PURPOSES: This paper presents the noise reduction effect of asphalt concrete pavement using steel slag aggregate. METHODS: Steel slag aggregates induce various mechanical effects because of their high stiffness and specific gravity. It is also known that the noise reduction effect is due to its high specific gravity and porous nature. In this study, the noise reduction in a steel slag asphalt concrete pavement section was measured and analyzed. RESULTS : On average, an asphalt concrete pavement with steel slag reduces road traffic noise by about 2 dB(A). In addition, the analysis of sound pressure levels by frequency showed lower sound pressure levels in steel slag asphalt concrete pavement than general HMA in all frequency ranges (from low to high frequencies). An analysis of the benefits with regard to noise, by assuming a road-traffic noise reduction of 2 dB(A) with asphalt concrete pavement using steel slag, shows that the noise abatement cost approach can save 1.6 million won a year over soundproof wall costs. In addition, the noise damage cost approach results in cost savings (with regard to noise) of between 19 and 60 million won per year depending on the population density. CONCLUSIONS: The use of steel slag aggregate as an asphalt concrete mixture material not only improves the mechanical performance but also has a noise reduction effect. It is expected that the steel slag asphalt concrete pavement can reduce the environmental burden by utilizing resources and provide a safer and more comfortable pavement condition to the road users.

Furnace slag powder used currently in Korea needs to add special functions in response to the increase of large-scale projects. In addition, it is advantageous in that it has a lower hydration heat emission rate than ordinary Portland cement and improves properies such as the inhibition of alkali aggregate reaction, watertightness, salt proofness, seawater resistance and chemical reslstance. However, furnace slag powder is not self-hardening, and requires activators such as alkali for hydration. Accordingly, if recycled fine aggregate, from which calcíum hydroxide is generated, and furnace slag, which requires alkali stimulation, are used together they play mutually complementary roles, so we expect to use the mixture as a resource-recycling construction material. Thus the present study purposed to examine the properties and characteristics of furnace slag powder and recycled aggregate, to manufacture recycled fine aggregate mortar using furnace slag and analyze its performance based on the results of an experiment, to provide materials on mortar using furnace slag as a cement additive and recycled fine aggregate as a substitute of aggregate, and ultimately to provide basic materials on the manufacturing of resource-recycled construction materials using binder and fine aggregate as recycled resources.

본 연구는 포장재로서 투수콘크리트의 실질적인 현장적용을 위한 자료제시와 성능향상 방안을 도출하기 위하여 슬래그골재와 플라이애시의 혼입률에 따른 포장용 투수콘크리트의 역학적 특성을 평가하였다. 시험결과, 포장용 투수콘크리트의 공극률 및 투수계수는 슬래그골재의 혼합비율이 증가함에 따라 증가하고 플라이애시 혼입률 증가에 의하여 감소하는 경향을 나타내었으며 국내 포장용 투수콘크리트에 관한 규정(8% 및 0.01cm/sec)을 만족하였다. 압축강도 및 휨강도는 슬래그골재의 혼입률이 증가함에 따라 감소하였으나, 플라이애시의 혼입률이 증가함에 따라 크게 증가하는 경향을 나타내어 플라이애시를 5% 이상 혼입하면 슬래그골재를 50% 사용한 경우에도 국내 포장콘크리트에 관한 규정(18MPa 및 4.5MPa 이상)을 만족하였다. 또한 강섬유를 0.75vol.% 혼입한 경우 사용하지 않은 경우에 비하여 휨강도가 22.8% 증가 하였다. 미끄럼저항성은 슬래그골재의 혼입률이 증가에 따라 BPN값은 증가하였고, 플라이애시의 혼입률 증가에 의해 BPN값은 감소하는 경향을 나타내었으며, 내마모성 및 동결융해저항성은 부순골재만을 사용한 경우에 비해 슬래그골재의 혼합비율이 증가함에 따라 감소하였고, 플라이애시를 10% 혼입한 경우에는 현저히 개선되어 혼입하지 않은 경우에 비하여 내마모성 및 내동해성이 각각 약 5.6% 및 14.3% 정도 개선되는 것으로 확인되었다.

