A powder mixture of 70 wt% Al2O3 and 30 wt% hydroxyapatite (HA) is sintered at 1300 ℃ or 1350 ℃ for 2 h at normal pressure. An MgF2-added composition to make HA into fluorapatite (FA) is also prepared for comparison. The samples without MgF2 show α & β-tricalcium phosphates (TCPs) and Al2O3 phases with no HA at either of the sintering temperatures. In the case of 1,350 ℃, a CaAl4O7 phase is also found. Densification values are 69 and 78 %, and strengths are 156 and 104MPa for 1,300 and 1,350 ℃, respectively. Because the decomposition of HA produces a H2O vapor, fewer large pores of 5-6 μm form at 1,300 ℃. The MgF2-added samples show FA and Al2O3 phases with no TCP. Densification values are 79 and 87%, and strengths are 104 and 143 MPa for 1,300 and 1,350 ℃, respectively. No large pores are observed, and the grain size of FA (1-2 μm) is bigger than that of TCP (0.7 μm ≥) in the samples without MgF2. The resulting TCP/Al2O3 and FA/Al2O3 composites fabricated in situ exhibit strengths 6-10 times higher than monolithic TCP and HA.

β-Tricalcium phosphate (TCP) was added to Al2O3 to make a biomaterial with good mechanical properties. Using a TCP powder synthesized by a polymer complexation method, Al2O3 composites containing 30 wt% TCP were fabricated and characterized for densification, phase, microstructure, strength, and fracture toughness. With optimizing the powder preparation conditions, a high densification of 97 % was obtained by sintering at 1350 ℃ for 2 h. No reaction between the two components occurred and there was no transition to α-TCP. TCP grains with a size of 2-4 μm were well surrounded by Al2O3 grains with a size of 1 μm or less. Strength 61(Brazilian) or 187(3-p MOR) MPa, and fracture toughness 1.7 (notched beam) or 2.5 (indentation) MPa·m1/2 were obtained, which are large improvements over the strength of TCP/Al2O3 composites and toughness of TCP and hydroxyapatite in previous studies.

산업화를 위한 지구자 및 12가지 식물성 원료 추출물의 생리학적 효과를 평가하기 위하여, 만성 에탄 올을 투여한 마우스 혈청 내에서의 생리학적 지표 및 간과 뇌 조직 내에서의 산화적 스트레스에 대한 보호효과를 확인하였다. 에탄올을 투여한 마우스의 혈당은 정상 대조군 그룹(NG)과 에탄올 투여 그룹 (EG)에서 각각 119.43mg/dL, 305.25mg/dL로 나타났고, 에탄올과 혼합 추출물을 동시에 투여한 그룹 (100, 200mg/kg body weight + 25% ethanol 5g/kg body weight, ME100, ME200)에서 각각 272.76mg/dL, 234.60mg/dL로 감소하였다. 혈중 에탄올 함량은 EG에서 4.08mg/dL를 나타내었고 ME100, 200에서 각각 3.85mg/dL, 3.08mg/dL로 감소하였으며, 혈중 아세트알데하이드 함량은 18.72mg/dL에서 각각 15.76mg/dL, 15.16mg/dL로 감소하였다. 또한 ME100, ME200은 혈청 내의 생 리학적 지표에서 간 독성 지표인 glutamine pyruvic transaminase(GPT), glutamic oxaloacetic transaminase(GOT)와 신장 독성 지표인 blood urea nitrogen(BUN), creatine(CRE), 혈중 total cholesterol(TCHO), triglyceride(TG)의 함량이 유의하게 감소하였다. 뇌 조직에서 에탄올에 의해 acetylcholinesterase(AChE)가 EG(116.10%)에서 NG(100.00%)와 비교하였을 때 증가된 활성을 나타냈 으나, ME에서 각각 109.00%와 108.47%로 유의적으로 감소하였다. ME에서 EG에 비해 간과 뇌 조직에 서 superoxide dismutase(SOD)의 함량이 증가하였고, oxidized glutathione(GSH)/total GSH 비율과 malondialdehyde(MDA)의 함량이 감소하였다. 이러한 결과들을 통해 지구자를 포함한 혼합 추출물은 간, 뇌 조직 및 혈액 등에서 만성 에탄올 섭취에 의해 유발된 산화적 스트레스를 효과적으로 보호할 수 있는 제품으로의 개발이 가능할 것으로 판단된다.

