PURPOSES : The objective of this study is to evaluate the mechanical properties of ternary blended cement concrete incorporated with pulverized reject ash (PRA) or pulverized fuel ash (PFA) based on a comparison with those of ordinary Portland cement (OPC) concrete. METHODS : To produce the concretes, the level of OPC replacement is set at 60%, which comprises 30%~45% ground granulate blast furnace slag and 15%~25% of fly ash (FA). The FA can be categorized into PFA, 4PRA (fineness 3,930 cm2/g3), and 8PRA (fineness 7,840 cm2/g3). The compressive strength, surface electric resistivity, initial absorption coefficient, and chloride ion penetrability of OPC and the ternary blended cement concrete are measured at predetermined periods after water curing. RESULTS : It is discovered that the mechanical properties of concrete with 8PRA are better than those of OPC concrete. The performance of 4PRA concrete is worse than that of 8PRA concrete, indicating that the fineness of the PRA can affect the mechanical properties of the ternary blended cement concrete. CONCLUSIONS : The use of PRA is feasible for the production of ternary blended cement concrete, provided that the appropriate mix design and grinding technology are used.

In this study, CO2 reduction type quaternary component high fluidity concrete was produced with more than 80%r eduction in cement quantity to increase the use of industrial by product sand enhance construction performance, there by reducing CO2 emissions. Furthermore, theq uality properties, and CO2 reduction performance of this concrete were evaluated. As a result of the quality evaluation of quaternary component blended high fluidity concrete with CO₂reduction, the target performance could be achieved with a 80% or more reduction of cement quantity by mixing a large amount of industrial byproducts. The required performance level was obtained even though the flow, mechanics, and durability characteristics decreased a little compared to conventional mix.

이 논문은 표면 차수벽형 석괴댐(Concrete-Faced Rock-Filled Dam) 콘크리트의 내구성능 개선에 관한 것이다. 댐은 영구 구조물이 며 그 중요성을 감안할 때 충분한 내구성능이 확보되어야 한다. 이 논문에서는 플라이애시와 PVA 섬유를 혼입함으로써 차수벽 콘크리트의 내 구성능을 개선하고자 하였으며, 플라이애시와 PVA 섬유 혼입율에 따른 내구성능 향상 검증을 위하여 기본물성 (강도, 소성수축, 자기수축)을 포함한 내구성능 검증 실험(염소이온 침투, 마모 저항성, 동결융해 저항성)을 수행하였다. 실험 결과, 플라이애시 15%와 PVA 섬유 0.1%를 혼 입하였을 때 내구성능 개선 효과가 뛰어난 것으로 나타났다. 검증된 차수벽 콘크리트의 현장 적용을 통해 표면 차수벽형 석괴댐의 안전성 및 내 구성 개선에 기여할 수 있을 것으로 판단된다.

The purpose of this study was to evaluate the sulfate attack of ternary blended concrete based on low-heat cement for reducing the heat of hydration. The main parameters were water-to-binder ratio and curing temperature on the matching mixtures. Test results revealed that compressive strength ratio at each age was superior to the developed mixtures than control mixtures. Whereas, the mass change ratio was superior to the control mixture at all ages.

본 논문은 강섬유의 일부를 철근집합체로 대체하여 초고강도 섬유보강 철근 콘크리트 I 형보의 연성거동을 유도하는 것을 목적으 로 한다. 강섬유와 철근집합체의 조합을 가진 초고강도 콘크리트 I 형보 대한 휨거동 실험을 수행하였다. 강섬유의 혼입률은 0%, 0.7%, 1%, 1.5%, 2%이다. 철근집합체와 PS강연선 집합체가 압축구역에서 콘크리트를 구속하기 위해 사용되었다. 철근집합체와 강연선 집합체의 길이 도 실험요소 중 하나이다. 이러한 실험요소를 조합하여 9개의 초고강도 철근 콘크리트 I 형보를 제작하였다. 강섬유 뿐만 아니라 종방향의 철근 집합체도 초고강도 철근 콘크리트 I형 보의 연성거동을 유도하는데 효과를 가지고 있다. 강섬유 혼입률 0.7% 또는 1%와 철근집합체를 사용한 조합이 I형 보의 효과적인 연성 거동을 보여주고 있다. 하중과 처짐관계 및 균열양상 등이 좁은 간격을 가진 작은 직경의 종방향 철근 집합체의 유용성을 나타내고 있다.

This study was evaluated compressive strength of age 28 days of binary blended concrete according to there type of superplasticizer and there type of w/c. In addition, we are proposed modification prediction model equation that can reflect efficiency of water reducing and influence of binders using Lyse equation to predict the compression strength through the conventional W/C.

The purpose of this study was to evaluate the shrinkage of ternary blended concrete based on low-heat cement for reducing the heat of hydration. The main parameters were water-to-binder ratio and curing temperature(5, 20, 40℃). Test results showed that the shrinkage significantly was influenced by water-to-binder ratio than binder type. The shrinkage strain of all of the mixtures was increased with increasing the curing temperature.

In this study, hydration heat analysis of ternary blended concrete using mock-up structure was conducted in order to evaluate the temperature rise and crack index. The results of the analysis of hydration heat, it was found that it was convenient to obtain the minimum crack index and temperature rise of 3:5:2 mixing.

