The purpose of this study is to experimentally analyze the seismic performance of beam-column specimens with vertical irregular, which were reinforced with RHS (Replaceable steel haunch system). a steel haunch system. To evaluate the seismic performance of the RHS, three specimens were manufactured and subjected to cycle loading tests. Retrofitted specimens have different beam-upper column stiffness ratio as a variable. The stiffness ratio of beam-upper column were considered to be 1.2 and 0.84. As a result of the test, the specimen reinforced with RHS showed improved maximum load and effective stiffness, and energy dissipation capacity compared to the non-retrofitted specimen with same beam-upper column stiffness ratio. The specimen with 0.84 beam-upper column stiffness ratio showed improved performance than the specimen with 12.

When reinforcing an existing reinforced concrete beam-column building with a precast concrete panel, special connection between the PC member and the RC member is required to solve the time dependent deformation of the RC member and to receive the large shear forces. The aim of this study is to obtain the shear strength of upper connection between the existing RC beam-column and infilled PC wall panels in experimentally and theoretically. Thus, the static shear loading tests were conducted on the 6 specimens with the plate connection. Shear failure was resulted from the weakest portion of interior PC panel, exterior RC, and the connection, when the PC portion which located at the center of specimen was pulled upward from the bottom. T he experimental result was compared with analytical result from ACI 318M-14 Chapter 17 for the shear strength of post-installed anchor and PCI Handbook 7th edition 6.8 Structural Steel Corbel (PCI Design Handbook 7th edition, 2010) for the strength of cast-in H-beam. The analytical and experimental results show final failure at the same location. The failure loading of experiment showed larger than average 6% to that of the analysis.

본 연구는 철근콘크리트 내부 보-기둥 접합부의 전단거동 예측에 관한 비선형 모델을 제안한 것이다. 보-기둥 접합부 패널존에서의 전단거동 모델을 위하여 면내전단 예측을 위한 연화트러스모델 이론을 수정한 이론을 적용하였다. 이로부터 접합부에서의 평형조건에 의한 등가 모멘트 및 회전 관계를 이용하여 접합부에서의 전단변형 관계를 접합부의 회전스프링의 특성관계로 변환하여 고려토록 하였다. 소개된 해석모델을 축력 및 전단을 받는 내부 철근콘크리트 보-기둥 접합부의 실험과 비교하였으며, 제시된 모델은 접합부에서의 전단력 뿐만 아니라 전단변형의 예측에도 유효한 것으로 판단되었다.

본 논문에서는 철근콘크리트 모멘트 골조의 보-기둥 접합부에 대한 비탄성 회전 능력의 성능을 조사한 연구 결과를 하고 있다. 총 91개의 보-기둥 접합부 실험체에 대해 상세히 조사되었으며, 그 중 28개의 실험체는 ACI 318-02의 상세 요구에 기초하여 특수 모멘트 골조 접합부로서 분류되었다. AISC-97 내진 기준에서 철골 모멘트 골조 접합부를 위해 정의된 허용기준이 분류된 철근콘크리트 모멘트 골조의 접합부에 대해 평가하기 위해서 사용되었다. 특수 모멘트 골조 접합부에 대한 설계 상세를 만족하는 28개의 실험체 중 27개의 특수 모멘트 골조 접합부가 충분한 강도를 가지고 있었으며, 급격한 강도 감소 없이 0.03 rad.의 소성 회전에 대해 연성 거동을 발휘할 수 있음을 보여 주었다. 접합부의 전단 강도, 기둥과 보에 대한 휨 강도 비율, 접합부내에서의 횡방향 철근비 등에 대한 제한이 보-기둥 접합부의 만족스런 내진 성능을 보여주는데 중요한 역할을 하였다.

본 논문에서는 지진하중을 받는 내부 및 외부 철근콘크리트 보-기둥 접합부의 강도 및 연성능력을 평가하였다. 접합부에 인접한 보에 소성힌지가 발생한 이후 접합부가 파괴할 경우 접합부 내력은 보의 소성힌지의 영향을 받아 감소하게 된다. 보에 소성힌지가 발생하면 보의 부재축방향 변형률은 급격하게 증가하게 되며, 증가된 부재축방향 변형률은 접합부의 변형에 영향을 주어 접합부의 강도를 저감시킨다. 이 논문에서는 보에 소성힌지가 발생하기 이전에 파괴하는 접합부의 내력과 보에 소성힌지가 발생한 이후에 파괴하는 접합부의 연성능력을 접합부의 변형능력 및 스트럿의 강도저감을 이용하여 평가하였다. 제시한 평가법은 52개의 접합부 실험체를 이용하여 검증하였다.

