The purpose of this study is to analyze the correlation between ecotoxicity and water quality items using Daphnia magna in public sewage treatment plant process and to obtain operational data to control ecotoxicity through research on removal efficiency. The average value of ecotoxicity was 1.39 TU in the influent, 1.50 TU in the grit chamber, and 0.84 TU in the primary settling tank and it was found that most organic matters, nitrogen, and phosphorus were removed through biological treatment in the bioreactor. Using Pearson’s correlation analysis, the positive correlation was confirmed in the order of ecotoxicity and water quality items TOC, BOD, T-N, NH3-N, SS, EC, and Cu. As a result of conducting a multilinear regression analysis with items representing positive correlation as independent variables, the regression model was found to be statistically significant, and the explanatory power of the regression model was about 81.6%. TOC was found to have a significant effect on ecotoxicity with B=0.009 (p<.001) and Cu with B=16.670 (p<.001), and since the B sign is positive (+), an increase of 1 in TOC increases the value of ecotoxicity by 0.009 and an increase in Cu by 1 increases the value of ecotoxicity by 16.670. TOC (β=0.789, p<.001) and Cu (β=0.209, p<.001) were found to have a significant positive effect on ecotoxicity. TOC and Cu have a great effect on ecotoxicity in the sewage treatment plant process, and it is judged that TOC and Cu should be considered preferentially and controlled in order to efficiently control ecotoxicity.

Molybdenum-tungsten (Mo-W) alloy sputtering targets are widely utilized in fields like electronics, nanotechnology, sensors, and as gate electrodes for TFT-LCDs, owing to their superior properties such as hightemperature stability, low thermal expansion coefficient, electrical conductivity, and corrosion resistance. To achieve optimal performance in application, these targets’ purity, relative density, and grain size of these targets must be carefully controlled. We utilized nanopowders, prepared via the Pechini method, to obtain uniform and fine powders, then carried out spark plasma sintering (SPS) to densify these powders. Our studies revealed that the sintered compacts made from these nanopowders exhibited outstanding features, such as a high relative density of more than 99%, consistent grain size of 3.43 μm, and shape, absence of preferred orientation.

Among the Additive Manufacturing (AM) technologies, the Binder-Jetting printing technology is a method of spraying an adhesive on the surface of powder and laminate layer by layer. Recently, this technique has become a major issue in the production of large casting products such as ship-building, custom vehicles and so on. In this study, we performed research to make actual mold castings and increase mechanical property by using special sand and water-based binders. For use as a mold, it has a strength of more than 3MPa and permeability. Various experiments were carried out to obtain suitable them. The major process parameters were binder jetting volume, binder types, layer thickness and heat treatment condition. As a result of this study, the binder drop quantity was measured to be about 60 pico-liter, layer thickness was 100μm and the heat treatment condition was measured about 1,000℃ and compressive strength were measured to be more than 5MPa. The optimum condition of this experiment was established through actual casting of aluminum. The equipment used in this study was a Freeforms T400 model (SFS Co., Ltd.), and the printing area of 420 * 300 * 250mm and resolution of 600dpi can be realized.

The CDI (Capacitive deionization) is one of the desalination technologies that use a carbon material electrode with large surface area and excellent electrical conductivity. Recently, research on a MCDI (Membrane Capacitive deionization) process, which is a combination of an ion-exchange membrane, has been actively conducted. In this study, we tried to find out the water quality of treated water and the concentration characteristics of concentrated water through TDS analysis by MCDI conventional and circulation process. In producing treated water, there was no significant difference in adsorption efficiency between MCDI conventional and circulation process. It was confirmed that both processes adsobed more than 96 %. However, the MCDI conventional process showed a low yield of 50 %, whereas the MCDI circulation process showed a high yield of 97.6 %. It's because, the wasted water was reused at desorption. In the case of the TDS concentration using MCDI circulation process, as the cycle progressed, the TDS concentration was concentrated up to 1,300 mg/L, but the rate gradually decreased. It is believed that this is because the volume of the concentrated water tank is limited, and the amount of soluble ions gradually decreases. As a result of analyzing the wasted water at MCDI circulation process through Ion Chromatography, it was confirmed that the concentration of all ions were concentrated. However, there was no significant difference in the types and proportions of analyzed ions. It is judged that the types and concentration of ions do not have a significant effect on adsorption and desorption in the MCDI circulation process.

