PURPOSES : The adhesive bonding strength of the grid between asphalt pavements is critical in pavement performance. The study is to compare and evaluate the interlayered bonding strength of asphalt mixture specimens with fiber-glass grid (FG) reinforcement and different tack coating materials based on the test results of the shear bonding test.
METHODS : Asphalt mixtures were molded with FG reinforcement using various tack coating materials namely RSC4 and D/B coat. The adhesive shear-bond strength was measured by inducing a monotonic shear loadnig rate of 5 mm/min at 20℃.
RESULTS : As expected, the asphalt mixture with non-reinforced FG exhibited the highest adhesive shear-bond strength, followed by that of the FG with D/B coating. The ranking order of superiority is as follows: Control (RSC4) > D/B+FG > RSC4+FG.
CONCLUSIONS : The results of this experimental study indicate that FG with RSC4 and D/B tack coats can be successfully used in asphalt concrete overlay construction with superior field performance. Based on the test results and literature review, the field bonding strength should exceed 300kPa in grid reinforced asphalt pavement.
Ice accumulation on Aluminum Conductor Steel Reinforced(ACSR) cable during winter is an important matter in terms of safety, economy, and efficient power supply. In this work, the ice adhesion strengths of ACSR cable oxidized during different periods(7 years oxidized and 15 years oxidized) are evaluated. At first, a plate type dry oxidation standard specimen, whose surface characteristics are similar to those of ACSR cable, is prepared. Dry oxidation standard specimens are heat-treated at 500 °C for 20, 60, and 120 minutes in order to obtain different degrees of oxidation. After the dry oxidation, surface properties are analyzed using contact angle analyzer, atomic force microscopy, spectrophotometer, and gloss meter. The ice adhesion strengths are measured using an ice pull-off tester. Correlations between the surface properties and the ice adhesion strength are obtained through a regression analysis indicating a Boltzmann equation. It is revealed that the ice adhesion strength of 15- year oxidized ACSR cable is approximately 8 times higher than that of ACSR-bare.
서 론 빠른 경제성장과 함께 <2016년 국토교통부> 자동차 등록대수는 2180만을 돌파하였다. 이처럼 많은 차량들이 도로를 사용하게 됨에 따라 기존의 아스팔트도로와 콘크리트도로가 많이 노후와 되어있는 추세이며, 이에 도로의 유지.보수 관리의 중요성이 높아지게 되었으며, 유지.보수간에 가장 많이 사용되는 공법 중에 하나인 덧씌우기 공법에 사용하는 택코트의 성능을 검토하기 위해 수행되었다. 실험 방법 및 사용재료 2.1 사용재료 실험에 사용된 택코트는 일반적으로 사용되어지는 RSC-4와 택코트 필름을 사용하였으며, 부착강도를 측정하기 위해 양생시간을 동일하게 하여 Pull of test를 통해 부착강도를 측정하였다. 2.2 실험 방법 휨몰드와 마샬 몰드를 사용하여 각각 택코트 RSC-4와 필름을 사용하여 공시체를 제작하였다. 1층 다짐 후 24시간 양생 후 2차 다짐을 한 후에 48시간 부착강도를 측정하였다. 그림1은 본 실험에 사용된 시편의 제작과정이며, 그림2는 부착강도 테스트 후의 모습이다. 결과 및 고찰 3.1 동일한 양생조건에서 콘크리트 위에 부착한 택코트 종류에 따른 부착강도 그림4은 휠트래킹 몰드로 만든 콘크리트에 부착한 택코트 종류에 따른 부착강도를 나타낸 그래프이다. 3.2 동일한 양생조건에서 아스팔트 위에 부착한 택코트 종류에 따른 부착강도 그림 5는 마샬 몰드로 만든 아스팔트 공시체 위에 부착한 택코트 종류에 따른 부착강도를 나타낸 그래프이다. RSC-4의 경우에는 살포 후 30분간 상온양생을 실시하였다 결 론 일반적으로 사용되어지고 있는 택코트 인 RSC-4의 경우 유화아스팔트라는 성질 때문에 충분한 양생이 필요하여 공기가 늘어나게 되어 실제 현장에서 규정에 맞게 사용하기가 힘든 실정이다. 도로 유지.관리 공법중 하나인 덧씌우기 공법에 사용되는 택코트의 종류와 부착하는 재료에 따른 부착 강도평가 실험결과는 다음과 같다. 1) 콘크리트 위에 각각 RSC-4와 택코트 필름을 부착하여 Pull-off-test 장비를 이용하여 부착강도를 평가한 결과 각각 0.77, 0.76 으로 비슷한 결과를 나타냈다. 2) 아스팔트에 부착한 RSC-4와 택코트 필름을 부착하여 부착강도를 평가했을때와 비슷한 경향을 나타냈다. 각각 1.241, 1.304로 택코트 필름과 보호필름을 사용한 쪽이 더 높게 나타났다. 이는 공사기간을 단축시킬 수 있을 뿐만 아니라 트래피커빌리티를 고려하였을 때 택코트 필름과 보호 필름을 사용하여 더 효율적으로 유지.보수를 할 수 있을 것으로 판단된다