본 연구에서는 기존 철근콘크리트건물 보-기둥 접합부의 내진 성능을 개선하기 위하여 탄소섬유를 사용하여 구조물을 보강한 후 실험을 수행하였다. 이를 위하여 6개의 철근콘크리트 보-기둥 접합부를 제작하였으며, 지진하중과 같은 반복하중이 작용할 때 보강재료 및 보강영역 등을 변수로 하여 실험을 수행하여 각 보강변수에 따른 보강효과를 평가하였다. 본 실험을 통하여 구조물의 내진 성능 및 연성능력을 증진시킬 목적으로 새로운 보강재료(탄소섬유판, 탄소섬유봉, 탄소섬유쉬트)로 설계된 보강 실험체(RPC-CP2, RPC-CR, RJC-CP, RJC-CR)들은 내력증진은 물론이고 안정적인 이력거동을 확보할 수 있었다.

본 연구에서는 철근콘크리트기둥과 철골보로 이루어진 혼합구조 접합부의 해석에 대한 유한 유소법을 이용한 해석 모델 방법을 제시하였다. 혼합구조 접합부에서 콘크리트와 강판이 접하는 접촉면은 두 접촉면 사이를 부착과 마찰의 개념으로 표현할 수 있는 주-종속 접촉 알고리즘(master-slave contact algorithm)을 이용하여 모델링하였다. 그리고, 휨응력의 지배를 받는 강관에는 비적합 모드 요소를 사용하였다. 본 연구에서의 혼합구조 특징은 보에서 기둥으로 힘의 전달을 원활히 하기 위하여 다이아프램이 사용되었고, 이러한 혼합구조 접합부 모델링 방법에 대한 타당성을 알아보기 위하여 3차원 비선형 해석을 행하여 실험결과와 비교한 결과 잘 일치하는 결과를 얻었다.

본 연구에서는 기존의 저자 등에 의해 수행된 유연도법에 근거한 보-기둥 섬유요소에 수치해석적 방법으로부터 전단변형 효과를 고려할 수 있도록 수정된 정식화 방안과 단면에 대한 비탄성 전단응답 이력 구성관계식을 새로이 제안함으로써 전단 및 휨 - 전단파괴 양상을 나타내는 철근콘크리트 보에 대한 합리적인 해석적 방안을 마련하는 것을 목표로 한다. 주요 실험변수들이 전단거동 특성에 미치는 영향을 파 악하기 위하여 모두 종방향 철근의 항복전에 전단파괴가 일어나도록 설계된 총 6개의 철근콘크리트 보 실험체를 검증 대상으로 저자 등에 의 해 새로이 수정된 구성관계식을 적용한 비선형 유한요소해석 프로그램(RCAHEST)을 통한 해석을 수행하였다. 모든 실험체에 대한 파괴모드 와 파괴시까지의 전반적인 거동 특성을 비교적 적절히 예측하고 있음을 확인하였으며 이러한 연구결과들은 향후, 대형화‧복잡화 되어가고 있 는 전체 구조물에 대한 신뢰도 높은 해석을 수행하기 3차원 해석에도 충분히 활용될 수 있을 것으로 기대된다.

When reinforcing an existing reinforced concrete beam-column building with a precast concrete panel, special connection between the PC member and the RC member is required to solve the time dependent deformation of the RC member and to receive the large shear forces. The aim of this study is to obtain the shear strength of upper connection between the existing RC beam-column and infilled PC wall panels in experimentally and theoretically. Thus, the static shear loading tests were conducted on the 6 specimens with the plate connection. Shear failure was resulted from the weakest portion of interior PC panel, exterior RC, and the connection, when the PC portion which located at the center of specimen was pulled upward from the bottom. The experimental result was compared with analytical result from ACI 318M-14 Chapter 17 for the shear strength of post-installed anchor and PCI Handbook 7th edition 6.8 Structural Steel Corbel (PCI Design Handbook 7th edition, 2010) for the strength of cast-in H-beam. The analytical and experimental results show final failure at the same location. The failure loading of experiment showed larger than average 6% to that of the analysis.

