A carbon fiber reinforced thermoplastic (CFRTP) was irradiated with a high energy electron-beam. As a result, the tensile strength of high-density polyethylene (HDPE)-based CFRTPs was significantly improved by gradually increasing the electron-beam dose. It was confirmed that the adhesion between CF and HDPE was improved and the surface properties of CF and HDPE were readily modified by electron-beam. It was verified from spectroscopic analysis that various oxygencontaining functional groups were formed on the surface of CF and HDPE by irradiation and we believe that strong attractive interactions took place among these functional groups at the interface of CFs and HDPE. Finally, it was conclusive that electron-beam irradiation provided two main effects on CFRTPs. One was cross-linking of thermoplastic resin for efficient load transfer from resin to CF and the other was formation of surface functional group and attractive interaction of these functional groups at the interface of fiber and matrix. These two effects showed synergetic contribution to enhance the mechanical properties of CFRTP.

Chemical cross-linking of different plant protein-based meat analogues was examined based on protein solubility of 8 different buffer solutions. The specific chemical bond and their interactions were further analyzed. Isolated soy protein (ISP), mung bean protein (MBP), peanut protein (PNP), pea protein (PP) and wheat gluten (WG) were texturized using a co-rotating twin-screw extruder at 50% moisture content. The results showed that protein solubility of meat analogues significantly decreased after extrusion, compared to their raw materials (P<0.05). The protein solubility of meat analogues increased with increasing reagent in buffer solutions. Hydrophobic interactions, hydrogen bonds, disulfide bonds and their interactions were found in the structure of meat analogues. The highest amount of covalent bond was observed in PP-meat analogues followed by ISP, WG, PNP, and the lowest MBP-meat analogues. The study demonstrated that PP are valuable raw materials for the development of meat analogue, which could promote high cross-linking bonds.

음이온 교환막은 전기투석, 전기흡착식 탈염(capacitive deionization), 연료전 지 등에서 탈염과 전기 에너지 생산에 활용될 수 있다. 가교되어 있지 않은 음 이온 교환막은 물이나 유기용매에 대해 취약하거나 내구성이 약해서 장기간 사용해야 하는 경우 멤브레인의 안정성에 문제가 될 수 있다. 본 연구에서는 폴리 페닐렌 옥사이드계 음이온 교환막과 가교제의 종류와 실험 조건에 따라 가교하고 가교된 멤브레인의 물성과 특성을 조사하였다. 가교제의 종류로는 BADGE, m-PDA, HMDA를 사용하였다. 가교제 함량에 따른 유기용매 용해 여부와 IR 특성 피크 변화를 조사하였다. 가교결합 반응속도는 HMDA>m-PDA>BADGE 가교 제 순으로 빨랐다. 가교 전후의 이온교환용량, 함수율 등을 측정하고 비교하였다. 가교된 음이온 교환막의 내화학성과 기계적 특성이 우수하였다.

본 연구에서는 다공성 폴리에틸렌 지지체를 기반으로 세 가지 가교제를 혼합 도입한 세공충진 이온교환막을 제조 하고 역 전기투석에서 멤브레인의 특성이 발전성능에 미치는 영향을 고찰하였다. 실험 결과, 분자 크기가 다른 가교제를 혼합 함으로써 이온교환막의 가교도 및 자유체적이 효과적으로 조절됨을 확인하였으며 상관 분석을 통해 멤브레인의 전기화학적 특성 및 이를 적용한 역 전기투석의 발전성능에 복합적인 영향을 미침을 알 수 있었다. 특히 세공충진 양이온 교환막은 최적 가교조건에서 상용막 대비 동등 이상의 발전 성능을 나타내었으며 음이온 교환막 또한 상용막에 근접하는 우수한 성능을 나 타내었다.

본 연구에서는 얇은 폴리에틸렌 계 다공성 필름(두께 = 25 μm)에 이오노머를 충진시킨 세공충진 이온교환막을 개발하였으며 이를 적용한 전 바나듐 레독스 흐름전지의 충방전 특성을 고찰하였다. 특히 분자 크기가 다른 가교제를 혼합함 으로써 이온교환막의 가교도 및 자유체적을 적절히 제어하여 저저항 및 저 바나듐 투과도를 나타내는 이온교환막을 제조하 고자 하였다. 실험 결과, 제조된 세공충진 이온교환막은 상용막 대비하여 동등 수준의 우수한 전기화학적 특성을 나타내었다. 또한 바나듐 이온 투과도 및 전 바나듐 레독스 흐름전지 성능 평가 실험을 통해 얇은 막 두께에도 불구하고 상용막 대비하여 낮은 바나듐 이온 투과도와 높은 충방전 효율을 나타냄을 확인하였다.

