A drop weight impact test was conducted in this study to analyze the mechanical and thermal properties caused by the changes in the ratio of carbon fiber reinforced plastic (CFRP) to ethylene vinyl acetate (EVA) laminations. The ratios of CFRP to EVA were changed from 10:0 (pure CFRP) to 9:1, 8:2, 6:4, and 5:5 by manufacturing five different types of samples, and at the same time, the mechanical/thermal properties were analyzed with thermo-graphic images. As the ratio of the CFRP lamination was increased, in which the energy absorbance is dispersed by the fibers, it was more likely for the brittle failure mode to occur. In the cases of Type 3 through Type 5, in which the role of the EVA sheet is more prominent because it absorbs the impact energy rather than dispersing it, a clear form of puncture failure mode was observed. Based on the above results, it was found that all the observation values decreased as the EVA lamination increased compared with the CFRP lamination. The EVA lamination was thus found to have a very important role in reducing the impact. However, the strain and temperature were inversely propositional.

At modern mechanical and automotive industry, the material with light weight proceeds in order to thr environmental issue and high performance. Machine part is fastened with numbers of bolts and nuts. Generally, the metal part at mechanical structure is fastened with bolt and nut through puncturing. But it is difficult to puncture at CFRP with the property of fiber structure like the general metal. In this study, the fracture behavior is investigated by the hole and crack at the plate of the unidirectional CFRP due to ply angle. The thickness of plate is 2 mm. Two laminates with the varied ply angles are layered and eight plies are made. The hole is placed at the center of plate and the cracks with the length of 2 mm are generated on both left and right sides from the hole. The finite element program of ANSYS is carried out in order to analyze the CFRP with fiber layer. As analysis, the maximum reaction force and equivalent stress are investigated due the angle of ply. The reaction force in case of the stacking angle of 90° is shown to be greatest among all specimens.

In order to provide the basis data for broad use and safe design of carbon fiber reinforced plastic, this paper aims at investigating the fracture behavior on CFRP specimen composed of one directional fiber through three point bending test. On the basis of experimental result, the improvement of composite layer specimen can be secured with the other data to compare the existing specimen. The fracture behavior happened at the experimental procedure is investigated in this study. The maximum loads of 1200 N, 1700N and 1600N are shown respectively at the specimens with the layer angles of 30°, 45° and 60°. The highest load is shown at the layer angle of 60° among all specimens and the longest displacement is maintained until each of the layer structure is broken down. The fracture due to the force applied from the outside can be prevented by applying the result of this study to the real structure. As structural safety can be evaluated and anticipated through this study, it is thought that the safe design is devoted.

In this study, the fracture property of the bonded structure with aluminum foam is analyzed by using the closed aluminium foam for impact absorber. DCB and TDCB specimens manufactured with the single lap joint method of mode 3 are designed by varying the thickness. The static analysis through ANSYS finite element program is carried out on the specimen model due to each thickness. Also, the static experiment is performed in order to verify the analysis result. This study aims at comparing the shear strengths of the bonded structures of DCB and TDCB made with aluminum foam and investigating the mechanical properties.

In this study, the fracture behavior of a thermoplastic-modified epoxy resin reinforced with continuous carbon fibers for two levels of fiber-matrix adhesion was performed. A carbon fiber with commercial sizing was used and also treated with a known silane, (3-glycidoxy propyl trimethoxysilane) coupling agent. Toughness was determined using the double cantilever test, together with surface analysis after failure using scanning electron microscope. The presence of polysulfone particles improved the fracture behavior of the composite, but fiber-matrix adhesion seemed to play a very important role in the performance of the composite material. There appeared to be a synergy between the matrix modifier and the fibermatrix adhesion coupling agent.

