PURPOSES : The purpose of this study is to evaluate the durability of ternary blended concrete mixtures adding ultra fine admixture. METHODS : From the literature review, crack was considered as the main distress failure criterion on concrete bridge deck pavement. To reduce the initial crack development due to drying shrinkage, CSA expansion agent and shrink reduction agent were used to ternary blended concrete mixtures as a admixture. Laboratory tests including chloride ion penetration test, surface scaling test, rapid freeze & thaw resistance test, non restrained drying shrinkage and restrained drying shrinkage test were conducted to verify the durability of ternary blended concrete mixtures. RESULTS : Based on the test results, proposed mixtures were verified as high qualified durable materials. Expecially initial drying shrinkage crack was not occurred in ternary blended concrete mixtures with CSA expansion agent. CONCLUSIONS : It is concluded that the durability of proposed ternary blend concrete mixture was acceptable to apply for the concrete bridge deck pavement.

PURPOSES : This study is to evaluate ASR(alkali silica reactivity) resistance of ternary blended binder adding ultra fine mineral admixture. METHODS : This study analyzes ASR expansion using ASTM C 1260 and 1567. RESULTS : This study showed that the fineness of mineral admixture had no effect on ASR expansion. The expansion of ternary blended binder(UFFA 20%+FGGBS 10%) were below 0.1%, and this binder met the ASR standard. Also when adding the CSA expansion agent, ASR expansion slightly decreased. The expansion of latex modified mixture increased by 80% comparing plain mixture. CONCLUSIONS : Ternary blended binder met the ASR standard, and this binder is available in concrete bridge deck overlay.

일반적으로 교량 슬래브는 구조용 콘크리트로 구체를 시공하고 난 후 교면포장용 콘크리트로 포장공사를 실시하여 완성한다. 교면포장은 교통하중과 환경하중에 저항할 수 있도록 적절한 강도와 내구성을 가지는 재료로 시공되어야 한다. 현재 국내에서 적용되고 있는 교면포장용 콘크리트에는 합성고무 라텍스 수지를 첨가한 콘크리트 (Latex Modified Concrete)와 실리카흄을 첨가한 콘크리트가 있으며, 이들 콘크리트는 일반콘크리트에 비해 내구성을 향상시킨 고내구성 교면포장용 콘크리트로 분류되나, 고가의 재료로 경제성을 저하시키는 요인이 있다. 기존의 고내구성 콘크리트보다 경제적 효율을 강화하고, 콘크리트의 내구성을 향상을 통해, 궁극적으로 콘크리트 교면 포장의 공용성능을 향상시키고자 고분말도 플라이애시와 슬래그를 첨가한 교면포장용 삼성분계 시멘트 콘크리트의 최적배합을 도출하고, 이에 대한 실내 내구성을 평가하고자 한다. 콘크리트 교면포장에서 발생되는 파손 중 가장 많은 부분을 차지하는 것이 균열이며, 그 주요한 원인이 콘크리트 수축에 의한 것이다. 이에 교면포장의 내구성능 조건을 만족시키기 위해 고분말도 혼화재를, 수축균열 억제를 위해 팽창제와 수축저감제를 검토하였다. 실내 내구성 평가를 위해 재령별 압축강도시험과 수축에 대한 검토를 위해 자기수축시험을 진행하였다. 또한 내구성 평가를 위해 동결융해저항성시험, 표면박리 시험을 진행 하였다. 표. 1은 고분말도 플라이애시와 슬래그로 치환한 삼성분계 시멘트 콘크리트에 팽창제와 수축저감제를 비율에 따라 첨가한 배합비이며, 비교배합으로 포틀랜드시멘트만 사용한 배합을 통해 결과를 비교하였다. 압축강도 시험결과 삼성분계 시멘트 콘크리트는 재령 90일에 60MPa이상을 나타내었으며, 팽창제 치환율에 따라 감소하였으나, 충분한 강도를 확보하였다. 자기수축 시험결과 팽창제 치환율의 증가에 따라 자기수축 거동이 환화되며, 치환율이 8%에서 12%로 증가 시 오히려 팽창거동이 전환되는 특성을 보였으며, 수축저감제를 사용 시 수축보상측면에서 유리하였다. 동결융해저항성 시험결과 C5S1배합을 제외한 모든 배합에서 상대동탄성계수가 90%이상 나타났으며, 표면박리저항성 시험결과 모든 배합에서 Boras Method 기준 “Acceptable”등급이상, ASTM기준 2등급이상을 나타내어 적정한 저항성을 확보한 것으로 평가되었다.

Furnace slag powder used currently in Korea needs to add special functions in response to the increase of large-scale projects. In addition, it is advantageous in that it has a lower hydration heat emission rate than ordinary Portland cement and improves properies such as the inhibition of alkali aggregate reaction, watertightness, salt proofness, seawater resistance and chemical reslstance. However, furnace slag powder is not self-hardening, and requires activators such as alkali for hydration. Accordingly, if recycled fine aggregate, from which calcíum hydroxide is generated, and furnace slag, which requires alkali stimulation, are used together they play mutually complementary roles, so we expect to use the mixture as a resource-recycling construction material. Thus the present study purposed to examine the properties and characteristics of furnace slag powder and recycled aggregate, to manufacture recycled fine aggregate mortar using furnace slag and analyze its performance based on the results of an experiment, to provide materials on mortar using furnace slag as a cement additive and recycled fine aggregate as a substitute of aggregate, and ultimately to provide basic materials on the manufacturing of resource-recycled construction materials using binder and fine aggregate as recycled resources.

