This study was carried out to investigate the proper wattage and installation distance for the efficient use of nano-carbon fiber infrared heating lamp (NCFIHL), a heating device advantageous for heating energy saving, when the production of watermelon plug seedlings in the plug seedling nursery in winter season. Six small beds were divided into plastic film, and 700 W and 900 W nano-carbon fiber infrared heating lamps were installed at 100 cm above the bed. 1 lamp at central (control), 60 cm interval (2 lamps), and 40 cm interval (3 lamps) heating lamps were installed in each bed inside the greenhouse. All treatments, except the control, were set to keep the night air temperature at 20℃ after lighting the NCFIHL. The leaf temperature showed a tendency to increase fast as the install distance was narrow. The leaf length and leaf width tended to increase as the installation distance of the 700 W heating lamp was narrow. The compactness was high in 700 W heating lamp with 40 cm of installation distance. Therefore, in consideration of maintaining the set temperature at night, installing 700 W electric lamps at 40 cm was an efficient power and installation distance for watermelon grafted seedlings considering economic feasibility.

본 연구는 나노섬유를 제조하는데 빠르고 효과적인 전기방사법을 이용하여 PVA(Polyvinyl alcohol)와 AgNO3를 혼합하여 제조한 용액을 금속산화물 기반 나노 섬유로 이루어진 투명 전극을 제조하고 그 특성을 분석하였다. PVA/AgNO3 혼합 용액을 전기방사법을 이용하여 유리기판 위에 나노 섬유 구조체 형태로 방사하여 250 ℃에서 2 시간 동안 열처리 과정을 통해 전기 전도성이 향상된 은 나노 섬유 기반 투명 전극을 제조하였다. 제조된 투명전극은 four-point probe 장비를 이용하여 전기적 특성을 분석하였으며, UV - Vis spectrophotometer 를 이용하여 제조된 투명전극의 투과도를 확인하였다. 또한, Scanning Electron Microscopy (SEM)과 Energy Dispersive Spectrometer(EDS)를 통해 은 나노 섬유의 표면 특성과 성분을 확인하였다. 이러한 분석들을 통해, 전기 방사 시간에 따른 면 저항과 투과도의 최적화된 조건을 확인할 수 있었으며, 은 나노 섬유로 이루어진 투명 전극은 전기적, 광학적, 기계적 특성이 우수하여 태양전지, 디스플레이, 터치스크린과 같은 차세대 유연 디스플레이에 적용 가능성을 보여주었다.

본 연구에서는 다공성 Polyacrylonitrile (PAN) 중공사막을 지지체막으로 하여 Poly styrene sulfonic acid (PSSA) 와 polyethyleneimine (PEI)을 이용하여 layer-by-layer법으로 선택층을 형성시켰다. 코팅용액에 Mg염을 첨가하여 염석법(salting out method)을 이용하였다. 코팅용액의 이온세기, 고분자 농도, 코팅시간 등을 달리하여 나노여과막을 제조하였으며 NaCl, MgCl2, CaSO4 100 mg/L를 공급액으로 하여 2 atm의 구동 압력에서 투과도와 염 배제율을 평가하였다. PSSA 20,000 ppm, 코팅시간 3분, 이온세기 1.0, PEI 30,000 ppm, 코팅시간 1분, 이온세기 0.1의 조건으로 코팅한 막이 가장 우수한 성능을 보여 주었다. 100 ppm의 NaCl, MgCl2, CaSO4 공급액에서 각각 20.4, 19.4, 18.7 LMH의 투과도와 67, 90, 66.6%의 염 배제율을 나타내었다.

본 연구에서는 한외여과 polysulfone (PSf) 중공사막에 첨가제를 섞는 방법을 통해 친수성 증가에 따른 분리막 특성 및 성능을 향상하고자 하였다. 15 nm 크기의 fumed silica (FS)를 0.1, 0.3, 0.5 wt%로 방사 용액에 분산시켜 혼합 매트릭스 분리막을 제조하였다. 단면 및 표면상태를 확인하기 위해 SEM 분석을 진행하였으며, FS가 함유될수록 중공사막의 평균 기공 반경이 4 nm 이상 증가하는 것을 확인하였다. 또한, 분리막의 친수성 분석을 위해 접촉각 측정을 진행하였으며, FS 함유로 분리막의 친수성이 높아진 것을 확인하였다. 수투과도의 경우 FS가 섞인 분리막은 91~96 LMH 수준을 보였으며 PSf 분리막보다 5~11%의 증가율을 보였다. 내오염성 평가에서도 친수도가 상승한 FS 혼합 중공사막 표면에 소수성을 띄는 BSA가 흡착되지 못하여 상대 유량 감소율이 PSf 단일막 보다 낮아졌음을 확인하였다.