본 연구에서는 간척지 풍 환경 특성에 따른 온실의 환 기효율 분석 연구에 대한 기초연구로서 단동 양지붕형온실을 대상으로 간척지 풍 환경을 적용한 풍동실험 및 PIV 실험을 수행하여 풍속, 환기방식에 다른 온실 내부 공기유동 분석을 수행하였다. 실질적인 간척지 풍환경 적용을 위하여 ESDU 프로그램을 활용하여 풍속 및 난류 프로파일을 설계하여 풍동실험에 적용하였으며 구현 결과 ESDU 대비 5%의 오차 및 상관계수 0.96이 도출 되었으며 적절한 오차범위라 판단하여 이를 기준으로 실험을 진행하였다. 벡터장, 컨투어장을 통한 분석 결과, 풍상측에서 유입 되는 공기가 온실 하부로 주기류층을 형성하고 온실 상부로는 주풍방향과 반대방향으로 다소 약한 기류를 형성 하는 것으로 측정되었다. 이는 환기 시, 온실 하부영역 이 가장 환기가 원활한 위치이며 후류가 형성되는 상부 영역은 저속의 순환구역으로 온실 내부에 있어 환기에 가장 취약한 위치임을 알 수 있었다. 또한 외부풍속 대비 온실 유입구 유속의 경우 상이하게 나타난 바, 이는 차후 환기량이나 환기효율의 산정에 있어 보다 실질적인 수치가 될 것으로 사료된다. 온실 내부 중앙부 기준 수직 높이에 대한 높이별 유속 수치 도출 및 분석결과, 풍속의 증가율에 비례하여 내부 유속 분포 수치 또한 비례해서 증가하는 것을 알 수 있었다. 환기방식에 따른 내부 유속 저감 비율은 측창 환기, 측창-천창 환기의 경우 각각 약 40%, 30%로 나타났으며 측창-천창 환기조건에서는 천창을 추가적으로 개방 함으로써 공기의 유입되는 면적이 증감함에 따라 온실을 기준으로 발생되는 부압이 감소하여 오히려 측창 환기조 건보다 더 큰 유속 수치가 도출된 것으로 사료된다. 이는 차후 질량교체 환기량, 추적가스 감쇠법 등의 방법을 통한 환기량 산정에 있어 환기방식에 따른 환기량의 변화양상에 대한 분석을 추가적으로 수행할 필요성을 지니는 자료로 판단된다. 본 연구를 통하여 도출된 결과를 바탕으로 전산유체 역학(Computational Fluid Dynamics, CFD) 시뮬레이션에 접목하여 앞서 도출된 정량적인 높이별 유속 수치 및 정성적 유동분포를 기준으로 검증 및 정확도 향상을 통한 환기분석 모델을 설계하고자 하였다. 온실 내부의 공기유동에 따른 보다 실질적인 환기 척도를 도출하여 다양한 온실형태별, 환경조건별, 환기방식별 환기경향 분석 및 예측이 가능할 것으로 전망되며 시뮬레이션을 활용한 온실 체적 전체 및 구역별 환기량을 예측하여 환기 취약 구역을 파악, 보완할 수 있을 것으로 기대된다.

Ultra high performance concrete which has recently been studied was developed to complement the brittle behaviour and dynamic uppermost limit of high strength concrete. Fiber reinforced concrete which mixed steel fiber is receiving attention as an alternative about this and is being developed to complement the disadvantages of high strength concrete including lower toughness coefficients and crack resistance and spalling in fires. Review about fiber reinforced ultra high strength concrete that this study tries to treat includes reduction of self shrinkage generated by high cement content per unit volume of concrete, evaluation of compression and tension strength to lower internal and external spalling resistance and fragility factors of member of framework, and flow characteristics of concrete which doesn't harden according to steel fiber amounts and used materials. As the result, the more fiber reinforcement increases, the more compression and tensile strength increase and deformation control of cement matrix and improvement of energy absorption ability showed the great effect in shrinkage reduction.

