Eleven sorghun-sudangrass hybrids have been recommended as the government recommended forage cultivars, however, their forage performance and quality have mostly been tested at two regions, such as Suweon in the Middle Northwestern Coast Region and Sunghw

Sixteen cultivars of corn(Zea mays L.) hybrids have been recommended as the government recommended corn hybrids since 1984, however, their forage performances have been mostly tested at two locations, such as Suweon and Sunghwan in the Middle parts of Kor

Low toxic concentrated oil dispersant using n-Paraffin and Di(ethylene glycol)mono butylether mixed solvent was prepared, and tested by oil dispersant performance test method, and oil dispersant efficiency was measured using vertical shaking method to 3 kinds of Crude oil, Bunker oil and W/O emulsions with different physical properties by appling the prepared dispersant. Although toxicity test was performed with Flat fish and Rock fish by appling the mixed oils emulsified using prepared oil dispersant, couldn't find the toxicity to them. Concentrated oil dispersant prepared has a good dispersion efficiency of 97.2% after 0.5min settling time and 28.3% after 10min settling time to Bunker B oil with 10% water solution. Especially, the concentrated oil dispersant showing the low toxicity to Oryzias Latipes(24hr, TLm) was 54,000 ppm and to Brine Shrimp Artemia(24hr, TLm) was 51,000ppm, and also, it was completely biodegradated to 99.1% after 7~8days.

이규화몰리브덴 고온발열체의 제조공정을 개발하였다. 원료분말은 상용 MoSi2분말이었으며 Bentonite, Si3N4, B, ThO2를 각각 가소제와 첨가제로 사용하였다. 이들은 진공압출, 소결, 단자부 기계가공, U자형 성형, 용접 등의 과정을 거쳐 U자형 발열체로 제조되었다. 사용제품의 분석결과 최근 사용온도가 크게 증가된 것으로 알려진 1900˚C용 발열체는 다량(33wt%)의 W이 Mo을 치환하고 있는 것으로 나타났다. 발열체의 전기비저항은 겉보기 밀도가 증가함에 따라 급격하게 감소하는 경향을 보였으며 첨가물들의 영향은 미미하였다. 1400-1600˚C에서 용접한 경우 용접면에서의 전기비저항은 비용접부보다 낮았으며 용접온도가 증사함에 따라 감소하였다. 발열시험결과 제조된 발열체는 표면온도가 1700˚C이하에서는 문제가 없었으며 1750˚C 이상의 온도에서는 원형의 융기가 표면에 발생하면서 급속하게 파괴되었다. 이 융기는 X-선 회절분석결과 SiO로 밝혀졌으며 따라서 발열체의 파괴는 MoSi2/SiO2계면에서의 Si(in MoSi2) + SiO2=2SiO(g)반응에 으해 일어나는 것으로 판단된다.

A field experiment was conducted at the forage experimental plots, Seoul National University, Suweon h m 1995 to 1996 to determine the effect of legume residues as a N source and N fertilizer on corn (Zea mays L.) silage yield, N uptake, and availability

전자빔 용해법에 의해 고순도 티타늄잉고트 및 버튼시편을 제조하였다. 이들 중 18개의 금속불순물을 GDMS(Glow Discharge Mass Spectrometry)로 그리고 탄소, 질소, 산소의 함량을 고온연소법으로 측정한 후 이들과 전기비저항, 경도와의 관계를 조사하였다. 99%와 99.6%스폰지를 용해한 경우 대부분의금속불순물들이 대폭 감소하는 큰 휘발 정련효과가 나타났으며 비금속불순물들의 경우는 장비의 진공상태에 따라 큰 영향을 받으며 정련효과를 기대할 수 없었다. 금속 불순물중 철은 가장 제거하기 어려운 원소로 밝혀졌으며 이는 원료 스폰기중에서 철이 주불순물이기 때문이며 추가적인 예비정련이 필요한 것으로 나타났다. 상온 및 액체질소온도에서의 전기비저항은 가스불순물의 량이 증가함에 따라 직선적으로 증가하였으며 이들의 저항비(ρRT /ρN2)는 가스불순물의 총량이 1,000ppm이하의 경우 불순물량이 감소함에 따라 급격하게 저하하였으며 이 이상인 경우 완만하게 감소하였다. 이들의 경도는 가스불순물의 량이 증가하였으며 산소당량의 평방근에 비례하는 것으로 나타났다.다.