본 연구에서는 polyvinylidene fluoride (PVDF) 중공사막을 지지체로 한 저압용 나노복합막을 제조하였다. Poly styrene sulfonic acid (PSSA)와 polyethyleneimine (PEI)을 layer-by-layer 및 염석 효과 방식으로 지지체막에 코팅하였다. 막의 투과도와 염 배제율 성능을 알아보고자 NaCl, MgCl2, CaSO4 100 mg/L수용액을 1 L/min의 유량으로, 2 bar의 압력을 상온에서 가해주었다. 20,000 ppm의 PSSA (이온세기 1.0)용액에 3분, 30,000 ppm (이온세기 0.1)용액에 1분 코팅한 막이 가장 우수하였다. 투과도와 염 배제율은 NaCl 공급액에서는 38.5 LMH, 57.1%, MgCl2는 37.9 LMH, 90.2%, CaSO4는 32.4 LMH, 54.6%로 각각 측정되었다.

Polyvinylidene fluoride (PVDF)의 중공사막 표면에 2번 딥코팅하여 layer-by-layer 방식으로 나노복합막을 제조하 였다. 1차 코팅에서 poly(vinylsulfonic acid)(PVSA)와 Poly(styrene sulfonic acid)(PSSA)의 농도, 이온세기(Ionic strength, IS) 등을 변화시키며 막을 제조하였으며, 2차 코팅 용액으로는 Poly(ethyleneimine) 10,000 ppm I.S = 0.3으로 고정하였다. 막의 특성평가를 위해 각각의 100 ppm NaCl, CaSO4, MgCl2, 그리고 25 ppm Methyl Orange (MO) 공급액에 대한 막의 투과도와 염배제율을 측정하였다. 코팅용액의 코팅 물질의 농도가 올라갈수록 염배제율이 상승하였으며, 본 실험 조건에서 PVSA보다 는 PSSA를 이용하여 제조한 중공사막이 염배제율이 높은 것을 확인하였다. 대표적으로 PSSA 30,000 ppm I.S = 1.0에서 중공사막을 제조하였을 때 25 ppm MO용액의 투과도 1.848 LMH, 염배제율 76.3%로 가장 높은 값을 나타내었다.

동절기에 공정육묘장에서 난방 에너지 절감과 우량묘 생산을 위해 나노탄소섬유적외선 난방등(NCFIHL, nanocarbon fiber infrared heating lamp)의 적정 전력과 설치 높이를 구명하는 것이 본 연구의 목적이다. 벤로형 유리 온실 내부에 수박 접목묘를 재배하기 위해 700과 900W NCFIHL을 육묘 베드(1.2 × 2.4m)에서 0.7, 1.0, 및 1.3m 높이로 각각 설치하였다. 수박(Citrullus lanatus (Thunb.) Manst.) ‘지존꿀’과 박(Lagenaria leucantha Rusby.) ‘선봉장’은 각각 접수와 대목으로 사용되었다. 접수와 대목은 편엽합접 방식으로 접목되었다. NCFIHL의 광도는 모든 처리에서 1μmol·m-2·s-1 이하였다. NCFIHL의 광분포는 대부분 적외선 영역에서 나타났다. 외기온도가 10oC 이하일 때 700과 900W NCFIHL을 0.7m 높이로 설치한 처리구와 900W NCFIHL을 1.0m 높이로 설치한 처리에서 야간 설정온도(20oC)를 유지하였다. 열화상 촬영에서는 900W NCFIHL을 0.7m 높이로 설치한 처리에서 가장 빨리 식물체의 온도가 올라갔다. Compactness는 700W NCFIHL을 1.3m 높이로 설치한 처리에서 우수하였다. 결과적으로 700W NCFIHL을 1.0m 이상으로 설치하는 것이 바람직하다고 판단된다.

GNPs have several excellent mechanical properties including high strength, a good young’s modulus, thermal conductivity, corrosion resistance, electronic shielding, etc. In this study, CF/GNP/Epoxy composites were manufactured using GNP weight ratios of 0.15 wt%, 0.3 wt%, 0.5 wt%, 0.7 wt% and 1 wt%. The composites were manufactured with a mechanical method (3-roll-mill). Tensile, impact and wear tests were performed according to ASTM standards D3039, D256 and D3181, respectively. The results show that the CF/GNP0.3wt%/Epoxy composites have good mechanical properties, e.g., tensile strength and impact and wear resistance. In this study, both carbon fabric and GNPs were used as reinforcements in the composites. The mechanical properties increased and weight loss decreased as the GNP content in the resin films was increased.

