The automotive industry is moving from the internal combustion engine to electric drive motors. Electricmotors uses a high voltage system requiring the development of resources and components to shield the system. There-fore, in this study, we analyze electromagnetic interference (EMI) shielding effectiveness (SE) characteristics of an autocrash pad according to the ratio of electrically conductive materials and propylene. In order to combine good mechan-ical characteristics and electromagnetic shielding of the automotive crash pad, metal-coated glass fiber (MGF) manufac-turing methods are introduced and compared with powder-type methods. Through this study, among MGF methods, wesuggest that the chopping method is the most effective shielding method.

In this study, material characteristics of glass fiber composite were evaluated by experiment. Tensile, compression and in-plane shear test were performed as test method of ASTM. Velocity of Tensile and compression test was 2mm/min and in-plane shear test was 4mm/min. At the test result, elastic modulus of tensile and compressive were similar. Maximum compressive strength and maximum compressive strain were smaller than the maximum tensile strength and maximum tensile strain.

In the study, tensile, compression and in-plane tests about longitudinal direction of glass fiber were performed. Also, to obtain the material properties of GFRP fabric composite, tensile test was performed. All test were performed by the test method of ASTM. Maximum compressive strength was smaller than the maximum tensile strength at the longitudinal direction test results. Elastic modulus of the tensile and compressive was almost similar at the compression test results in the longitudinal direction. Based on the GFRP fabric composite test results, GF91 was showed good performance at maximum compressive, maximum strain and elastic modulus.

2008년부터 2012년까지 임진강 하구역에서 어류 군집과 실뱀장어 소상을 조사한 결과 다음과 같다. 채집된 어류는 총 18과 42종이었으며 이 중 한국고유종은(Microphysogobio jeoni) 1종으로 고유화빈도가 0.04%이었다. 국외에서 도입된 외래어종은 떡붕어(Carassius cuvieri)와 초어(Ctenophayngodon idellus) 2종이 출현하였고 개체수 비교풍부도는 0.06%로 매우 낮았다. 출현한 어종 중 순수담수어에 속하는 종은 17종(40.5%), 회유성 6종 (14.2%), 기수성 8종 (19.1%), 해산어 11종(26.1%) 등 이었다. 개체수 구성비가 높은 종은 뱀장어(Anguilla japonica (glass eels, 49.8%)), 웅어 (Coilia ectens, 23.3%), 두우쟁이 (Saurogobio dabryi, 8.1%), 강주걱양태(Repomucenus olidus, 3.3%), 점농어(Lateolabrax maculata, 2.9%), 가숭어(Chelon haematocheilus, 2.8%)등 이었으며 생체량에 있어서는 C. ectens (33.6%), C. haematocheilus (14.2%), 잉어(Cyprinus carpio, 10.5%), 숭어(Mugil cephalus, 9.1%), S. dabryi (7.6%) 등이 풍부하였다. 우점종은 개체수에 있어 A. japonica (glass eels)이었고 C. ectens가 아우점종이었다. 파주시에서 연간 어획된 양은 83.6~240.3 t이었으며 2011년과 2012년에 급격히 감소하였다. 어획된 어류 중 생체량에 있어 M. cephalus (48.0~80.0%), C. carpio (6.7%), 붕어(Carassius auratus, 4.9%), 메기 (Silurus asotus, 3.9%), 황복(Takifugu obscurus, 2.5%), A. japonica (adult, 2.2%), 동자개(Pseudobagrus fulvidraco, 2.1%) 등의 순으로 풍부하였다. 연간 포획된 A. japonica (glass eels)는 양은 0.03~1.13 t이었고 연평균 212.0 kg이었으며 개체당 평균 체중이 0.16 g으로 약 1,325,000개체이었다.

The Mg-enriched magnesium aluminum silicate (MAS) glass is known for its higher mechanical strength and chemical resistance. Among such glasses, cordierite (Mg2Al4Si5O18) is well known to have a low thermal expansion and low melting point. Polycrystalline engineering ceramics such as alumina can be strengthened by a surface modification with low thermal expansion materials. The present study involves the synthesis of cordierite by a sol-gel process and investigates the effect of glass penetration on the surface of alumina. The cordierite powders were prepared from Al(OC3H7)3, Mg(OC2H5)2 and tetraethyl orthosilicate by hydrolysis and condensation reaction. The cordierite powders were characterized by X-ray diffraction (XRD, Rigaku), scanning electron microscope (SEM, JEOL: JSM-5610), energy dispersive spectroscopy (EDS, JEOL: JSM-5610), and universal testing machine (UTM, INSTRON). The X-ray diffraction patterns showed that the synthesized particles were μ-cordierite calcined at 1100˚C for 1 h. The shape of synthesized cordierite was changed from μ-cordierite to α-cordierite with increasing calcination temperature. Synthesized cordierite was used for surface modification of alumina. Cordierite powders penetrated deeply into the alumina sample along grain boundaries with increasing temperature. The results of surface modification tests showed that the strength of the prepared alumina sample increased after surface modification. The strength of a surface modified with synthesized cordierite increased the most, to about 134.6MPa.

