This study investigates engineering characteristic of recycled aggregate concrete which incorporated various amount of recycled aggregate(0%, 30%, 50%, 100%). For the purpose of the investigation of engineering characteristic, compressive stress and air content, slump were evaluated. Evaluated results of compressive stress was shown that compressive stress and slump decreased depending on amount of recycled aggregate increased. On th other hand, air contents increased depending on amounts of recycled aggregate decreased.

In this study, the vibratory crusher was developed to develop the high quality recycled coarse aggregate for concrete. The vibratory crusher was installed on the production line of recycled aggregate and the produced recycled aggregate was compared with that from conventional crusher for evaluation of the performance of vibratory crusher and the quality of the produced recycled aggregate. The results showed that the performance of the recycled aggregate was better than conventional aggregate by 39% in water absorption ratio, 10% in absolute dry density, 31% in resistance to wearing, 14% in satisfactory particle size distribution, 41% in volume of clay ball and 32% in safety, thus showing that the quality of the recycled coarse aggregate is much improved. The microscopic observation showed that a lot of mortar, minute cracks and segregation have been removed.

In this study, the experiments were carried out in order that flexural behavior evaluated High-strength Concrete Beams reinfrced with FRP plates according ro replacement ration of recycled aggregate. As a result, maximum load was higher than existiong of unreinforced when the reinforced with FRP plates and no decrease in load about increased fo replacement ration of recycled aggregate. Some specimens was greater than ACI 440-2R referemce value.

본 연구에서는 순환골재 콘크리트의 성능에 대한 양생방법의 영향에 대하여 실험적으로 고찰하였다. 순환골재 콘크리트 제조를 위하여부순골재에 순환골재를 0, 25, 50, 75 및 100%로 대체하였으며, 증기양생한 콘크리트의 압축 및 쪼갬인장강도, 투수공극, 염소이온 침투저항성 및 건조수축을 소정의 재령에서 측정하여 수중양생한 콘크리트의 성능과 비교하였다. 실험결과에 따르면, 양생방법에 관계없이 순환골재 대체율이 증가할수록 콘크리트의 역학적 성능은 감소하였다. 한편, 초기재령에서 증기양생된 콘크리트는 수중양생된 콘크리트와 비교하여 매우 우수한 성능을 나타내었다. 그러나, 장기재령 (28일)에서 증기양생의 효과는 초기재령에 비하여 두드러지게 나타나지 않음을 알수 있다. 결론적으로, 본 연구의 범위 내에서 순환골재 콘크리트의 성능향상을 위하여 증기양생법의 적용이 유용할 것으로 판단된다.

It is expected that construction waste include a waste concrete is continuously increase each year in the future. Theamount of construction waste is a lot and according to the nature of construction waste, it does not have a seriousenvironmental pollution and hazards. Therefore it is used as recycled aggregate directly or through a simple intermediatetreatment. The purpose of this study, recycled aggregate concrete used in a building structure system. Thus this studyfigure out which physical and mechanical characteristics of recycled aggregates concrete. According to replacement levelof recycled aggregates compared with natural aggregate, examine a life cycle CO2 emission and review cost efficiencyfor the practical use of recycled aggregate concrete. The result of this study that recycled aggregate concrete decline aCO2 emission and decrease material cost when a replacement level is increase. Carbon dioxide emissions per unit volumein aggregate by dry process according to substitution ratio compared with 0%, in 30% is 0.10%, in 50% is 0.34%, in100% is 0.58% reduce. Aggregate by wet process according to substitution ratio compared with 0%, in 30% is 0.02%,in 50% is 0.20%, in 100% is 0.35% reduce.