This study evaluated the standard consistency, setting time, hydration heat, and compressive strength of binary blended cement concrete (general and high strength) using air cooled ladle furnace slag (LFS) of 3, 5, 7, 10wt.% as an admixture for ordinary portland cement (OPC). Results showed that binary blended cements using the LFS of lower than 5wt.% shortened the setting time and reinforced the compressive strength of concrete (general and high-strength) compared to OPC concretes although binary blended cements needed more water to achieve the standard consistency. This indicated that LFS could be used as a useful admixture for manufacturing binary blended cement. Thus, we expected that the upcycling of LFS would be contributed to save energy consumption and reduce the greenhouse gas emission from the field of cement industry.

This paper presents an experimental investigation in order to evaluate fresh and hardened properties of LP (Limestone Powder) blended cement concrete. The cement contents of the mixtures are replaced by LP in the range of 10%, 15%, 25%, and 35%, while a control mixture is prepared with only OPC (Ordinary Portland Cement). The fresh concrete properties like slump and air content are similar to those of control mixture up to 35% of replacement ratio of LP, however a delay in setting time is evaluated. The hardened properties including compressive strength, flexural strength, and rapid freezing and thawing resistance shows similar results of control mixture up to 15% of replacement. Relatively lower strength development is evaluated over 25% replacement of LP. For accelerated carbonation test, resistance to carbonation rapidly decreases with increasing LP replacement ratio due to the limited amount of Ca(OH)2. From the study, LP replacement under 15% can be adopted considering reduction of strength and resistance to carbonation.

콘크리트의 배합에 있어서 포졸란 물질의 사용은 수화된 시멘트내의 칼슘 실리케이트 수화물을 증가시키고 미세 공극을 채워줌으로써 콘크리트의 투수성을 감소시킨다. 또한 콘크리트 내의 전체 염기량을 낮추어 알카리 골재반응에 의한 균열의 방지에도 효과가 있다. 본 연구에서는 포졸란 물질 중 반응성이 가장 우수한 나노실리카를 사용한 콘크리트 시멘트의 미세구조를 나노압입을 이용하여 분석할 것이다. 물질 표면의 경도를 측정하여 물질의 강도 및 강성을 파악하는 방법은 금속에 대하여 100여년간 수행되어 왔다. 콘크리트의 강도를 파악하는데 있어서도 슈미트 햄머를 이용하여 콘크리트의 표면경도를 측정하고 강도와 연관 짓는 방법이 널리 사용되고 있다. 나노압입 실험은 이러한 이론적인 배경을 바탕으로 나노 스케일의 압입 시험기를 사용하여 시멘트 페이스트를 구성하고 있는 미세구조의 기계적 특성을 파악하는 방법이다. 향후 콘크리트의 동결융해 실험, 알카리 골재 반응, 프리스트레스 강선과의 접착력 실험과 연계하여 균열에 대한 높은 내구성을 요구하는 콘크리트의 제작에 최적화된 나노실리카의 배합비를 산출하기 위한 기초연구로 사용될 것이다.

In this study, the hydration characteristics of low heat concrete with respect to the binder type are investigated experimentally. According to research results, TBC(Ternary Blended Cement)1, 2 applied low heat concrete, the heat of hydration was found to be reduced and the 28 days compressive strength was superior to that of FAC(Fly Ash Cement).

When concrete is exposed to sulfate attack, ettringite is produced to cause internal expansion and crack. In this study, the sulfate resistance of remicon latex-modified concrete was compared with latex and admixture ratio. From the results, when latex content was increased, the sulfate resistance of remicon latex-modified concrete was improved.

본 연구는 초고강도콘크리트의 배합에 사용되는 3성분계 혼합시멘트의 최적조합을 도출하기 위한 실험연구이다. 3성분계 혼합시멘트는 포틀랜드시멘트, 고로슬래브 미분말 0%, 30%, 40%, 50% 및 플라이애시 0%, 10%, 20%, 30%로 구성하였다. 물결합재비 0.18의 초고강도콘크리트를 대상으로 각 실험체의 압축강도와 공극구조를 조사한 결과, 플라이애시 10%, 고로슬래그 미분말 30%를 혼합한 3성분계 혼합시멘트를 사용한 콘크리트의 압축강도는, 50nm 이상의 공극량 감소에 의해, Plain 콘크리트에 비해 현저히 증가하였다.

시멘트 대체 재료로서 플라이애쉬의 사용은 시멘트 생산비용을 절감시키는 효과를 창출하였다. 반면에 플라이애쉬 혼입콘크리트는 OPC에 비해 상대적으로 긴 양생시간과 초기강도의 발현 저하를 들 수 있어 이의 해결을 위해 물리적 방법, 온도 및 화학적 방법 등과 같은 다양한 활성화 기술의 적용을 통하여 플라이애쉬 혼입 콘크리트의 수화를 가속시킬 수 있고, 콘크리트의 부식 저항성을 향상시킬 수가 있다. 본 연구에서는 10～40%의 치환률을 가진 활성화된 플라이애쉬 시편을 통해 개방 회로형 전위측정(Open circuit potential measurement)을 수행하였고, 투수시험, 급속염화물침투시험 및 SEM(Scanning electron microscopy)촬영을 통해 OPC 콘크리트와 비교․분석 하였다. 또한, 치환률의 임계범위 20～30%의 경우에 있어서 활성화된 플라이애쉬를 사용한 콘크리트가 열화저항성에 있어서 개선효과가 나타나고 있음을 확인하였다. 또한 플라이애쉬를 화학적으로 활성화시킨 경우가 본 연구에서 수행된 다른 활성화 방법들에 비해 더욱 좋은 결과를 나타나고 있음도 확인하였다.