HYB(FRP Hybrid Bar) is composite structural material that combines reinforced bar and FRP. HYB has high elastic modulus and after-yield-hardening properties, despite its corrosion resistance and light weight. HYB under development has relatively stable corrosion durability. This study performs fundamental experiments for the long period UV exposed HYB, and carries out pull-out test for the freezing-thawing exposed specimens of ordinary reinforced bar, HYB, and UV exposed HYB. The effect of UV exposure and freezing-thawing did not affect the tensile property and strength of HYB. However, the bond strength reduction on the environment of accelerated corrosion should be considered in further study.
PCB 제조에서 photoresist와 Copper Clad Laminate(CCL)의 구리표면과의 부착력을 항상시 키기 위하여 사용되는 soft etching제를 제조하기 위하여 과산화수소 사용을 배제하고, 유기산과 유기과 산화물을 이용하여 산의 종류, 농도, 에칭시간 등에 따른 구리표면의 에칭속도, 표면 조도, 및 오염도 등 을 조사하였다. 또한 에칭 후의 표면의 얼룩을 제거하기 위한 안정제의 최적 배합 및 농도도 확립하였 다. 본 연구 결과 유기산의 종류 중에서는 아세트산이 초기 구리 에칭속도가 가장 빨랐으며, 농도가 0.04 M이었을 때 0.4 μm/min이였다. 유기과산화물인 APS의 농도는 높을수록 에칭속도가 가장 빨랐으나, 표면 오염이 심각하였다. 안정제 용액의 조성도 표면 오염도에 큰 영향을 주었다. 결과적 0.04 M 아세 트산, 0.1M APS에 4 g/L의 안정제(ST-1)를 첨가한 에칭액의 경우 0.37 μm/min의 에칭속도와 표면 오염이 전혀 없으며, 표면 조도도 가장 우수하였다. 즉, CCL과 photoresist와 접착력을 향상시킬 수 있 을 것으로 판단된다.
High temperature plasma coating technology has been applied to recover damaged aluminum dies from wear by spraying pure aluminum and alumina powder. However, the coated mixed powder layer composed of aluminum and alumina often undergoes a detachment from the substrate, making the coated substrate die unable to maintain its expected life span. In this study, in order to increase the bonding strength between the substrate and the coating layer, a pure aluminum layer was applied as an intermediate bond layer. In order to prepare the specimen with variable bond coating conditions, the bond coat layers with a various gun speed from 10 cm/sec to 30 cm/sec were prepared with coating cycle variations ranging from three to nine cycles. The specimen with a bond coat layer coated with a gun speed of 20 cm/sec and three coating cycles exhibited ~13MPa of adhesion strength, while the specimen without a bond coat layer showed ~6 MPa of adhesion strength. The adhesion strength with a variation of bond coat layer thickness is discussed in terms of coating parameters.
본 연구에서는 유변물성측정기를 이용하여 HPMC 첨가량, 물 양, HPMC 분자량, 셀룰로오스 에테르 치환체 및 치환도가 쌀 반죽의 압축 및 접착 특성에 미치는 영향에 대해 살펴보았다. HPMC 첨가량이 증가함에 따라 접착강도는 꾸준히 증가하였으나, 압축강도는 2% HPMC 첨가량에서 최대 강도를 보였다. HPMC의 분자량이 증가하거나, 물 양이 감소할수록 쌀 반죽의 압축강도 및 접착강도가 증가하는 결과를 보였다. 이들 인자 외에도, 셀룰로오스 에테르의 치환체 및 치환도도 쌀 반죽의 압축강도 및 접착 강도를 결정하는 중요한 인자임을 확인하였다.