본 연구는 순환굵은골재 콘크리트의 활용성 증대 및 규준 정립에 관한 연구의 일환으로 순환굵은골재 치환율에 따른 고강도 철근콘크리트 보의 휨 특성을 검토하고자 한다. 실험은 콘크리트 설계강도 40MPa, 50MPa, 60MPa 순환굵은골재 치환율 0%, 30%, 50%, 100%를변수로 총 12개의 실험체를 제작하여 최종 파괴 시까지 변위제어 방식에 의해 2점 가력하였다. 실험결과 천연골재를 사용한 실험체와 비교시 균열발생 및 파괴양상의 경우, 순환굵은골재를 사용한 철근콘크리트 보의 실험체는 천연골재 철근콘크리트 보 실험체에 비해 균열이 비교적 압축측까지 진전하는 특성을 보였으나 전반적으로 균열양상은 유사하게 나타났으며, KCI 설계기준식에 의한 계산값 및 실험결과의 비교결과 순환굵은골재 치환율에 관계없이 1.08~1.29로 기준값을 상회하는 것으로 나타나 순환굵은골재를 사용한 콘크리트 보의 휨 부재설계에 적용 가능할 것으로 판단된다. 따라서 순환굵은골재 활용성 증대를 위해 추가적인 실험을 통하여 순환굵은골재의 구조적 기준정립이 필요할 것으로 판단된다.

In this study, the amount of construction waste created from Demolition and reconstruction of old buildings by environmental contamination by construction waste has been raised as a social problem, according as a means to settle problems the government is being encouraged the use Recycled aggregate. However recycled aggregate has not yet been applied to structures in many cases. Due to uncertain technical verification of long-term durability, the use of recycled aggregate is being limited. Accordingly in this study, High Strength Concrete Beams use Recycled coarse Aggregate to evaluate the performance of the bending and establish national standards for structural design of recycled aggregates aims to provide the basic data.

In this study we propose an effective method, Coating processing methods, which can improve the quality of recycled aggregate relatively easily without new equipment investment and complex treatment process and verify the improved effect using the devised method, Coating processing methods. To attain the research aim we used adequately diluted silicate solution for coating and carried out several property valuation for twelve types of material with different coating method. Also we formed concrete with coated aggregates which showed the best property. In conclusion the aggregates with the method of repeated impregnation in the silicate and drying showed the most excellent quality while other coating methods also resulted in an improvement of aggregate quality but failed to meet the KS Standard. Lastly with the optimal material we could obtain the approved compressive strength from the concrete allowing it to be utilized for road facility of which standard compressive strength of design is under 24MPa.

In this study, specimens were produced to reach design standard strengths 40, 50 and 60MPa on age 28 days to evaluate the usability of high strength recycled aggregate concrete and the applicability of compressive strength by Impact Echo method and numerical analysis, and after 0, 30, 50 and 100% recycled coarse aggregates were substituted and mixed into each combination, totally 12 combinations were set. And, through compressive strength test, Impact Echo method, shock reverberation technique and numerical analysis on 1, 3, 7 and 28 days of age

이 연구에서는 순환굵은골재를 사용한 철근콘크리트 보의 휨거동을 평가한다. 이를 위하여 골재의 종류와 흡수율이 서로 다른 3개의 실험체를 제작하였다. 모든 실험체는 4점 가력을 받도록 계획하였으며, 전단의 영향이 크도록 전단경간비를 2.5로 계획하였다. 실험체의 모멘트-곡률 관계를 예측하기 위하여 인장증강효과를 고려한 비선형 휨해석을 수행하였으며, 실험체의 전체 거동을 평가하기 위하여 전단의 영향을 고려할 수 있는 비선형 유한요소해석을 수행하였다. 실험결과, 흡수율 6%의 순환굵은골재를 사용한 실험체의 휨강도와 균열특성은 천연골재를 사용한 실험체와 서로 유사함을 확인할 수 있었다. 그리고 실험결과와 해석결과를 비교한 결과, 기존 해석방법을 이용하여 순환굵은골재를 사용한 철근콘크리트 보의 거동을 타당하게 예측할 수 있음을 확인할 수 있었다.

In this study, prevention of scouring around bridge piers, used to form a fishway is applied to block of rivers occured corrosion, sometimes make significant reduction, in the life of the product due to the river's condition. Accordingly, rivers PC block by applying the GFRP Rebar with recycled aggregate was to enhance economy and increase durability.

