In this study, we designed and manufactured a large angular contact ball bearing (LACBB) with low deformation using JIS-SUJ2 steel and analyzed changes in its structural characteristics and chemical composition upon heat treatment. The bearing was produced by hot forging and heat treatment including a quenching and tempering (Q/T) process, and its properties were analyzed using 4 mm thick specimens. A difference in the size distribution of the carbide in the outer and inner parts of the bearing was observed and it was confirmed that large and non-uniform carbide was distributed in the inner part of the bearing. After heat treatment, the hardness value of the outer part increased from 13.4 HRC to 61 HRC and the inner part increased from 8.0 HRC to 59.7 HRC. As a result of X-ray diffraction (XRD) measurements, the volume fraction of the retained austenite contained in the outer part was calculated to be 3.5~4.8 % and the inner part was calculated to be 3.6~5.0 %. The surface chemical composition and the content of chemical bonds were quantified through X-ray photoelectron spectroscopy (XPS), and a decrease in C=C bonds and an increase in Fe-C bonds were confirmed.

This study aims to evaluate the structural safety of a structural thermal barrier, installed inside the structure of a building and performed the role of a load-bearing element and an insulation simultaneously, contributing to the realization of net-zero buildings. To ensure the reliability of the analysis model, the analysis results derived from LS-DYNA were compared with the experimental results. Based on the results shown through the flexural experiment, the reliability of the thermal cross-section insulation structure model for slabs was validated. In addition, the effect of the UHPC block on the load support performance and its contribution to vertical deflection was verified.

This paper reports the results of an experimental examination using X-rays to test annealing materials for lapped bearing steel (STB2), to confirm the validity of the weighted averaging analysis method. The distribution behavior for the sin diagram and the presence or absence of differences in the peak method, half-value breadth method, and centroid method were investigated. When lapping the annealed bearing steel (STB2) material, a residual stress state with a non-directional steep gradient appeared in the surface layer, and it was found that the weighted averaging analysis method was effective. If there is a steep stress gradient, the sin diagram is curved and the diffraction intensity distribution curve becomes asymmetric, resulting in a difference between the peak method, half-value breadth method, and centroid method. This phenomenon was evident when the stress gradient was more than 2~3 kg/mm2/μm. In this case, if the position of the diffraction line is determined using the centroid method and the weighted averaging analysis method is applied, the stress value on the surface and the stress gradient under the surface can be obtained more accurately. When the stress gradient becomes a problem, since the curvature of the sin diagram appears clearly in the region of sin > 0.5, it is necessary to increase the inclination angle  as much as possible. In the case of a lapping layer, a more accurate value can be obtained by considering  in the weighted averaging analysis method. In an isotropic biaxial residual stress state, the presence or absence of  can be determined as the presence or absence of strain for sin≈0.4.

강진은 적절한 내진 설계 기술이 적용되지 않으면 건물 붕괴로 인하여 극심한 피해가 발생할 수 있다. 이를 해결할 수 있는 면진 기술은 구조물과 지반 사이에 베어링 장치를 적용하여 지진 에너지를 흡수하고 건물에 전달되는 진동을 감쇠한 다. 본 연구는 고무 마찰 베어링 장치의 구조물 적용성을 검증하고 지진으로부터 안전성을 확보하기 위하여 고무 마찰 베어링 프레임 구조물에 대한 수치해석을 수행하였다. 수치해석 결과로써 최대 지붕 가속도와 총 밑면 전단력이 감소되어 내진 성능을 확인하였다. 또한, 최대 층간 변위 및 최대 잔류 층간 변위에 대한 분석 결과로 프레임 구조물을 경제적 복구 수준의 결과를 도 출하여 고무 마찰 베어링 장치의 우수한 내진 성능을 확인하였다.

Generally the non-bearing walls in apartment buildings in Korea are not considered as a lateral force resisting members for the design consideration. This engineering practice caused large crack damages and brittle fractures of the non-bearing walls when subjected to Pohang earthquakes in 2017 since those have not been designed for seismic loading. In this study, finite element analysis was conducted for slot type non-bearing wall connection system to reduce damages and concentrate damages to the designated damping device through separation from the structural wall members. Steel plate and dowel bar systems designed for the dissipation of seismic energies were modeled and analyzed to investigate the damage reductions. Finally, the test result and the analysis result were compared and verified.