고분말도 슬래그를 사용할 경우 초기재령에서의 강도발현은 우수하나 수화열 및 품질관리에 따른 문제가 발생하기 쉽다. 본 연구 에서는 3000급 저분말도의 고로슬래그 미분말을 혼입한 콘크리트의 강도특성 및 내구특성을 분석하였다. 작업성을 기준으로 3가지 배합을 고려하였으며, 압축강도와 내구특성시험이 수행되었다. 강도특성 결과 3000급 슬래그를 혼입한 콘크리트는 28일 재령에서 OPC(Ordinary Portland Cement) 배합 대비 강도가 떨어지지만 장기재령에서는 잠재수경성의 촉진으로 인하여 큰 차이가 나타나지 않았다. 탄산화 및 동결융해 실험에서는 4200급 슬래그 배합 대비 약간 우수한 저항성능이 나타났는데, 이는 동일 슬럼프를 목표로 배합을 진행하여 3000급 슬래그 배합에 단위수량을 적게 고려하였기 때문이다. 장기재령의 경우, 3000급 슬래그 배합의 염화물확산계수는 OPC 배합 대비20% 수준으로 감소하여 우수한 내염해특성이 평가되었다. 단위수량을 조정하고 3000급 저분말도의 고로슬래그 미분말을 혼입하여 사용할 경우, 기존 분말도의 슬래그가 사용된 콘크리트 및 OPC 콘크리트와 비교시 우수한 작업성능과 내구특성을 확보할 수 있을 것으로 판단된다.

This research and development analysis provides numerical analysis techniques that can be used conveniently to determining the safety of the current state and to predict the stability in the future. It also seeks to present algorithms of back analysis to develop unified management system for control, prediction, coordination, and information modeling that can reasonably handle appropriate responses to structural behavior at project sites and design changes.

시멘트 산업은 탄소배출 감축을 위한 주요 산업분야로 고려되고 있으며, 콘크리트 분야에서 시멘트 사용량 저감을 위한 노력이 진행되고 있다. 이에 대한 노력의 일환으로 시멘트의 일부를 대체하여 사용할 수 있는 산업부산물을 다량으로 활용하기 위한 연구가 진행되고 있다. 산업부산물을 사용한 콘크리트는 내구성, 친환경성 및 경제성 등의 장점을 가지고 있으나, 응결시간 지연, 초기강도 저하 등의 문제점이 있다. 따라서 이 연구에서는 시멘트의 사용량을 줄이고 산업부산물인 플라이애시를 치환하여 사용하면서도 초기강도가 저하되는 문제점을 해결하는 것을 목표로 하였다. 이에 따라, 먼저 고분말도 시멘트 사용에 의한 수화반응 촉진으로 양생온도에 관계없이 모든 재령에서 강도가 증진되는 것을 확인하였다. 이어서 고분말도 시멘트에 플라이애시를 치환하여 강도발현 특성을 검토한 결과, 초기 재령에서도 보통 포틀랜드 시멘트와 비교하여 동등 이상의 강도 발현이 가능하였다. 또한, 플라이애시를 30%까지 치환하여도 수직․수평부재 거푸집 해체 시기를 단축할 수 있는 것을 확인하였다.

최근 온실가스 감축을 위해 시멘트 클링커를 대체하여 고로슬래그 미분말을 다량 치환한 하이볼륨 슬래그 시멘트에 대한 연구 활 발히 진행되고 있다. 하지만, 수화열 및 내구성 등 다양한 장점에도 불구하고 초기 재령에서의 낮은 강도 발현 등의 문제점으로 인해 실제 현장 의 적용에 한계점을 가지고 있다. 본 연구는 이러한 점을 극복하고자 GGBFS 혼입률에 따른 페이스트의 압축강도, 수화열 등의 특성을 분석하 였다. GGBS 분말도에 따른 4종류와 치환율 35%, 50%, 65%, 80% 4수준으로 하여 총 16개의 배합에 대해 실험을 수행하였다. 실험결과 낮은 물-바인더 비에 의한 고성능 하이볼륨 슬래그 시멘트 페이스트 배합은 초기 재령에서의 낮은 압축강도의 한계점을 극복할 수 있을 것으로 판단된 다. 또한 GGBS의 분말도는 고성능 하이볼륨 슬래그 시멘트 페이스트의 초기 재령에서의 압축강도 증진에는 효과가 있지만, 28일 이후의 장기 강도에는 큰 영향이 없는 것으로 나타났다.

In this paper, analyzed the effect on repair mortar by anhydrite blain, by observing workability.

The purpose of this study is to analyse the hydration reaction of paste according to fineness of non-cement binder, as a basic for the development of non-cement concrete block. As the fineness of binder increased, compressive strength of paste increased, and C-S-H gel was produced actively.

This study was performed an evaluation of physical & mechanical properties of mortar by Non-Sintered binder of ball milling time according to fineness.