본 연구에서는 폐콘크리트에서 발생하는 순환잔골재가 구조용 재료로서 많은 문제점이 있음을 인지하고 순환잔골재가 포함하고 있는 미분말이 강도증진 효과와 유동성을 증가 시킬 수 있다는 특성을 이용하여 자기충전 콘크리트(Self-Compacting Concrete, 이하 SCC로 표기)에 활용하게 되었다. 즉 순환잔골재가 갖는 미분말이 자기충전 콘크리트 특성인 고강도(40 MPa 이상)와 높은 유동성(JSCE 2등급)을 발현하기에 적당하여 폐콘크리트에서 발생하는 순환잔골재를 일반잔골재 대비 순환잔골재의 혼입률을 25%씩 증가시켜, 총 5수준으로 달리하여 자기충전 콘크리트에 적용하였으며, 이에 따라 굳지 않은 콘크리트의 물리적 특성, 경화한 콘크리트의 역학적 및 내구 특성을 검토하여 순환잔골재를 자기충전 콘크리트 재료로서 활용 가능성을 검토하고자 한다. 그 결과 물리적, 역학적 및 내구특성의 5수준 배합비율 중 일반잔골재 대비 순환잔골재는 50% 혼입률까지 적용 가능하다는 결론을 얻었으며, 그 이상의 혼입률에서는 오히려 성능저하가 발생한다는 것을 알 수 있었다. 또한 실생활에서의 적용 가능성을 알아보기 위한 실구조물의 적용성이 차후 검토 되어야 할 것으로 판단된다.

본 논문은 순환골재를 보강토 옹벽의 뒷채움재로 활용 가능한지 알아보기 위한 연구이다. 순환골재는 건설폐기물인 폐콘크리트에서 얻어지는 재활용재료로 천연골재에 비하여 1/3~1/5로 가격이 저렴하며 천연자원 고갈 및 환경파괴 문제에 대처할 수 있다. 현재까지 보조기층재료 정도로 제한적으로 적용되어 왔으나, 급속하게 증가하는 건설폐기물의 재활용 필요성이 계속적으로 대두되고 있다. 따라서 본 연구에서는 순환골재의 뒷채움재 활용성을 알아보기 위하여 현장에서 지오그리드형 보강재 내시공성 시험을 실시하고 보강재의 손상도 검사를 실시하였다. 현장 내시공성 시험에 사용된 순환골재 시료의 최대 건조밀도는 1.88g/㎤, 최적함수비는 11.3% 정도로 나타났으며, 상대다짐도 95%이상으로 다짐을 실시하였다. 또한, 실험에 사용된 지오그리드 면적은 12㎡(4m×3m)이었다. 내시공성 시험전 지오그리드에 대한 인장강도시험을 10회 실시한 결과, 평균인장강도는 80.5kN/m이었으며 내시공성 시험후에 대한 인장강도는 평균 74.5kN/m로 나타나, 강도감소율은 7.5%로 내시공성 감소계수는 1.1로 기준치 1.1~3을 만족하였다. 따라서 지오그리드형 보강재에 대한 내시공성 시험결과, 보강토 옹벽에 지오그리드형 보강재 사용시 순환골재를 뒷채움재로 활용 가능한 것으로 나타났다.

이 연구에서는 나선철근으로 횡구속된 순환골재 콘크리트의 구조적 거동을 평가하였다. 주요 실험변수는 골재의 종류와 나선철근의 철근비로 계획하였다. 총 18체의 실험체를 제작하였으며, 실험체의 직경과 높이는 각각 150mm와 300mm이었다. 실험체는 사용된 굵은 골재의 종류에 따라 2가지로 구분할 수 있으며, 나선철근의 철근비는 0%에서 1.75%까지 변화하도록 계획하였다. 실험체의 축방향 및 횡방향 변형을 측정하기 위하여, 6개의 LVDT를 실험체에 부착하였다. 또한 나선철근의 변형률을 측정하기 위하여 스트레인 게이지를 120도 간격으로 나선철근에 부착하였다. 실험결과로부터, 나선철근으로 횡구속된 순환 골재콘크리트의 구조 성능은 나선철근의 철근비와 관계없이 천연골재 콘크리트와 서로 유사함을 확인하였다.