본 연구에서는 수치해석을 통하여 반복하중으로 인해 곡관에 형성되는 피로균열에 대한 분석을 수행하였다. 곡관의 수치해석 모델을 개발하였으며, 균열 형성 시점과 형성 과정에 기초하여 수치해석 모델을 검증하였다. 요소에 erosion 기능을 적용하여 피로균열을 표현하고 형성 시점을 추정하고자 하였으며, 두께방향으로 다수의 요소를 배치하여 균열의 형성 과정 또한 모사하고자 하였다. 100 mm 변위에 대한 실험결과와 비교하여 균열의 형성 시점 및 형상이 잘 일치하는 것을 확인하였으며, 추가적인 다른 변위에 대한 균열의 형성 시점 또한 예측하였다. 본 모델을 사용하여 다양한 형태의 하중에 대해 해석을 수행한다면 곡관의 형상 및 특성에 따른 하중과 균열 형성시점의 관계를 예측할 수 있을 것으로 기대된다.

In this study, we numerically analyze fatigue cracks of curved pipes under cyclic loadings. Numerical models of the curved pipes are developed. The models are verified with the experimental results in terms of fatigue lives and development process of the fatigue cracks. Erosion technique is applied to the solid elements in order to describe shapes of the fatigue cracks and estimate the fatigue lives. Also, development of the fatigue cracks is described by allocating sufficient number of solid elements in the radial direction. Fatigue lives and shapes of the crack resulting from numerical analyses show good agreement with those of the experiment considering ±100mm displacement. In addition, estimation of the fatigue life caused by displacement with different magnitude is conducted. We expect that the model can be applied to understand the relation between fatigue lives and characteristics of pipes or loadings.

As CFRP with only a single material shows the various fracture properties, it has been applied to the many areas through the whole industry. The method bonding with adhesive has been recommended to apply the CFRP to structure. But it is inevitable that the mechanical joints with bolt, nut and rivet have been used sometimes. This study investigates the effect that these joints influence the CFRP panel through the analysis result. The analysis models as CFRP panels with the thickness of 5 mm have four kinds of layer angles which are 30°, 45°, 60° and 75°. The fracture property is examined when the pressure by the mechanical joint is applied to the upper panel. As the joint pressure is distributed most effectively in case of the layer angle of 60°, it is shown that this pressure becomes lower and the deformation of panel becomes lowest. On the basis of this study result, it is thought that the foundation data for the design of CFRP structure can be provided and contributed to the safety design of structure.

As a part of light weight, the adhesive has been applied to joint the mechanical structure. The porous material is used with aluminum foam in case of the structure bonded with only adhesive. In order to confirm the durability, it is necessary to investigate the fracture toughness at the bonded joint. So, the fracture property at joint interface of aluminum foam different from the non-porous material becomes especially important. In this study, the tapered double cantilever beams(TDCB) with the type of mode Ⅲ are manufactured with aluminum foam. The fracture toughness at the joint of the structure bonded with only a adhesive can be obtained. The static analyses are carried out and verified the results by the experiment. As the results of static analyses, the reaction forces ranged from 0.30 to 0.41 kN at all specimens are shown when the forced displacements are proceeded as much as 7 to 9 mm. As the results of analyses and experiments are compared with each other, there is a little bit of difference between these results. Through the result of this study, the mechanical properties at TDCB specimens with the type of mode Ⅲ can be understood.

As CFRP with only a single material shows the various fracture properties, it has been applied to the many areas through the whole industry. The method bonding with adhesive has been recommended to apply the CFRP to structure. But it is inevitable that the mechanical joints with bolt, nut and rivet have been used sometimes. This study investigates the effect that these joints influence the CFRP panel through the analysis result. The analysis models as CFRP panels with the thickness of 5 mm have four kinds of layer angles which are 30°, 45°, 60° and 75°. The fracture property is examined when the pressure by the mechanical joint is applied to the upper panel. As the joint pressure is distributed most effectively in case of the layer angle of 60°, it is shown that this pressure becomes lower and the deformation of panel becomes lowest. On the basis of this study result, it is thought that the foundation data for the design of CFRP structure can be provided and contributed to the safety design of structure.