Furnace slag powder used currently in Korea needs to add special functions in response to the increase of large-scale projects. In addition, it is advantageous in that it has a lower hydration heat emission rate than ordinary Portland cement and improves properties such as the inhibition of alkali aggregate reaction, watertightness, salt proofness, seawater resistance and chemical resistance. However, furnace slag powder is not self-hardening, and requires activators such as alkali for hydration. Accordingly, if recycled fine aggregate, from which calcium hydroxide is generated, and furnace slag, which requires alkali stimulation, are used together they play mutually complementary roles, so we expect to use the mixture as a resource-recycling construction material. Thus the present study purposed to examine the properties and characteristics of furnace slag powder and recycled aggregate, to manufacture recycled fine aggregate mortar using furnace slag and analyze its performance based on the results of an experiment, to provide materials on mortar using furnace slag as a cement additive and recycled fine aggregate as a substitute of aggregate, and ultimately to provide basic materials on the manufacturing of resource-recycled construction materials using binder and fine aggregate as recycled resources.

콘크리트의 수축현상은 체적 변화를 발생시키며 균열의 원인이 되어 구조물 내구성 및 안정성에 영향을 미친다. 콘크리트의 수축 에 영향을 미치는 요인은 매우 다양하며, 특히 골재는 시멘트 페이스트의 변형을 구속하여 수축 발생을 억제하기 때문에 골재의 특성은 수축 현상에서 중요하게 고려하여야 하는 부분이다. 한편, 골재 부족 현상으로 인해 천연 골재 대체재 개발 및 적용에 대한 연구가 다방면으로 진행되고 있으며 콘크리트용 골재로 사용 되는 재료도 점차 다양해지고 있다. 따라서 본 연구에서는 전기로 산화 슬래그를 굵은 골재로 사용한 콘크리 트의 수축 특성을 평가하기 위해 수축 실험을 진행하였으며, 실험 결과와 수축 예측 모델을 비교하여 기존 예측 모델의 적용성을 검토하였다. 실험 결과, 전기로 산화 슬래그를 굵은 골재로 사용함에 따라 수축량이 감소하는 결과가 나타났으며, 특히 자기수축 저감 효과가 크게 나타났다. 예측 모델과의 비교 시 건조수축과 자기수축 각각 GL2000 모델과 Tazawa 모델이 가장 유사한 예측값을 나타냈으나, 보다 정확한 예측을 위해서는 골재 및 혼화재의 물성을 고려할 수 있도록 보완이 필요한 것으로 판단된다.

철강 생산으로 인하여 부산되는 철강슬래그 역시 계속적으로 증가하여 2018년에 2,423 만톤에 이르고 있으나 고로슬래그를 제외한 철강부산물은 단순매립 등으로 재활용되고 있어 산업부산물의 유효활용을 통한 자원순환형 사회 구축 및 천연자원 고갈방지를 위해서는 다양한 활용기술 개발이 절실히 요구되고 있는 실정이다. 한편, 근래 무분별한 해양개발 및 환경오염 등으로 광대한 해양생물의 서식기반이 소실되어 수산자원의 감소현상이 심화되고 있어 이에 대한 대책이 시급한 실정이다. 따라서 본 연구에서는 다량 부산되는 복합슬래그를 천연골재 대체재료로 재활용하는 방안 제시와 해수정화가 가능한 친환경 다공질콘크리트의 배합요인별 공학적 특성 및 적용성 검토연구를 수행하였다. 배합요인별 공극률 시험결과 모든 조건에서 오차범위 2.5%이내의 결과를 나타내었다. 압축강도시험결과 최적 혼입률은 복합슬래그골재 30%, 혼입시 가장 우수한 친환경 다공질콘크리트 제조가 가능하였다. 입상인공Zeolite를 혼입함으로서 침지일수 14일에 총질소 및 총인 농도가 36.8∼54.6%까지 감소하여 입상인공제올라이트의 효과를 확인하였다.

