PURPOSES : Given that large-scale repair works of expressway bridge pavements have high maintenance cost and long traffic blocking time, the thin overlay method that maintains the existing pavement is attracting attention. In this study, because the bridge thin overlay has not been introduced in Korea yet, the basic physical properties of the epoxy thin overlay, which is mainly used for the bridge thin overlay, were investigated, and the skid resistance and bond performance were analyzed. METHODS : Basic physical property tests were performed on each of the epoxy binders, aggregates, and mixtures used in epoxy thin overlay. They were also compared and reviewed against foreign standards. The epoxy binders were tested for viscosity, gel time, and thermal compatibility. The aggregates were tested in terms of water absorption, specific gravity, and gradation. The compressive and flexural strengths of the mixtures were investigated. The epoxy thin overlay has the possibility of detachment of aggregates, so the skid resistance was tested according to the paving phase. In addition, to investigate the bond performance, which is the most important performance of the epoxy thin overlay, the bond strength test was performed by varying the moisture condition and treatment condition of the existing layer surface. RESULTS : The basic physical properties of the materials used in the epoxy thin overlays satisfied foreign standards except for the gradation of aggregates. The skid resistance did not satisfy the standard when the epoxy was exposed, whereas the skid resistance did satisfy the standard when the aggregates were exposed, even after the abrasion test. The bond strength of the epoxy thin overlay satisfied the standard in all cases. The bond strength was the highest when the relative humidity of the existing layer surface was 60%. CONCLUSIONS : The materials of epoxy thin overlay that could be obtained in Korea satisfied the basic physical property standards except for aggregate gradation. Given that the aggregate gradation could be adjusted, it can be concluded that the epoxy thin overlay could be introduced in Korea. In addition, it was confirmed that the skid resistance and bond strength of the epoxy thin overlay were high enough to be used in general road conditions. It was determined that the existing layer surface should maintain an optimal relative humidity of approximately 60% because the moisture condition affects the bond strength.

최근 국내에서 토목 및 건축구조물의 노후화 및 성능저하에 따른 사회적인 우려가 발생하고 있다. 일반적으로 노후 구조물의 보수보강 방법으로는 외부 부착공법이 가장 많이 사용되고 있으며 시공 용이성을 위하여 GFRP나 CFRP Sheet나 Plate를 활용한 부착 보강방법이 활발히 적용되고 있다. 그러나 이들 방법은 온도에 취약하며 탄소섬유의 경우 경제성이 낮다는 우려가 발생한다. 본 연구에서는 친환경적이고 내열성이 상대적으로 우수한 현무암 섬유(BFRP)를 활용하여 온도변화 및 콘크리트 표면 내 균열발생에 따른 BFRP-콘크리트의 인장 부착성능 및 파괴 패턴을 실험적으로 평가하였다. 그 결과 구조물의 온도가 상승함에 따라 BFRP-콘크리트 계면의 부착성능은 약 30%정도 감소하는 것으로 나타났으며 내열성 수지를 사용한 보강재의 경우 일반 함침용 에폭시 수지보다 부착성능이 다소 우수한 것으로 평가되었다. 콘크리트 표면 내 균열 발생된 경우 균열의 폭이 증가함에 따라 부착 성능은 약 20%씩 감소하는 것으로 나타났다. 하지만 균열보수제로 보강 후 계면에서의 부착성능의 경우, 보강 전 대비 약 30% 정도의 개선효과를 나타내었다.

최근에 국내에는 다양한 원인에 의한 구조물의 안정성을 우려하는 사회적인 관심이 생겼으며 이에 따른 구조물의 보수·보강에 다양한 연구가 진행되고 있다. 우리나라는 4계절이 뚜렷하며 특히 겨울과 봄에는 일교차가 심하게 발생하는 특징이 있다. 이러한 날씨는 철근콘크리트 구조물에게 동결융해작용을 발생시켜 성능저하의 원인이 되며 구조물의 안정성을 위협할 수 있다. 현재 구조물 보수·보강 방법으로는 탄소섬유나 유리섬유로 FRP(Fiber Reinforced Polymer)를 활용하여 Plate나 Sheet 형태의 부착 보강하는 방법이 일반화 되어있다. 하지만 다소 고가이며 유리섬유는 인체에 유해하다는 연구결과가 있다. 때문에 본 연구에서는 친환경적이고 내열성이 우수한 현무암섬유(Basalt Fiber)를 활용하여 동결융해 작용에 의한 콘크리트의 성능저하를 조건으로 BFRP-콘크리트의 부착성능 및 파괴패턴을 비교 분석하였다. 동결융해시험에 따른 부착강도평가는 동일한 섬유와 수지가 함침된 BFRP를 활용하여 동결융해Cycle(0, 100, 200, 300)과 콘크리트 압축강도(24MPa, 30MPa)를 변수로 부착성능을 평가하였으 며 Case1(선 부착 후 동결융해)과 Case2(선 동결융해 후 부착)로 나누어 진행하였다. Case1과 2 모두 콘크리트 파괴의 형태를 보 였으며 Case2의 경우 Case1에 비하여 부착강도가 감소됨을 나타내었고 동결융해 Cycle이 진행될수록 콘크리트 계면의 성능은 저하되고 부착강도는 평균 약 25%정도 감소하는 것을 확인하였다.