When reinforcing an existing reinforced concrete beam-column building with a precast concrete panel, special connection between the PC member and the RC member is required to solve the time dependent deformation of the RC member and to receive the large shear forces. The aim of this study is to obtain the shear strength of upper connection between the existing RC beam-column and infilled PC wall panels in experimentally and theoretically. Thus, the static shear loading tests were conducted on the 6 specimens with the plate connection. Shear failure was resulted from the weakest portion of interior PC panel, exterior RC, and the connection, when the PC portion which located at the center of specimen was pulled upward from the bottom. The experimental result was compared with analytical result from ACI 318M-14 Chapter 17 for the shear strength of post-installed anchor and PCI Handbook 7th edition 6.8 Structural Steel Corbel (PCI Design Handbook 7th edition, 2010) for the strength of cast-in H-beam. The analytical and experimental results show final failure at the same location. The failure loading of experiment showed larger than average 6% to that of the analysis.

이 연구의 목표는 학교 건물과 같은 저층 보-기둥 철근콘크리트 구조 건물에서 프리캐스트 벽패널을 사용한 새로운 내진보강 방법 을 개발하는데 있다. 1개의 무 보강 보-기둥 실험체와 U형 PC 패널로 보강한 2개의 보강 보-기둥 실험체에 대한 정적 이력 하중실험을 진행하 였다. 앵커 접합부 실험체는 전단 파괴될 것으로 해석되었고 철판 용접 접합부 실험체는 휨 파괴할 것으로 예측되었다. 실험체의 종국 내력은 상부 접합부의 전단 내력과 PC 패널 절곡 부 휨 위험단면에서 휨 내력 중 약한 것으로 결정되었다. 이 실험체에서, 한쪽 RC기둥이 가 하중(미는 실험 하중)을 받아 PC 패널 부재를 밀게 된다면, 다른 쪽 내부 수직부재는 상부 전단 접합부로부터 부 하중(당기는 실험 하중)을 받게 되어있었 다. 가 하중을 받는 2개의 부재는 합성 휨 거동이 지배적이므로 합성단면의 휨 내력이 실험체의 최종 내력을 결정하게 되지만, 이 경우 최종 내 력에 대하여 상부 전단 접합부 강도의 직접적인 영향은 없다고 볼 수 있다. 그러나 부 하중(당기는 하중)을 받는 RC 기둥과 PC 패널 부재는 비 합성 거동이 지배적이고 실험체의 최종 내력은 상부 전단 접합부 전단내력의 크기에서 직접 영향을 받는 것으로 파악되었다. ACI 318M-11 Appendix-D 앵커 전단설계에 기초한 전단내력 그리고 실험에서 얻은 최대하중을 적용하여 마이다스 젠 탄성설계에 의하여 계산한 전단 외력 에 대한 비교 해석결과는 실험결과와 일치하는 해석결과를 보여주었다.

이 연구의 목표는 학교 건물과 같은 저층 보－기둥 철근콘크리트 구조 건물에서 프리캐스트 벽패널을 사용한 새로운 내진보강 방법을 개발하는 것이다. 1개의 무 보강 보－기둥 실험체와 U형 PC 벽패널로 보강한 2개의 보강 보－기둥 실험체에 대한 정적 이력 하중실험을 진행하였다. 앵커접합 PR1-UA 실험체와 철판접합 PR1-UP 실험체는 무 보강 실험체보다 평균 2.8배(평균 591.8 kN)의 강도 증가를 보여 주었다. 최대 변위비도 1.4%에서 2.7%사이 값을 보여주었다. RC 골조 우측 상단에서 좌측방향으로 가력 할 때 우측에 있는 RC 기둥과 보강 PC 패널의 수직 요소는 완전 합성상태로 가정하였고, 좌측에 있는 RC 기둥과 PC 패널은 완전 비 합성 거동하는 것으로 가정하여 해석한 결과 전체적인 휨 거동은 실험 결과와 대체적으로 부합하는 것으로 판단되었다.

In this study, experimental research was carried out to evaluate and improve the seismic performance of reinforced concrete beam-column joint regions using strengthening materials (CFRP sheet, AFRP sheet, embedded CFRP rod) in existing reinforced concrete structure. Therefore it was constructed and tested seven specimens retrofitting the beam-column joint regions using such retrofitting materials. Specimens, designed by retrofitting the beam-column joint regions of existing reinforced concrete structure, were showed the stable failure mode and increase of load-carrying capacity due to the effect of crack control at the times of initial loading and confinement of retrofitting materials during testing. Specimens LBCJ-CRUS, designed by the retrofitting of CFRP Rod and CFRP Sheet in reinforecd beam-column joint regions were increased its maximum load carrying capacity by 1.54 times and its energy dissipation capacity by 2.36 times in comparison with standard specimen LBCJ for a displacement ductility of 4 and 7. And Specimens LBCJ-CS, LBCJ-AF series were increased its energy dissipation capacity each by 2.04~2.34, 1.63~3.02 times in comparison with standard specimen LBCJ for a displacement ductility of 7.