본 연구에서는 일반 굵은골재와 더불어 전기로산화슬래그를 굵은골재로 대체하였을 때, 초기재령시기에 동결피해를 입은 콘크리트의 압축강도 특성을 평가하였다. 실험결과, 초기 재령시기에 동결 피해를 입었을 때, 전기로산화슬래그를 굵은골재로 혼입한 콘크리트의 경우에 압축강도 발현율이 일반 굵은골재를 사용한 콘크리트의 경우보다 더 감소하는 것으로 나타났다.

본 논문에서는 혼합골재 종류 변화 및 CGS 치환율에 따른 콘크리트의 내구성 특성을 분석하였다. 실험결과 CGS 치환율이 증가할수록 AE공기량의 영향으로 내동해성은 저하, 조직치밀화의 영향으로 탄산화는 지연되는 것으로 나타났다.

In this study, the fundamental properties of concrete using industrial waste as aggregate were evaluated. The concrete specimens were prepared using the steel slag as coarse aggregate and heavyweight waste glass. It was found that when the electric arc furnace slag substitution ratio increased, air contents and density also increase. However, the slump is decreased with an increase in the substitution ratio of electric arc furnace slag.

This study evaluated the fluidity and compressive strength of concrete by replacement ratio of blast furnace slag fine aggregate and ferronickel slag fine aggregate to investigate the possibility of replacing natural fine aggregate with steel slag for fine aggregate. Test results show that the use of steel slag fine aggregate improves the fluidity of concrete and compressive strength of concrete was higher than plain concrete.

In this study, as series of studies to provide how to apply coal gasification slag(CGS) as one of byproducts for high strength concrete, from a newly introduced power generation method in Korea, the possibility of using a mixed aggregate with 25 percent of CGS as a concrete residual were investigated. The results indicated that the compressive strength of concrete using CGS at early age was lower than that using CS, but compressive strength at 28 days showed similar levels of strength enhancement.

현재 많은 국가들이 천연자원이 고갈되는 문제에 직면해있고, 골재 공급이 어려운 상황이다. 이러한 상황을 고려하기 위하여 대체자원 개발을 위한 다양한 연구들이 수행되어왔다. 특히, 방사성 폐기물의 차폐를 위해 사용되는 고밀도 채움재는 많은 양의 골재를 필요로 한다. 또한, 채움재의 차폐 성능 개선을 위해서는 채움재의 밀도 증가가 요구된다. 따라서 밀도가 높은 산업폐자원의 중량콘크리트 골재로의 활용성을 확대하기 위한 기초 자료의 제공을 위해 본 연구가 수행되었다. 실험결과, OPC의 경우, 고밀도 폐유리에 의해 감소된 콘크리트의 강도는 제강슬래그를 사용해도 개선되지 않으나, 광물질 혼화재를 결합재로 사용하면 성능이 개선되었다. 따라서 고밀도 폐유리와 제강슬래그를 중량 콘크리트에 적용할 경우, 광물질 혼화재와 함께 사용하고, FA보다는 BFS를 사용하는 것이 바람직한 것으로 나타났다. 한편, 제강슬래그를 중량콘크리트의 골재로 대체할 경우, 제강슬래그의 높은 밀도로 인하여 탄성계수와 차폐성능의 개선이 가능할 것으로 판단된다.

In this paper, the mechanical properties of GGBFS concrete according to the replacement ratio of electric arc furnace oxidizing slag fine aggregate was evaluated. As the replacement rate of EOS fine aggregate increased, the amount of slump and air content decreased. In addition, EOS concrete increased the initial compressive strength, but, it tended to decrease at 28 days.

This study is a basic study to CGS, which originates from the IGCC, as fine aggregate for concrete. The study measured density, water absorption ratio, solid volume percentage for grain shape, fineness modulus, grading curve of physical properties of fine aggregate. As a result, the density and solid volume percentage for grain sheet were found to be satisfactory in the aggregate for content (KS F 2527).Water evaluation ratio, fitness modulus, and grinding curve did not meet KS standards. Therefore, it is deemed necessary to adjust the grain size through sieving in case of fineness modulus and grinding curve.

