The polymer-ceramic hybrid, known as 'ceramer', was synthesized by a sol-gel process by incorporating different amount of alkoxide as source of silicon in resorcinol-formaldehyde in presence of basic catalyst to get different percentage of silicon in ultimate carbonized composites. FTIR of the ceramer confirms that it is a network of Si-O-Si, Si-O-CH2 and Si-OH type groups linked with benzene ring. Different amount of silicon in the ceramer exhibits varying temperature of thermal stability and lower coefficient of thermal expansion as compared to pure resorcinol-formaldehyde resin. The lower value of CTE in ceramer is due to existence of silica and resorcinol -formaldehyde in co-continuous phase. Unidirectional composites prepared with ceramer matrix and high-strength carbon fibers show lower value of flexural strength at polymer stage as compared to those prepared with resorcinol-formaldehyde resin. However, after heat treatment to 1450℃, the ceramer matrix composites show large improvement in the mechanical properties, i.e. with 7% silicon in the ceramer, the flexural strength is enhanced by 100% and flexural modulus value by 40% as compared to that of pure resorcinol-formaldehyde resin matrix composites.

본 연구는 당근과 양파에서 발아력 증진에 미치는 osmotic priming과 SMP효과를 비교하기 위해 수행되었다. Osmotic priming과 SMP 처리과정중 작물별 수분흡수율은 처리 1시간 후 급속한 수분흡수가 이루어졌고, 두 작물 모두 osmotic priming이 SMP보다 수분흡수 속도가 빨랐다. 이러한 경향은 처리 4시간까지 유지되었다. 처리최종일의 수분흡수율은 당근과 양파에서 osmotic priming이 SMP보다 2%높았다. Osmotic priming과 SMP 처리는 두 작물 모두 발아율을 향상시키지 못했지만 T50 및 MDG는 단축되어 조기발아 하였으며, 이러한 경향은 저온인 15℃에서 더욱 현저하였다. Osmotic priming과 SMP 처리 후 초기함수율로 재건조하면 당근에서는 발아속도에 큰 차이가 없었으나, 양파에서는 표면건조에 비해 발아속도가 지연되었다. Osmotic priming과 SMP 상호처리간 발아력을 비교한 결과 두 작물 모두 SMP 처리가 osmotic priming보다 발아촉진에 효과적이었다. 당근과 양파종자를 osmotic priming과 SMP 처리하면 묘출현율도 향상되었고, 묘출현에 소요되는 일수를 단축시켜 신속한 묘출현을 유도하였다. 그러나 묘출현에 이은 유묘의 초기생육에는 통계적인 유의성은 인정되지는 않았으나 osmotic priming과 SMP 처리된 종자는 무처리에 비해 향상되었다.

본 연구의 목적은 축대칭 하중을 받는 원통형 펄의 엄밀해를 구하는데 있어서, 간략하면서도 엄밀한 해를 구하는 방법을 제시하고자 하는데 있다. 이는 임의 형상의 구조해석을 위한 강력한 도구이긴 하지만 여전히 근사해석인 유한요소법에 대체될 수 있을 것이다. 이를 위해 본 논문은 반복법의 일종인 인도행렬법을 이용한 절점역계의 분배방식을 사용하였다. 원통형 쉘의 분배와 전달인자는 한성지반상의 보에 대한 미분방정식으로부터 구해진 것이다. 이러한 방법을 축대칭 집중하중과 정수압을 받는 원통형 쉘에 각각 적용해 보았고, 그 결과는 BEF 이론해와 비교할 때 만족할 만 하였다.

본 연구에서는 자유진동, 조화하중, 그리고 백색잡음실험을 통해 얻어지는 진동수, 감쇠비, 모드 벡타와 같은 구조물의 모드정보를 이용하여 강성행렬과 감쇠행렬을 구성하였다. 입력신호로는 지진하중을 모사 하는 바닥판 가속도를 이용하였고, 출력신호는 각층 절대가속도를 사용하였다. 각각의 실험에서 얻어지는 구조물 모드정보의 제한조건과 그에 따른 시스템 식별 모델들의 특성을 비교하였다. 본 연구의 결과는 진동대 실험을 위한 기초적인 동적 실험 및 분석에 이용될 수 있을 것으로 판단된다.

Growth behavior of two different types of grains, faceted and rounded, in a liquid matrix has been studied in the (75WC-25TiCN)-30Co system. Powder samples were sintered above the eutectic temperature for various times under a carbon saturated condition. (Ti,W)(C,N) grains with a rounded shape and WC grains with a faceted shape coexisted in the same Co based liquid. With increasing sintering time, the average size of (Ti.W)(C,N) grains increased continuously and very large WC grains appeared. The growth of rounded (Ti,W)(C,N) grains followed a cubic law, =kt, where r is the average size of the grains, the initial average size, k the proportionality constant and t the sintering time. indicating a diffusion-controlled growth. On the other hand, the growth of the faceted WC grains resulted in a bimodal grain size distribution, showing an abnormal grain growth. These observations show that the growth behavior of different types of grains is governed by their shape, faceted or rounded, even in the same liquid matrix.

