Using as sintering additives and Si as a raw powder, the continuously porous in-situ bodies were fabricated by multi-pass extrusion process and their microstructures were investigated depending on the addition of carbon (0-9wt%) in the mixture powder. The introduction of fibers observed in the unidirectional continuous pores as well as in the pore-frame regions of the nitrided bodies can be an effective method in increasing the filtration efficiency. In the case of no carbon addition, the network type fibers with high aspect ratio appeared in the continuous pores with diameters of 150-200 nm. However, in the case of 9wt% C addition, the fibers were found without any network type and had diameters of 200-250 nm.

Processing techniques for producing microcellular silicon carbide, mullite, and cordierite ceramics have been developed by a reaction method that incorporates a polysiloxane and reactive fillers. The techniques developed in this study offer substantial flexibility for producing microcellular ceramics whereby cell size, cell density, degree of interconnectivity, composition, and porosity can all be effectively controlled. It is demonstrated that the adjustment of filler composition enables the possibility of tailoring the composition and properties of the microcellular ceramics. The present results suggest that the proposed novel processing techniques are suitable for the manufacture of microcellular ceramics with high morphological uniformity.