Lightweight steel is a crucial material that is being actively studied because of increased carbon emissions, tightening regulations regarding fuel efficiency, and the emergence of UAM, all of which have been recently labeled as global issues. Hence, new strategies concerning the thickness and size reduction of steel are required. In this study, we manufacture lightweight steel of the Fe-Mn-Al-C system, which has been recently studied using the DED process. By using 2.8 wt.% low-Mn lightweight steel, we attempt to solve the challenge of joining steel parts with a large amount of Mn. Among the various process variables, the laser scan power is set at 600 and 800W, and the laser scan speed is fixed at 16.67 mm/s before the experiments. Several pores and cracks are observed under both conditions, and negligibly small pores of approximately 0.5 μm are observed.

In this study, a new manufacturing process for a multilayer-clad electrical contact material is suggested. A thin and dense BCuP-5 (Cu-15Ag-5P filler metal) coating layer is fabricated on a Ag plate using a high-velocity oxygen-fuel (HVOF) process. Subsequently, the microstructure and bonding properties of the HVOF BCuP-5 coating layer are evaluated. The thickness of the HVOF BCuP-5 coating layer is determined as 34.8 μm, and the surface fluctuation is measured as approximately 3.2 μm. The microstructure of the coating layer is composed of Cu, Ag, and Cu-Ag-Cu3P ternary eutectic phases, similar to the initial BCuP-5 powder feedstock. The average hardness of the coating layer is 154.6 HV, which is confirmed to be higher than that of the conventional BCuP-5 alloy. The pull-off strength of the Ag/BCup-5 layer is determined as 21.6 MPa. Thus, the possibility of manufacturing a multilayer-clad electrical contact material using the HVOF process is also discussed.

본 연구에서는 폴리술폰 분리막을 이용한 바이오가스 정제 공정으로 고선택성 소재를 이용한 2단 공정의 높은 회 수율 및 경제성과 동등한 수준의 회수율을 확보하기 위해 저온 고압의 분리막 공정을 설계하고 평가하였다. 폴리술폰 고분자 를 4성분계 도프를 이용하여 비용매 유도 상전이법으로 중공사 분리막을 제조하였다. 기체 분리용 중공사 분리막은 1.6 m2의 유효 막면적을 갖는 샘플을 제조하여 상온 및 저온에서 기체 투과 특성을 평가하였다. 제조된 기체분리막 모듈의 온도에 따 른 기체 투과 특성을 분석하기 위하여 온도별 단일 기체 투과도를 평가한 결과 이산화탄소와 메탄 투과도는 20°C에서 각각 412, 12.7 GPU이며, -20°C에서는 각각 280, 3.6 GPU로써 이상 선택도는 32.4에서 77.8로 향상되었다. 단일 기체 투과 테스 트 후 혼합 기체에 대한 분리 테스트를 진행하였으며, 모듈 1단 구성 및 2단 구성(막 면적비 1:1, 1:2, 1:3)을 통하여 투과 거 동을 살펴보았다. 1단 구성에서는 stage-cut이 상승함에 따라 메탄의 농도가 상승하지만, 반대로 회수율은 떨어지는 결과를 나 타내었다. 2단 구성 테스트에서는 메탄 농도 97% 기준에서 막 면적비 1:1보다 1:3이 메탄의 회수율이 더 높게 측정되었으며, 공급 기체의 온도가 낮을수록 메탄의 회수율이 높아짐을 확인하였고, 최종적으로 폴리술폰 2단 공정에서 메탄 농도 97%, 회 수율 97%의 결과를 달성하였다.