본 연구는 고상폐기물인 준설토와 혼합물질인 점토 및 유리프리트를 이용하여 기능성을 갖는 건축자재용으로의 재활용 가능성을 검토하고자 실시되었다. D항만 준설토의 중금속 함량은 Zn이 526.0~13,150.1 mg/kg의 범위를 나타내는 등 심한 오염상태이었다. 준설토(30P)의 주요 화학조성은 SiO₂(48.30 wt%), Al₂O₃(16.60 wt%), CaO(10.10 wt%), Fe₂O₃(7.75 wt%)이었으며, 점토는 SiO₂가 70.82 wt%, Al₂O₃ 18.78 wt%, 유리프리트는 SiO₂가 71.75 wt%, CaO 13.99 wt%, Na₂O 8.51 wt% 함유되어 있었다. 준설토를 점토에 10~40 wt% 첨가한 후 1,000℃와 1,100℃에서 소성한 시편의 압축 강도는 각각 132.6~178.5 kgf/cm2와 581.2~793.7 kgf/cm²이었다. 준설토가 40 wt% 첨가된 경우 (SC46) 1,100℃에서 소성한 경우가 793.7 kgf/cm²로 1,000℃에서 소성한 경우의 153.0 kgf/cm² 보다 5배 이상 높게 나타나 1,100℃ 온도가 소성에 더 적합한 것으로 판단되었으며, KS 1종벽돌 기준을 만족시켰다. 또한, 시편의 용출시험 결과 폐기물관리법상 지정폐기물 판정기준치를 크게 하회하는 것으로 나타났다.

For the artistic column used by Glass Fiber Reinforced Plastic(GFRP), the connection of steel with GFRP were needed. Due to the fabricating characteristics of hand laminating, GFRP surfaces had to be connected. Because there were no existed data of these connection, experimental study has to be followed so that the structural strength and buckling mode could be investigated. In this paper, therefore, the axial tests of steel with GFRP were performed. The connection of GFRP's surfaces could be also tested as well. As a result, it could be figured out that the strength of these connections were determined by the adhesive strength.

간척지에서 대단위 유리온실 단지 조성에 대비하여 현장에서 필요한 기술을 개발하고자 전북 부안군 계화면에 벤로형 고측고 유리온실을 설치하여 파프리카를 품종별로 재배하여 일반농가와 생육과 수량을 비교하였다. 재배방식은 행거식 벤치시스템을 사용하여 암면 수경재배를 실시하였으며, LPG를 연소한 액화탄산가스를 낮동안 평균 500~600mg․L-1이 되게 공급하였고, 수평식 지열히터펌프를 활용하여 주로 야간에 22~24℃ 이하가 되도록 온도를 관리하였다. 양액의 관리는 순환식 시스템을 이용하였으며, 누적일사량 500J 마다 공급하여 배액을 20~40% 정도 유지하게 하였다. 재배기간 동안 칠레이리응애 등 9종의 천적을 응애, 진딧물, 총채벌레, 가루이, 나방류가 발생이 확인될 때 투입하여 무농약으로 재배하였다. 농가에서 많이 재배되는‘쿠프라’,‘콜레티’,‘부기’의 3품종을 재배한 결과 10a당‘콜레티’의 수량이 가장 많은 21.18ton,‘쿠프라’가 18.54ton,‘부기’가 15.45ton 순이었다. 경남과 전북의 일반농가와 10a당 수량을 비교한 결과 함안농가는 14.52ton, 창원농가는 20.89ton, 김제농가는 16.21ton을 각각 수확하여 수량성은 큰 차이가 없었다. 월별 수량을 비교한 결과 1그룹이 수확되는 12월에 수량이 높았으나, 1월에 감소한 후에 일사량이 많아지는 7월까지 증가하였다. ‘쿠프라’품종에 대하여 생육상황을 일반농가와 비교한 결과 평균 분지길이(방아다리)는 경남 창원의 유리온실에서 가장 짧았고, 경남 함안의 비닐하우스에서 재배한 경우 계화도의 유리온실과 비슷하게 길었다. 초장과 마디수는 계화도 유리온실에서 가장 양호하였으나, 착과수는 전북 김제의 유리온실에서 가장 많은 19.6개/주 정도였다. 이상의 결과로 볼 때 전북 계화면 간척지에서 유리온실을 설치하여 파프리카를 재배할 경우 다른 농가와는 큰 차이 없이 수량을 확보할 수 있었고, 천적을 활용한 무농약 재배 및 순환식 수경재배가 가능하였다.