In this study, the fracture property of impact absorption is investigated using the carbon fiber composite material. And this property is compared with the carbon fiber composite material with aluminum foam. Carbon fiber composite material has the high specific strength and rigidity and the superior durability and fatigue life and light weight. On the ground of these properties, this material has been used widely at the fields of airplane, national defence industry, vehicle and the various industrial areas. Aluminum foam can also be applied at the various areas as it is the material with the superior properties. And this foam is the material which can solve the problem on the light weight of particular product. At the condition of the impact energy of 20J, the maximum loads of CFRP sandwich composite and CFRP sandwich composite with aluminum foam core are shown to be 5.7 kN and 6.5 kN respectively. In case of maximum energies, these values are shown to be 19 J and 17.5 J respectively. At the impact energy of 50 J, the maximum loads of CFRP sandwich composite and CFRP sandwich composite with aluminum foam core are shown to be 7 kN and 8.8 kN respectively. In case of maximum energies, these values are shown to be 43 J and 48 J respectively. At the impact energy of 80 J, the maximum loads of CFRP sandwich composite and CFRP sandwich composite with aluminum foam core are shown to be 9.2 kN and 11 kN respectively. In case of maximum energies, these values are shown to be 70 J and 63 J respectively. As the result of this study, the mechanical properties are investigated through the impact experiments on the composites composed of the closed aluminum foam and the carbon fiber reinforced plastic used frequently as absorbents.

Because aluminum foam is porous material, the frature property is different from that of non-porous material. This aluminum foam can be used with the joint bonded with adhesive in order to utilize the light weight to the maximum. So, the study of fracture property on bonded surface can be important. In this study, the analyses on the specimens with two kinds of configuration as DCB(Double Cantilever Beams) and TDCB(Tapered Double Cantilever Beams) aluminum foams of mode Ⅲ type bonded with adhesive are carried out and compared with each other. And the fracture properties the adhesive surfaces of the structure with bonded aluminum foams are studied as the static experiments on these verifications are done. DCB and TDCB specimens used in this study have the variable of thickness(t) as 35mm, 45mm and 55mm. As the result of this study, the range of reaction forces are 0.3 to 0.8 kN and 0.5 to 1.2 kN at DCB and TDCB specimens respectively. The results of the static experiments can also be confirmed with these similar results. These study results can be obtained by only a simulation without the special experimental procedures. The mechanical properties of the bonded structures composed of DCB and TDCB aluminum foams with mode Ⅲ type can be thought to be analyzed effectively.

Nowadays, the study of CFRP reinforced with carbon fiber is focused on improving the the mechanical property. The study on the fracture data of CFRP are not properly made out than that of the general mechanical joint. In this study, the fracture property of mode 1 at the same condition of tensile experiment is investigated by applying the layer angle to laminated CFRP with the thickness of 15 mm. When the reaction forces until dropping out the bonded surface are compared with the cases of the layer angles of 0°, 45° and 60°, the reaction force is shown to be most and the elapsed time until dropping out the bonded surface is longest at that of 45°. The deformation energy is also shown to have the highest value by dropping out the adhesive interface. As the basis of the analysis result of this study, the most safety with fracture resistance is shown in the case of 45°. the bonded structure applying the appropriate layer angle is thought to have the structural safety.

The fatigue strength of a nickel-base superalloy was studied. Stress-controlled fatigue tests were carried out at 700 oC and 5 Hz using triangular wave forms. In this study, two kinds of testing procedures were adopted. One is the conventional tension-zero fatigue test(R = 0). The other was a procedure in which the maximum stress was held at 1000 MPa and the minimum stress was diverse from zero to 1000 MPa at 24 and 700 oC. The results of the fatigue tests at 700 oC indicate that the fracture mechanism changed according to both the mean stress and the stress range. At a higher stress range, γ ' precipitates are sheared by a/2<110> dislocation pairs coupled by APB. Therefore, in a large stress range, the deformation occurred by shearing of γ ' by a/2<110> dislocations, which brought about crystallographic shear fracture. As the stress range was decreased, the fracture mode gradually changed from crystallographic shear fracture to gradual growth of fatigue cracks. At an intermediate stress range, as it became more difficult for a/2<110> dislocation pairs to shear γ ' particles, cracks started to propagate in the matrix, avoiding the harder γ ' particles. High mean stress induced creep deformation, that is, γ ' particles were sheared by {111}<112> slip systems, which led to the formation of stacking faults in the precipitates. Thus, the change in fracture mechanism brought about the inversion of the S-N curves.

