핵생성과 부착특성을 크게 향상시켰기 때문인 것으로 사료되며 이러한 효과는 무전해 도금의 경우에도 마찬가지였다. 그리고 기판과 증착온도에 따른 선택성을 보면 350˚C이하에서는 pd-HF 활성화 처리에 의해서 SiO2에 대하여 TiN으로의 선택성을 가지나 그 이상의 온도에서는 선택성이 상실되었다.