목적: 수도권지역의 10대 이상의 고객을 대상으로 일반 안경원과 프렌차이즈 안경원의 서비스 만족도를 조사하고자 하였다. 방법: 안경원 이용 경험이 있는 수도권지역 소비자를 대상으로 연구를 실시하였다. 고객이 서비스 품질을 평가하는 기준을 유형성, 신뢰성, 대응성, 공감성, 확신성, 그리고 전문성의 6가지 기준으로 조정하였다. 기준에 맞는 예제들을 수집하여 설문 조사하고 통계처리를 하였다. 결과: 일반 안경원과 프렌차이즈 안경원은 서비스에 대한 고객의 만족도가 다르게 나타났다. 신뢰성, 대응성 그리고 확신성에 해당하는 설문 중 제품의 품질, 충실한 A/S, 그리고 렌즈의 관리법과 사용법을 묻는 질문에는 프렌차이즈 안경원이 선호되었고 유형성과 공감성 설문에는 친밀함과 편안함을 주는 일반 안경원이 선호되는 경향을 보였다. 결론: 소비자의 선호도를 분석했을 때 각각의 장점을 강조하여 일반 안경원과 프렌차이즈 안경원의 특색에 맞는 서비스를 강화한 차별화가 필요한 것으로 보인다.

Concrete and steel has been used as the main material of structure from building and drainage pipe. However, many problems such as corrosion and rupture had occurred in the Water Supply and the Sewer System. Additionally, the government has invested big budget to Deteriorated pipe replacement and maintenance. Replacement of existing pipelines in order to solve these problems, GFRP pipe(glass fiber composite material pipes) is aspiring to replace the tube. GFRP has high strength, restore performance, durable and lightweight properties. However, high strength GFRP pipe is weak in buckling problem. This study is to analysis Optimization Design models for resisting bucking problem of GFRP pipes. Thus, various tests Changed the angle of Glass-Fiber-Reinforced Layer and the resin content of resin-mortar were performed for GFRP pipes to estimate material characteristics of GFRP in this study. Buckling analysis of composite structures under external uniform pressure was performed with the results obtained through test.

휨 거동 및 전단부의 전단거동으로 인한 철근상세 및 사용되어지는 철근의 과다로 인하여 취성파괴의 양상이 발생 하고 있다. 이에 본 실험에서는 유리섬유망을 이용하여 철근과의 휨 및 변위 거동을 통하여 무보강철근과 유리섬유망의 ply 수에 따른 휨거동 실험을 통하여 균열을 살펴보고서 향후 휨 거동에 적정한 유리섬유망의 철근의 배치겹수에 대한 사용량을 검토하고자 한다.

The quartz glasses were prepared by fumed silica powders sintering method at , , in air and the effect of sintering temperature on their properties were investigated. The X-ray diffraction pattern, the OH concentration, the light transmittance, the apparent porosity and the density were analyzed. The transparent quartz glass were obtained above . The OH-group and macroscopic pores were removed above and highest density and light transmittance were obtained at .

A bulk metallic glass-forming alloy, metallic glass powders was used for good commercial availability and good formability in supercooled liquid region. In this study, the Ni-based metallic glass was synthesized using by high pressure gas atomized metallic glass powders. In order to create a bulk metallic glass sample, the metallic glass powders with ball-milled Ni-based amorphous powder with 40%vol brass powder and Cu powder for 20 hours. The composite specimens were prepared by Spark Plasma Sintering for the precursor. The SPS was performed at supercooled liquid region of Ni-based metallic glass. The amorphous structure of the final sample was characterized by SEM, X-ray diffraction and DSC analysis.

Opal glass samples having different chemical compositions were synthesized and transparent glass was obtained after melting. The effects of TiO2, BaF2, and CeO2 content on the color of the opal glass were studied by observing images of the opal samples and analyzing the results via ultraviolet visible spectroscopy and color spectrometry. The aesthetic properties of the opal glass were determined by studying the transmittance of visible light in the 400 nm to 700 nm range. The basic chemical composition of opal glass was SiO2 52.9 wt%, Al2O3 12.35 wt%, Na2CO3 15.08 wt%, K2CO3 10.35 wt%, Ca3(PO)4 4.41 wt%, MgCO3 1.844 wt%, LiCO3 2.184 wt%, and TiO2 0.882 wt%. The glass samples were prepared by varying the weight percentage of TiO2, BaF2, and CeO2. The transmittance of visible light was decreased from 95 % to 75 % in the glass samples in which TiO2 content was increased from 0 to 3.882 wt%. In the blue spectrum region, as the content of TiO2 increased, the reflectance value was observed to become higher. This implies that TiO2 content induces more crystal formation and has an important effect on the optical properties of the glass. The opalescence of opal samples that contained CeO2 or BaF2 is stronger than that in the samples containing TiO2. Opal glass samples comprising TiO2 had tetragonal lattice structures; samples including CeO2 as an additive had cubic lattice structures (FCC, CeO2).