PURPOSES : The main purpose of this study is suggest of field bond strength evaluation method for more objective evaluation method through Evaluation of Bond Strength Properties with changing aspect ratio and temperature. METHODS : The evaluation is laboratory bond strength test. Using the core machine, the pull-off test method ; the bond strength test of interface layer the universal testing machine. RESULTS: As a result of the laboratory bond strength evaluation, it was verified that the bond strength by aspect ratio decreases linearly with increasing aspect ratio and the bond strength properties by temperature change existed at high and low temperature condition relative to odinary temperature condition. CONCLUSIONS: According to the results of laboratory bond strength evaluation, the field bond strength evaluation results suggest applying the proposed correction factor (0.8, 1.0, 1.4, 1.9) according to aspect ratio(0.5, 0.1, 1.5, 2.0), For more objective evaluation of the bond strength, it is analyzed that the evaluation value is within 6 ~ 32℃ and the result can be obtained within 5% of the coefficient of variation.

PURPOSES : A geo-grid pavement, e.g., a stress-absorbing membrane interlayer (SAMI), can be applied to an asphalt-overlay method on the existing surface-pavement layer for pavement maintenance related to reflection cracking. Reflection cracking can occur when a crack in the existing surface layer influences the overlay pavement. It can reduce the pavement life cycle and adversely affect traffic safety. Moreover, a failed overlay can reduce the economic value. In this regard, the objective of this study is to evaluate the bonding properties between the rigid pavement and a SAMI by using the direct shear test and the pull-off test. The predicted fractural energy functions with the shear stress were determined from a numerical analysis of the moving average method and the polynomial regression method. METHODS : In this research, the shear and pull-off tests were performed to evaluate the properties of mixtures constructed using no interlayer, a tack-coat, and SAMI with fabric and without fabric. The lower mixture parts (describing the existing pavement) were mixed using the 25-40-8 joint cement-concrete standard. The overlay layer was constructed especially using polymer-modified stone mastic asphalt (SMA) pavement. It was composed of an SMA aggregate gradation and applied as the modified agent. The sixth polynomial regression equation and the general moving average method were utilized to estimate the interlayer shear strength. These numerical analysis methods were also used to determine the predictive models for estimating the fracture energy. RESULTS: From the direct shear test and the pull-off test results, the mixture bonded using the tack-coat (applied as the interlayer between the overlay layer and the jointed cement concrete) had the strongest shear resistance and bonding strength. In contrast, the SAMI pavement without fiber has a strong need for fractural energy at failure. CONCLUSIONS : The effects of site-reflection cracking can be determined using the same tests on cored specimens. Further, an empiricalmechanical pavement-design analysis using the finite-element method (FEM) must be done to understand the appropriate SAMI application. In this regard, the FEM application analysis and bonding property tests using cored specimens from public roads will be conducted in further research.

서 론 빠른 경제성장과 함께 <2016년 국토교통부> 자동차 등록대수는 2180만을 돌파하였다. 이처럼 많은 차량들이 도로를 사용하게 됨에 따라 기존의 아스팔트도로와 콘크리트도로가 많이 노후와 되어있는 추세이며, 이에 도로의 유지.보수 관리의 중요성이 높아지게 되었으며, 유지.보수간에 가장 많이 사용되는 공법 중에 하나인 덧씌우기 공법에 사용하는 택코트의 성능을 검토하기 위해 수행되었다. 실험 방법 및 사용재료 2.1 사용재료 실험에 사용된 택코트는 일반적으로 사용되어지는 RSC-4와 택코트 필름을 사용하였으며, 부착강도를 측정하기 위해 양생시간을 동일하게 하여 Pull of test를 통해 부착강도를 측정하였다. 2.2 실험 방법 휨몰드와 마샬 몰드를 사용하여 각각 택코트 RSC-4와 필름을 사용하여 공시체를 제작하였다. 1층 다짐 후 24시간 양생 후 2차 다짐을 한 후에 48시간 부착강도를 측정하였다. 그림1은 본 실험에 사용된 시편의 제작과정이며, 그림2는 부착강도 테스트 후의 모습이다. 결과 및 고찰 3.1 동일한 양생조건에서 콘크리트 위에 부착한 택코트 종류에 따른 부착강도 그림4은 휠트래킹 몰드로 만든 콘크리트에 부착한 택코트 종류에 따른 부착강도를 나타낸 그래프이다. 3.2 동일한 양생조건에서 아스팔트 위에 부착한 택코트 종류에 따른 부착강도 그림 5는 마샬 몰드로 만든 아스팔트 공시체 위에 부착한 택코트 종류에 따른 부착강도를 나타낸 그래프이다. RSC-4의 경우에는 살포 후 30분간 상온양생을 실시하였다 결 론 일반적으로 사용되어지고 있는 택코트 인 RSC-4의 경우 유화아스팔트라는 성질 때문에 충분한 양생이 필요하여 공기가 늘어나게 되어 실제 현장에서 규정에 맞게 사용하기가 힘든 실정이다. 도로 유지.관리 공법중 하나인 덧씌우기 공법에 사용되는 택코트의 종류와 부착하는 재료에 따른 부착 강도평가 실험결과는 다음과 같다. 1) 콘크리트 위에 각각 RSC-4와 택코트 필름을 부착하여 Pull-off-test 장비를 이용하여 부착강도를 평가한 결과 각각 0.77, 0.76 으로 비슷한 결과를 나타냈다. 2) 아스팔트에 부착한 RSC-4와 택코트 필름을 부착하여 부착강도를 평가했을때와 비슷한 경향을 나타냈다. 각각 1.241, 1.304로 택코트 필름과 보호필름을 사용한 쪽이 더 높게 나타났다. 이는 공사기간을 단축시킬 수 있을 뿐만 아니라 트래피커빌리티를 고려하였을 때 택코트 필름과 보호 필름을 사용하여 더 효율적으로 유지.보수를 할 수 있을 것으로 판단된다