As a part of light weight, the adhesive has been applied to joint the mechanical structure. The porous material is used with aluminum foam in case of the structure bonded with only adhesive. In order to confirm the durability, it is necessary to investigate the fracture toughness at the bonded joint. So, the fracture property at joint interface of aluminum foam different from the non-porous material becomes especially important. In this study, the static facture analysis was carried out with DCB specimen bonded with adhesive as the loading type of mode Ⅲ. The thicknesses of specimens are 35, 45 and 55 mm. When the forced displacements 5 mm applied on the specimen proceed at specimen thicknesses of 35, 45 and 55 mm, the maximum stresses is shown to be happened at the range from 3.3 MPa to 3.6 MPa. The maximum equivalent stress happened at the specimen thickness of 35mm becomes highest among four kinds of specimens. The static experiment is carried on in order to verify these analyses representatively. As the experimental data become similar with the simulation data, it is thought that these analysis data can be applied at analyzing them into the adhesive joint of real porous material.

Bone fractures are most often seen in racetrack horses because of the high level of intensity in racing. These issues are the main cause of decreased performance in racehorses. Mesenchymal stem cells (MSCs) have been explored to improve intra-articular therapy in racehorses. MSCs are essential for the repair and regeneration of damaged tissues. In this study, the effect of intra-articular injection of MSCs in racehorses was investigated. Before accessing the MSC therapy, synovial fluids were obtained from the fracture site of racehorses, and adipose tissue was collected for MSC isolation. Using the MSC specific marker, adipose tissue-derived MSCs were identified. The racehorses received intra-articular injection of autologous MSCs (or allogeneic) (3 × 107 cells/3 mL). After 1 or 2 weeks, synovial fluids were collected from racehorses. To test the effect of MSC injection using ELISA, we analyzed inflammatory factors from the untreated samples compared to MSC-treated samples of racehorses. The level of pro-inflammatory factors (interleukin-1β and prostaglandin E2) was significantly decreased in synovial fluids of MSC-injected racehorses, compared to before accessing the MSC therapy, whereas, the level of anti-inflammatory factor (interleukin-10) was higher than prior to accessing the MSC therapy. Further studies are needed to investigate the anti-inflammatory mechanism of MSC in racehorses.

The present study is undertaken to evaluate the effect of volume fraction on the results of Charpy impact test for the rubber matrix filled with nano sized silica particles composites. The Charpy impact tests are conducted in the temperature range 0°C and –10°C. The range of volume fraction of silica particles tested are between 11% to 25%. The critical energy release rate GIC of the rubber matrix composites filled with nano sized silica particles is affected by silica volume fraction and it is shown that the value of GIC decreases as volume fraction increases. In regions close to the initial crack tip, fracture processes such as matrix deformation, silica particle debonding and delamination, and/or pull out between particles and matrix which is ascertained by SEM photographs of Charpy impact fracture surfaces.

An aluminum foam is the super light metal which can be adjusted with the adhesive by using the joint method. In this study, the tapered double cantilever beams(TDCB) with the type of mode Ⅲ are manufactured with aluminum foam. The fracture toughness at the joint of the structure bonded with only a adhesive can be obtained. The static analyses are carried out and verified the results by the experiment. As the results of static analyses, the reaction forces ranged from 0.30 to 0.41 kN at all specimens are shown when the forced displacements are proceeded as much as 8 to 9 mm. The tapered double cantilever specimen for mode Ⅲ with the thickness of 55 mm is carried out by the static experiment representatively to verify the analysis results. As the results of analyses and experiments are compared with each other, there is a little bit of difference between these results. So, the simulation results of this study can be thought to be confirmed. It is thought that even the only analysis data omitting the extra experimental procedure can be verified in order to use the data practically. Through the result of this study, the mechanical properties at TDCB specimens with the type of mode Ⅲ can be understood.