가교(cross-link)는 사슬 내 외부의 유동성 감소 및 사슬 간격 변화, 내화학성, 내가소성, 선택도 등 기체분리막의 성능을 향상시키기 위한 여러 가지 개질 방법 중 하나이다. 본 연구는 선형의 지방족 가교제를 도입하여 폴리이미드 분리 막을 제조하였고 기존 폴리이미드 분리막이 가지고 있는 기체 분리 성능보다 더욱 향상시키고자 하였다. 가교 후 지방족 가교제의 분해와 주쇄의 이미드 고리의 풀림으로 인해 가교 전 보다 열분해 온도는 감소함을 확인하였다. 또한, 가교제의 사슬길이, 가교도와는 관계없이 가교 후 기체의 확산 감소로 인한 투 과도가 감소하는 것을 확인하였다. 기체분리특성은 CH4, N2, O2, CO2에 대한 단 일 기체로 측정하였으며 CO2/CH4, O2/N2 선택도는 가교 전보다 후가 더욱 향상 된 결과를 나타내었다.

For the fabrication of the Si negative electrode in Li-ion batteries (LIBs) containing the cross-linking polymer binder, in this work, the urethane acrylate (UA) oligomer was synthesized via a simple synthetic process. The cross-linked poly(urethane acrylate) (CPUA)/carbone black (CB)/Si composite (CPUA/CB/Si composite) was fabricated through reactions between their reactive vinyl segments in the UA oligomer. Interestingly, the CPUA/CB/Si composite showed better cycle performance than the poly(vinylidene fluoride) (PVdF)/CB/Si composite (PVdF/CB/Si composite) and the polyurethane (PU)/CB/Si composite (PU/CB/Si composite). The CPUA/CB/Si composite had the best lithiation of about 2586 mAh g-1. The UA oligomer showed a good compatibility with the electrode materials and current collector after and before a curing process.

가교는 사슬 간격과 사슬 내 외부의 유동성을 감소시켜 분리막의 선택도, 내화학성 등을 증가시키는 것 과 같이 기체분리막의 성능을 향상시키기 위한 여러 방법 중 하나이다. 본 연구에서는 지방족 가교제 중 선형가교제를 사용하여 폴리이미드 분리막의 기체 분리 성능을 높이고자 하였고, 선형가교제의 알킬 길이에 따른 영향 또한 비교 분석 하였다. 가교 여부는 이미드 그룹의 특성피크 증가와 이미드 그룹의 특성피크 감소를 통해 확인하였다. 기체분리특성은 CH4, N2, O2, CO2 단일 기체에 대해서 측정하였으며 가교제 및 가교도에 관계없이 가교 후 기체의 확산 감소로 인해 네 기체 모두 투과도가 감소하였다. 반면 CO2/CH4, O2/N2 기체상의 선택도는 가교 전보다 향상된 결과를 나타내는 것을 확인하였다.

Cellulose acetate (CA) has been used for microfiltration/ultrafiltration applications because of its good solubility in common solvents. However, it is sensitive to chemical and physical degradation. Therefore, in this study, cellulose acetate was crosslinked with terephthaloyl chloride (TPC) in dimethylacetamide (DMAc) solution to complement these weakness. Cross-linking was confirmed by increasing in dope solution viscosity and FT-IR. To indicate the chemical resistance, weight loss was observed after the cross-linked CA membranes were immersed in ethanol, hexane, acetone and DMAc solvent for 24h. The physical properties were evaluated by the tensile strength. In the result of experience, effect of the degree of cross-linking by increasing of the concentration of TPC improved the chemical and physical properties of CA.

In recent decades, there has been an increasing interest in the use of carbon fiber reinforced plastic (CFRP) in aerospace, renewable energy and other industries, due to its low weight and relatively good mechanical properties compared with traditional metals. However, due to the high cost of petroleum-based precursors and their associated processing costs, CF remains a specialty product and as such has been limited to use in high-end aerospace, sporting goods, automotive, and specialist industrial applications. The high cost of CF is a problem in various applications and the use of CFRP has been impeded by the high cost of CF in various applications. This paper presents an overview of research related to the fabrication of low cost CF using polyethylene (PE) control technology, and identifies areas requiring additional research and development. It critically reviews the results of cross-linked PE control technology studies, and the development of promising control technologies, including acid, peroxide, radiation and silane cross-linking methods.