In this study, expedite curing period at curing temperature being 40, 60, 80℃ similar to strength of standard 28days curing temperature to confirm methods and applicability of early estimation of strength by warm water curing. Also, checked the effect related to different conditions such as using various kinds of material, differentiating quantity of material, with or without fiber mixing at same rate of water-bonding material. Existing method proposed by KS and JIS to estimate strength of 28 days standard curing temperature curing for 7days at 40℃ is not relevant because it takes so long to estimate strength. Already known method of estimating strength of 28days standard curing temperature curing for 3days in 60℃ warm water, too, is not relevant to apply 3day cycle of super high-rise. It also had the problem which didn’t consider fiber mixed concrete. According to the result of experiment, traits and rate of strength revelation were different relating to the kinds and quantity of bonding material. Strength value of mix without fiber was higher than that of mix with fiber, but without any relation to that, over 96% of similar confidence level with strength of 28 days standard curing temperature was shown in 7 days at 40℃, 3 days at 60℃, 2days at 80℃. Confidence level of estimation method of 2 days at 80℃ was similar to those of estimation methods of 4 days at 40℃, 3 days at 60℃, so it(2 days at 80℃) is regarded as the most relevant method because it’s possible to estimate strength fastly. As a result it can be said that early quality control of recently increasing super high-rise may be possible through estimation method of 2 days at 80℃.

This paper has fabricated insulation gang-form adhering general gang-form to the polyisocyanurate board and analyzed type of members, temperature record by locations and strength development after placing the concrete, in order to ensure efficient concrete quality under cold weather. According to our test, we can see that general gang-form member with curing under the same conditions as the actual field has a trend of constantly decreasing concrete temperature regardless to surface or central area due to rapid outdoor air temperature reduction, while in the case of insulation gang-from I and II, temperature increased up to around 25℃ after 12 hours under rapid outdoor air temperature change and temperature distribution did not appear large separation according to hydration reaction measurement locations. In addition, results of measurement for temperature records on weak insulation area by types of gang-forms showed that the temperature record distribution on the form tie surface and horizontal bar surface of angle bar has generally similar trend as the temperature records on the surface of the insulation gang-form, while corner area of the insulation gang-form did not have large insulation effect. It is determined that it requires additional curing measure for the weak corner area of the insulation gang-form in the future.

In this study, the drying shrinkage of concrete used for the reduction of expansive additive and shrinkage reducing agent committed to the concrete Mixing characteristics, compressive strength and drying shrinkage of examining my new honhwajaeryoin elements by putting in concrete Their characteristics were compared and analyzed. Experiments, SP was fixed jeryangeul equally expansive additive and shrinkage reducing agent in the formulation of the Injection rate increased with increasing fluidity, shrinkage reducing air flow rates increase the amount of air even if the input Increases with, and if the expansion of re-injection rates increase rather than decrease was found that the volume of air. I committed to the elements of the concrete, but an increase in inputs even if the air content of concrete or no liquidity Were confirmed to have no effect. In addition, the compressive strength test Shrinkage Reducing the dosage increases, Tended strength falls, inflation 5.0% of material inputs in the formulation was found to be the highest. Element material Concrete with Shrinkage Reducing committed a similar compressive strength falls with increasing dosage tended Unlike the small degree of shrinkage reducing agent was affected. Shrinkage characteristics include all three admixture With increasing dosage can reduce the drying shrinkage was observed that, if the shrinkage reducing agent, of the elements and almost Reducing the level of contraction was found to be. Therefore, the element first, if you commit to concrete admixtures to Characteristics of the concrete mix does not affect the lapse rate contract that can be used as a highly admixture is judged to be here.

This study is analyzing a member kind after placing concrete, the location-based temperature record, and the strength development, by making insulation gang-form with application of polyurethane form to general gang-form for securing efficient concrete quality in the condition of cold weather. According to our experimental results, the member of general gang-form with curing in the same condition as the actual field didn’t drop to under 3˚C until before 24 hours in the early part, but fell to under 0˚c from 36 hours later because a large rise in temperature caused by hydration reaction didn't occur. On the other hand, in case of insulation gang-form, the temperature on the surface and the central part didn't go down to under 3˚C before 12 hours in the early part and didn't fall to under it even until 72 hours after it while the peak temperature went up to 12˚C. Thus, it could be known to definitely have excellent insulation effect compared to space heating curing, which is generally performed on the spot. In comparison with space heating curing whose error in curing temperature is big every field, it is judged to likely have great effect on improvement in concrete quality given the work construction in cold weather and on early demolding in a cast during winter.

In case of general concrete, autogenous shrinkage is about 10% of the drying shrinkage. Therefore it was not considered significant to be a subject matter about managing the crack control and design. It was reported that cracks can be generated from the autogenous shrinkage. Because of the low W/B rate and the high unit binder of the high strength concrete. In this study, autogenous shrinkage and drying shrinkage are examined which is the main reason of the cracks of the high strength concrete based on the previous studies. Comparing the data from this study and previous studies, we developed the shrinkage reduced concrete using shrinkage reducing agent. The purpose of this study is to provide the data for reducing and managing the column shortening of the high strength concrete structures.

