In this study, to increase the strength and enhance the sintering property of Al2O3, Y2O3 and La2O3 were added; the effects of these additions on the sintering characteristics of Al2O3 were observed. Adding 1 % of Y2O3 to Al2O3 repressed the development of abnormal particles and reduced the grain boundary migration of Al2O3, curbing pores to capture particles; as such, the material showed a fine microstructure. But, when over 2% of Y2O3 was added, the sintering property was reduced because of abnormal particle grain growth and pore formation in particles. Adding 1 % of Y2O3 and La2O3 to Al2O3 led to the development of abnormal particles and formed pores in the particles; when over 3% of La2O3 was added, the sintering property was reduced because the shape of the Al2O3 particles changed to angled plates.

Poly-methylmetacrylate (PMMA) is mainly applied in the plastic manufacturing industry, but PMMA is weak and gradually got discolor. The strength of PMMA can be improved through organic-inorganic hybrid nano composites with inorganic nano particles such as, SiO2 or ZrO. However, inorganic nano particles are mostly agglomerated spontaneously. In this study, the zeta potential is controlled using different types of organic solvent with different concentrations, dispersibillity of SiO2 nano particles on the PMMA particle are analyzed. When 3 M acetic acid is used, absolute value of the zeta potential is higher, SiO2 nano particle is well attached, and dispersed on the PMMA particle surface. Results indicate that the absolute value of the zeta potential affects the stability of SiO2 dispersion.

본 연구는 고방사성해수폐액에 함유되어 있는 주요 고방사성 핵종인 Cs을 제거하기 위하여 IE911 (crystalline silicotitanate) 에 의한 흡착 제거를 수행하였다. Cs의 효율적 흡착제거 및 2차 고체폐기물의 발생량을 최소화하기 위하여 IE911-Cs 흡착 은 m/V (흡착제 질량/용액 부피) 비=2.5 g/L, 흡착시간은 1 시간 정도가 효과적이었다. 이때 Cs은 약 99%, Sr은 5% 이하가 각각 흡착되었다. 또한 IE911-Cs 흡착은 Langmuir 등온식 및 유사 (pseudo) 2차 속도 식으로 표현할 수 있으며, 흡착속도상 수(k2)는 Cs의 초기농도 및 입자크기 증가에 따라 감소하는데 반하여, m/V 비, 온도 및 교반속도 증가에 따라서는 증가하고 있다. IE911-Cs 흡착의 활성화에너지는 약 79.9 kJ/mol 로, IE911-Cs 흡착이 보다 강력한 결합 형태를 이룬 화학적 흡착임 을 보여주고 있다. 그리고 음수 값의 Gibbs 자유에너지 및 엔탈피는 IE911-Cs의 흡착반응이 정반응의 발열반응이고, 저온에 서 반응이 상대적으로 활발함을 의미하며, 음수 값의 엔트로피는 흡착된 Cs이 IE911에 균일하게 정렬되어 있음을 나타낸다.

TiO2 nanowires were grown by thermal oxidation of TiO powder in an oxygen and nitrogen gas environment at 1000 oC. The ratio of O2 to N2 in an ambient gas was changed to investigate the effect of the gas ratio on the growth of TiO2 nanowires. The oxidation process was carried out at different O2/N2 ratios of 0/100, 25/75, 50/50 and 100/0. No nanowires were formed at O2/N2 ratios of less than 25/75. When the O2/N2 ratio was 50/50, nanowires started to form. As the gas ratio increased to 100/0, the diameter and length of the nanowires increased. The X-ray diffraction pattern showed that the nanowires were TiO2 with a rutile crystallographic structure. In the XRD pattern, no peaks from the anatase and brookite structures of TiO2 were observed. The diameter of the nanowires decreased along the growth direction, and no catalytic particles were detected at the tips of the nanowires which suggests that the nanowires were grown with a vapor-solid growth mechanism.

소나무재선충병의 나무주사 방제방법은 매년 5∼6회 정도 추진하는 항공방제 및 지상방제의 문제점을 보완하며, 매개충이 산란하기 전인 후식과정에 효율적인 방제를 함으로서 밀도를 효과적으로 억제하기 위하여 추진하였다. 조사방법은 수고 2m정도의 조림지 소나무에 솔잎혹파리 나무주사로 등록된 약제 3종과 대조약제 1종을 선발하여 흉고직경당 0.5㎖을 나무주사 후 솔수염하늘소를 1본에 10개체씩 독립적으로 신초에 접종하여 망으로 씌워 살충효과를 조사하였으며, 농약 잔류기간을 조사하기 위하여 약제처리된 가지를 정기적으로 수거하여 잔류농약을 분석하였다. 조사결과 Thiamethoxam은 100% 살충에 소요되는 기간이 처리직후 5.3일, 60일차 2.4일로 우수한 살충효과를 나타내었으며, Imidacloprid, Emamectin benzoate는 처리직후와 60일차에서 100% 살충에 필요한 시간이 10일 이상으로 나타나 효과가 저조하였다. Phosphamidon의 경우 처리직후에는 100%살충에 소요되는 일수가 7.1일이 소요되어 효과가 다소 우수하였으나 60일차에서는 32.1일로 효과가 매우 감소되었다. 수체내 잔류농도는 Thiamethoxam, Imidacloprid, Emamectin benzoate는 60일 경과후에도 농도가 증가하는 경향을 보였으나, Phosphamidon은 급격히 감소하였다. 따라서 재선충 피해임지내 소나무에 살충제 나무주사를 1회 처리하여도 살충효과가 우수할 것으로 기대된다.

북방수염하늘소는 중부지방의 잣나무에 소나무재선충병을 옮기는 매개충으로 솔수염하늘소보다 피해임지내 밀도가 높아 방제가 어려운 실정이다. 이러한 북방수염하늘소의 밀도를 억제하기 위하여 감마선을 처리하여 매개충의 충태별 우화율, 부화율, 성충수명, 산란수 등을 조사하였다. 번데기 시기에 감마선 조사시 40Gy까지는 100%의 우화율을 보였으나, 50Gy부터 우화율이 88±3.3%으로 감소하기 시작하였으며, 성충수명은 20Gy처리시 75.0±4.0일이었으나 30Gy부터 33.3±4.0일로 수명이 크게 감소하기 시작하였다. 또한 총 산란수는 20Gy이상에서 대조구에 비해 50%정도의 산란수가 감소하는 경향을 보였다. 그러나 성충 시기에 감마선 조사시에는 성충수명이 40.7±7.0일에서 42.0±6.8일로 무처리의 39.9±6.2일과 비교할 때 조사선량에 관계없이 수명에 큰 영향이 없는 것으로 조사되었으며, 부화율은 50Gy에서 4.9±2.0%로 낮은 부화율을 보였고 산란수에서도 대조구의 19.0±5.5와 비교하였을 때 뚜렷한 차이가 나타나지 않았다. 따라서 번데기 시기보다 성충시기에 50Gy 감마선을 처리시 불임화 효율이 우수한 것으로 판단되었다