기체분리막의 성능을 향상시키기 위한 여러 개질 방법 중 가교는 사슬 간격과 사슬 내 외부의 유동성을 감소시켜 분리막의 선택도, 내화학성, 내가소성등을 증가시키는 장점을 지닌다. 본 연구에서는 선형의 지방족 가교제를 사용하여 폴리이미드 분리막의 기체 분리 성능을 향상시키고자 하였으며, 가교제의 알킬길이에 따른 영향 또한 알아보았다. 가교 여부는 이미드 그룹의 특성피크 증가와 이미드 그룹의 특성피크 감소를 통해 확인하였다. 기체분리특성은 CH4, N2, O2, CO2 단일 기체에 대해 측정하였으며 가교제 및 가교도에 관계없이 가교 후 기체의 확산 감소로 인해 네 기체 모두 투과도가 감소하였다. 반면 CO2/CH4, O2/N2 기체상의 선택도는 가교 전보다 향상된 결과를 나타내었다.

고농도의 초산수용액을 분리⋅농축하기 위해 polyacrylonitrile (PAN) 중공사 복합막을 제조한 후 투과증발 분리실험을 통해 제조된 복합막의 분리성능을 확인하였다. 제조된 중공사 복합막의 코팅여부를 알아보고자 SEM 사진을 측정하였으며 코팅두께가 3.85 µm로 균일하게 코팅된 것을 확인할 수 있었다. 또한 막의 투과성능평가 실험을 수행한 결과 가교제의 농도와 가교온도가 증가함에 따라 투과도는 감소하고 선택도는 증가하는 경향을 나타내었고, 대표적인 결과로 가교제인 glutaraldehyde 농도 13 wt%, 가교온도 140°C에서 투과도 250 g/m2⋅hr, 선택도 13의 결과를 얻을 수 있었으며, 또 다른 가교제로서 poly (acrylic acid) 농도 9 wt%, 가교온도 140°C일 때 투과도 330 g/m2⋅hr, 선택도 9의 값을 얻을 수 있었다.

최종당화산물은 환원당과 단백질, 지질 또는 핵산 사이의 당화반응에 의해서 생성되는 물질로 이 물질은 피부 노화 과정에 밀접하게 연관되어 있다고 보고되어 있다. 본 연구에서는 항산화 활성, 최종당화산물 생성 저해, 콜라겐과 최종당화산물의 교차결합 저해 및 억제, 엘라스타제 활성 저해 효능 시험을 통해서 비자나무 유박 추출물의 항노화 효과를 평가하였다. 시험 결과, 비자나무 유박 추출물은 폴리페놀과 플라보노이드를 함유하고 있으며, DPPH와 ABTS 자유라디칼을 50% 소거할 수 있는 농도는 각각 16.4 μg (Dried materials, DM)/mL과 16.7 μg DM/mL 로 관찰되었다. 또한, 비자나무 유박 추출물은 농도 의존적으로 최종당화산물 생성과 엘라스타제 활성을 저해하였고, 콜라겐과 최종당화산물의 교차결합을 저해 및 억제하 였다. 따라서 본 연구 결과를 바탕으로 비자나무 유박 추출물은 항노화 효능이 있는 화장품 소재로서 활용 가치가 있음을 확인하였다.

본 연구에서는 생체재료인 콜라겐과 합성 단량체인 아크릴아마이드를 연속가교 하여, 하이드로젤 기반의 콜라겐 겔을 제조하였다. 아크릴아마이드의 함량 및 가교 정도에 따라, 1.5 kPa에서 3.0 kPa까지 다양한 강도 (E)를 갖는 콜라겐 겔을 제조할 수 있었다. 또한, 콜라겐 겔에 다공성 기공을 도입하고 진피세포를 내부에 담지하여, 겔 강도에 따른 세포 성장 및 거동을 확인하였다. 상대적으로 강도가 높은 겔에서 세포의 성장은 느렸지만 GAG 합성 및 분비는 활성화되는 것을 확인하였다. 콜라겐 겔의 기계적 물성에 따라 세포의 성장 및 활성이 영향을 받는 것을 알 수 있었으며, 이는 향후 인공피부 제조 및 응용, 나아가 다양한 조직공학 분야의 기반 기술로 활용 가능하리라 기대된다.

The purpose of this experimental study is to carry out test for the surface finishing material of parking lot using Cross-linking agent(Zinc Oxide). The specimen was fabricated by KS F 4937, Cross-linking agent 2%, 3%, 4% is mixed in water soluble acrylic resin. As a result, bond strength of surface finishing material using Zinc oxide 4% was confirmed to be superior than surface finishing material using ordinary Acrylic resin.