Aluminum nitride (AlN) nanopowders with low degree of agglomeration and uniform particle size were synthesized by carbothermal reduction of alumina and subsequent direct nitridization. Boehmite powder was homogeneously admixed with carbon black nanopowders by ball milling. The powder mixture was treated under ammonia atmosphere to synthesize AlN powder at lour temperature. The effect of process variables such as boehmite/carbon black powder ratio, reaction temperature and reaction time on the synthesis of AlN nanopowder was investigated.

In the present study, the focus is on the effect of cobalt oxide powder in the carbothermal reduction of the titanium-cobalt-oxygen based oxide powder by solid carbon for the optimizing synthesis process of ultra fine TiC/Co composite powder. The titanium-cobalt-oxygen based oxide powder was prepared by the combination of the spray drying and desalting processes using the titanium dioxide powder and cobalt nitrate as the raw materials. The titanium-cobalt-oxygen based oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under flowing argon atmosphere. Changes in the phase structure and thermal gravity of the mixture during carbothermal reduction were analysed using XRD and TGA. Titanium-cobalt-oxygen based oxide powder desalted at had a mixture of . And the one desalted at had a mixture of . In the case of the former powder, the reduction of cobalt oxide powder in the titanium-cobalt-oxygen based oxide powder occurred at lower temperature than the latter one. However, the carbothermal reduction of titanium dioxide powder in the titanium-cobalt-oxygen based oxide powder with a mixture of occurred at higher temperature than the one with a mixture of . And also, the former powder showed a lower TiC formation ability than the latter one.

650의 LiCl-LiO 용융염계에서 10 g UO/batch 규모의 장치를 이용해서 우라늄산화물의 전해환원 특성에 대한 평가를 수행하였다. 일체형 음극은 고체전극, 우라늄산화물과 우라늄산화물을 담아주는 다공성 용기(멤브레인)로 구성된다. 멤브레인 재료로는 325-mesh 스테인레스강막과 다공성 마그네시아 도가니를 사용하였다. 일체형 음극의 재질에 따른 LiCl-3 wt LiO계와 UO-LiCl-3 wt LiO계의 순환 전압측정법 결과로부터 전해환원 반웅 메커니즘을 규명하였다. 일체형 음극의 재질에 따른 우라늄산화물의 직접 및 간접 전해환원에 대한 실험을 수행하였다. 그 결과, 325-mesh스테인레스강막을 사용하여 직접 및 간접 전해환원으로 금속전환을 수행하였을 때 낮은 전류효율로 인해 우라늄산화물을 금속우라늄으로 환원시키지 못했으며, 마그네시아 다공성 도가니를 사용하여 간접 전해환원으로 금속전환을 수행하였을 때는 높은 전류효율로 인해 우라늄산화물을 금속우라늄으로 환원시킬 수 있었다

In the present study, the focus is on the analysis of carbothermal reduction of oxide powder prepared from waste WC/Co hardmetal by solid carbon under a stream of argon for the recycling of the WC/Co hard-metal. The oxide powder was prepared by the combination of the oxidation and crushing processes using the waste hardmetal as the raw material. This oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under a flowing argon atmosphere. The changes in the phase structure and gases discharge of the mixture during carbothermal reduction was analysed using XRD and gas analyzer. The oxide powder prepared from waste hardmetal has a mixture of . This oxide powder reduced at about , formed tungsten carbides at about , and then fully transformed to a mixed state of tungsten carbide (WC) and cobalt at about by solid carbon under a stream of argon. The WC/Co composite powder synthesized at for 6 hours from oxide powder of waste hardmetal has an average particle size of .

In the present study, the focus is on the analysis of carbothermal reduction of the titanium-cobalt-oxygen based oxide powder by solid carbon for the optimizing synthesis process of ultra fined TiC/Co composite powder. The titanium-cobalt-oxygen based oxide powder was prepared by the combination of the spray drying and desalting processes using the titanium dioxide powder and cobalt nitrate as the raw materials. The titanium-cobalt-oxygen based oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under a flowing argon atmosphere. The changes in the phase structure and thermal gravity of the mixture during carbothermal reduction were analysed using XRD and TGA. The synthesized titanium-cobalt-oxygen based oxide powder has a mixture of and . This oxide powder was transformed to a mixed state of titanium car-bide and cobalt by solid carbon through four steps of carbothermal reduction steps with increasing temperature; reduction of to and Co, reduction of , to the magneli phase(, n>3), reduction of the mag-neli phase(, n>3) to the (2n3) phases, and reduction and carburization of the (2n3) phases to titanium carbide.

The reduction mechanism of the composite powders mixed with and CuO has been studied by using thermogravimetry (TG), X-ray diffraction, and microstructure analyses. The composite powders were made by simple Turbula mixing, spray drying, and ball-milling in a stainless steel jar with the ball to powder ratio of 32 to 1 at 80 rpm for 1 h without process controlling agents. It is observed that all the oxide composite powders are converted to W-coated Cu composite powder after reducing treatment under hydrogen atmosphere. For the formation mechanism of W-coated Cu composite powder, the sequential reduction steps are proposed as follows: CuO contained in the ball-milled composite powder is initially reduced to Cu at the temperature range from 20 to 30. Then, powder is reduced to W via W and W at higher temperature region. Finally, the gaseous phase of formed by reaction of with water vapour migrates to previously reduced Cu and deposits on it as W reduced by hydrogen. The proposed mechanism has been proved through the model experiment which was performed by using Cu plate and powder.der.