A new display device is required, which has concepts of flatness and slimness. FED can be one of the solutions. When we use flat panel, we can save the raw material and reduce the production time by eliminating the printing process, drying process, and wa

A liquid chromatographic method, using matrix solid-phase dispersion (MSPD) is developed for the extraction of residual furazolidone in chicken eggs. Blank or fortified egg samples (0.5 g) were blended with Octadecylsilyl (Bulk C,,, 40 pm, 18%. load, endcapped. 2 g) derivatized silica. After homogenization, C,,/egg and Na2S0, matrix were transferred to a column made of 10 ml glass synnge and filter paper and compressed 4.0-4.5 ml volume. The column was washed with 8 ml of hexane and dried under N, gas. Furazolidone was eluted with acetonitrile (8 ml) under gravity. The eluate containing furazolidone was free from interfering compounds when analyzed by HPLC with UV detection (365 nm, photodiode array). Calibration curves were linear (r = 0.99985) and inter- (1.47%) and intra-assay (5.29%) variabilities for the concentration range examined (7.8-497 ngig of eggs, 20 pl injection volume) were indicative of an acceptable methodology for the analysis of furazolidone. Average recovery of furazolidone added to egg was 96.2%. The limit of detection for the proposed method was 1 ng/g for furazolidone. The method using MSPD is proposed as an alternative assay to the classical method which involves the use of large volumes of a harmful solvent and requires a long tedious separation and clean-up processes prior to its determination.

포유동물의 암컷 생식기관에 존재하는 다양한 종류의 matrix metallo-proteinase (MMP)는 난소와 자궁의 구성성분의 주기적인 변화를 조절하며 이중 난소의 MMP는 난포의 성장과 배란 그리고 퇴화 동안 조직재구성에 매우 중요한 역할을 한다고 알려져 있다. 본 실험에서는 근래에 새로 발견된 사람의 난포액에 존재하는 분자량 약 110kDa인 MMP-2 isoform GA110을 동정하고 자 하였다. 난포액으로부터 GA110 단백질을 분리하기 위하여 난포액에 5mM ethylenediaminetetraacetic acid(EDTA)를 처리한 후 DEAE Sepharose Fast Flow를 이용한 chromatography를 시행하였다. 그 결과, 난포액 단백질들은 0.2M NaCl 의 분획에서 GA110 활성을 나타내었고 anti-human MMP-2 antibody에 대한 면역반응도 뚜렷이 나타났다. DEAE Sepharose Fast Flow에서 얻은 분획 중 GA110의 활성과 면역반응을 모두 나타내는 분획만을 모아 Gelatin Sepharose 4B affinity chromatography로 다시 분리하였다 분리한 결과 resin에 흡착된 단백질 (eluate) 분획들에서 매우 뚜렷한 GA110 gelatinase 활성을 나타내었으며 면역반응 또한 관찰되었다. 이 분획들의 단백질을 농축한 후 zymography를 시행하여 나타난 GA110 단백질 band를 잘라 내었으며 이로부터 단백질을 electroelution하여 농축한 후 reducing agent인 2-mercaptoethanol를 처리하였다. 이를 전기영동 후 MMP-2 (propeptide region) antibody를 사용하여 immunoblotting 한 결과 70-72kDa의 단백질만이 면역반응을 나타내었다. 마지막으로 위와 같이 준비된 70-72kDa 단백질의 아미노산 서열을 Edman degradation 방법으로 분석하였다. 그 결과 이 단백질의 N 말단의 10개의 아미노산 배열 순서가 알려진 사람의 proMMP-2의 전체 배열순서 중 propetide domain의 N 말단에서부터 다섯 번째에서 시작하여 10개의 아미노산의 서열과 정확하게 일치하였다. 위 결과들로 미루어 사람의 난포액에 존재하는 MMP-2의 새로운 isoform인 GA110은 70-72kDa의 ProMMP-2가 disulfide bond를 통해 homodimer 구조를 이루고 있는 것으로 여겨진다.

A new display device development using CRT and CDT technology is required, which has concepts of flatness and slimness. Screen printing technology can be one of the solutions. In this case, good panel flatness is the precondition. Therefor, we did process capability analysis of panel flatness and regression analysis between panel flatness and BM(black matrix) position by experiments.

탄성지반 위에 놓인 보-기둥 요소의 총포텐셜 에너지로부터 변분원리를 적용하여 지배방정식과 힘-변위 관계식을 유도하였다. 4계 상미분방정식 형태의 지배방정식을 4개의 변위 파라메타를 도입하여 1계 연립미분방정식 형태의 선형 고유치 문제로 전환하고, 힘-변위 관계식을 적용하여 엄밀한 정적, 동적 요소강성행렬을 유도하였다. 직접강성법을 이용하여 구조물 강성행렬을 구하고, 2차원 보-기둥구조의 엄밀한 좌굴하중과 고유진동수를 구하고, 결과를 유한요소해와 비교함으로써 본 연구의 타당성을 검증하였다. 이러한 엄밀한 해석방법은 Hermitian 다항식을 형상함수로 도입하여 요소의 강성행렬을 산정하는 유한요소법과 비교할 때, 요소의 수를 대폭 줄일 수 있는 장점이 있다.

본 연구에서는 횡강성 영향행렬을 이용한 최적설계의 효율성을 높이기 위해 각 층에서 층별 영향행렬을 구하는 계산모듈을 개발하고 가상하중법에 의한 민감도 해석을 수행한다. 아울러 최적설계결과를 실무에 직접 적용할 수 있도록 층별 횡강성 증대계수에 근거하여 횡하중 저항시스템의 부재단면크기를 재산정하는 방안을 강구한다. 이를 위해 단면 재산정 방안은 연속형과 이산형 단면설계법으로 나누어 고려되며, 단면특성과 단면치수와의 관계가 설정된다. 특히 강도구속조건에 대한 초기설계가 먼저 수행된 후 횡변위 구속조건을 초과하는 횡변위를 제어하는데 있어서 횡하중 저항 시스템만이 저항하도록 설계한다. 본 연구에서 제안된 고층건물의 횡변위 제어 및 단면 재산정 방안을 검토하기 위해 두 가지 형태의 45층 삼차원 구조물이 고려된다.