본 연구에서는 모형실험을 통하여 다짐도 및 매입깊이에 따른 나선철항의 인발저항력을 검토하였다. 그 결과 다짐도 및 매입깊이가 증가할수록 인발저항력은 증가하는 것으로 나타났으며, 특히 다짐률 85%의 지반조건에서 인발저항력은 매입깊이 25cm, 30cm, 35cm 및 40cm 별로 각각 48.9kgf, 57.9kgf, 86.2kgf 및 116.6kgf로 다른 지반조건일 때 보다 현저하게 높은 인발저항력이 나타났다. 그리고 다짐률에 따른 인발저항력은 각 매입깊이 조건별(30cm, 35cm 및 40cm)로 다짐률 75% 및 85%에서 급격하게 증가하는 유사한 경향이 나타났다. 나선철항의 인발저항력은 지반의 다짐률에 따라 상당한 차이를 보였으며 극한인발저항력의 최대값은 다짐률 85%의 지반조건 및 매입깊이 40cm에서 116.6kgf로 나타났다. 이는 나선철항의 제원을 고려해볼 때 매우 높은 것으로 판단된다. 따라서 평소 나선철항 주변 지반의 유지관리를 철저히 한다면 바람에 대한 피해를 효과적으로 경감시켜 줄 수 있을 것으로 판단된다. 그리고 나선 철항은 플라스틱 필름을 고정하는 용도뿐만 아니라 온실 형태별로 개수 및 간격 등 적절한 설치방법이 제시된다면 온실의 구조적 안정성에도 기여를 할 수 있을 것으 로 예상된다. 또한 본 연구의 결과를 검토해 볼 때 온실에 나선설항의 설치시 유용한 효과를 기대하기 위해서는 매입깊이 35cm 이상 그리고 다짐률은 85%이상을 적용해야 할 것 으로 판단되며, 본 실험에서 다짐률 85%에 해당하는 모형지반의 상대밀도는 67%정도 였다.

P/M high speed steel (1.26% C, 4.42% Cr, 6.54% W, 4.92% Mo, 3.21 % V, 8.77% Co, bal. Fe) was applied to hot former die. It showed that the die life became 2.7 times higher than that of cast/wrought SKH 55 tool steel which is commercially used. The increase of die life was corresponding to the improved hardness and transverse rupture strength of PM high speed steel due to the finer grain and carbide as well as the uniform carbide distribution. The P/M high speed steel with the promoted die life could be an alternative to the conventional SKH55.

0.05wt%C-Cu첨가열연강판에서 590MPa급을 가지며 10% pre-strain을 가한 후 780MPa급 이상을 가지는 Cu첨가형 열연강판의 최적 Cu 및 Mn첨가량 규명을 위해 경도 및 인장시험과 투과 전자현미경으로 조사하였다. Cu 첨가형 열연강판에서 고용강화와 시효경화를 고려한 적정 Cu 첨가량은 1.2wt% 전후였으며, Mn첨가량은 0.75-0.85wt%범위였다. 0.05%C-1.2%Cu-0.75%Mn-0.04%Nb첨가 강판에서 과시효조건에서 관찰되는 조대한 석출물은 면심입방정 구조인 ε-Cu인 것으로 확인되었으며, 열연상태에서는 590MPa급을 가지며, 10% pre-strain을 부여한 후 550˚C에서 30분 열처리할 경우 780MPa급의 인장강도를 가지는 Cu첨가형 열연강판의 제조가 가능하였다.

방화구획 내 벽체에는 콘크리트, 조립식 패널, 건식벽체 등을 사용한 내화구조가 주로 적용되고 있으나 근래에 들어 시야 확보 및 미적 관점에 대한 관심이 증가하여 유리로 구성된 벽체의 수요가 발생하고 있다. 본 연구에서는 차열 유리를 적용한 스틸 내화벽체에 관한 것으로써 내부 방화구획에 적용 가능한 60분 내화벽체와 외부 벽체 및 커튼월에 적용 가능한 90분 내화벽체에 대하여 내화시험 및 성능분석을 수행 하였다. 시험 결과, 각 시험체의 요구 내화성능을 충족하는 것으로 나타났으며, 추가적으로 유한요소해석을 통한 유리벽체의 내화성능을 평가 하였으며 그 결과 1차적으로 시험체의 내화성능을 예측하는 것이 가능한 것으로 판단되었다.