고로슬래그 미분말을 순환골재 모르타르 및 콘크리트의 제조에 활용할 경우, 순환골재에서 용출된 Ca(OH)2가 고로슬래그에 대한 자극제 역할을 수행하여 수화반응을 개선할 수 있을 것으로 판단되고 고로슬래그를 통해 알칼리 저감 효과를 얻을 것으로 예상되어 본 연구를 진행하게 되었다. 그 결과 고로슬래그 미분말을 혼입․사용한 순환 잔골재 모르타르는 재령 3일에서는 고로슬래그 혼입율에 따라 강도가 감소하는 결과를 나타냈다. 이는 고로슬래그의 수화반응이 일어나지 않았기 때문으로 판단되며 또한, 순환 잔골재 혼입률에 관계없이 고로슬래그 미분말의 혼입률이 증가함에 따라 재령 3일 측정한 수화활성도도 저하되는 것으로 나타났다. 재령 7일에서는 순환 잔골재에서 용출된 수산화칼슘(Ca(OH)2)이 자극제 역할을 수행하여 고로슬래그 미분말을 혼입한 배합의 압축강도 발현이 천연 잔골재를 사용한 모르타르보다 서서히 증가하는 결과를 보이기 시작하였으며 이로 인해 재령 7일 측정한 고로슬래그 미분말을 단계별로 혼입한 배합의 수화활성도가 고로슬래그를 혼입하지 않은 배합보다 높아지는 것으로 나타났다. 재령 28일에서는 고로슬래그 미분말 혼입률 30% 배합에서는 고로슬래그의 수화반응으로 인해 천연 잔골재를 사용한 배합보다 높은 압축강도를 보이기 시작하였으며 이때 측정한 수화활성도는 천연 잔골재를 사용한 배합과 특별한 차이를 보이지 않았으며, 이는 지속적으로 수산화칼슘(Ca(OH)2)이 공급되지 못하였기 때문으로 판단된다.

폐콘크리트로부터 생산된 순환골재의 사용은 환경보존과 자원의 재활용 관점에서 매우 유용하며, 순환골재 콘크리트에서 압축, 인장, 휨 및 부착강도, 탄성계수 등이 중요한 기계적 특성요소로 작용하게 된다. 특히 압축을 받는 순환골재 콘크리트의 응력-변형률 관계 및 파괴진전 양상 규명은 순환골재 콘크리트를 사용한 구조물 설계 및 수치해석 등 이론적 연구에서도 매우 중요한 의미를 가진다. 따라서 본 연구에서는 순환골재 콘크리트의 파괴진전특성을 규명하기 위하여 압축하중을 받는 콘크리트의 미세균열 등 손상특성을 검출하기 위하여 AE 기법을 사용하였다. 압축거동특성 및 AE 신호특성을 분석한 결과, 순환굵은골재 콘크리트의 균열 및 파괴거동은 천연 및 순환잔골재를 사용한 콘크리트와 상이한 것으로 나타났다.

본 연구는 재생굵은골재를 이용한 콘크리트의 성능을 개선하기 위하여 SBR 라텍스를 활용하여 재생골재 콘크리트를 제조하고, 유동성과 역학적 성능 및 건조수축에 대하여 검토하였다. 실험결과 SBR 라텍스를 6%정도 혼입하면 재료분리에 저항하는 유동성을 확보할 수 있고, 압축강도 증진 및 휨강도 개선에 큰 효과가 있는 것을 알 수 있었다. 또한 건조수축의 감소에 우수한 재생골재 콘크리트를 제조할 수 있을 것으로 판단된다.

기존 연구에서 살펴보면, 철근콘크리트구조물에 발생한 화재로 인해 경화된 시멘트 페이스트와 골재의 수축과 팽창의 차이에 따라 조직이 와해되고, 열응력에 의해 균열이 발생하여 내구성이 저하한다. 그래서 성능저하의 정확한 진단은 일반적인 콘크리트구조물에서 방화성능저하의 매커니즘에 관한 기초가 요구되며, 고온에 노출된 콘크리트의 특성에 대한 기초 정보와 데이터는 성능저하의 정확한 진단을 위해 필요하다. 따라서, 본 연구는 다양한 콘크리트 시험체를 제작하여, 고온 환경에서 노출시켜, 폭열을 관찰하고, 공학적인 특성을 평가함으로서 화재피해를 입은 콘크리트구조물 성능저하의 빠르고 정확한 진단을 위한 기초적인 데이터를 제공하고자 한다.