Poly (vinylidene fluoride) (PVDF)의 소수성 중공사막 표면에 계면중합하여 복합막을 제조하였다. Piperazine (PIP)과 trimesoyl chloride (TMC)의 농도변화, polyethylene glycol (PEG)의 함량변화에 따라 막을 제조하였으며, 막의 특성평가를 위해 100 ppm의 NaCl, CaSO₄, MgCl₂ 용액과 NaCl과 CaSO₄를 혼합하여 제조한 300 ppm의 공급액에 대한 막의 투과도와 배제율을 알아보고자 하였다. TMC를 사용하여 계면중합하였을 때 막의 투과도와 배제율이 가장 높게 나타났으며, 0.1~1 wt%로 TMC 농도를 변화시켜 가며 실험을 수행한 결과 0.1 wt%일 때 NaCl 100 ppm에 대해 투과도 48.3 LMH (L/m²·hr)와 배제율 59%로 가장 높은 값을 나타내었다. 또한, 투과도를 향상시키기 위해 annealing처리와 piperazine에 PEG를 첨가하여 실험을 수행하였다. 실험결과 처리하지 않은 막에 비해 투과도는 전체적으로 향상되는 모습을 나타냈지만배제율이 감소하는 경향을 나타내었다.

The electrospinning process was established as a promising method to fabricate nano and micro-textured scaffolds for tissue engineering applications. A BCP-loaded PCL micro-textured scaffold thus can be a viable option. The biocompatibility as well as the mechanical properties of such scaffold materials should be optimized for this purpose. In this study, a composite scaffold of poly (ε-caprolactone) (PCL)-biphase calcium phosphate (BCP) was successfully fabricated by electrospinning. EDS and XRD data show successful loading of BCP nano particles in the PCL fibers. Morphological characterization of fibers shows that with a higher loaded BCP content the fiber surface was rougher and the diameter was approximately 1 to 7 μm. Tensile modulus and ultimate tensile stress reached their highest values in the PCL- 10 wt% BCP composite. When content of nano ceramic particles was low, they were dispersed in the fibers as reinforcements for the polymer matrix. However, at a high content of ceramic particles, the particles tend to agglomerate and lead to decreasing tensile modulus and ultimate stress of the PCL-BCP composite mats. Therefore, the use of nano BCP content for distribution in fiber polymer using BCP for reinforcement is limited. Tensile strain decreased with increasing content of BCP loading. From in vitro study using MG-63 osteoblast cells and L-929 fibroblast like cells, it was confirmed that electrospun PCL-BCP composite mats were biocompatible and that spreading behavior was good. As BCP content increased, the area of cell spreading on the surface of the mats also increased. Cells showed the best adherence on the surface of composite mats at 50 wt% BCP for both L-929 fibroblast-like cells and MG-63 osteoblast cell. PCL- BCP composites are a promising material for application in bone scaffolds.

This paper deals with the effects of the surfactant and preplate process (sensitization and activation) on electroless copper plating on carbon nano-fiber (CNF). Ultrasonic irradiation was applied both during dispersion of CNF and during electroless plating containing preplate process. The dispersion of CNF and flatness of the plated copper film were discussed based on the changes in surfactant concentration and preplate process time. It was clearly shown that high concentration of surfactant and long time of preplate process could promote the agglomeration of CNF and uneven copper plating on CNF.

장미 생산농가의 대부분은 겨울철 난방비가 생산비의 가장 큰 몫을 차지한다. 요즘과 같은 고유가 시대에 농가의 부담을 줄이기 위하여 난방비 절감율이 높은 난방시스템에 대한 연구를 수행하였다. 복사열을 이용한 적외선 등 난방의 경우 식물체와 같은 물체를 먼저 가열하여 주변의 기온이 올리는 방식으로 빠르게 온도를 높일 수 있고 경유를 이용한 난방방식에 비해 비용이 절감되는 장점이 있다. 농가에 설치된 나노탄소 섬유 적외선 등 난방시스템의 현지조사를 실시하여 난방효과 및 난방비 절감율을 분석하고, 나노탄소섬유 적외선 등 난방시스템과 전기히터 난방시스템에서 생산된 '오렌지 플레쉬' 장미의 생육과 절화수명을 조사하였다. 나노탄소섬유 적외선 등의 경우 온실 내부 공기 설정온도가 20℃인 경우 식물체 온도는 1~2℃정도 더 높게 나타났을 뿐만 아니라 베드와 근권부 온도는 17~19℃ 정도로 유지하는 등 우수한 난방의 효과를 알 수 있었고, 전기히터 난방시스템과 온수보일러 난방시스템의 추정 난방비를 비교한 결과 난방비 절감 효과가 아주 높게 나타났다. 장미의 생육을 조사한 결과 전기히터 난방시스템에서 생육한 장미와 차이가 없었으며 화색이나 염색의 발현이 더 좋았다. 절화수명에서는 나노탄소섬유 적외선 등에서 생육한 장미가 생체중과 수분 흡수량이 높아 다소 더 길어진 절화수명을 뒷받침 해 주었다.