This study analyzes the effects of the number of angles and bends on resistance in a conductor-embroidered stitch circuit for efficient power transfer through a conductor of wearable energy harvesting to study changes in power lost through connection with actual solar panels. In this study, the angle of the conductive stitch circuit was designed in units of 30°, from 30° to 180°, and the resistance was measured using an analog Discovery 2 device. The measured resistance value was analyzed, and in the section of the angle where the resistance value rapidly changes, it was measured again and analyzed in units of 5°. Following this, from the results of the analysis, the angle at which the tension was applied to the stitch converges was analyzed, and the resistance was measured again by varying the number of bends of the stitch at the given angle. The resistance decreases as the angle of the stitch decreases and the number of bends increases, and the conductor embroidery stitch can reduce the loss of power by 1.61 times relative to general embroidery. These results suggest that the stitching of embroidery has a significant effect on the power transfer in the transmission through the conductors of wearable energy harvesting. These results indicate the need for a follow-up study to develop a conductor circuit design technology that compares and analyzes various types of stitches, such as curved stitches, and the number of conductors, so that wearable energy harvesting can be more efficiently produced and stored.

In this study, the appearance change and the heat․moisture transfer properties of knitted fabric by yarn shrinkage were examined to obtain useful data on the development of thermo-sensitive functional materials. Eleven types of knitted fabric were knitted using highly bulky acrylic-blended yarn. After shrinking the specimens using dry heat treatment, the appearance change and thickness were measured. An HEC simulator was adopted for measuring the heat․moisture transfer properties of specimens by yarn shrinkage. When holes were arranged vertically in the mesh structure, the specimens with 2,500 and 5,000 holes showed high percent change of hole area, appearance, and thickness. When holes were diagonally arranged in the mesh structure, the percent change of hole area in the specimen with 1,250 holes was larger than the one with 2,500 holes. However, the dimensional stability of the specimen with 2,500 holes was better because of its smaller appearance and thickness change. In the tuck structure, the percent change of hole area in the specimen with 625 and 416 holes was relatively large compared with the appearance and thickness change. Furthermore, the hole size in the tuck structure was smaller than that in the mesh structure but the percent change of hole area was larger. Therefore, it was proved that the tuck structure is more suitable than the mesh structure for developing thermo-sensitive functional materials. Heat․moisture transfer property test verified that the change of hole area by yarn shrinkage enabled obtaining the thermal effect due to the distinct temperature difference in the inner layer.

PET 중공필라멘트 복합 DTY(Draw Textured Yarns)와 ATY(Air-jet Textured Yarns)는 경량의 스포츠 의류를 포함한 고감성 의류용으로 많이 사용되고 있다. 본 연구는 중공섬유 복합 DTY와 ATY 복합사 직물의 수분 및 열이 동에 관계되는 쾌적특성에 중공 복합사 및 직물의 구조 특성이 어떠한 영향을 미치는 가에 대한 분석이다. 기공의 크기가 큰 중공 복합 직물의 흡수성이 우수하였고 커버팩터는 영향을 미치지 않았다. 또한 ATY사 직물이 DTY사 직물에 비해 흡수성이 우수하였다. 반면, 건조특성은 기공 사이즈가 미세한 직물이 기공사이즈가 큰 직물 보다 건조시간이 짧았으며 낮은 커버팩터와 기공 사이즈가 작은 하이멀티사 직물이 중공 복합직물에 비해 건조 특성이 우수하였다. 직물의 기공 사이즈는 공기투과도와 열전도도 특성에 가장 중요한 인자였다. 직물의 큰 기공 도는 중공 복합 직물의 기공도와 열전도도에 비선형적인 반비례 상관관계를 나타냈다.

본 연구에서는 생체모방기술을 응용하여 감성의류용 구조발색사를 방사하고, 이를 사용하여 직물을 제직 감량 가공하여 이들의 발색성 및 촉감 물성을 측정하여 감성의류용 용도의 적용성을 확인하여 다음과 같은 연구결과를 얻었다. 삼각단면을 가진 37층의 폴리에스테르와 나일론을 교호로 적층한 구조발색사의 방사조건을 확립하였으며, 이 세 가지 사의 발색성을 multi angle spectro-photometer로 확인하였다. 그리고 이 사들로 제직한 구조발색 직물 세 가지의 겉보기 색차와 반사율을 분석한 결과, 700nm에서 400nm까지의 파장에서 발색성을 확인하였다. 또한, 직물의 밀도와 조직이 다른 세 가지 구조발색 직물을 제직하고 감량 가공 처리하여 직물 역학특성치에서 촉감을 측정한 결과, 100℃, 60분 감량 처리한 시료가 최적설계(194ends/in × 105picks/in) 및 감량 조건임을 확인할 수 있었다. 그리고 감량 처리 시 온도와 처리시간 증가에 따라 감량률이 13%에서 최대 23%까지 증가함을 확인할 수 있었다. 이때 직물의 신축특성, 굽힘강성 및 전단강성은 감소하며 압축특성은 증가하는 현상을 보였다. 그리고 최적설계조건인 1번 직물시료를 100℃, 60분 감량 처리할 때 촉감이 가장 우수하며 일본 몰포 직물보다 더 우수한 촉감치를 얻었다.