HYB(FRP Hybrid Bar) is composite structural material that combines reinforced bar and FRP. HYB has high elastic modulus and after-yield-hardening properties, despite its corrosion resistance and light weight. HYB under development has relatively stable corrosion durability. This study performs fundamental experiments for the long period UV exposed HYB, and carries out pull-out test for the freezing-thawing exposed specimens of ordinary reinforced bar, HYB, and UV exposed HYB. The effect of UV exposure and freezing-thawing did not affect the tensile property and strength of HYB. However, the bond strength reduction on the environment of accelerated corrosion should be considered in further study.

노후 콘크리트의 보수 방법에는 교량상판의 덧씌우기나 노후된 도로의 보수처럼 바닥판 또는 기존 콘 크리트를 보호함과 동시에 공용기간 중 콘크리트의 내구성 증진을 위하여 복합 구조체로 형성된 접착식 콘크리트 덧씌우기 포장이 일반적으로 사용되고 있으며, 이와 같은 복합 구조체는 신･구 콘크리트 간 부 착력에 따라 공용 중 차량하중, 환경하중 하에서 일체화된 역학적 거동과 장기공용성 확보에 커다란 영향 을 받게 된다. 이처럼 공용성 확보를 위한 중요인자인 부착강도를 평가하는 대표적 시험방법으로는 쪼갬 인장시험, 경사전단시험, Pull-out시험 및 니플 파이프 직접인장시험 등 다양한 시험법으로 사용되고 있 으나, 실내시험에 국한된다는 한계성을 지니고 있어 실내 및 현장평가에 동시 적용이 가능한 직접인발 시 험법이 가장 널리 사용되고 있다. 직접인발 시험법에 있어 실내 부착강도 평가의 경우 KS F 2762 「콘크 리트 보수보호재의 접착 강도 시험방법」을 준용하고 있으나, 현장 부착강도 평가의 경우는 유일하게 한국 도로공사에서 시행하고 있는 품질성능평가(QPI)에 의거하여 시행되고 있다. 실내 부착강도 시험에서는 규정된 밑판과 시험체를 사용할 경우 세장비(포설두께/코어직경)를 일정하게 유지하여 정량적 평가를 할 수 있으나, 구조물에 대한 유지보수공사 시 열화정도 및 구조물 특성 상 포설두께를 전 구간에 걸쳐 일정 하게 유지할 수 없어 현장 부착강도 평가 시 실내와 달리 세장비를 일정하게 유지하는 것이 어려운 실정 이다. 압축강도 및 인장강도의 경우 많은 연구를 통하여 시편의 세장비에 따른 강도변화와 이를 보정하기 위한 보정계수가 제안되어 사용되고 있으나 현장 부착강도의 경우 세장비의 편차가 압축강도 및 인장강도 시편보다 매우 큼에도 불구하고 현장 부착강도 시편의 세장비 차이에 따른 영향을 고려하지 못하고 있는 실정이다. 따라서 본 연구에서는 압축강도 및 인장강도에서와 같이 시편의 세장비가 부착강도에 미치는 영향을 분석하고자 실내 및 현장 부착강도를 다양한 조건하에 실시하였으며 이를 통해 부착강도 평가 시 세장비에 따른 보정계수를 도출하고자 하였다. 세장비 효과 및 보정계수를 산출하기 위하여, 실내 부착강도 시험법의 포설두께 및 코어직경을 표준비 율(1.0)로 선정하여 세장비 0.5, 1.0, 1.5, 2.0 등 총 4가지 변수에 대한 시험을 진행하였다.