In the microelectronics packaging industry, the adhesion strength between Cu and polyimide and the thermal stability are very important factors, as they influence the performance and reliability of the device. The three different buffer layers of Cr, 50%Cr-50%Ni, and Ni were adopted in a Cu/buffer layer/polyimide system and compared in terms of their adhesion strength and thermal stability at a temperature of 300˚C for 24hrs. A 90-degree peel test and XPS analysis revealed that both the peel strength and thermal stability decreased in the order of the Cr, 50%Cr-50%Ni and Ni buffer layer. The XPS analysis revealed that Cu can diffuse through the thin Ni buffer layer (200Å), resulting in a decrease in the adhesion strength when the Cu/buffer layer/polyimide multilayer is heat-treated at a temperature of 300˚C for 24hrs. In contrast, Cu did not diffuse through the Cr buffer layer under the same heat-treatment conditions.
The magnetron sputtering was used to deposit Ni buffer layers on the polyimide surfaces to increase the adhesion strength between Cu thin films and polyimide as well as to prevent Cu diffusion into the polyimide. The Ni layer thickness was varied from 100 to 400Å. The adhesion strength increased rather significantly up to 200Å of Ni thickness, however, there was no significant increase in strength over 200Å. The XPS analysis revealed that Ni thin films could increase the adhesion strength by reacting with the polar C=O bonds on the polyimide surface and also it could prevent Cu diffusion into the polyimide. The Cu/Ni/ polyimide multilayer thin films showed a high stability even at the high heating temperature of 200˚C, however, at the temperature of 300˚C, Cu diffused through the Ni buffer layer into polyimide, resulting in the drastic decrease in adhesion strength.
본래 약한 구리계 리드프레임/EMC(Epoxy Molding Compound) 계면의 접착력은 솔더 리플로우 (solder reflow) 공정 중에 종종 박형 플라스틱 패키지의 팝콘 균열 현상(popcorn-cracking phenomena)을 일으킨다. 본 연구에서는 리드프레임/EMC 계면의 접착력을 향상시키기 위하여 리드프레임을 알칼리 용액에 담궈 표면에 brown oxide를 형성시켰으며, EMC로 몰딩(molding)하여 SDCB(Sandwiched Double Cantilever Beam) 시편 및 SBN(Sandwiched Brazil-Nut) 시편을 준비하여 접착력을 측정하였다. 리드프레임의 brown oxide 처리는 미세한 바늘모양의 CuO 결정들을 리드프레임 표면에서 형성시켰으며, 리드프레임/EMC 계면의 접착력을 향상시켰다. 접착력의 향상은 산화층의 평균두께와 직접적인 관련이 있었다. 이는 미세한 바늘모양의 CuO 결정들이 EMC와 기계적인 고착(mechanical interlocking)을 하기 때문으로 생각된다.
강유전체 재료의 하부전극으로 사용되고 있는 Pt/Ti 박막의 접착력에 대한 열처리 분위기의 영향을 연구하였다. 시편의 접착력은 90˚ 필 테스트 방법을 사용하여 정량적으로 측정하였다. 열처리 후 사용된 분이기에 관계없이 모두 접착력이 감소하였는데 특히 산소분위기에서 열처리 한 시편의 접착력이 매우 크게 감소하였다. AES depth profile과 단면 TEM을 이용하여 계면반응을 관찰한 결과 산소열처리시에는 Ti가 외부에서 확산해 온 산소와 반응하여 rutile TiO2상이 형성됨을 알 수 있었다. 그러므로 산소열처리 후에 일어나는 접착력의 급격한 감소 원인은 열처리시 취약한 TiO2상이 형성되며 이로 인해 Ti 접착층이 고갈되기 때문임을 알 수 있었다.
This paper presents a study on the adhesive strength testing of self-adhesive waterproofing/anti-corrosion sheet used for waterproofing of the large diameter steel pipe interior of water treatment facilities. After the sheet has been applied, similar physical and chemical immersion conditions are simulated in the testing to determine the effects of deterioration through adhesion strength testing.
This study is the adhesion strength of the sprayed metal in accordance with a proportion ratio of the Zn-Al. Results showed the most excellent adhesion strength for metal spraying Al100 For the metal spraying Zn100, ZnAl85, ZnAl95 exhibited a similar level of adhesion strength results.