The monofilament with 0.304mm of diameter was produced using a polybutylene succinate (PBS) resin, and a gill net was made by it. We investigated the impact of heat setting temperature on the mechanical properties, knot state and height of gill net. Heat treatment was carried out using the high pressure steam machine for 20 minutes at temperature of 55℃, 60℃, 70℃ and 75℃. Before heat treatment, the strength and elongation of PBS monofilament were estimated to be 48.1kg/mm2, 23.8% at unknot, 37.6kg/mm2, 18.8% at single knot, 26.6kg/mm2, 22.9% at double knot in dry condition, respectively. The strength and elongation of PBS monofilament with double knot were decreased as heat setting temperature increased, and the decreasing rate of strength was showed to be higher than that of elongation. It was not found any differences in strength and elongation of PBS monofilament yarn with double knot at the 65℃ and 70℃ of heat setting temperature by 5% significance of T-test, but there was a significant difference at the 70℃ and 75℃ of heat setting temperature. The net's height and length from leg to leg appeared no differences at the 70℃ and 75℃ of heat setting temperature. In results, it was investigated that the PBS monofilament gill net with the maximized physical properties could be manufactured at 70℃ of heat setting temperature using a high pressure steam machine for 20 minutes.

건축용 막재는 일반적으로 직포와 코팅으로 구성되며, PTFE 계열 막재는 유리섬유로 만들어진 직포에 테프론 코팅으로 구성된다. 일반적으로 PTFE 막재에 사용되는 직포에는 β-yarn이 주로 사용되며, β-yarn이 아닌 α-yarn이 사용된 막재도 점차적으로 사용되는 시점이다. 그러나 α-yarn으로 직조된 직포로 만들어진 건축용 막재의 특성에 관한 정보는 일반 막재에 비해 많이 부족한 편이다. 따라서 건축용 막재를 구성하는 직포를 만드는 원사의 굵기에 따른 막재의 역학적 특성에 대한 연구가 필요하다. 본 연구에서는 실험을 통하여 원사가 서로 다른 막재의 인장 특성을 비교 분석하고자 한다.

최근 호주의 CSIRO에서 개발된 고광택 wool 섬유인 "옵팀"® 이 수입되어 고감성의류 제조에 산업화 되고 있다. 그러나 "옵팀"® 섬유의 가격이 너무 비싸 소재수급이 원활치 못한 실정이다. 본 연구에서는 호주에서 개발되어 상용화되고 있는 기술인 Optim® wool 연신기술과는 다른 물빨래가 가능하며 광택이 있으며 낮은 생산 코스트를 가지는 소모연신사를 개발하는 것을 목적으로 한다. 이를 위해서 연신사가 개발된 연신기계를 이용하여 만들어지며 이를 사용하여 고감성직물을 제직하였다. 이들 직물시료의 여러 가지 물성을 측정하고 의류의 봉제성과 의복형성성능과 같은 의류의 특성이 분석되었다. 이 연구를 통하여 마지막 목적인 옵팀섬유와 같은 고광택을 가진 소모 연신사를 사용하여 고감성직물을 만드는 것이 이루어졌다.

Testing device was newly designed and built to measure the dynamic contact angle. The measurement was made using microscope interfaced with computerized image analysis system while the dynamic condition being controled using Instron. As specimens for the experiment, two different types of fibers, i.e., hydrophilic and hydrophobic, were prepared. In case of hydrophilic fiber, the increase of twist level gave the increase of contact angle. However, in hydrophobic yarn the increase of twist level gave the decrease of contact angle. When saline was used as a telling liquid, the increase of the concentration gave the increase of contact angle. The results rationalized clearly on the basis of known concepts could be used in designing fabric structure for the improvement of comport performance.

Random and/or periodic defects occur in all spun yarns. These irregularities can often lead to defects in finished fabric. Yarn evenness tests are used to obtain statistical data about yarn properties, such as CV%, which is useful in comparing several sets of similar data that differ in mean value but may have some commonality in relative variation. Although this statistical data is helpful in determining relative yam quality, accurate predictions of how the yarn will appear in fabric form are still difficult to obtain. As an promising alterative, wavelet analysis has been employed to localize yarn defect so as to predict the visual qualities of the fabrics.

최근 고감성 PET 사를 이용하여 생산한 PET 직물은 고감성 의류용 직물로서 많이 사용되고 있다. 이러한 고감성 의류용 PET 직물은 다양한 공정을 거치면서 장력이나 열 등의 영향을 받음으로서 사의 물성의 변화를 초래하여 감성 의류용도의 PET 직물에 많은 결점을 유발시킴으로서 직물 생산시 공정조건 설정 등의 어려움에 직면하고 있다. 이러한 고감성 의류에 치명적인 문제를 유발하는 문제점에 관한 감성사 제조시의 공정조건 변화와 관련된 연구논문은 많이 발표가 되지 못하고 있다. 따라서 본 연구에서는 국내 7개 원사 Maker의 cake내의 Denier 별 PET 사의 물성을 균일한 길이의 Layer를 설정하여 분석, 조사하고 Layer 별 물성 차이와 습·건열 열처리 온도에 따른 사의 수축률 등을 비교함으로서 감성 의류용 직물 생산에 필요한 기초 물성 Data를 제공하고 PET 사의 품질향상을 도모함으로서 최종 감성 의류용 직물 소재 개발에 기여할 수 있는 기초자료를 제공하고자 한다.

Plasma polymerization of Perfluoropropene(PFP) was carried out in a tubular type reactor. The Plasma was generated by coupling inductively under the fixed discharge power of 25W and the pressure of 100, 140, and 200 mTorr of radio frequency generator. PFP plasma polymerization thin films were deposited in acrylic yams. For 1 hours, the acrylic yams treated and untreated by PFP plasma were immersed in boiling water. Then the reduction of contraction coefficient of acrylic yams were measured respectively. As a result of this experiment, untreated acrylic yams were reduced around 23%, while treated yams were contracted about 18-2%.