Graphite was diffusion-bonded by hot-pressing to W-25Re alloy using a Ti interlayer. For the joining, a uniaxial pressure of 25 MPa was applied at 1600 oC for 2 hrs in an argon atmosphere with a heating rate of 10 oC min−1. The interfacial microstructure and elemental distribution of the W-25Re/Ti/Graphite joints were analyzed by scanning electron microscopy (SEM). Hot-pressed joints appeared to form a stable interlayer without any micro-cracking, pores, or defects. To investigate the high-temperature stability of the W-25Re/Ti/Graphite joint, an oxy-acetylene torch test was conducted for 30 seconds with oxygen and acetylene at a 1.3:1 ratio. Cross-sectional analysis of the joint was performed to compare the thickness of the oxide layer and its chemical composition. The thickness of W-25Re changed from 250 to 20 μm. In the elemental analysis, a high fraction of rhenium was detected at the surface oxidation layer of W-25Re, while the W-25Re matrix was found to maintain the initial weight ratio. Tungsten was first reacted with oxygen at a torch temperature over 2500 oC to form a tungsten oxide layer on the surface of W-25Re. Then, the remaining rhenium was subsequently reacted with oxygen to form rhenium oxide. The interfacial microstructure of the Ti-containing interlayer was stable after the torch test at a temperature over 2500 oC.

티타늄은 표면에 형성되는 보호성 부동태 피막 때문에 일반부식과 해수에서 내식성이 강하지만 염산, 황산, 인산 등의 산에서는 보호성 산화물 피막이 파괴된다고 알려져 있다. 본 연구에서는 Ti에 Al 및 V등을 첨가한 α+β계에 대하여 1066℃와 966℃에서 5시간 용체화 열처리를 실시하고, 이 시편을 550℃, 600℃, 및 650℃에서 각각 1시간, 4시간, 8시간 및 16시간 시효열처리한 후 마이크로비커스 경도를 측정하고, 이 시편을 1N H₂SO₄ 용액에서 전기화학적 분극법으로 부식을 계측하였으며, 분극을 마친 시편의 표면을 현미경 조직사진으로 부식상태를 검토하였다. 시험 결과 용체화열처리한 시편이 모재와 시효열처리한 시편보다 높은 내식성을 나타내며. 용체화 온도가 높고 시간이 길어질수록 내식성은 증가하였다.

Metastable phase characteristics of beta Ti alloys were investigated to consider the relationship of the microstructureand diffraction pattern in TEM. TEM analysis showed that the microstructure was mottled as a modulated structure, and thediffraction pattern was composed of spot streaks between the main spots of a stable beta phase with a specific latticerelationship. The modulated structure may be induced by short distance slip or atom movement during a very short intervalof solution treated and quenched (STQ) materials. The athermal ω phase, which could be precipitated at low temperature aging,is also analysed by the metastable phase. The metastable phases including athermal ω phase had a common characteristic ofhardened and brittle behavior because the dislocation slip was restricted by a super lattice effect due to short distance atommovement at the metastable state.

Alumina dispersion strengthening copper(ADSC) alloy has great potential for use in many industrial applications such as contact supports, frictional break parts, electrode materials for lead wires, and spot welding with relatively high strength and good conductivity. In this study, we investigated the oxidation behavior of ADSC alloys. These alloys were fabricated in forms of plate and round type samples by surface oxidation reaction using Cu-0.8Al, Cu-0.4Al-0.4Ti, and Cu-0.6Al-0.4Ti(wt%) alloys. The alloys were oxidized at 980 oC for 1 h, 2 h, and 4 h in ambient atmosphere. The microstructure was observed with an optical microscope(OM) and a scanning electron microscope(SEM) equipped with energy-dispersive X-ray spectroscopy(EDS). Characterization of alumina was carried out using a 200 kV field-emission transmission electron microscope(TEM). As a result, various oxides including Ti were formed in the oxidation layer, in addition to γ-alumina. The thickness of the oxidation layer increased with Ti addition to the Cu-Al alloy and with the oxidation time. The corrected diffusion equation for the plate and round type samples showed different oxidation layer thickness under the same conditions. Diffusion length of the round type specimen had a value higher than that of its plate counterpart because the oxygen concentration per unit area of the round type specimen was higher than that of the plate type specimen at the same diffusiondepth.

The effects of processing parameters on the flow behavior and microstructures were investigated in hotcompression of powder metallurgy (P/M) Ti-6Al-4V alloy. The alloy was fabricated by a blended elemental (B/E)approach and it exhibited lamellar α+β microstructure. The hot compression tests were performed in the range of tem-perature 800-1000℃ with 50℃ intervals, strain rate 10−4-10 s−1, and strain up to 0.5. At 800-950℃, continuous flowsoftening after a peak stress was observed with strain rates lower than 0.1 s−1. At strain rates higher than 1 s−1, rapiddrop in flow stress with strain hardening or broad oscillations was recorded. The processing map of P/M Ti-6Al-4V wasdesigned based on the compression test and revealed the peak efficiency at 850℃ and 0.001 s−1. As the processing tem-perature increased, the volume fraction of β phase was increased. In addition, below 950℃, the globularization of phaseat the slower strain rate and kinking microstructures were found. Based on these data, the preferred working conditionof the alloy may be in the range of 850-950℃ and strain rate of 0.001-0.01 s−1.

Zr-Ti alloy powders were successfully synthesized by magnesium thermal reduction of metal chlorides. The evaporated and mixed gasses of were injected to liquid magnesium and the chloride components were reduced by magnesium leading to the formation of . The released Zr and Ti atoms were then condensed to particle forms inside the mixture of liquid magnesium and magnesium chloride, which could be dissolved fully in post process by 1~5% HCl solution at room temperature. By the fraction-control of individually injected and gasses, the final compositions of produced alloy powders were changed in the ranges of Zr-0 wt.%~20 wt.%Ti and their purity and particle size were about 99.4% and the level of several micrometers, respectively.