이 논문은 고강도 콘크리트를 사용한 철근콘크리트 외부 보-기둥 접합부의 실험결과를 보고한 것이다. 실험체의 주요 실험변수는 접합부 파괴모드, 콘크리트 압축강도, 철근의 정착 방법이다. 모든 실험체는 ACI 352R-02 기준에 바탕을 두어 J파괴와 BJ파괴가 되도록 계획하였다. 주철근은 90도 표준갈고리로 하거나 확대머리철근으로 하였다. 실험결과는 콘크리트 압축강도에 제한되는 현행 ACI 설계 기준식이 고강도 콘크리트를 사용한 보-기둥 접합부의 강도를 다소 과소평가하고 있음을 보여준다. 또한 확대머리철근을 가진 J파괴형 보-기둥 접합부의 강도는 표준갈고리를 가진 접합부보다 약 10% 이상 높게 평가되었다.

In this study, experimental research was carried out to improve and evaluate the seismic performance of reinforced exterior concrete beam-column joint strengthened with different anchorage length of embedded CFRP Rods in existing reinforced concrete building. Test result shows that retrofitting specimen(RBCJ-SR2T1, SR2T2) designed by the improvement of seismic performance of reinforced concrete beam-column joints, maximum load-carrying capacities were increased 2.24 ~ 2.24 times in comparison with the standard specimen(RBCJC). Also, retrofitting specimens showed stable hysteretic behavior compared to the standard specimen(RBCJC).

In this study it was developed FRP rod embedding FBG sensor, and compared the performance of sensor of the new rods and the existing strain gauge by applying the reinforced concrete beam-column joint in the same location. And it was found that new FRP rod was improved the structural performance and sufficiently sensing accuracy.

본 연구에서는 기존 철근콘크리트 건물의 보-기둥 접합부의 내진성능의 개선을 위해 보-기둥 접합부 영역을 FRP보강재(매입형 CFRP Rod, CFRP시트)를 사용하여 보강한 후 내진성능을 평가하였다. 총 6개의 실험체를 제작하고 실험을 수행하여 내진성능을 평가하였으며, 본 연구의 실험결과를 근거로 다음과 같은 결론을 얻었다. 기존 철근콘크리트 보-기둥 접합부의 접합부 영역을 보강한 결과, 초기 재하시 접합부 영역의 균열억제 효과와 재하 전 과정을 통하여 보강재의 구속효과로 인하여 균열억제 효과가 커서 안정적인 파괴형태 및 내력향상 효과를 나타내었다. 매입형 CFRP Rod와 CFRP시트를 활용한 RC 외부 보-기둥 접합부 실험체 RBCJ-SRC2는 표준실험체 RBCJ와 비교하여 변위연성4, 7에서 각각 최대 내력은 1.97배, 에너지소산능력은 2.08배 증가하였다. 또한, 실험체 RBCJ-SR시리즈와 비교하여 최대내력이 1.09~1.11배 증가하였다. 그리고 실험체 RBCJ-CS, RBCJ-SR시리즈, RBCJ-SRC2는 변위연성 5, 6에서 표준실험체 RBCJ 보다 에너지소산능력이 1.10~2.30배 증가하였다. 그리고 에너지소산능력은 변위연성 4에서 13.0~14.4% 증가하였다.

In this study, experimental research was carried out to improve and evaluate the seismic performance of reinforced concrete beam-column joint using Groove and Embedding FRP Rod and CFRP Sheet in existing reinforced concrete building. Test result shows that retrofitting specimen(RBCJ-SR2, SRCB2) designed by the improvement of seismic performance of reinforced concrete beam-column joints load-carrying capacities were increased 1.78 ~ 2.29 times in comparison with the standard specimen.

In this study, experimental research was carried out to improve and evaluate the seismic performance of reinforced concrete beam-column joint using Embedded Carbon Fiber Rod and Carbon Fiber Sheet in existing reinforced concrete building. Test result shows that retrofitting specimen(LBCJ-SP45, CS2, CRUS) designed by the improvement of seismic performance of reinforced concrete beam-column joints load-carrying capacities were increased 1.34 ~ 1.54 times in comparison with the standard specimen.