사용중인 중화학 설비의 재료물성의 경년열화적 특성을 평가하기 위하여 기존 실험법의 인장시험편이나 충격시험편을 채취하기는 실제적으로 불가능하다. 인장강도등 인장특성과 비교한 결과 인장강도, 연신율, 항복강도, 종탄성계수와 소형펀치실험의 각 특성과 선형적 관계를 얻을 수 있었다. 또한 경년열화도를 평가하는 두구인 파면천이온도(FATT)와 비교하기 위하여 저온 소형펀치실험을 실시한 결과 충격실험을 통하여 구한 FATT온도와 소형펀치실험의 천이온도 ( Tsp )와 일정한 관계가 있음이 밝혀져 사용재의 열화도를 평가할 수 있다.

항해 중인 함정은 늘 충돌 가능성이 존재하지만 충돌회피를 위한 명확한 기동지침은 없고 함교 당직사관의 직관적 판단에 의존하 는 경향이 있다. 본 연구에서는 항해 중인 함정이 방위끌림이 없는 장애물을 조우하는 상황에서 함교 당직사관을 대상으로 언제 어떻게 충돌 을 회피하는지 설문조사를 실시하였다. 설문 결과를 활용하여 방위끌림이 없는 장애물 조우 상황, 주·야간 충돌 회피 방법을 분석하였다. 조함이 까다로운 지역은 평택, 목포 순이었고, 주로 협수로 내에서 발생하였다. 빈도는 4시간 항해 시 평균 1회 정도로 나타났으며, 1:1 조우 상황보다 다수 선박 조우가 많았다. 충돌침로 확인 시 전자해도보다 육안 확인 결과를 더 신뢰하였고, 충돌회피 고려 요소로 최단 접근거리, 최단 접근시간을 우선시하였다. 피항의무선과 침로유지선의 충돌회피 기동상 특별한 차이는 없었지만 주·야간 시 최단 접근거리의 차이는 존재 했다. 충돌회피 시대부분의 항해사들은 변침·변속을 함께 사용하는 것을 선호하며 타각 10~15°, 변속 ±5knots, 변침침로는 타함 함미 정방향에서 함미 가중치를 두었다. 이러한 결과들은 승조원들에게 부임 함정의 충돌 회피 기준을 제공하는데 도움이 될 것이며 나아가 AI, 빅데이터 기반의 무인함정 충돌회피 알고리즘 개발에도 적용될 것이다.

시멘트 산업은 탄소배출 감축을 위한 주요 산업분야로 고려되고 있으며, 콘크리트 분야에서 시멘트 사용량 저감을 위한 노력이 진행되고 있다. 이에 대한 노력의 일환으로 시멘트의 일부를 대체하여 사용할 수 있는 산업부산물을 다량으로 활용하기 위한 연구가 진행되고 있다. 산업부산물을 사용한 콘크리트는 내구성, 친환경성 및 경제성 등의 장점을 가지고 있으나, 응결시간 지연, 초기강도 저하 등의 문제점이 있다. 따라서 이 연구에서는 시멘트의 사용량을 줄이고 산업부산물인 플라이애시를 치환하여 사용하면서도 초기강도가 저하되는 문제점을 해결하는 것을 목표로 하였다. 이에 따라, 먼저 고분말도 시멘트 사용에 의한 수화반응 촉진으로 양생온도에 관계없이 모든 재령에서 강도가 증진되는 것을 확인하였다. 이어서 고분말도 시멘트에 플라이애시를 치환하여 강도발현 특성을 검토한 결과, 초기 재령에서도 보통 포틀랜드 시멘트와 비교하여 동등 이상의 강도 발현이 가능하였다. 또한, 플라이애시를 30%까지 치환하여도 수직․수평부재 거푸집 해체 시기를 단축할 수 있는 것을 확인하였다.

The purpose of this study is to corroborate hydration and porosity of cement paste by the low water-cement ratio specimen. The test results show that calcium hydroxide was increased as the moisture was supplied from the outside and the porosity was lowered with a rapid manner.

In this study, hydration heat, autogenous shrinkage and compressive strength of the specimens has been verified with moisture supply on the hardened cement paste depending upon the difference in moisture condition of the fine aggregates. The result showed that, autogenous shrinkage was significantly reduced and also the compressive strength was improved due to the continuous moisture supply regarding on fine aggregates.