The autothermal reforming reaction of methane was investigated to produce hyd rogen with Ni/CeO2-ZrO2, Ni/Al2O3-MgO and Ni-Ru/Al2O3-MgO catalysts. Honeycomb metalli c monolith was applied in order to obtain high catalytic activity and stability in autothermal r eforming. The catalysts were characterized by XRD, BET and SEM. The influence of various catalysts on hydrogen production was studied for the feed ratio(O2/CH4, H2O/CH4). The O2/CH4 and H2O/CH4 ratio governed the methane conversion and temperature profile of reactor. Th e reactor temperature increased as the reaction shifted from endothermic to exothermic reactio n with increasing O2/CH4 ratio. Among the catalysts used in the experiment, the Ni-Ru/Al2O3-MgO catalyst showed the highest activity. The 60% of CH4 conversion was obtained, and th e reactor temperature was maintained 600℃ at the condition of GHSV=10000h-1 and feed ratio S/C/O=0.5/1/0.5.

A new High Frequency Induction Heating (HFIH) process has been developed to fabricate dense reinforced with Fe-Ni magnetic metal dispersion particles. The process is based on the reduction of metal oxide particles immediately prior to sintering. The synthesized /Fe-Ni nanocomposite powders were formed directly from the selective reduction of metal oxide powders, such as NiO and . Dense /Fe-Ni nanocomposite was fabricated using the HFIH method with an extremely high heating rate of . Phase identification and microstructure of nanocomposite powders and sintered specimens were determined by X-ray diffraction and SEM and TEM, respectively. Vickers hardness experiment were performed to investigate the mechanical properties of the /Fe-Ni nanocomposite.

Ni coated composite was successfully Prepared by the electroless deposition Process. The average size of Ni particles coated on the matrix powder was about 20 nm. It was hard to find any reaction compound as an impurity at interface between and Ni particles after sintering. The characterization of microstructure crystal structure and fracture behavior of the sintered body were investigated using XRD, TEM and Victors hardness tester, and compared with those of the sintered monolithic body. Many dislocations were observed in the Ni phase due to the difference of thermal expansion coefficient between and Ni phase, and no observed microcracks at their and Ni interface. In the /Ni composite, the main fracture mode showed a mixed fracture with intergranular and transgranuluar type having some ,surface roughness. The fracture toughness was slightly increased due to the plastic deformation mechanism of Ni phase in the /Ni composite.

Processing and properties of composites with Ni-Fe content of 10 and 15 wt% were investigated. Homogeneous powder mixtures of /Ni-Fe alloy were prepared by the solution-chemistry route using , and powders. Microstructural observation of composite powder revealed that Ni-Fe alloy particles with a size of 20nm were homogeneously dispersed on powder surfaces. Hot-pressed composites showed enhanced fracture toughness and magnetic response. The properties are discussed based on the observed microstructural characteristics