An A-B-A-C single subject research design was used to assess the effectiveness of transcutaneous electrical nerve stimulation(TENS) and inhibitive techniques on spasticity in a 10-year-old girl with cerebral palsy. Stimulation electrodes were placed over the sural nerve of the right leg. The standard method of cutaneous stimulation, TENS with impulse frequency of 100 Hz, was applied. Inhibitive techniques including stretch, antagonist contraction, and weight bearing were used. The tonus of the leg muscle was measured by means of a surface-EMG biofeedback unit. Visual analysis of data indicate that the child showed clinically significant reduction of spasticity in passive ankle movement following 30 minutes of TENS and inhibitive techniques application, respectively. The effect of TENS on spasticity inhibition was similar to that of inhibitive techniques. This result suggests that for this child with cerebral palsy, the application of TENS to the sural nerve may induce short-term post-stimulation inhibitory effects on the spasticity of cerebral palsy. Replication of this study with a more complex single-subject design involving more subjects is recommended to confirm this result.

아크용해로와 진공유도로를 사용하여 니켈-수소 전지의 음극용으로 주목받고 있는 AB2 타입의 ZrV xMn1-xNi1.0, ZrVxMn0.8-xNi1.2, ZrVxMn0.6-xNi1.4합금을 용해하였다. 이들 합금은 용해한 상태에서 C14과 C15의 혼합상을 갖는 것으로 나타났으며 합금조성 및 열처리에 따라 혼합상분율이 크게 변화하였다. 이들의 결정상 및 상분율은 합금원소들의 평균원자반경비(rA/r/sub B)에 따라 결정되는 것으로 밝혀졌으며 특히 열처리한 합금의 경우에는 평균원자반경비가 1.254일때를 경계로 하여 두 상의 명확간 안정구역이 설정되었다. 가압한 분위기에서 아크용해한 경우 합금성분의 손실은 미미하였으나 진공유도로를 사용하여 용해한 경우 Mn이 다량 휘발감소하여 조성이 크게 변화하였다.

This experiment was conducted in 1992 and 1993 at the forage experimental field, College of Agriculture and Life Sciences, Seoul National University, Suweon to determine timing of rye(Secde cemde L.) harvest and residue chemical treatment prior to tillage

This experiment was conducted at the forage experimental field, College of Agriculture and Life Sciences, Seoul National University, Suweon in 1992 and 1993 to investigate the effects of tillage method-conventional and rotary-till, rye (Secde cereale L.)

은 튜브에 장입되기 전의 초기 분말의 입자 크기가 Ag/Bi-2223초전도 선재의 미세구조와 상전이, 임계 전류 밀도등에 미치는 영향에 대해 고찰하였다. 분말의 입자 크기는 하소 분말을 볼밀을 이용하여 0-48 시간 동안 분쇄하여 조절하였다. 열처리 후 최종 초전도 선재의 전기적 성질은 초기 분말의 입자 크기에 영향을 받는 것으로 나타났으며 분말의 분쇄에 의한 반응성의 증가에 의해 열처리시 2223 상으로의 상전이가 빠르게 일어났고 이차상의 크기와 분율이 감소된 미세구조를 얻을 수 있었다. 그러나 과다한 분쇄에 의한 반응성의 증가에 의해 열처리시 2223상으로의 상전이가 빠르게 일어났고 이차상의 크기와 분율이 감소된 미세구조를 얻을 수 있었다. 그러나 과다한 분쇄는 분말의 비정질화를 유발하여 2223 상으로의 전이를 방해함으로써 선재의 임계 전류 밀도를 감소시키는 결과를 나타내었다.

This experiment was conducted from 1991 to 1993 at the forage experimental field, College of Agriculture and Life Sciences, SNU, Suweon to investigate the effects of previous crop residues on growth and yield of succeeding corn(2ea mays L.) and also to de

니켈-수소화물전지의 음극재료로서 주목을 받고 있는 다원계 Zr기 Laves 합금의 조성에 따른 결정구조, 방전특성등을 조사하였다. 전극은 아크 용해한 합금을 분쇄한 분말과 PVA를 다공성니켈 foam에 충진하여 제작하였고 충방전시험은 6M KOH 용액중에서 수행하였다. 대상 합금은 ZrNi2를 기본조성으로 하여 이중 Ni의 일부를 V, Mn, Cr, Mo 또는 W로 치환한 삼원계 및 사원계 합금이었다. 이들 합금의 충방전 실험결과 ZrV0.5Mn0.5Ni1.0의 경우가 260 mAh/g로 가장 높은 방전용량을 나타내었다. 이 합금의 방전용량은 방전전류밀도의 영향을 크게 받았으며 10 mA/g과 200mA/g의 방전전류에서 각각 300mAh/g와 150mAh/g이었다. 이 합금을 1100˚C에서 열처리한 경우 저율방전시에는 방전용량의 변화가 거의 없었으나 수소의 확산이 율속이 될 것으로 생각되는 고율 방잔시에서는 방전용량이 현저하게 감소하였다. 이러한 현상은 열처리에 의해 수소의확산을 용이하게 해주는 격자결함이 감소하기 때문이 아닌가 생각된다.