Yellow phosphor dispersed color conversion glasses are promising phosphor materials for white LED applications because of their good thermal durability, chemical stability, and anti-ultraviolet property. Six color conversion glasses were prepared with high Tg and low Tg specimens of glass. Luminous efficacy, luminance, CIE (Commission Internationale de l'Eclairage) chromaticity, CCT (Correlated Color Temperature), and CRI (Color Rendering Index) of the color conversion glasses were analyzed according to the PL spectrum. Color conversion glasses with high Tg glass frit, sintered at higher temperature, showed better luminous properties than did color conversion glasses with low Tg glass frit. The characteristics of the color conversion glass depended on the glass composition rather than on the sintering temperature. The XRD peaks of the YAG phosphor disappeared in the color conversion glass with major components of B2O3-ZnO-SiO2-CaO and, in the XRD results, new crystalline peaks of BaSi2O5 appeared in the color conversion glass with major components of Bi2O3-ZnO-B2O3-MgO. The characteristics of CIE chromaticity, CCT, and the CRI of low Tg color conversion glasses showed worse color properties than those of high Tg color conversion glasses. However, these color characteristics of low Tg glasses were improved by thickness variation. So color conversion glasses with good characteristics of both luminous and color properties were attained.

For the purpose of improving the durability problem, translucent opal glass was fabricated as a substitute for the polycarbonate diffuser of LED lighting. Calcium phosphate was used as an opacifier of opal glass and melted in an electric furnace. The opaque effect was identified according to the change of the cooling procedure. As results, translucent opal glass was obtained by the melting of a batch with a composition of 3.8% calcium phosphate at 1550˚C for 2 hrs and then the cooling of the material in the furnace. For the cooling condition of the glass sample, HTCG (High Temperature Cooled Glass) was found to have better optical properties than LTAG (Low Temperature Annealed Glass). It had excellent optical properties for a diffuser of LED lighting, with no dazzling from direct light due to its high haze value of over 99% and low parallel transmittance value of under 1%. For the thermal properties, it had an expressed thermal expansion coefficient of 5.7×10-6/˚C and a softening point of 876˚C; it also had good thermal properties such as good thermal shock resistance and was easy to apply to the general manufacturing process in the forming of glass tubes and bulbs. Therefore, it is concluded that this translucent opal glass can be used as a glass diffuser material for LED lighting with high heat resistance and high durability; this material is suitable as a substitute for polycarbonate diffusers.

원전에서 발생되는 방사성폐기물에 대한 고화처리 방법 중 하나인 유리화기술이 일부 가연성폐기물에 대해 적용되고 있다. 국내외적으로 중저준위 방사성폐기물의 효과적인 감용과 안정적인 처분을 위해 다양한 폐기물에 대한 유리화기술 적용방안이 확대 연구되고 있으며, 최근에는 가연성폐기물 뿐만 아니라 알루미늄 금속과 같은 비가연성폐기물에도 유리화 연구가 활발하게 진행되고 있다. 공기조화계통 (HVAC)에는 주로 필터가 이용되고 있으며, 사용 후 필터는 여과재 (유리섬유 및 알루미늄)를 이용하여 배기체를 흡착하기 때문에 방사성폐기물로 처리가 되어야 한다. 본 연구는 필터에 대한 처리기술 연구를 위해 유도가열식 저온용융로 (Cold Crucible Induction Melter: CCIM)를 이용한 유리화 타당성 연구를 수행하였다. 사용후 필터에 대한 유리화 (Vitrification)는 먼저 유리섬유 및 알루미늄 함량을 고려한 최적의 유리조성을 개발 하였으며, 개발된 유리조성을 이용하여 최적의 폐기물 저감을 위한 용융변수와 최종 생성된 유리고화체의 특성을 분석하였다. 사용후 필터 유리화용 조성유리는 주로 SiO2와 B2O3로 구성되어 있다. 전기로를 이용한 용융물 특성시험에서는 폐기물 투입률 및 최종 생성물인 유리고화체의 특성이 검토되었다. 본 연구에서는 알루미늄 금속과 유리섬유로 구성된 필터에 대한 유리조성 개발과 이를 통해 생성된 유리고화체의 물리화학적 특성을 검토하고 유리화 타당성을 확인하였다.