본 논문은 전기로 산화슬래그 골재를 사용하여 콘크리트를 제작하여 물리적 성능을 평가하였다. 실험은 전기로 산화슬래그 골재를 치환하여(잔골재-굵은골재) 0%-0%, 0%-100%, 50%-100%, 100%-100%으로 각 4수준으로 일반강도영역 W/C 45%와 고강도영역인 W/C 30% 의 2수준으로 제작하여 진행하였다. 굳지 않은 콘크리트에서는 공기량, 플로우 및 슬럼프, 단위용적질량 실험을 진행하였으며, 경화 콘크리트 에서는 압축강도 및 휨강도, 단위용적질량 실험을 통하여 물리적 특성을 검토하였다. 본 연구의 실험결과 전기로 산화슬래그의 혼입량이 증가 함에 따라 콘크리트의 강도 증진 효과가 나타났으며, 이는 전기로 산화슬래그 골재 내에 β-C2S로 인하여 골재 내외부에서 강도 증진 효과를 발 휘한 것으로 사료된다.

As the amount of slag generated annually increases, attempts to recycle slag as high value products are underway in order to develop an efficient resource recycling industry based on slag and derive economic benefits as well. However, the application of electric arc furnace (EOS) slag as construction material is practically limited because of the unstable substances included in it, such as free CaO.(EOS contains a small amount of free CaO, but several limitations still exist. Slag is stored for more than 3 months depending on the quantity of slag, which leads to additional economic loss. In this study, the amount of free CaO present in EOS is quantitatively evaluated to examine its qualities as a potential construction material and verify its application as concrete material. The quantitative analysis of free CaO present in EOS is performed using ethylene glycol. The free CaO contents of EOS samples were found to be below 0.5%. This satisfies the criteria specified in KS F 4571, which states that the CaO content should be below 40% and CaO/SiO2 ratio should be below 2.0. In addition, it was confirmed that free CaO content difference appears to be dependent on the aging period and storage position.

본 연구에서는 경량기포 콘크리트를 이용한 육성용 토양골재의 적용성을 평가하기 위해서 고로슬래그 기반 기포콘크리트의 총 8 배합과 인공토양골재를 제조하였다. 고로슬래그 기반 기포콘크리트 배합의 주요변수는 단위결합재량으로서 100에서 800 kg/m3으로 변화하 였다. 경량기포콘크리트는 플로우, 슬러리 및 절건 밀도와 재령별 압축강도를 측정하였으며, 파쇄된 인공토양골재는 pH, 입도분포, 투수계수, 양이온치환용량(CEC), 유기물함유량(C/N비)을 측정하였다. 측정결과 경량기포콘크리트의 플로우, 슬러리 및 절건밀도와 재령별 압축강도는 단위결합재량이 증가함에 따라 증가하였다. 경량기포콘크리트의 단위결합재량이 500 kg/m3 이상인 배합의 28일 압축강도는 4 MPa 이상이었 다. 인공토양골재에 3일 이상의 15% 희석된 제1인산암모늄의 수용액침지는 pH를 저감시키는데 효과적이었다. 또한 제조된 인공토양골재는 양이온 치환용량(CEC) 측면에서 상급으로 평가되었지만 C/N비 측면에서는 조경시방서를 만족시키지 못하였다.

Converter slag contains free-CaO and free-MgO that has a problem causing a breakdown in the water and reaction. To solve this problem, it was treated the aging process that is inserting a converter slag aggregate in water before placing concrete. As a result, aging process was very effective in the compressive strength of the concrete.

This study evaluates the material performance of slump value and compressive strength of the concrete which was made by recycled sand and blast furnace slag powder(BFSP). The main variables are replacement ratio of BFSP. As a result, it was evaluated that more detailed evaluation is needed in long-term strength development and the compensation of slump value to the replacement ratio of BFSP.